CN105860909A - New application and preparation method of adhesive for rapid adhering for sand planting - Google Patents
New application and preparation method of adhesive for rapid adhering for sand planting Download PDFInfo
- Publication number
- CN105860909A CN105860909A CN201610440952.4A CN201610440952A CN105860909A CN 105860909 A CN105860909 A CN 105860909A CN 201610440952 A CN201610440952 A CN 201610440952A CN 105860909 A CN105860909 A CN 105860909A
- Authority
- CN
- China
- Prior art keywords
- parts
- plants
- sandbinder
- sand
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the field of grinding tools and in particular relates to a new application and preparation method of an adhesive for rapid adhering for sand planting. As the adhesive for rapid adhering for sand planting, a TPU (thermoplastic polyurethane) hot melt adhesive mainly comprises the following raw components in parts by weight: 22-40 parts of TPU, 15-32 parts of rosin glycerin, 18-36 parts of polyvinyl chloride and 10-30 parts of nano calcium carbonate. The preparation method has the beneficial effects that the adhesive has the effects of optimizing the process, improving the efficiency, saving energy and reducing the cost and is environment-friendly and healthy; the prepared adhesive is solid at normal temperature, is immediately molten into adhesive coating liquid when the temperature reaches the melting point, has very good viscosity, returns to solid in a very short time when the temperature is reduced close to the normal temperature, is simple to cure, is environment-friendly and energy-saving, is convenient to operate and has a wide range of application; the time of the production process is greatly shortened and the length of production drying tunnel equipment is reduced from 100M to 2-4M, thus saving the space and the time; and the production process is simple.
Description
Technical field
The present invention relates to abrasive tool industry, plant sand agent new opplication and preparation method thereof particularly to a kind of Rapid pasting.
Background technology
Conventional sand technology of planting is that gravity plants sand and electrostatic sand-planting, and the two is respectively arranged with pluses and minuses.In implantation process of sand, binding agent is indispensable important component.Binding agent is the important materials in coated abrasive tool manufacture, abrasive particle being sticked on base material.Mostly using various kinds of resin binding agent to be used in mixed way on coated abrasive tool, and add enough fillers toughness with enhancing binding agent itself, and improve adhesive property and improve grinding performance, abrasive band typically requires addition anti-static material to improve processing characteristics.Conventional binding agent is that oiliness or water-based glue are as binding agent, its technique is: be coated on base material front by gluing machine, rolling after dehumidifying no less than 100M baking box, be dried, solidifying, enters back into 60 DEG C of constant temperature barns, can go to lower road technique after at least 48 hours.Exist following not enough: equipment is numerous and jumbled, and activity time is up to 48 hours, and production efficiency is low.
Summary of the invention
The invention aims to solve shortcoming present in prior art, and a kind of Rapid pasting proposed plants sand agent new opplication and preparation method thereof.
A kind of Rapid pasting plants sandbinder, counts by weight, main containing following raw material components: thermoplastic polyurethane 22-40 part, Colophonium glycerol 15-32 part, polrvinyl chloride 18-36 part, nano-calcium carbonate 10-30 part.
Described Rapid pasting plants sandbinder, counts by weight, main containing following raw material components: polyurethane 25-38 part, Colophonium glycerol 18-30 part, polrvinyl chloride 20-32 part, nano-calcium carbonate 15-25 part.
Described Rapid pasting plants sandbinder, counts by weight, main containing following raw material components: polyurethane 36 parts, Colophonium glycerol 22 parts, polrvinyl chloride 26 parts, nano-calcium carbonate 16 parts.
Described thermoplastic polyurethane is TPU PUR.
Described prepares the method that Rapid pasting plants sandbinder, concrete operation step is as follows: 1), thermoplastic polyurethane, Colophonium glycerol, polrvinyl chloride, nano-calcium carbonate feed particles are poured in mixing plant by weight, mechanical agitation 30-150min, make each feed particles be evenly distributed；2) by after mix homogeneously feed particles drying equipment, inserted in injection-moulding device hopper by conveying equipment；3), injection-moulding device operating temperature is set 180 DEG C-230 DEG C, make mixing raw material reach melting state, then injection-moulding device extrusion device is transported to coating or film pressing device；4), coated or film pressing device, melted mucus is coated uniformly on base material, follow-up use.
