CN105860312B - Functionalization alloy resin - Google Patents
Functionalization alloy resin Download PDFInfo
- Publication number
- CN105860312B CN105860312B CN201610305151.7A CN201610305151A CN105860312B CN 105860312 B CN105860312 B CN 105860312B CN 201610305151 A CN201610305151 A CN 201610305151A CN 105860312 B CN105860312 B CN 105860312B
- Authority
- CN
- China
- Prior art keywords
- compatilizer
- functionalization
- copolymer
- alloy resin
- mass percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of functionalization alloy resin is grouped as: polystyrene 2-55% by the following group calculated according to mass percent;Styrene-acrylonitrile copolymer 2-55%;Polyethylene 1-35%;Ethylene-vinyl acetate copolymer 10-25%;Ethylene-acrylic acid copolymer 0-15%;Compatilizer 5-10%;Hydrogenated styrene-butadiene block copolymer 5-25%;Polyethylene wax 0.3-0.6%;Four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester 0.15-0.3%;Three [2.4- di-tert-butyl-phenyl] phosphite ester 0.4-0.6%.Material of the present invention adapts to ABS and HIPS double-layer coextrusion, and material reclamation rate is very economical, and has extraordinary interface compatibility.
Description
Technical field
The present invention relates to the resist chemicals of refrigerator lining used in refrigerator manufacturing industry and refrigerator door end cap injection molding material
Functional resin new material, more particularly to a kind of anti-1- chloro-3,3,3 ,-trifluoropropene (abbreviation LBA), 1,1,1,3,3- five fluorine
The refrigerator lining film covered resin and refrigerator of the deep-etching of propane (abbreviation HFC-245fa) and pentamethylene polyploid foaming refrigerant
Door body end cap injection molding material.
Background technique
It comes into force from Montreal Protocol in 1998 with after Chinese Government's signature Kyoto Protocol in 1997, people just open
Begin to find the course for substituting CFC-11 (F-11) foaming agent.Since man invented Refrigeration Technique, the first generation of refrigerant
Product is CFC-11 (F-11), has eliminated one fluorine dichloroethanes (HCFC-141b) of transitional product later, subsequently into the
Two generation products, that is, pentamethylene foaming agent epoch.
The third generation freeze foaming agent be HFC-245fa (1,1,1,3,3- pentafluoropropane) and HFC-365mfc (1,1,1,3,
3- 3-pentafluorobutane).
Forth generation refrigeration foaming agent is LBA (the chloro- 3,3,3- trifluoro propene of 1-).
Why both at home and abroad to refrigeration foaming replacement so frequent? because of first generation refrigerant CFC-11 (freon-
11) very big to the depletion of the ozone layer of atmosphere, cause atmosphere ozone layer because the chloride ion in F-11 is under photochemical action
Meeting ozone decomposition is converted to oxygen and atmosphere is made to generate black hole, to destroy the environment and greenhouse effects of human survival.It is international
Environmental protection organization releases this transitional product of HCFC-141b.Ozone layer and greenhouse effects are destroyed since HCFC-141b is equally existed
Defect is only smaller than CFC-11 (F-11) harmfulness.Pentamethylene foaming technique is highly developed at present, but the thermally conductive system of foam
Number in the left and right 20mW/ (m.k), continues to reduce extremely difficult always.Therefore, novel third generation foaming refrigerant HFC- has been selected
245fa and HFC-365mfc.
It is sent out as Chinese freon (HCFCs) eliminates the propulsion of plan, HFC-245fa and HFC-365mfc as pentamethylene
The substitute products of infusion and HCFC-141b have entered China for many years.Section, Hisense dragon large-scale use HFC-245fa hair in 2009
Infusion.HFC-245fa does not have to be applied to household electric appliances as pure foaming agent as foreign countries, is more and pentamethylene foaming agent
It is used in mixed way.Since the GWP value (global warming potential, Global Warming Potential) of HFC-245fa is very high, in
Government, state does not encourage to promote.Therefore, HFC-245fa, HFC-365mfc are an awkward transitional product.At the same time,
In January, 2015, Europe is forbidden to use HFC-245fa.The U.S. is forbidden to use HFC-245fa within 2016, and Chinese Government also can be gradually
Forbid the use of HFC-245fa.
