CN105860881A - Removable adhesive - Google Patents
Removable adhesive Download PDFInfo
- Publication number
- CN105860881A CN105860881A CN201610464506.7A CN201610464506A CN105860881A CN 105860881 A CN105860881 A CN 105860881A CN 201610464506 A CN201610464506 A CN 201610464506A CN 105860881 A CN105860881 A CN 105860881A
- Authority
- CN
- China
- Prior art keywords
- glue
- solvent
- factice
- acrylic acid
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a removable adhesive which is composed of the following raw materials in percentage by weight: 80-90% of acrylic acid factice, 0.5-4% of curing agent and 10-20% of solvent. In order to solve the above problems, the invention provides a removable adhesive, so that the adhesive sticker produced from the removable adhesive can be recycled, thereby lowering the input cost, stabilizing the properties and being simple to operate.
Description
Technical field
The present invention relates to adhesive sticker production technical field, be specifically related to a kind of formula moving glue.
Background technology
Adhesive sticker is also self-adhesive label material, is that the back side scribbles with paper, thin film or special material as fabric
Adhesive, to be coated with the silicon protection sheet a kind of composite as base stock.Existing adhesive sticker is raw by glue configuration
After output is come, can not recycle through using, waste resource, increase cost.
Summary of the invention
The present invention solves the problems referred to above, it is provided that a kind of formula moving glue, be allowed to the adhesive sticker produced
Can recycle, reduce input cost, stable performance, simple to operate.
The technical solution of the present invention: a kind of formula moving glue, is made up of following raw material, acrylic acid oil
Glue, firming agent and solvent, the part by weight of described raw material is: acrylic acid factice 80%-90%, firming agent
0.5%-4%, solvent 10%-20%.
As the further optimization of this programme, the part by weight of described raw material is: acrylic acid factice 80%, solidification
Agent 0.5%, solvent 10%.
As the further optimization of this programme, the part by weight of described raw material is: acrylic acid factice 90%, solidification
Agent 4%, solvent 20%.
As the further optimization of this programme, the part by weight of described raw material is: acrylic acid factice 85%, solidification
Agent 2.2%, solvent 15%.
Further optimization as this programme, it is characterised in that add auxiliary agent, described auxiliary agent in described formula
Part by weight be 1.5%.
As the further optimization of this programme, described auxiliary agent is normal heptane.
As the further optimization of this programme, described solvent is toluene.
As the further optimization of this programme, described firming agent is XR-100 aziridine crosslinker.
As the further optimization of this programme, the described preparation method moving glue is to control temperature at 5 DEG C-40 DEG C
Being stirred above-mentioned raw materials, mixing time controls at 15 minutes about-30 minutes, and room temperature is placed 20 minutes
Can use.
Beneficial effects of the present invention:
1. inventive formulation is simple, configuration is easy, and the adhesive sticker being allowed to produce can weigh after using
Multiple recycling, reduces and pollutes, reduction input cost, and the adhesive sticker produced, and stable performance is viscous
Property is good;2. the present invention is by adding auxiliary agent, can be finely adjusted moving glue, meets different client to glue
The demand of water, simple to operate.
Detailed description of the invention
All features disclosed in this specification, or disclosed all methods or during step, except mutually
Beyond the feature repelled mutually and/or step, all can combine by any way.
Any feature disclosed in this specification (including any accessory claim, summary), unless especially
Narration, all can be by other equivalences or have the alternative features of similar purpose and replaced.That is, unless chatted especially
Stating, each feature is an example in a series of equivalence or similar characteristics.
Embodiment 1:
A kind of formula moving glue, is made up of the part by weight of following raw material: acrylic acid factice 80%-90%, solid
Agent 0.5%-4%, solvent 10%-20%, auxiliary agent 1.5%.
Collocation method: controlling temperature and be stirred above-mentioned raw materials at 5 DEG C-40 DEG C, mixing time controls 15
Minutes about-30 minutes, room temperature was placed and can be used for 20 minutes.
Embodiment 2:
A kind of formula moving glue, is made up of the part by weight of following raw material: acrylic acid factice 80%, firming agent
0.5%, solvent 10%, auxiliary agent 1.5%.
Collocation method: controlling temperature and be stirred above-mentioned raw materials at 5 DEG C-40 DEG C, mixing time controls 15
Minutes about-30 minutes, room temperature was placed and can be used for 20 minutes.
Embodiment 3:
A kind of formula moving glue, is made up of the part by weight of following raw material: acrylic acid factice 90%, firming agent
4%, solvent 20%, auxiliary agent 1.5%.
Collocation method: controlling temperature and be stirred above-mentioned raw materials at 5 DEG C-40 DEG C, mixing time controls 15
Minutes about-30 minutes, room temperature was placed and can be used for 20 minutes.
Inventive formulation is simple, configuration is easy, and the adhesive sticker being allowed to produce can repeat after using
Recycle, reduce and pollute, reduce input cost, and the adhesive sticker produced, stable performance, viscosity
Good.
The basic teaching of the present invention is illustrated, and for having the people of the usual technical ability in this area, many is prolonged
Stretching and change will be aobvious and the person of being apparent from.Due to description disclose the present invention can without departing from the present invention spirit or
Other particular form of general characteristics is implemented, and some forms of these particular forms have been noted, institute
With, description embodiments of the disclosure should be regarded as illustrating rather than restriction.The scope of the present invention is by appended
Claim defines rather than is defined by described above, for falling into the equalization of claim
Within the scope of being changed of meaning and scope will be included in it.
Claims (9)
1. the formula that can move glue, it is characterised in that be made up of following raw material, acrylic acid factice, firming agent and
Solvent, the part by weight of described raw material is: acrylic acid factice 80%-90%, firming agent 0.5%-4%, solvent
10%-20%.
A kind of formula moving glue the most according to claim 1, it is characterised in that the weight ratio of described raw material
Example is: acrylic acid factice 80%, firming agent 0.5%, solvent 10%.
A kind of formula moving glue the most according to claim 1, it is characterised in that the weight ratio of described raw material
Example is: acrylic acid factice 90%, firming agent 4%, solvent 20%.
A kind of formula moving glue the most according to claim 1, it is characterised in that the weight ratio of described raw material
Example is: acrylic acid factice 85%, firming agent 2.2%, solvent 15%.
5. according to one of any a kind of formula moving glue described in claim 1-4, it is characterised in that described in join
Adding auxiliary agent in side, the part by weight of described auxiliary agent is 1.5%.
One the most according to claim 5 can move glue formula, it is characterised in that described auxiliary agent is normal heptane.
7. according to one of any a kind of formula moving glue described in claim 1-4, it is characterised in that described molten
Agent is toluene.
8. according to one of any a kind of formula moving glue described in claim 1-4, it is characterised in that described solid
Agent is XR-100 aziridine crosslinker.
One the most according to claim 1 can be moved glue and be prepared, it is characterised in that the described preparation side moving glue
Method is, controls temperature and is stirred above-mentioned raw materials at 5 DEG C-40 DEG C, and mixing time controls at 15 minutes-30
About minute, room temperature is placed and can be used for 20 minutes.