CN105883187B - A kind of Bunch buckle and preparation method thereof - Google Patents
A kind of Bunch buckle and preparation method thereof Download PDFInfo
- Publication number
- CN105883187B CN105883187B CN201410564247.6A CN201410564247A CN105883187B CN 105883187 B CN105883187 B CN 105883187B CN 201410564247 A CN201410564247 A CN 201410564247A CN 105883187 B CN105883187 B CN 105883187B
- Authority
- CN
- China
- Prior art keywords
- parts
- bunch buckle
- injection molding
- preparation
- constraint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses belong to a kind of Bunch buckle and preparation method thereof that can fetter a plurality of line tied up with fixture technology field.Its button two sides is equipped with multiple ringent constraint circles, and constraint circle is equipped with roughness, and the both ends of button are equipped with fixing head.Bunch buckle of the invention is arranged multiple ringent constraints circles, can fix single line in each constraint circle, and to reach separated fixation, openning shape makes line easily penetrate to fetter and enclose, and the setting of roughness is conveniently taken Bunch buckle, prevents it from falling off from hand；The preparation method of Bunch buckle of the present invention is process using the composition by developing repeatedly through straightforward procedure, and the Bunch buckle being made into takes into account the requirement of toughness and rigidity, is suitble to large-scale industrial production.
Description
Technical field
The invention belongs to tie up to use fixture technology field, and in particular to a kind of Bunch buckle and its preparation that can fetter a plurality of line
Method.
Background technique
Bunch buckle is a kind of button of bunch, is made of plastic material or metal material, and general Bunch buckle will fetter
A plurality of line after being gathered using a plurality of line, then is fixed using Bunch buckle, due to not having clamping mechanism between a plurality of line, very
It is easy kinking, random line, many occasions for needing bunch, such as company's power supply line, every line is needed all to distinguish one from the other, is guaranteed not disorderly
Line, current Bunch buckle cannot be met the requirements.
In addition, the Bunch buckle anti-pressure ability of metal material is strong, but toughness is small, easily snaps off, it is not easy to stretch, plastics material
The Bunch buckle of matter, toughness is strong, and still, hardness is small, and anti-pressure ability is weak, and a plurality of line of tying is easy to happen loosening.
Summary of the invention
The purpose of the present invention is to provide a kind of Bunch buckles and preparation method thereof, and solving current Bunch buckle cannot the same time-division
The a plurality of line of the constraint opened, the problem of resistance to compression and toughness properties cannot be taken into account.
A kind of Bunch buckle, 1 two sides of button are equipped with multiple ringent constraint circles 2, and constraint circle 2 is equipped with roughness 3, button
1 both ends are equipped with fixing head 4.
The roughness 3 is the concave-convex linear delineated using icking tool.
The preparation method of the Bunch buckle carries out in accordance with the following steps:
1) according to parts by weight, following component materials are mixed: 60-70 parts of nylon, 10-20 parts of polypropylene, herba digitariae extracts
5-8 parts of object, 1-2 parts of polyacrylamide, 1-2 parts of iron oxide, 0.5-1 parts of vegetable wax, 3-8 parts of adhesive, 2-4 parts of filler；
2) pelletizer will be put into after mixture to be granulated, the particle that partial size is 2-4mm is made, it is spare；
3) manufactured particle is put into injection molding machine, the temperature of injection molding device feeding-port is 200-210 DEG C, and the temperature of nozzle is
250-280 DEG C, melt 4-6min, then injects the material of fusing in mold by injection molding machine outlet end, injection molding；
4) concave-convex linear is depicted on constraint circle using icking tool and forms roughness.
The herba digitariae extract the preparation method comprises the following steps: herba digitariae is dried, be ground into powder, the 70% of 5-10 times of weight be added
Ethanol solution refluxing extraction 2 times, then filter residue is used water refluxing extraction 1 time, merges the filtrate of 3 extractions, be evaporated and be made.
Described adhesive is neoprene, carragheen, polyurethane, polystyrene, polyacrylate, ethene-vinyl acetate
Copolymer, one of epoxy resin and more than one.
The filler is active carbon, quartz, medical stone or foam.
The vegetable wax is Brazil wax, candelila wax, rice bran wax, sugarcane wax, laurel wax, castor bean wax, George Simond
Haze tallow, lacquer tree fat, ouricury wax, one of pesudotsuga taxifolia wax.