Thus inference, forth generation product LBA (1- chloro-3,3,3 ,-trifluoropropene) will be mainstream refrigerant foamed products, LBA
Without combustibility, GWP value is extremely low, and Energy Efficiency Ratio pentamethylene foaming agent improves 10%-12%, and thermal conductivity ratio HFC-245fa is low
8%.Good intensity, dimensional stability and cementability are possessed using the hard polyurethane foam that LBA foams.
Since LBA is at high price, the Haier of China's Mainland, the refrigerator that section, Hisense is imperial, beautiful are all made of the use of LBA 5-9%
Amount, the compound prescription of pentamethylene 12-14%.China's Mainland is popular to be known as polyploid foaming technique.But since LBA pentamethylene is compound
There is stronger chemical corrosivity and stress cracking resistance, therefore mainly (high with HIPS to refrigerator manufacturing industry liner material after formula
Impact-resistant polystyrene) and ABS (acrylonitrile-butadiene-styrene (ABS)) be liner extrusion board.But it also can be because after plastics sucking moulding
LBA, pentamethylene corrode and generate cracking, and refrigerator product is caused to scrap, and China Patent No. ZL200710191400.5 is using PE/
PS alloy, but due to the limitation of material, the material application of HIPS refrigerator lining is only adapted to, and cannot be general with ABS, simultaneously because
PE/PS alloy material is because PE material adapted is more, so that material has the characteristic of PE and influences refrigerator lining material and polyurethane
Foam cementability.Although using sided corona treatment HIPS plate surface, plastic uptake during squeezing out overlay film PE/PS alloy resin
The poor compatibility of refrigerator lining material and polyurethane foam material after molding and generate from bubble phenomenon, and influence refrigerator product quality
Reliability.Therefore, the present invention is in view of LBA, HFC-245fa, pentamethylene polyploid foaming agent are to refrigerator lining macromolecule material
The corrosivity of material causes refrigerator lining material corrosion and stress cracking.
Currently, refrigerator manufacturing industry refrigerator lining material is mainly that (one butadiene one of benzene alkene eyeball is styrene copolymerized by ABS both at home and abroad
Object) and HIPS (high impact polystyrene);This two kinds of material, which does not have, bears LBA, pentafluoropropane, the polynary foaming agent of pentamethylene
Corrosion, therefore refrigerator manufacturing industry selects forth generation foaming refrigerant LBA to will cause refrigerator lining material corrosion and stress cracking.
Summary of the invention
The technical problem to be solved in the present invention is that: a kind of functionalization alloy resin is designed, this alloy resin can be kept away
Exempt from chloro- 3,3,3- trifluoro propene (LBA) the polyploid foaming agent pair of pentamethylene, 1,1,1,3,3- pentafluoropropane (HFC-245fa), 1-
The corrosion of refrigerator lining material of main part (ABS, HIPS) and stress cracking, guarantee refrigerator integral product quality, while with (ABS,
HIPS) refrigerator proprietary material has good compatibility.
In order to solve the above-mentioned technical problem, the present invention proposes a kind of following technical scheme: functionalization alloy resin, by following
It is grouped as according to the group that mass percent calculates:
The above technical solution is further limited in that the compatilizer is self-control compatilizer, preparation method is as follows
It is described: glycidyl methacrylate 1%-5%, the maleic anhydride 0.5-1.5%, diformazan being calculated by mass percentage
Base formamide 0.2-0.5%, cumyl peroxide 0.05-0.1%, polyethylene 70-85%, hydrogenated styrene-fourth diblock
Copolymer 5-15%, four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester 0.4%-0.6% pass through double spiral shells
Bar extruder melting graft forms, and the sum of each raw material component mass percent of the compatilizer is equal to 100%.
The above technical solution is further limited in that the compatilizer is hydrogenated styrene-butadiene block copolymerization
Object, polycthylene grafted cis-butenedioic anhydride, polyethylene to graft glycidyl methacrylate or styrene-acrylonitrile-cis-butenedioic anhydride copolymer.
