CN105856596A - Manufacturing method for composite material with surface provided with concave-convex three-dimensional decorative patterns - Google Patents
Manufacturing method for composite material with surface provided with concave-convex three-dimensional decorative patterns Download PDFInfo
- Publication number
- CN105856596A CN105856596A CN201610265365.6A CN201610265365A CN105856596A CN 105856596 A CN105856596 A CN 105856596A CN 201610265365 A CN201610265365 A CN 201610265365A CN 105856596 A CN105856596 A CN 105856596A
- Authority
- CN
- China
- Prior art keywords
- film
- decorative pattern
- convex
- stereo concave
- concave
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a manufacturing method for a composite material and discloses a manufacturing method for a composite material with the surface provided with concave-convex three-dimensional decorative patterns. The method includes the following steps that firstly, a film is softened, an embossing roller is used for hot pressing, a film with the surface provided with the concave-convex three-dimensional decorative patterns is formed, a color adhesive is then sprayed, aluminum plating is conducted after drying, and a transferrable alumite film with the surface provided with the concave-convex three-dimensional decorative patterns is manufactured; and secondly, the surface of the alumite film with the surface provided with the concave-convex three-dimensional decorative patterns is coated with a complex adhesive, then drying is conducted, the film is compounded with a base material, after the film is cured for three days in a heat insulation room, the film is stripped off, and the composite material with the surface provided with the concave-convex three-dimensional decorative patterns is obtained. By means of the manufacturing method, the manufactured aluminum-plated film with a concave-convex 3D effect formed on the surface of the composite material film solves the technical problem that in the prior art, an aluminum-plated layer of aluminum-plated fabric only can be a flat layer. By means of the aluminum plating technology in the manufacturing method, an aluminum layer is firm, and the problems that in the prior art, a metal powder layer is poor in firmness and is liable to be disengaged are solved.
Description
Technical field
The present invention relates to the preparation method of composite, particularly relate to the compound of surface band stereo concave-convex decorative pattern
The preparation method of material.
Background technology
Along with the raising of people's living standard, to garment material, ornament materials, packaging material etc. tend to top grade
Changing innovationization, people are ornamental to it, and comfortableness, the requirement of perception and practicality improves constantly, therefore
Market must trend towards innovation, cubic materials (such as fabric).
Summary of the invention
The shortcoming that the present invention is directed to prior art, it is provided that the composite of a kind of surface band stereo concave-convex decorative pattern
Preparation method, composite of surface band stereo concave-convex decorative pattern that this invention makes is applicable to stage dress ornament face
Material, swimsuit fabric, sportswear fabric, footwear face material, box material, toy material, packaging material,
Ornament materials etc..
In order to solve above-mentioned technical problem, the present invention is addressed by following technical proposals:
The preparation method of the composite of surface band stereo concave-convex decorative pattern, comprises the following steps,
A. film is softened by baking oven, the film after softening with knurling rolls hot pressing, form surface band concavo-convex vertical
The film of body decorative pattern；Again with flower roller coat coloring agent, after oven for drying, with aluminum-spraying machine to film stereo concave-convex decorative pattern
Aluminizing in side, is fabricated to surface and has the transferable anodized aluminium film of stereo concave-convex decorative pattern；The present invention is producing
During form ridge design in film surface hot pressing, on the one hand carry with base material stripping for later stage anodized aluminium film
Supply convenience.On the other hand, the embossing of anodized aluminium film is also later stage fabric or substrate surface formation stereo concave-convex
Decorative pattern provides template.
B. surface has the transferable anodized aluminium film surface of stereo concave-convex decorative pattern by flower roller coat compound adhesive, then
Through oven for drying, with hot-pressing roller, surface had transferable anodized aluminium film and the base material of stereo concave-convex decorative pattern
Compound；
After solidifying three days in moist closet, stripping film, obtain the composite of surface band stereo concave-convex decorative pattern.
Film in the present invention produces ridge design by knurling rolls high temperature embossing rear surface, by flower roller coat look
Glue, after baking oven high temperature is dried, then is aluminized stereo concave-convex patterned surface by aluminum-spraying machine, forms surface and has recessed
The transferable anodized aluminium film of convex three-dimensional pattern；Again by flower roller coat composite glue, pass through through oven for drying
Hot-pressing roller is combined the film of compound adhesive with base material, and heat preservation solidification was stood with concavo-convex on isolated surface after three days
The composite of body decorative pattern.The flower of the concavo-convex 3D stereoeffect that the composite material surface that the present invention prepares is formed
Line, surface refraction degree is very strong, fastness is very firm, resistance to water is fine.
