CN105860453A - Outdoor sunlight-resistant pbt material and preparation method thereof - Google Patents
Outdoor sunlight-resistant pbt material and preparation method thereof Download PDFInfo
- Publication number
- CN105860453A CN105860453A CN201610231210.0A CN201610231210A CN105860453A CN 105860453 A CN105860453 A CN 105860453A CN 201610231210 A CN201610231210 A CN 201610231210A CN 105860453 A CN105860453 A CN 105860453A
- Authority
- CN
- China
- Prior art keywords
- mentioned
- powder
- weight
- zinc oxide
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an outdoor sunlight-resistant pbt material. The outdoor sunlight-resistant pbt material is prepared from, by weight, 0.2-0.7 part of alkylphenol ethoxylates, 70-80 parts of caprolactam, 10-13 parts of attapulgite, 1-1.4 parts of zinc acetate, 2-3 parts of gamma-aminopropyltriethoxysilane, 18-20 parts of oxalic acid, 300-370 parts of polybutylene terephthalate, 4-6 parts of sodium myrastate, 2-4 parts of polyethyleneimine, 1-2 parts of 2-aminoethyl heptadeceny-limidazoline, 1-2 parts of sodium N-lauroylsarcosinate, 0.1-0.2 part of 2-hydroxy-4-n-octyloxybenzophenone and 3-4 parts of wollastonite powder. The material has a good sunlight-resistant property, can be widely used for outdoor materials and is long in service life and good in durability.
Description
Technical field
The present invention relates to field of material technology, particularly relate to a kind of outdoor Sun-proof pbt material and preparation method thereof.
Background technology
ZnO was widely studied in the last few years as a kind of photocatalyst-type anti-biotic agent, and it generates strong oxygen under photocatalysis
The active function groups of the property changed kills antibacterial.It has nontoxic, nonirritant, good stability, and difficult decomposition under high temperature, timeliness is long
For a long time, cheap, the advantage such as aboundresources, have broad application prospects；
The common carrier being presently used for loaded optic catalyst mainly has CNT (CNTs) and activated carbon, mesoporous material, Linesless charcoal
Black and zeolites etc. can obtain the nano-particle of size uniform by load, in turn ensure that functional nano-composites simultaneously
High stability.Nano-photocatalyst/porous mineral compound system, i.e. assembles Nano semiconductor photocatalyst or loads to mineral
In the hole of material or on surface, not only solve the agglomeration traits of nano-photocatalyst granule, reduce its consumption, also simultaneously
Utilize the high-specific surface area of porous mineral, strong characterization of adsorption to realize in water or the targeting enrichment of pollutants in air, urged by light
Agent is more effectively carried out light degradation；
Therefore nano-photocatalyst/porous mineral compound system can improve the disposal efficiency of catalysis material, reduces again
Its consumption and preparation cost, accomplished to have complementary advantages, and this support type composite had both remained the character of nano-particle itself,
Closed by the interface between nano-particle and matrix simultaneously, some new assembly effects can be produced again, make whole complex
System shows as distinctive synergistic enhancing effect, thus significantly improves the functional characteristic of material, but presently used carrier is the most all deposited
In the shortcoming such as expensive, surface activity point is low, therefore, research and develop a kind of novel carrier material and be the most increasingly subject to
The attention of scholars, find a kind of cheap, surface activity is high and the novel carriers of good stability seems the most necessary；
Polyamide due to its good mechanical property, barrier property, anti-wear performance, acid-proof alkaline and good processing characteristics,
Increasingly become indispensable material as engineering plastics and non-fibre material, its application relate to auto parts and components, cord fabric,
The fields such as tyre equatorial, electronic apparatus, household supplies, consumption becomes kinds most in polyamide product.But applying
Cheng Zhong, the polar group of polyamide 6 material makes it be prone to absorb moisture, causes dry state and low temperature impact strength is low, product
Easily there is the phenomenon such as plastic deformation, serious wear in product poor stability, friction, additionally, uses as mine engineering plastics, do not possess
Antistatic property, easily produces gas explosion etc., thus affects the stability of its product size, antiwear and friction reduction property and electrically
Can, which has limited its range of application；
Attapulgite, as a kind of natural nanometer fibrous clay mineral, has 2:1 type layer chain structure, in its crystal structure
There is a large amount of pore passage structure, and have that specific surface area is big, surface activity site is many, energy of adsorption
By force, excellent biocompatibility and the chemically and thermally feature such as stability, be a kind of economical and practical carrier material, giving birth to
The aspects such as thing, environment, new material have broad application prospects；Therefore it is an object of the invention to nano-photocatalyst with recessed
Convex rod stone is effectively combined, and is the most effectively distributed in polyamide, prepares a kind of novel composite.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of outdoor Sun-proof pbt material and
Preparation method.