The performance characteristic of the binding agent of described preparation is as follows: hot pressing temperature 100 DEG C-150 DEG C,
Described Rapid pasting plants the production technology of sand, and concrete grammar step is as follows: 1): the coating or compound of base material；The raw material mixed in proportion is coated uniformly on base material by coating equipment, or TPU hot melt adhesive film (containing outsourcing customized TPU hot melt adhesive film) is compound on base material by equipment complex, and remove release paper；, 2): melt: through 130 DEG C of-150 DEG C of baking ovens of 4M 20 seconds-50 seconds；Make to reach to melt viscous liquid state；3): plant sand: enter and plant sand room, by planting sand device, after upper sand, in 1 point, spontaneous curing enters subsequent processing.
Described prepares the method that Rapid pasting plants sandbinder, described in be coated in base material be sponge or paper substrate or fabricbase or release paper.
Described Rapid pasting plants sandbinder application in planting sand field.
The application in planting sand field of the described TPU PUR.
To achieve these goals, present invention employs following technical scheme:
The Advantageous Effects that the present invention has in terms of existing technologies:
1. the present invention is first by modified hot melt adhesive, is called for short: TPU PUR, is successfully applied to plant sand technical field, is the great innovation of a technical field.
2. the present invention optimizes technique, raising efficiency, the saving energy, reduces cost, environment protection health；Place: save more than 60%；Efficiency: list improves more than 500% from hardening time from the point of view of angle；Energy-conservation: to carry out ratio from apparatus for production line power, original more than 400KW within being down to 50KW, energy-conservation more than 80%；Fall this: with every 1.0KG consumption, by original 30.00 yuan/drop present 16.00 yuan/.
3. the binding agent that prepared by the present invention, is solid-state under room temperature, when temperature reaches fusing point, at once melts for snearing shape liquid, and have the best viscosity, when temperature is reduced close to room temperature, recover to solid-state in very short time, solidification is simple, environmental protection, energy-conservation, easy to operate, of many uses.
4. being greatly shortened the time of production technology, by 100M, production drying tunnel device length is reduced to 2M-4M, save room and time, production technology is simple.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.
Embodiment
1
A kind of Rapid pasting plants sandbinder, counts by weight, main containing following raw material components: thermoplastic polyurethane 22 parts, Colophonium glycerol 15 parts, polrvinyl chloride 18 parts, nano-calcium carbonate 10 parts.
Described thermoplastic polyurethane is TPU PUR.
Described prepares the method that Rapid pasting plants sandbinder, concrete operation step is as follows: 1), thermoplastic polyurethane, Colophonium glycerol, polrvinyl chloride, nano-calcium carbonate feed particles are poured in mixing plant by weight, mechanical agitation 30min, make each feed particles be evenly distributed；2) by after mix homogeneously feed particles drying equipment, inserted in injection-moulding device hopper by conveying equipment；3), injection-moulding device operating temperature is set 180 DEG C, make mixing raw material reach melting state, then injection-moulding device extrusion device is transported to coating or film pressing device；4), coated or film pressing device, melted mucus is coated uniformly on base material, follow-up use.
The performance characteristic of the binding agent of described preparation is as follows: hot pressing temperature 100 DEG C.
Described Rapid pasting plants the production technology of sand, and concrete grammar step is as follows: 1), the coating or compound of base material；The raw material mixed in proportion is coated uniformly on base material by coating equipment, or TPU hot melt adhesive film (containing outsourcing customized TPU hot melt adhesive film) is compound on base material by equipment complex, and remove release paper；2): melt: through 130 DEG C of baking ovens of 4M 20 seconds；Make to reach to melt viscous liquid state；3): plant sand: enter and plant sand room, by planting sand device, after upper sand, in 1 point, spontaneous curing enters subsequent processing.