Beneficial effects of the present invention: multiple ringent constraint circles are arranged in Bunch buckle of the invention, can in each constraint circle
To fix single line, to reach separated fixation, openning shape makes line easily penetrate constraint circle, and the setting of roughness is conveniently taken beam
Cableties prevent it from falling off from hand；The preparation method of Bunch buckle of the present invention, using the composition by developing repeatedly, through simple
Method is process, and the Bunch buckle being made into takes into account the requirement of toughness and rigidity, is suitble to large-scale industrial production.
Detailed description of the invention
Fig. 1 is Bunch buckle structural schematic diagram of the present invention；
In figure, 1- button, 2- constraint circle, 3- roughness, 4- fixing head.
Specific embodiment
The present invention will be further described in the following with reference to the drawings and specific embodiments.
Embodiment 1
A kind of Bunch buckle, as shown in Figure 1,1 two sides of button are equipped with multiple ringent constraint circles 2, constraint circle 2 is equipped with thick
The both ends in rough portion 3, button 1 are equipped with fixing head 4.The roughness 3 is the concave-convex linear delineated using icking tool.
The Bunch buckle of the present embodiment is arranged multiple ringent constraint circles, can fix single line in each constraint circle, with
Reach separated fixation, openning shape makes line easily penetrate constraint circle, and the setting of roughness is conveniently taken Bunch buckle, prevents it from hand
In fall off.
Embodiment 2
The preparation method of Bunch buckle described in embodiment 1 carries out in accordance with the following steps:
1) according to parts by weight, following component materials are mixed: 65 parts of nylon, 15 parts of polypropylene, polyacrylamide 1.5
Part, 1.5 parts of iron oxide, 0.8 part of Brazil wax, 5 parts of neoprene, 3 parts of medical stone；
2) pelletizer will be put into after mixture to be granulated, the particle that partial size is 2-4mm is made, it is spare；
3) manufactured particle is put into injection molding machine, the temperature of injection molding device feeding-port is 200-210 DEG C, and the temperature of nozzle is
250-280 DEG C, melt 4-6min, then injects the material of fusing in mold by injection molding machine outlet end, injection molding；
4) concave-convex linear is depicted on constraint circle using icking tool and forms roughness.
The Bunch buckle anti-pressure ability of preparation is 513MPa, tensile capacity 483MPa.
Embodiment 3
The preparation method of Bunch buckle described in embodiment 1 carries out in accordance with the following steps:
1) according to parts by weight, following component materials are mixed: 65 parts of nylon, 15 parts of polypropylene, 6 parts of herba digitariae extract,
1.5 parts of polyacrylamide, 1.5 parts of iron oxide, 0.8 part of Brazil wax, 5 parts of neoprene, 3 parts of medical stone；
2) pelletizer will be put into after mixture to be granulated, the particle that partial size is 2-4mm is made, it is spare；
3) manufactured particle is put into injection molding machine, the temperature of injection molding device feeding-port is 200-210 DEG C, and the temperature of nozzle is
250-280 DEG C, melt 4-6min, then injects the material of fusing in mold by injection molding machine outlet end, injection molding；
4) concave-convex linear is depicted on constraint circle using icking tool and forms roughness.
The herba digitariae extract the preparation method comprises the following steps: herba digitariae is dried, be ground into powder, the 70% of 5-10 times of weight be added
Ethanol solution refluxing extraction 2 times, then filter residue is used water refluxing extraction 1 time, merges the filtrate of 3 extractions, be evaporated and be made.
The Bunch buckle anti-pressure ability of preparation is 614MPa, tensile capacity 588MPa.
Embodiment 4
The preparation method of Bunch buckle described in embodiment 1 carries out in accordance with the following steps:
1) according to parts by weight, following component materials are mixed: 60 parts of nylon, 10 parts of polypropylene, 5 parts of herba digitariae extract,
1 part of polyacrylamide, 1 part of iron oxide, 0.5 part of sugarcane wax, 3 parts of polyurethane, 2 parts of active carbon；
2) pelletizer will be put into after mixture to be granulated, the particle that partial size is 2-4mm is made, it is spare；
3) manufactured particle is put into injection molding machine, the temperature of injection molding device feeding-port is 200-210 DEG C, and the temperature of nozzle is
250-280 DEG C, melt 4-6min, then injects the material of fusing in mold by injection molding machine outlet end, injection molding；
4) concave-convex linear is depicted on constraint circle using icking tool and forms roughness.