The present invention is achieved by the following technical solutions:
A kind of outdoor Sun-proof pbt material, it is made up of the raw material of following weight parts:
Alkylphenol polyoxyethylene 0.2-0.7, caprolactam 70-80, attapulgite 10-13, zinc acetate 1-1.4, γ-aminopropyl
Triethoxysilane 2-3, ethanedioic acid 18-20, polybutylene terephthalate (PBT) 300-370, myristic acid soda soap 4-6, poly-second
Alkene imines 2-4,2-aminoethyl 17 alkenyl imidazoline 1-2, N-sodium lauroyl sarcosine 1-2,2-hydroxyl-4-n-octyloxy hexichol
Ketone 0.1-0.2, wollastonite in powder 3-4.
The preparation method of a kind of described outdoor Sun-proof pbt material, comprises the following steps:
(1) take above-mentioned myristic acid soda soap, join in the deionized water of its weight 20-27 times, stir, drip 4-
The sodium hydroxide of 6mol/l, regulation pH is 10-13, adds above-mentioned wollastonite in powder, rises high-temperature and is 40-50 DEG C, insulated and stirred 20-
30 minutes, filter, precipitation is washed, mixes with attapulgite after drying, calcine 1-2 hour at 300-350 DEG C, join 3-
Being acidified 3-5 hour in the hydrochloric acid of 5mol/l, souring temperature is 20-35 DEG C, filters, precipitation is washed 3-4 time, at 80-90 DEG C
It is dried, wears into fine powder, obtain activation attapulgite powder；
(2) take the 16-20% of above-mentioned ethanedioic acid weight, join in the dehydrated alcohol of its weight 25-30 times, stir；
(3) above-mentioned zinc acetate is joined in its weight 70-80 times, 46-50% ethanol solution, add above-mentioned activation concavo-convex
Rod soil powder, ultrasonic 10-20 minute, drips the ethanol solution of above-mentioned ethanedioic acid, magnetic agitation 3-4 minute after dropping, sucking filtration,
Product after sucking filtration is dried 3-5 hour at 110-116 DEG C, sends in Muffle furnace, at 600-640 DEG C, calcine 1.7-2 little
Time, cooling, obtain zinc oxide load powder；
(4) by abovementioned alkyl phenol polyethenoxy ether, polymine mixing, the anhydrous second of compound weight 13-20 times is joined
In alcohol, ultrasonic 1-2 minute, add above-mentioned gamma-aminopropyl-triethoxy-silane, stir, obtain silane dispersion fluid；
(5) above-mentioned zinc oxide load powder is joined in the dehydrated alcohol of its weight 30-40 times, add 2-hydroxyl-4-the most pungent
Epoxide benzophenone, rises high-temperature and is 80-90 DEG C, mix with above-mentioned silane dispersion fluid, insulated and stirred 1.7-2 hour, sucking filtration, will
Precipitation washing 2-3 time, is vacuum dried 20-30 minute at 50-60 DEG C, obtains amino modified zinc oxide load powder；
(6) above-mentioned N-sodium lauroyl sarcosine is joined in the deionized water of its weight 14-20 times, add 2-aminoethyl 17
Alkenyl imidazoline, stirs, and obtains aqueous dispersions；
(7) take the 10-16% of above-mentioned caprolactam weight, the 20-30% of residue ethanedioic acid weight, load with amino modified zinc oxide
Powder mixes, and adds the distilled water of compound weight 8-10 times, is sent in reactor, rises high-temperature and is 190-200 DEG C, insulation
React 3-4 hour, add above-mentioned aqueous dispersions, stir, slowly cool to room temperature, be filtered to remove filtrate, precipitation is dried,