The composite material film surface that the present invention prepares forms the metallized film of concavo-convex 3D stereoeffect, solves
Fabric aluminium coated of aluminizing in prior art can only be the technical barrier of levelling blanket.Aluminum plating process in the present invention,
Aluminium lamination is firm, solves metal bisque fastness in prior art poor, holds caducous problem.
As preferably, in step A, film is the one in CPP film, PVC film, BOPP film.
As preferably, in step A, the baking oven that film is controlled at 60 DEG C～200 DEG C by temperature is softened, uses
Film after the knurling rolls hot pressing softening of 60 DEG C～200 DEG C, forms the film of surface band stereo concave-convex decorative pattern；Again
With flower roller coat coloring agent, temperature controls after the oven for drying of 40 DEG C～200 DEG C, concavo-convex vertical to film with aluminum-spraying machine
Aluminizing in body decorative pattern side, is fabricated to surface and has the transferable anodized aluminium film of stereo concave-convex decorative pattern, rolling.
As preferably, in step B, base material is the one in fabric, paper, PP film, PE film, PVC film.
Fabric is cotton, burlap, silk, woollen goods, leather, chemical fibre, blending, Modal, corium etc..
As preferably, in step B, oven temperature controls at 30 DEG C～150 DEG C.
As preferably, in step B, moist closet temperature controls at 30 DEG C～80 DEG C.
As preferably, the coloring agent in step A is the one in water-base cement, PUR, being combined in step B
Glue is the one in water-base cement, PUR.Coloring agent be the colored water-base cement water-base cement of toner (i.e. containing),
One in colored PUR (i.e. the PUR containing toner).
As preferably, the coloring agent in step A is the one in PU resin, epoxy resin, in step B
Compound adhesive is the one in PU resin, epoxy resin.Coloring agent is that colored PU resin is (i.e. containing toner
PU resin), one in the colored epoxy resin epoxy resin of toner (i.e. containing).
As preferably, the coloring agent in step A is ink, and the compound adhesive in step B is ink.
Composite in the present invention be applied to stage fabric, swimsuit fabric, leisure fabric, footwear face material,
Box material, toy material, packaging material, ornament materials etc..
Film in the present invention produces ridge design by knurling rolls high temperature embossing rear surface, by flower roller coat look
Glue, after baking oven high temperature is dried, then is aluminized stereo concave-convex patterned surface by aluminum-spraying machine, forms surface and has recessed
The transferable anodized aluminium film of convex three-dimensional pattern；Again by flower roller coat composite glue, pass through through oven for drying
Hot-pressing roller is combined the film of compound adhesive with base material, and heat preservation solidification was stood with concavo-convex on isolated surface after three days
The composite of body decorative pattern.The flower of the concavo-convex 3D stereoeffect that the composite material surface that the present invention prepares is formed
Line, surface refraction degree is very strong, fastness is very firm, resistance to water is fine.
The composite material film surface that the present invention prepares forms the metallized film of concavo-convex 3D stereoeffect, solves
Fabric aluminium coated of aluminizing in prior art can only be the technical barrier of levelling blanket.Aluminum plating process in the present invention,
Aluminium lamination is firm, solves metal bisque fastness in prior art poor, holds caducous problem.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is described in further detail.
Embodiment 1
The preparation method of the composite of surface band stereo concave-convex decorative pattern, comprises the following steps,
A. the baking oven that film is controlled at 60 DEG C by temperature is softened, after softening with the knurling rolls hot pressing of 60 DEG C
Film, form the film of surface band stereo concave-convex decorative pattern；Again with flower roller coat coloring agent, temperature controls at 40 DEG C
Oven for drying after, with aluminum-spraying machine, is aluminized in film stereo concave-convex decorative pattern side, is fabricated to surface and has concavo-convex
The transferable anodized aluminium film of three-dimensional pattern, rolling；
B. surface has the transferable anodized aluminium film surface of stereo concave-convex decorative pattern by flower roller coat compound adhesive, then
Control the oven for drying at 30 DEG C through excess temperature, with hot-pressing roller, surface is had the transferable of stereo concave-convex decorative pattern
Anodized aluminium film is combined with base material；
After temperature controls to solidify three days in the moist closet of 30 DEG C, stripping film, obtain surface band concavo-convex vertical
The composite of body decorative pattern.
In step A, film is CPP film.
In step B, base material is fabric.
Coloring agent in step A is ink, and the compound adhesive in step B is PU resin.