The described base material that is coated in is sponge.
Described Rapid pasting plants sandbinder application in planting sand field.
The application in planting sand field of the described TPU PUR.
Embodiment
2
A kind of Rapid pasting plants sandbinder, counts by weight, main containing following raw material components: thermoplastic polyurethane 40 parts, Colophonium glycerol 32 parts, polrvinyl chloride 36 parts, nano-calcium carbonate 30 parts.
Described Rapid pasting plants sandbinder, counts by weight, main containing following raw material components: thermoplastic polyurethane 25-38 part, Colophonium glycerol 18-30 part, polrvinyl chloride 20-32 part, nano-calcium carbonate 15-25 part.
Described Rapid pasting plants sandbinder, counts by weight, main containing following raw material components: thermoplastic polyurethane 36 parts, Colophonium glycerol 22 parts, polrvinyl chloride 26 parts, nano-calcium carbonate 16 parts.
Described thermoplastic polyurethane is TPU PUR.
Described prepares the method that Rapid pasting plants sandbinder, concrete operation step is as follows: 1), thermoplastic polyurethane, Colophonium glycerol, polrvinyl chloride, nano-calcium carbonate feed particles are poured in mixing plant by weight, mechanical agitation 150min, make each feed particles be evenly distributed；2) by after mix homogeneously feed particles drying equipment, inserted in injection-moulding device hopper by conveying equipment；3), injection-moulding device operating temperature is set 230 DEG C, make mixing raw material reach melting state, then injection-moulding device extrusion device is transported to coating or film pressing device；4), coated or film pressing device, melted mucus is coated uniformly on base material, follow-up use.
The performance characteristic of the binding agent of described preparation is as follows: hot pressing temperature 150 DEG C,
Described Rapid pasting plants the production technology of sand, and concrete grammar step is as follows: 1): the coating or compound of base material；By TPU hot melt adhesive film, containing outsourcing customized TPU hot melt adhesive film, it is compound on base material by equipment complex, and removes release paper；2): melt: through 150 DEG C of baking ovens of 4M 50 seconds；Make to reach to melt viscous liquid state；3): plant sand: enter and plant sand room, by planting sand device, after upper sand, in 1 point, spontaneous curing enters subsequent processing.
The described base material that is coated in is paper substrate.
Described Rapid pasting plants sandbinder application in planting sand field.
The application in planting sand field of the described TPU PUR.
Embodiment
3
A kind of Rapid pasting plants sandbinder, counts by weight, main containing following raw material components: thermoplastic polyurethane 25 parts, Colophonium glycerol 18 parts, polrvinyl chloride 20 parts, nano-calcium carbonate 15 parts.
Described thermoplastic polyurethane is TPU PUR.
Described prepares the method that Rapid pasting plants sandbinder, concrete operation step is as follows: 1), thermoplastic polyurethane, Colophonium glycerol, polrvinyl chloride, nano-calcium carbonate feed particles are poured in mixing plant by weight, mechanical agitation 60min, make each feed particles be evenly distributed；2) by after mix homogeneously feed particles drying equipment, inserted in injection-moulding device hopper by conveying equipment；3), injection-moulding device operating temperature is set 200 DEG C, make mixing raw material reach melting state, then injection-moulding device extrusion device is transported to coating or film pressing device；4), coated or film pressing device, melted mucus is coated uniformly on base material, follow-up use.
The performance characteristic of the binding agent of described preparation is as follows: hot pressing temperature 105 DEG C,
Described Rapid pasting plants the production technology of sand, and concrete grammar step is as follows: 1), the coating or compound of base material；Customized for outsourcing TPU hot melt adhesive film is compound on base material by equipment complex, and removes release paper；2): melt: through 140 DEG C of baking ovens of 4M 30 seconds；Make to reach to melt viscous liquid state；3): plant sand: enter and plant sand room, by planting sand device, after upper sand, in 1 point, spontaneous curing enters subsequent processing.
Described prepares the method that Rapid pasting plants sandbinder, described in be coated in base material be release paper.