The herba digitariae extract the preparation method comprises the following steps: herba digitariae is dried, be ground into powder, the 70% of 5-10 times of weight be added
Ethanol solution refluxing extraction 2 times, then filter residue is used water refluxing extraction 1 time, merges the filtrate of 3 extractions, be evaporated and be made.
The Bunch buckle anti-pressure ability of preparation is 610MPa, tensile capacity 577MPa.
Embodiment 5
The preparation method of Bunch buckle described in embodiment 1 carries out in accordance with the following steps:
1) according to parts by weight, following component materials are mixed: 70 parts of nylon, 20 parts of polypropylene, 8 parts of herba digitariae extract,
2 parts of polyacrylamide, 2 parts of iron oxide, 1 part of ouricury wax, 8 parts of polyacrylate, 4 parts of quartz；
2) pelletizer will be put into after mixture to be granulated, the particle that partial size is 2-4mm is made, it is spare；
3) manufactured particle is put into injection molding machine, the temperature of injection molding device feeding-port is 200-210 DEG C, and the temperature of nozzle is
250-280 DEG C, melt 4-6min, then injects the material of fusing in mold by injection molding machine outlet end, injection molding；
4) concave-convex linear is depicted on constraint circle using icking tool and forms roughness.
The herba digitariae extract the preparation method comprises the following steps: herba digitariae is dried, be ground into powder, the 70% of 5-10 times of weight be added
Ethanol solution refluxing extraction 2 times, then filter residue is used water refluxing extraction 1 time, merges the filtrate of 3 extractions, be evaporated and be made.
The Bunch buckle anti-pressure ability of preparation is 622MPa, tensile capacity 591MPa.
Embodiment 6
The preparation method of Bunch buckle described in embodiment 1 carries out in accordance with the following steps:
1) according to parts by weight, following component materials are mixed: nylon66 fiber part, 18 parts of polypropylene, 7 parts of herba digitariae extract,
1.8 parts of polyacrylamide, 1.2 parts of iron oxide, 0.9 part of laurel wax, 4 parts of polystyrene, 3 parts of quartz；
2) pelletizer will be put into after mixture to be granulated, the particle that partial size is 2-4mm is made, it is spare；
3) manufactured particle is put into injection molding machine, the temperature of injection molding device feeding-port is 200-210 DEG C, and the temperature of nozzle is
250-280 DEG C, melt 4-6min, then injects the material of fusing in mold by injection molding machine outlet end, injection molding；
4) concave-convex linear is depicted on constraint circle using icking tool and forms roughness.
The herba digitariae extract the preparation method comprises the following steps: herba digitariae is dried, be ground into powder, the 70% of 5-10 times of weight be added
Ethanol solution refluxing extraction 2 times, then filter residue is used water refluxing extraction 1 time, merges the filtrate of 3 extractions, be evaporated and be made.
The Bunch buckle anti-pressure ability of preparation is 613MPa, tensile capacity 583MPa.
Claims (1)
1. a kind of preparation method of Bunch buckle, which is characterized in that carry out in accordance with the following steps:
1) according to parts by weight, following component materials are mixed: 70 parts of nylon, 20 parts of polypropylene, 8 parts of herba digitariae extract, poly- third
2 parts of acrylamide, 2 parts of iron oxide, 1 part of ouricury wax, 8 parts of polyacrylate, 4 parts of quartz；
2) pelletizer will be put into after mixture to be granulated, the particle that partial size is 2-4mm is made, it is spare；
3) manufactured particle is put into injection molding machine, the temperature of injection molding device feeding-port is 200-210 DEG C, and the temperature of nozzle is 250-
280 DEG C, 4-6min is melted, is then injected the material of fusing in mold by injection molding machine outlet end, injection molding；
4) concave-convex linear is depicted on constraint circle using icking tool and forms roughness；
The herba digitariae extract the preparation method comprises the following steps: herba digitariae is dried, be ground into powder, 70% ethyl alcohol of 5-10 times of weight be added
Solution refluxing extraction 2 times, then filter residue is used water refluxing extraction 1 time, merges the filtrate of 3 extractions, be evaporated and be made；
The structure of the Bunch buckle are as follows: button (1) two sides are equipped with multiple ringent constraint circles (2), and constraint circle (2) is equipped with thick
The both ends of rough portion (3), button (1) are equipped with fixing head (4)；The roughness (3) is the concave-convex linear delineated using icking tool.