Embodiment 2
The preparation method of the composite of surface band stereo concave-convex decorative pattern, comprises the following steps,
A. the baking oven that film is controlled at 200 DEG C by temperature is softened, soften with the knurling rolls hot pressing of 200 DEG C
After film, form the film of surface band stereo concave-convex decorative pattern；Again with flower roller coat coloring agent, temperature controls at 200 DEG C
Oven for drying after, with aluminum-spraying machine, is aluminized in film stereo concave-convex decorative pattern side, is fabricated to surface and has concavo-convex
The transferable anodized aluminium film of three-dimensional pattern, rolling；
B. surface has the transferable anodized aluminium film surface of stereo concave-convex decorative pattern by flower roller coat compound adhesive, then
Control the oven for drying at 150 DEG C through excess temperature, with hot-pressing roller, surface is had the transferable of stereo concave-convex decorative pattern
Anodized aluminium film is combined with base material；
After temperature controls to solidify three days in the moist closet of 80 DEG C, stripping film, obtain surface band concavo-convex vertical
The composite of body decorative pattern.
In step A, film is PVC film.
In step B, base material is PP film.
Coloring agent in step A is water-base cement, and the compound adhesive in step B is the one in water-base cement, PUR.
Coloring agent in step A is the one in PU resin, epoxy resin, and the compound adhesive in step B is PU
One in resin, epoxy resin.
Coloring agent in step A is ink, and the compound adhesive in step B is ink.
Embodiment 3
The preparation method of the composite of surface band stereo concave-convex decorative pattern, comprises the following steps,
A. the baking oven that film is controlled at 60 DEG C～200 DEG C by temperature is softened, with 60 DEG C～the embossing of 200 DEG C
Film after roller hot pressing softening, forms the film of surface band stereo concave-convex decorative pattern；Again by flower roller coat coloring agent, temperature
Degree controls after the oven for drying of 40 DEG C～200 DEG C, aluminizes film stereo concave-convex decorative pattern side with aluminum-spraying machine,
It is fabricated to surface and there is the transferable anodized aluminium film of stereo concave-convex decorative pattern, rolling；
B. surface has the transferable anodized aluminium film surface of stereo concave-convex decorative pattern by flower roller coat compound adhesive, then
Control, 30 DEG C～the oven for drying of 150 DEG C, with hot-pressing roller, surface is had stereo concave-convex decorative pattern through excess temperature
Transferable anodized aluminium film is combined with base material；
After temperature controls to solidify three days in the moist closet of 30 DEG C～80 DEG C, stripping film, obtain surface band recessed
The composite of convex three-dimensional pattern.
In step A, film is the one in CPP film, PVC film, BOPP film.
In step B, base material is the one in fabric, PP film, PE film, PVC film.
Coloring agent in step A is water-base cement, and the compound adhesive in step B is PUR.
Embodiment 4
The preparation method of the composite of surface band stereo concave-convex decorative pattern, comprises the following steps,
A. the baking oven that film is controlled at 100 DEG C by temperature is softened, soften with the knurling rolls hot pressing of 100 DEG C
After film, form the film of surface band stereo concave-convex decorative pattern；Again with flower roller coat coloring agent, temperature controls at 150 DEG C
Oven for drying after, with aluminum-spraying machine, is aluminized in film stereo concave-convex decorative pattern side, is fabricated to surface and has concavo-convex
The transferable anodized aluminium film of three-dimensional pattern, rolling；
B. surface has the transferable anodized aluminium film surface of stereo concave-convex decorative pattern by flower roller coat compound adhesive, then
Control the oven for drying at 120 DEG C through excess temperature, with hot-pressing roller, surface is had the transferable of stereo concave-convex decorative pattern
Anodized aluminium film is combined with base material；
After temperature controls to solidify three days in the moist closet of 50 DEG C, stripping film, obtain surface band concavo-convex vertical
The composite of body decorative pattern.
In step A, film is BOPP film.
In step B, base material is PE film.
Coloring agent in step A is PUR, and the compound adhesive in step B is water-base cement.
Embodiment 5
The preparation method of the composite of surface band stereo concave-convex decorative pattern, comprises the following steps,
A. the baking oven that film is controlled at 80 DEG C by temperature is softened, after softening with the knurling rolls hot pressing of 120 DEG C
Film, form the film of surface band stereo concave-convex decorative pattern；Again with flower roller coat coloring agent, temperature controls at 80 DEG C
Oven for drying after, with aluminum-spraying machine, is aluminized in film stereo concave-convex decorative pattern side, is fabricated to surface and has concavo-convex
The transferable anodized aluminium film of three-dimensional pattern, rolling；
B. surface has the transferable anodized aluminium film surface of stereo concave-convex decorative pattern by flower roller coat compound adhesive, then
Control the oven for drying at 50 DEG C through excess temperature, with hot-pressing roller, surface is had the transferable of stereo concave-convex decorative pattern
Anodized aluminium film is combined with base material；
After temperature controls to solidify three days in the moist closet of 40 DEG C, stripping film, obtain surface band concavo-convex vertical
The composite of body decorative pattern.