Grind to form fine powder, obtain pre-polymerization modified zinc oxide load powder；
(8) above-mentioned pre-polymerization modified zinc oxide load powder is mixed with remaining caprolactam, add compound weight 4-7 times
Distilled water, is sent in reactor, rises high-temperature and is 200-230 DEG C, adds remaining ethanedioic acid, insulation reaction 3-3.5 hour,
Discharging cools down, and is vacuum dried 1-2 hour at 50-60 DEG C, obtains polymeric modification zinc oxide load powder；
(9) being mixed with remaining each raw material by above-mentioned polymeric modification zinc oxide load powder, high-speed stirred is uniform, sends into twin screw and squeezes
Go out machine extrusion, through tie rod, cooling, pelletizing, dried, to obtain final product.
The invention have the advantage that first attapulgite is calcined and acidification by the present invention, attapulgite can be increased
The silicone hydroxyl group on stone surface, gives attapulgite surface more negative charge, increases its absorbability to metal cation,
By the attapulgite in-situ precipitate of absorption Zn2+ ion is obtained presoma, obtain ZnO/ attapulgite composite wood by calcination
Material, with attapulgite as carrier, can improve the dispersibility of ZnO nanoparticle, it is thus achieved that have the composite of high antibacterial activity,
Attapulgite as layer chain silicate clay, the advantages such as tool specific surface area is big and lateral reactivity site is many, load nano-ZnO
After, considerably increasing the contact area of ZnO and microorganism, high adsorption activity based on attapulgite, antibacterial can be by antibacterial material
Material absorption is forming enrichment about so that ZnO nano granule is easier to directly contact with antibacterial, thus plays its antibacterial characteristics
Cause inactivation of bacteria, then this composite is participated in the pre-polymerization process of caprolactam, utilize caprolactam open-loop products
Aminocaproic acid reacts with the amino of composite material surface, makes composite material surface be grafted a certain amount of polyamide prepolymer aggressiveness, at it
Surface forms one layer of strong boundary layer；Participate in the polymerization process of polyamide the most again, due to the polyamides of composite material surface grafting
Amine performed polymer can participate in the ring-opening polymerisation of caprolactam, therefore, it is possible to form " micronetwork " structure with masterbatch as core, enters
And add intensity and the toughness of polyamide substrate material, and, beneficially composite is in the dispersion of polyamide substrate material；
The material of the present invention has good Sun-proof performance, can be widely applied to exterior material, and service life is long, good endurance.
Detailed description of the invention
A kind of outdoor Sun-proof pbt material, it is made up of the raw material of following weight parts:
Alkylphenol polyoxyethylene 0.2, caprolactam 70, attapulgite 10, zinc acetate 1, γ aminopropyl triethoxysilane 2,
Ethanedioic acid 18, polybutylene terephthalate (PBT) 300, myristic acid soda soap 4, polymine 2,2 aminoethyl 17 thiazolinyl miaow
Oxazoline 1, N sodium lauroyl sarcosine 1,2 hydroxyoctyloxybenzophenone 0.1, wollastonite in powder 3.
