CN105885573A - Aqueous fluorescent false-proof crack finish paint - Google Patents
Aqueous fluorescent false-proof crack finish paint Download PDFInfo
- Publication number
- CN105885573A CN105885573A CN201410536230.XA CN201410536230A CN105885573A CN 105885573 A CN105885573 A CN 105885573A CN 201410536230 A CN201410536230 A CN 201410536230A CN 105885573 A CN105885573 A CN 105885573A
- Authority
- CN
- China
- Prior art keywords
- finish paint
- crackle
- paint
- aqueous
- aqueous fluorescent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an aqueous fluorescent false-proof crack finish paint. The aqueous fluorescent false-proof crack finish paint comprises an organic fluorescent pigment and an aqueous acrylic acid emulsion. The crack finish paint also comprises a film-forming auxiliary agent, a moistening dispersant, an antifoaming agent, a thickening agent, ammoniacal liquor and ethanol. The film-forming auxiliary agent is any one of propylene glycol monomethyl ether, propanediol butyl ether, and propylene glycol methyl ether acetate; the moistening dispersant is any one of sodium hexametaphosphate, sodium metasilicate, and sodium disilicate; and the antifoaming agent is any one of tributyl phosphate, dibutyl phosphate, and silicone oil. The crack finish paint has the characteristics of counterfeiting resistance and environmental protection.
Description
Technical field
The present invention relates to crackle finish paint field, particularly relate to a kind of aqueous fluorescent false proof crackle finish paint.
Background technology
Crackle paint is a kind of artistic coating, can be used for glass, door and window, cement wall surface and furniture etc. decoration and
Protectiveness application, also has application in furniture and interior decoration.At present, some of China's export America and Europe are imitated
Ancient furniture is also using crackle paint.The feature of crackle paint is mainly made up of priming paint and cracking finish paint.Priming paint can
Using any colored paint, principle is the high shrinkage shape that the surface tension difference utilizing finish paint on priming paint produces
Become crackle.But traditional solvent-borne type crackle finish paint can discharge VOC (volatile organic compound in using
Thing).Instrument after its construction cleans and also to use corresponding organic solvent, there is the pollution to environment and right
The person murder by poisoning of operating personnel.And existing crackle finish paint but lack reliably popular readily identified false proof
Defencive function, the true and false of consumer's None-identified product, it is impossible to meet people to false proof the wanting of luxury goods
Ask.
Summary of the invention
It is an object of the invention to for above-mentioned deficiency of the prior art, it is provided that one has antiforge function and ring
The aqueous fluorescent false proof crackle finish paint protected.
For reaching above-mentioned purpose, technical scheme is as follows:
A kind of aqueous fluorescent false proof crackle finish paint, including following raw material, organic fluorescent pigment 30-40%, crackle
Paint with self-cross linking type aqueous acrylic emulsion 50-60%, coalescents 0.5-1%, Ricinate 0.5-1%,
Defoamer 0.1-0.5%, thickener 0.5-1%, ammoniacal liquor 0.1-0.5%, ethanol balance.
Described crackle paint self-cross linking type aqueous acrylic emulsion is the HD253 self-cross linking type water of Hua Jinsi company
Property acrylic emulsion.
Described fluorescent pigment is Eu (TTA)3Phen、Eu(Y)(TTA)3The rare earth compounding fluorescent material such as Phen
End.
Described coalescents is any one in propylene glycol monomethyl ether, propandiol butyl ether, propylene glycol methyl ether acetate
Kind.
Described Ricinate is any one in calgon, sodium metasilicate, sodium disilicate.
Described defoamer is any one in tributyl phosphate, dibutylphosphoric acid ester, silicone oil.
Concrete processing step is:
1, by following weight ratio outfit raw material: fluorescent pigment 30-40%, crackle paint self-cross linking type aqueous third
Olefin(e) acid emulsion 50-60%, coalescents 0.5-1%, Ricinate 0.5-1%, defoamer 0.1-0.5%,
Ammoniacal liquor 0.1-0.5%, ethanol balance；
2,1/3 crackle paint self-cross linking type aqueous acrylic emulsion is added in grinding distribution machine, in stirring
In the case of (rotating speed is 2500 turns/min) be sequentially added into Ricinate and fluorescent pigment, grinding distribution
30min, obtains the mill base of fineness≤15um；
3, in the case of stirring, (rotating speed is 1000 turns/min) is sequentially added into 2/3 crackle paint self-crosslinking
Type aqueous acrylic emulsion, coalescents, defoamer, ethanol, be uniformly dispersed, and finally adjusts pH with ammoniacal liquor
Value i.e. obtains aqueous fluorescent false proof crackle finish paint for 8-9.
Compared with prior art, the medicine have the advantages that the invention provides one have antiforge function,
The aqueous fluorescent false proof crackle finish paint of environmental protection.The crack pattern of beauty, crackle paint crackle can be formed after covering with paint
Changeful, in picturesque disorder, have art stereo aesthetic feeling, and when being irradiated by ambient light, can produce
The fluorescence phenomenon of different form and aspect, along with external light stops irradiating, this fluorescence phenomenon disappears immediately, has
Well antifalse effect.Use environment-friendly materials, described aqueous fluorescent false proof crackle finish paint to possess environmental protection simultaneously
Advantage.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1: fluorescent pigment 30%, crackle paint self-cross linking type aqueous acrylic emulsion 60%, film forming helps
Agent 0.5%, Ricinate 0.5%, defoamer 0.1%, ammoniacal liquor 0.1%, ethanol balance.
Embodiment 2: fluorescent pigment 40%, crackle paint self-cross linking type aqueous acrylic emulsion 50%, film forming helps
Agent 1%, Ricinate 1%, defoamer 0.5%, ammoniacal liquor 0.5%, ethanol balance.
Embodiment 3: fluorescent pigment 35%, crackle paint self-cross linking type aqueous acrylic emulsion 55%, film forming helps
Agent 0.7%, Ricinate 0.7%, defoamer 0.3%, ammoniacal liquor 0.3%, ethanol balance.
Applicant states, above-described embodiment only for technology design and the feature of the present invention are described, its object is to
Allow person skilled in the art will appreciate that present disclosure and to implement according to this, can not be limited this with this
The protection domain of invention.Person of ordinary skill in the field it will be clearly understood that any improvement in the present invention,
The equivalence of raw material each to product of the present invention is replaced and the interpolation of auxiliary element, concrete way choice etc., all falls
Within the scope of protection scope of the present invention and disclosure.
Claims (4)
1. an aqueous fluorescent false proof crackle finish paint, it is characterised in that: include following raw material, organic fluorescence
Pigment 30-40%, crackle paint self-cross linking type aqueous acrylic emulsion 50-60%, coalescents 0.5-1%,
Ricinate 0.5-1%, defoamer 0.1-0.5%, thickener 0.5-1%, ammoniacal liquor 0.1-0.5%, ethanol
Surplus.
A kind of aqueous fluorescent false proof crackle finish paint the most according to claim 1, it is characterised in that institute
Stating coalescents is any one in propylene glycol monomethyl ether, propandiol butyl ether, propylene glycol methyl ether acetate.
A kind of aqueous fluorescent false proof crackle finish paint the most according to claim 1, it is characterised in that institute
Stating Ricinate is any one in calgon, sodium metasilicate, sodium disilicate.
A kind of aqueous fluorescent false proof crackle finish paint the most according to claim 1, it is characterised in that institute
Stating defoamer is any one in tributyl phosphate, dibutylphosphoric acid ester, silicone oil.