Compared with prior art, the invention has the following advantages:
Domestic and international Refrigeration Technique is described in background technique because the reason of environmental protection promotes foaming refrigerant to enter forth generation LBA
Epoch, China's Mainland major part enterprise use LBA, HFC-245fa, pentamethylene multiplexed combination foaming technique.But due to this more
First body foaming agent is very big to refrigerator manufacturing industry inner container of icebox materials A BS, HIPS corrosivity, and product of the present invention all material is state
Interior production or the high molecular material that market can be purchased at home.Pass through science, reasonable, effectively preparation.It is squeezed using twin-screw
The alloy resin of multifunction low cost made of machine is kneaded out.
Certain domestic Packaged Ice Inc., using the more first foaming formulations of LBA 8%, pentamethylene 10-12%, refrigerator lining material is used
ABS extrusion board, using LBA, pentamethylene foaming cracking comprehensively after plastics sucking moulding.Honeywell Inc. and the Packaged Ice Inc. to mesh
It is preceding to find out solution not yet.Last the said firm can only carry out the 4th using second generation pentamethylene foaming technique is used comprehensively
It can only postpone promoting for LBA foaming technique technique.Other one domestic Packaged Ice Inc. uses always China Patent No.
Although ZL200710191400.5 patented product solves LBA pentamethylene foaming etching problem using overlay film HIPS coextrusion process,
But there are refrigerator inner membrances and polyurethane foam material adhesion problem.Using the invention patent product, LBA pentamethylene pair can solve
In the corrosion and foaming process of ABS, HIPS refrigerator lining material from bubble phenomenon.Main technique is using double-layer coextrusion technique skill
Art.
The present invention is viscous according to pentamethylene, the chemical property of LBA, HFC-245fa refrigeration foaming agent and blown polyurethane materials
It connects performance requirement and has invented the material that a kind of EVA, PE, EAA are anti-LBA, HFC-245fa, pentamethylene corrodes, pass through grafting PS
(saturating benzene) and AS and the SEBS high score novel resistant to chemical etching and stress cracking made of melting mixing in double screw extruder
Sub- alloy material.
Specific embodiment
The present invention proposes a kind of functionalization alloy resin, is grouped as by the following group calculated according to mass percent:
The PS (polystyrene) is conducive to the rigidity and mouldability of alloy resin as one of basic raw material.
The AS (styrene-acrylonitrile copolymer) is that one kind is corrosion-resistant, anti-internal stress is rigid, heat resistance is high well
Molecular material.
The PE (polyethylene) is a kind of resistant to chemical etching, cheap and good-quality high molecular material.
The EVA (ethylene-vinyl acetate copolymer) is that a kind of compatibility is very good, and chemical-resistance is fine, can be with
The extraordinary high molecular material of polyurethane foam material cementability.
The EAA (ethylene-acrylic acid copolymer) is a kind of high cohesiveness material, it is therefore an objective to reinforced alloys resin and poly-
The closer bonding of urethane foamed material.
The compatilizer using extremely strong functional group be grafted on corresponding high molecular polymer, due to functional group
The high molecular material that polar group promotes interface incompatible has interface compatibility, generates new alloy material.
The outsourcing compatilizer that the compatilizer can divide self-control compatilizer and buy on the market.
The preparation method of the self-control compatilizer is as described below: the GMA (methacrylic acid being calculated by mass percentage
Ethylene oxidic ester) 1%-5%, MAH (maleic anhydride is also referred to as cis-butenedioic anhydride) 0.5-1.5%, DMF (dimethylformamide) 0.2-0.5%,
DCP (cumyl peroxide) 0.05-0.1%, PE (polyethylene) 70-85%, SEBS (hydrogenated styrene-fourth di-block copolymer
Object) 5-15%, antioxidant 1010 0.4%-0.6% formed by double screw extruder melting graft, each original of the compatilizer
Expect that the sum of constituent mass percentage is equal to 100%.Wherein GMA, MAH are polar functional group needed for compatilizer product, and DMF is main
Control grafting reflection during cross-linking reaction, DCP is to play initiator in reaction process, PE SEBS be mainly compatilizer production
The material of main part of product, antioxidant 1010 (four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters) are to prevent
Material of main part oxidative degradation is protected in high temperature extrusion process.