The preparation method of a kind of described outdoor Sun-proof pbt material, comprises the following steps:
(1) take above-mentioned myristic acid soda soap, join in the deionized water of its weight 20 times, stir, dropping 4mol/l's
Sodium hydroxide, regulation pH is 10, adds above-mentioned wollastonite in powder, and rising high-temperature is 40 DEG C, and insulated and stirred 20 minutes filters, will be heavy
Form sediment and wash, mix with attapulgite after drying, calcine 1 hour at 300 DEG C, join in the hydrochloric acid of 3mol/l and be acidified 3 hours,
Souring temperature is 20 DEG C, filters, precipitation is washed 3 times, is dried, wears into fine powder, obtain activation attapulgite powder at 80 DEG C；
(2) take the 16% of above-mentioned ethanedioic acid weight, join in the dehydrated alcohol of its weight 25 times, stir；
(3) above-mentioned zinc acetate is joined in its weight 70 times, the ethanol solution of 46%, adds above-mentioned activation attapulgite powder,
Ultrasonic 10 minutes, dripping the ethanol solution of above-mentioned ethanedioic acid, magnetic agitation 3 minutes after dropping, sucking filtration, by the product after sucking filtration
Thing is dried 3 hours at 110 DEG C, sends in Muffle furnace, calcines 1.7 hours at 600 DEG C, cooling, obtains zinc oxide load powder；
(4) by abovementioned alkyl phenol polyethenoxy ether, polymine mixing, the dehydrated alcohol of compound weight 13 times is joined
In, ultrasonic 1 minute, add above-mentioned γ aminopropyl triethoxysilane, stir, obtain silane dispersion fluid；
(5) above-mentioned zinc oxide load powder is joined in the dehydrated alcohol of its weight 30 times, add 2 hydroxyl n-octyloxy hexichol
Ketone, rising high-temperature is 80 DEG C, mixes with above-mentioned silane dispersion fluid, insulated and stirred 1.7 hours, sucking filtration, precipitation is washed 2 times,
It is vacuum dried 20 minutes at 50 DEG C, obtains amino modified zinc oxide load powder；
(6) above-mentioned N sodium lauroyl sarcosine is joined in the deionized water of its weight 14 times, add 2 aminoethyl 17 thiazolinyls
Imidazoline, stirs, and obtains aqueous dispersions；
(7) take the 10% of above-mentioned caprolactam weight, the 20% of residue ethanedioic acid weight, mix with amino modified zinc oxide load powder
Closing, add the distilled water of compound weight 8 times, be sent in reactor, rising high-temperature is 190 DEG C, and insulation reaction 3 hours adds
Enter above-mentioned aqueous dispersions, stir, slowly cool to room temperature, be filtered to remove filtrate, precipitation is dried, grinds to form fine powder,
Pre-polymerization modified zinc oxide load powder；
(8) above-mentioned pre-polymerization modified zinc oxide load powder is mixed with remaining caprolactam, add the steaming of compound weight 4 times
Distilled water, is sent in reactor, and rising high-temperature is 200 DEG C, adds remaining ethanedioic acid, insulation reaction 3 hours, and discharging cools down,
It is vacuum dried 1 hour at 50 DEG C, obtains polymeric modification zinc oxide load powder；
(9) being mixed with remaining each raw material by above-mentioned polymeric modification zinc oxide load powder, high-speed stirred is uniform, sends into twin screw and squeezes
Go out machine extrusion, through tie rod, cooling, pelletizing, dried, to obtain final product.
Performance test:
Hot strength is 96MPa；
Notch impact strength (KJ/m2) 10.10；
Vertical combustion (1.6mm) FV-O；
The zinc oxide load powder wherein prepared is O.lg/L to colibacillary minimum inhibitory concentration.
Claims (2)
1. an outdoor Sun-proof pbt material, it is characterised in that it is made up of the raw material of following weight parts:
Alkylphenol polyoxyethylene 0.2-0.7, caprolactam 70-80, attapulgite 10-13, zinc acetate 1-1.4, γ-aminopropyl
Triethoxysilane 2-3, ethanedioic acid 18-20, polybutylene terephthalate (PBT) 300-370, myristic acid soda soap 4-6, poly-second
Alkene imines 2-4,2-aminoethyl 17 alkenyl imidazoline 1-2, N-sodium lauroyl sarcosine 1-2,2-hydroxyl-4-n-octyloxy hexichol
Ketone 0.1-0.2, wollastonite in powder 3-4.