Described Rapid pasting plants sandbinder application in planting sand field.
The application in planting sand field of the described TPU PUR.
Embodiment
4
Step of preparation process is with embodiment 1, and difference is: the weight portion of material component is thermoplastic polyurethane 38 parts, Colophonium glycerol 30 parts, polrvinyl chloride 32 parts, nano-calcium carbonate 25 parts.
Embodiment
5
1, step of preparation process with embodiment 2, the weight portion of material component is: thermoplastic polyurethane 26 parts, Colophonium glycerol 22 parts, polrvinyl chloride 26 parts, nano-calcium carbonate 16 parts.
Embodiment
6
Step of preparation process with embodiment 2, the weight portion of material component is: thermoplastic polyurethane 26.5 parts, Colophonium glycerol 23.5 parts, polrvinyl chloride 26.2 parts, nano-calcium carbonate 17.8 parts.
The above; only invent preferably detailed description of the invention; but protection scope of the present invention is not limited thereto; any those familiar with the art applies in the technical scope that the invention discloses; according to technical scheme and inventive concept equivalent or change in addition thereof, all should contain within protection scope of the present invention.
Claims (10)
1. a Rapid pasting plants sandbinder, it is characterised in that: count by weight, main containing following raw material components: thermoplastic polyurethane 22-40 part, Colophonium glycerol 15-32 part, polrvinyl chloride 18-36 part, nano-calcium carbonate 10-30 part.
Rapid pasting the most according to claim 1 plants sandbinder, it is characterised in that: count by weight, main containing following raw material components: polyurethane 25-38 part, Colophonium glycerol 18-30 part, polrvinyl chloride 20-32 part, nano-calcium carbonate 15-25 part.
Rapid pasting the most according to claim 1 plants sandbinder, it is characterised in that: count by weight, main containing following raw material components: polyurethane 26 parts, Colophonium glycerol 22 parts, polrvinyl chloride 26 parts, nano-calcium carbonate 16 parts.
Rapid pasting the most according to claim 1 plants sandbinder, it is characterised in that: described thermoplastic polyurethane is TPU PUR.
The most according to claim 1 prepare the method that Rapid pasting plants sandbinder, it is characterized in that: concrete operation step is as follows: 1): thermoplastic polyurethane, Colophonium glycerol, polrvinyl chloride, nano-calcium carbonate feed particles are poured in mixing plant by weight, mechanical agitation 30-150min, makes each feed particles be evenly distributed；2): after mix homogeneously feed particles drying equipment, inserted in injection-moulding device hopper by conveying equipment；3): injection-moulding device operating temperature is set 180 DEG C-230 DEG C, make mixing raw material reach melting state, then injection-moulding device extrusion device is transported to coating or film pressing device；4): coated or film pressing device, melted mucus is coated uniformly on base material, or extrudes and through automatic levelling in release paper or prolong swaging and become TPU hot melt adhesive film, follow-up use.
The method of sandbinder is planted in stickup the most according to claim 4, it is characterised in that: the performance characteristic of the binding agent of described preparation is as follows: hot pressing temperature 100 DEG C-150 DEG C.
Rapid pasting the most according to claim 1 plants the production technology of sand, it is characterized in that, concrete grammar step is as follows: 1): the coating or compound of base material: be coated uniformly on base material by coating unit by the raw material mixed in proportion, or be compound on base material by equipment complex by TPU hot melt adhesive film, and remove release paper；2): melt: through 130 DEG C of-150 DEG C of baking ovens of 4M 20 seconds-50 seconds；Make to reach to melt viscous liquid state；3): plant sand: enter and plant sand room, by planting sand device, after upper sand, in 1 point, spontaneous curing enters subsequent processing.
The most described prepare the method that Rapid pasting plants sandbinder, it is characterised in that being coated in base material described in: is sponge or paper substrate or fabricbase or release paper.
Rapid pasting the most according to claim 1 plants sandbinder application in planting sand field.
The TPU PUR the most according to claim 4 application in planting sand field.