In step A, film is CPP film.
In step B, base material is PVC film.
Coloring agent in step A is PU resin, and the compound adhesive in step B is epoxy resin.
Embodiment 6
The preparation method of the composite of surface band stereo concave-convex decorative pattern, comprises the following steps,
A. the baking oven that film is controlled at 180 DEG C by temperature is softened, soften with the knurling rolls hot pressing of 180 DEG C
After film, form the film of surface band stereo concave-convex decorative pattern；Again with flower roller coat coloring agent, temperature controls at 190 DEG C
Oven for drying after, with aluminum-spraying machine, is aluminized in film stereo concave-convex decorative pattern side, is fabricated to surface and has concavo-convex
The transferable anodized aluminium film of three-dimensional pattern, rolling；
B. surface has the transferable anodized aluminium film surface of stereo concave-convex decorative pattern by flower roller coat compound adhesive, then
Control the oven for drying at 120 DEG C through excess temperature, with hot-pressing roller, surface is had the transferable of stereo concave-convex decorative pattern
Anodized aluminium film is combined with base material；
After temperature controls to solidify three days in the moist closet of 70 DEG C, stripping film, obtain surface band concavo-convex vertical
The composite of body decorative pattern.
In step A, film is CPP film.
In step B, base material is paper.
Coloring agent in step A is the one in water-base cement, PUR, the compound adhesive in step B be water-base cement,
One in PUR.
Coloring agent in step A is epoxy resin, and the compound adhesive in step B is PU resin.
In a word, the foregoing is only presently preferred embodiments of the present invention, all made according to scope of the present invention patent
Impartial change with modify, all should belong to the covering scope of patent of the present invention.
Claims (9)
1. the preparation method of the composite of surface band stereo concave-convex decorative pattern, it is characterised in that: comprise the following steps,
A. film is softened by baking oven, the film after softening with knurling rolls hot pressing, form surface band concavo-convex vertical
The film of body decorative pattern；Again with flower roller coat coloring agent, after oven for drying, with aluminum-spraying machine to film stereo concave-convex decorative pattern
Aluminizing in side, is fabricated to surface and has the transferable anodized aluminium film of stereo concave-convex decorative pattern；
B. surface has the transferable anodized aluminium film surface of stereo concave-convex decorative pattern by flower roller coat compound adhesive, then
Through oven for drying, with hot-pressing roller, surface had transferable anodized aluminium film and the base material of stereo concave-convex decorative pattern
Compound；
After solidifying three days in moist closet, stripping film, obtain the composite of surface band stereo concave-convex decorative pattern.
The preparation method of the composite of surface the most according to claim 1 band stereo concave-convex decorative pattern, its feature
Being: in step A, film is the one in CPP film, PVC film, BOPP film.
The preparation method of the composite of surface the most according to claim 1 band stereo concave-convex decorative pattern, its feature
It is: in step A, the baking oven that film is controlled at 60 DEG C～200 DEG C by temperature is softened, with 60 DEG C～200 DEG C
Knurling rolls hot pressing soften after film, form the film of surface band stereo concave-convex decorative pattern；Again with flower roller coat look
Glue, temperature controls after the oven for drying of 40 DEG C～200 DEG C, with aluminum-spraying machine to film stereo concave-convex decorative pattern side
Aluminize, be fabricated to surface and there is the transferable anodized aluminium film of stereo concave-convex decorative pattern, rolling.
The preparation method of the composite of surface the most according to claim 1 band stereo concave-convex decorative pattern, its feature
Being: in step B, base material is the one in fabric, paper, PP film, PE film, PVC film.
The preparation method of the composite of surface the most according to claim 1 band stereo concave-convex decorative pattern, its feature
Being: in step B, oven temperature controls at 30 DEG C～150 DEG C.
The preparation method of the composite of surface the most according to claim 1 band stereo concave-convex decorative pattern, its feature
Being: in step B, moist closet temperature controls at 30 DEG C～80 DEG C.
The preparation method of the composite of surface the most according to claim 1 band stereo concave-convex decorative pattern, its feature
Being: the coloring agent in step A is the one in water-base cement, PUR, the compound adhesive in step B is aqueous
One in glue, PUR.
The preparation method of the composite of surface the most according to claim 1 band stereo concave-convex decorative pattern, its feature
Being: the coloring agent in step A is the one in PU resin, epoxy resin, the compound adhesive in step B is
One in PU resin, epoxy resin.
The preparation method of the composite of surface the most according to claim 1 band stereo concave-convex decorative pattern, its feature
Being: the coloring agent in step A is ink, the compound adhesive in step B is ink.