2. the preparation method of an outdoor Sun-proof pbt material as claimed in claim 1, it is characterised in that include following
Step:
(1) take above-mentioned myristic acid soda soap, join in the deionized water of its weight 20-27 times, stir, drip 4-
The sodium hydroxide of 6mol/l, regulation pH is 10-13, adds above-mentioned wollastonite in powder, rises high-temperature and is 40-50 DEG C, insulated and stirred 20-
30 minutes, filter, precipitation is washed, mixes with attapulgite after drying, calcine 1-2 hour at 300-350 DEG C, join 3-
Being acidified 3-5 hour in the hydrochloric acid of 5mol/l, souring temperature is 20-35 DEG C, filters, precipitation is washed 3-4 time, at 80-90 DEG C
It is dried, wears into fine powder, obtain activation attapulgite powder；
(2) take the 16-20% of above-mentioned ethanedioic acid weight, join in the dehydrated alcohol of its weight 25-30 times, stir；
(3) above-mentioned zinc acetate is joined in its weight 70-80 times, 46-50% ethanol solution, add above-mentioned activation concavo-convex
Rod soil powder, ultrasonic 10-20 minute, drips the ethanol solution of above-mentioned ethanedioic acid, magnetic agitation 3-4 minute after dropping, sucking filtration,
Product after sucking filtration is dried 3-5 hour at 110-116 DEG C, sends in Muffle furnace, at 600-640 DEG C, calcine 1.7-2 little
Time, cooling, obtain zinc oxide load powder；
(4) by abovementioned alkyl phenol polyethenoxy ether, polymine mixing, the anhydrous second of compound weight 13-20 times is joined
In alcohol, ultrasonic 1-2 minute, add above-mentioned gamma-aminopropyl-triethoxy-silane, stir, obtain silane dispersion fluid；
(5) above-mentioned zinc oxide load powder is joined in the dehydrated alcohol of its weight 30-40 times, add 2-hydroxyl-4-the most pungent
Epoxide benzophenone, rises high-temperature and is 80-90 DEG C, mix with above-mentioned silane dispersion fluid, insulated and stirred 1.7-2 hour, sucking filtration, will
Precipitation washing 2-3 time, is vacuum dried 20-30 minute at 50-60 DEG C, obtains amino modified zinc oxide load powder；
(6) above-mentioned N-sodium lauroyl sarcosine is joined in the deionized water of its weight 14-20 times, add 2-aminoethyl 17
Alkenyl imidazoline, stirs, and obtains aqueous dispersions；
(7) take the 10-16% of above-mentioned caprolactam weight, the 20-30% of residue ethanedioic acid weight, load with amino modified zinc oxide
Powder mixes, and adds the distilled water of compound weight 8-10 times, is sent in reactor, rises high-temperature and is 190-200 DEG C, insulation
React 3-4 hour, add above-mentioned aqueous dispersions, stir, slowly cool to room temperature, be filtered to remove filtrate, precipitation is dried,
Grind to form fine powder, obtain pre-polymerization modified zinc oxide load powder；
(8) above-mentioned pre-polymerization modified zinc oxide load powder is mixed with remaining caprolactam, add compound weight 4-7 times
Distilled water, is sent in reactor, rises high-temperature and is 200-230 DEG C, adds remaining ethanedioic acid, insulation reaction 3-3.5 hour,
Discharging cools down, and is vacuum dried 1-2 hour at 50-60 DEG C, obtains polymeric modification zinc oxide load powder；
(9) being mixed with remaining each raw material by above-mentioned polymeric modification zinc oxide load powder, high-speed stirred is uniform, sends into twin screw and squeezes
Go out machine extrusion, through tie rod, cooling, pelletizing, dried, to obtain final product.