Outsourcing compatilizer includes the hydrogenated styrene-butadiene block copolymer (trade mark that Ke Teng company produces
SEBS1901), PE-g-MAH (polycthylene grafted cis-butenedioic anhydride), PE-g-GMA (polyethylene to graft glycidyl methacrylate) or
SMA compatilizer (styrene-acrylonitrile-cis-butenedioic anhydride copolymer).
The SEBS (hydrogenated styrene-butadiene block copolymer) be very good chemical corrosion resistance, good weatherability,
The rubber material of the good toughening of compatibility, cold tolerance.
The polyethylene wax plays lubricating action in the process of production and processing.
The antioxidant is 1010 and irgasfos 168, prevents macromolecule from degrading in process of production.
The preparation method of above-mentioned functionalization alloy resin is: first weighing the following component calculated according to mass percent: poly-
Styrene 2-55%, styrene-acrylonitrile copolymer 2-55%, polyethylene 1-35%, ethylene-vinyl acetate copolymer 10-
25%, ethylene-acrylic acid copolymer 0-15%, compatilizer 5-10%, hydrogenated styrene-butadiene block copolymer 5-25%,
Polyethylene wax 0.3-0.6%, four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester 0.15-0.3%, three
[2.4- di-tert-butyl-phenyl] phosphite ester 0.4-0.6% all pours into high-speed mixer and stirs 5 minutes, then will stir equal
Above-mentioned each component after even is directly placed into double-screw extruding pelletizing machine extruding pelletization.
Embodiment 1
According to mass percent, PS 55%, AS 5%, PE 14%, EVA 10% are taken, self-control compatilizer 5% above-mentioned,
SEBS 10%, polyethylene wax 0.4%, antioxidant 1010 0.2%, irgasfos 168 0.4%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment adapts to HIPS refrigerator PP Pipe Compound double-layer coextrusion overlay film bottom, after plastic uptake foaming, isolation LBA,
The polynary foaming agent of FC-245fa, pentamethylene corrodes HIPS material.This overlay film is protective film.
Its physical index: melt index 5-6g/10min, tensile strength are greater than 26Mpa.Notch impact strength is greater than
200J/m, heat distortion temperature are greater than 75 DEG C, and elongation at break is resistant to chemical etching excellent greater than 120%.
Embodiment 2
According to mass percent, take PS 5%, AS 55%, PE 2%, EVA 15%, self-control compatilizer 5% above-mentioned,
SEBS 17%, polyethylene wax 0.3%, antioxidant 1010 0.3%, irgasfos 168 0.4%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment adaptation ABS refrigerator inner liner plates double-layer coextrusion is laminating, is laminating co-extrusion film by secondary formula materials, this is covered
The main purpose for closing film is the corrosion for protecting ABS plate not by LBA, HFC-245fa, the polynary foaming agent of pentamethylene, overlay film thickness
Account for entire plate thickness 10%.
Its physical index: melt index 2.5-3.5g/10min, tensile strength are greater than 32MPa, and notch impact strength is greater than
180J/m, temperature shape temperature are greater than 80 DEG C, and elongation at break is greater than 60%, excellent chemical-resistance.
Embodiment 3
According to mass percent, PS 40%, AS 6%, PE 14%, EVA 14%, EAA 5%, compatilizer 10% are taken
(being made of self-control compatilizer 5% above-mentioned and outsourcing compatilizer SEBS 1,901 5%), SEBS 5%, polyethylene wax 0.3%,
Antioxidant 1010 0.2%, irgasfos 168 0.5%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment adapts to the laminating protective film of HIPS refrigerator lining materials double-layer co-extrusion, laminating co-extrusion thickness accounts for plate thickness
10%;This coating plastics sucking moulding inner container of icebox is engaged with the polynary foaming agent of LBA, HFC-245fa pentamethylene, has bubble excellent
Function good and resistant to chemical etching, stress crack resistant characteristic.
Its physical index: melt index 6-8g/10min, tensile strength are greater than 24MPa;Notch impact strength is greater than 300J/
M, heat distortion temperature are greater than 70 DEG C, and fracture extension rate is greater than 150%.
Embodiment 4
According to mass percent, take PS 5%, AS 50%, PE4%, EVA 20%, EAA 4%, compatilizer 6% (by preceding
State self-control compatilizer 3% and outsourcing compatilizer SEBS1901 3% composition), SEBS 10%, polyethylene wax 0.4%, antioxidant
1010 0.2%, irgasfos 168 0.4%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment adapts to injection molding process, is suitable for refrigerator door end cap material and is molded.Door foaming material LBA, HFC-
The polynary foam process of 245fa pentamethylene is resistant to chemical etching and stress cracking injection moulded door body end lid material.
Its physical index: melt index is greater than 4.5g/10min, and tensile strength is greater than 35MPa, and notch impact strength is greater than
160J/m, temperature shape temperature are greater than 78 DEG C, and elongation at break is greater than 30%, excellent chemical-resistance and stress crack resistant.
Case study on implementation 5
According to mass percent, PS 3%, AS 55%, PE 1%, EVA 20%, EAA 2%, outsourcing compatilizer are taken
SEBS1901 2%, SEBS 16%, polyethylene wax 0.4%, antioxidant 1010 0.2%, irgasfos 168 0.4%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment is suitable for HIPS refrigerator material superficial layer light coating materials, this material is to adapt to HIPS refrigerator material double-layer coextrusion to make
For liner fabric, there is oil resistivity corrosion, stress crack resistant.Has the function of high bright layer simultaneously.This light coating materials of overlay film Zhan is total
The 2-5% dosage of thickness.
Its physical index: melt index is greater than 5g/10min, and tensile strength is greater than 38MPa, and notch impact strength is greater than
100J/m, temperature shape temperature are greater than 82 DEG C, and elongation at break is greater than 30%, excellent grease resistance stress cracking.
Embodiment 6
According to mass percent, PS 39%, AS 4%, PE 15% are taken;EVA 20%, EAA 3%, compatilizer 8% (by
Outsourcing compatilizer PE-g-MAH 3% and self-control compatilizer 5% above-mentioned composition), SEBS 10%, polyethylene wax 0.3%, antioxygen
Agent 1,010 0.2%, irgasfos 168 0.5%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment is suitable for HIPS refrigerator special-purpose board double-layer coextrusion overlay film material, overlay film material occupation proportion is plate thickness
5-8% completely cuts off LBA-HFC-245fa, corrosion of the polynary foaming agent of pentamethylene to HIPS refrigerator lining.This overlay film material is also one layer
Protective film.
Its physical index: melt index 4-6g/10min, tensile strength are greater than 21MPa, and notch impact strength is greater than 210J/
M, heat distortion temperature are greater than 70 DEG C, and elongation at break is greater than 130%, the polynary foaming agent of the excellent HFC-245 of resistance to LBA, pentamethylene
Corrosion and chemically-resistant stress cracking, have the function of ideal bonding polyurethane foamed material.
Embodiment 7
According to mass percent, take PS 3%, AS 55%, PE 2%, EVA 13%, EAA 2%, compatilizer 7% (by
Outsourcing compatilizer PE-g-GMA 3% and outsourcing compatilizer PE-g-MAH 4% are formed), SEBS 17%, polyethylene wax 0.6%,
Antioxidant 1010 0.2%, irgasfos 168 0.5%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment adapts to ABS refrigerator lining materials double-layer co-extrusion overlay film material, overlay film amount is that plate thickness accounts for plate thickness
8%;It is also applied for injection molding process application.The corrosion of main performance amount chemical-resistance and stress cracking.
Its physical index: melt index 4g/10min, tensile strength are greater than 36MPa;Notch impact strength is greater than 200J/m,
Heat distortion temperature is greater than 78 DEG C, and fracture extension rate is greater than 60%.
Embodiment 8
According to mass percent, PS 30%, AS 35%, PE 5%, EVA 15%, EAA 1.5%, compatilizer are taken
2.5% (being made of self-control compatilizer 1.5% above-mentioned and outsourcing compatilizer SEBS1901 1%), SEBS 10%, polyethylene wax
0.3%, antioxidant 1010 0.15%, irgasfos 168 0.6%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment is adapted to injecting products, resistant to chemical etching and stress crack resistant.
Its physical index: melt index 5g/10min, tensile strength are greater than 34MPa, and notch impact strength is greater than 150J/m,
Heat distortion temperature is greater than 74 degrees Celsius, and elongation at break is greater than 20%.
Embodiment 9
According to mass percent, take PS 15%, AS 40%, PE 2.2%, EVA 25%, EAA 1.8%, it is above-mentioned from
Compatilizer 5% processed, SEBS 10%, polyethylene wax 0.3%, antioxidant 1010 0.2%, irgasfos 168 0.4%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment is adapted to injecting products and coated products, resistant to chemical etching and stress crack resistant.
Its physical index: melt index 7g/10min, tensile strength are greater than 30MPa, and notch impact strength is greater than 140J/m,
Heat distortion temperature is greater than 72Shi degree, and elongation at break is greater than 20%.
Embodiment 10
According to mass percent, take PS 2%, AS 40%, PE 2%, EVA 20%, EAA 3%, compatilizer 10% (by
Outsourcing compatilizer PE-g-GMA 5% and outsourcing compatilizer PE-g-MAH 5% are formed), SEBS 25%, polyethylene wax 0.3%,
Antioxidant 1010 0.2%, irgasfos 168 0.5%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment is adapted to injecting products and coated products, resistant to chemical etching and stress crack resistant.
Its physical index: melt index 8g/10min, tensile strength are greater than 28MPa, and notch impact strength is greater than 240J/m,
Heat distortion temperature is greater than 72Shi degree, and elongation at break is greater than 40%.
Embodiment 11
According to mass percent, take PS 48%, AS 2%, PE 10%, EVA 20%, EAA 3%, compatilizer 6% (by
Self-control compatilizer 3% and outsourcing compatilizer SEBS1901 3% above-mentioned composition), SEBS 10%, polyethylene wax 0.3%, antioxygen
Agent 1,010 0.2%, irgasfos 168 0.5%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment is adapted to injecting products and coated products, resistant to chemical etching and stress crack resistant.
Its physical index: melt index 10g/10min, tensile strength are greater than 23MPa, and notch impact strength is greater than 260J/
M, heat distortion temperature are greater than 72Shi degree, and elongation at break is greater than 80%.
Embodiment 12
According to mass percent, take PS 2%, AS 50%, PE 35%, EVA18%, outsourcing compatilizer SMA8%,
SEBS 13%, polyethylene wax 0.4%, antioxidant 1010 0.2%, irgasfos 168 0.4%.
It all pours into high-speed mixer to stir 5 minutes, above-mentioned each component after mixing evenly is then directly placed into double spiral shells
Bar extruding granulator extruding pelletization.
The present embodiment 12 is adapted to injecting products and coated products, resistant to chemical etching and stress crack resistant.
Its physical index: melt index 5g/10min, tensile strength are greater than 38MPa, and notch impact strength is greater than 140J/m,
Heat distortion temperature is greater than 82Shi degree, and elongation at break is greater than 40%.
In functional alloy resin production refrigerator lining materials process of the invention, all manufacture craft equipment and original material
Technique used in material production refrigerator lining is identical, without transformation.
Claims (3)
1. a kind of functionalization alloy resin, which is characterized in that it is grouped as by the following group calculated according to mass percent:
2. functionalization alloy resin according to claim 1, which is characterized in that the compatilizer is self-control compatilizer,
Preparation method is as described below: glycidyl methacrylate 1%-5%, the maleic anhydride being calculated by mass percentage
0.5-1.5%, dimethylformamide 0.2-0.5%, cumyl peroxide 0.05-0.1%, polyethylene 70-85%, hydrogenation of benzene
Ethylene-fourth diblock copolymer 5-15%, four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol ester 0.4%-
0.6% is formed by double screw extruder melting graft, and the sum of each raw material component mass percent of the compatilizer is equal to
100%.
3. functionalization alloy resin according to claim 1, which is characterized in that the compatilizer is hydrogenated styrene-
Butadiene block copolymer, polycthylene grafted cis-butenedioic anhydride, polyethylene to graft glycidyl methacrylate or styrene-propene
Nitrile-cis-butenedioic anhydride copolymer.