CN105839255A - Flame-retardant yarn for children's clothing and preparing method of flame-retardant yarn - Google Patents
Flame-retardant yarn for children's clothing and preparing method of flame-retardant yarn Download PDFInfo
- Publication number
- CN105839255A CN105839255A CN201610305482.0A CN201610305482A CN105839255A CN 105839255 A CN105839255 A CN 105839255A CN 201610305482 A CN201610305482 A CN 201610305482A CN 105839255 A CN105839255 A CN 105839255A
- Authority
- CN
- China
- Prior art keywords
- flame
- retardant
- yarn
- retardant yarn
- fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a flame-retardant yarn for children's clothing and a preparing method of the flame-retardant yarn. The flame-retardant yarn is prepared from, by mass, 40-60 parts of flame-retardant viscose, 10-20 parts of flame-retardant acrylic fibers, 30-40 parts of modal fibers and 2-5 pats of anti-static fibers. In the preparing process, all the raw materials are mixed evenly; the procedures of blowing, cotton carding, drawing, roving and spinning are conducted in sequence to obtain the flame-retardant yarn. According to the flame-retardant yarn and the preparing method, various fibers are adopted to be blended, the selected fibers contain no halogen and are complementary in nature and good in spinnability, and woven fabric is capable of absorbing moisture, breathable, soft, smooth and comfortable to wear, has permanent flame retardance and completely meets the requirement for fireproofness and flame retardance of children's clothing.
Description
Technical field
The present invention relates to textile technology field, specifically a kind of garment for children flame-retardant yarn and preparation method thereof.
Background technology
Along with economic growth and social progress, people's awareness of the importance of fire prevention progressively strengthens, and Fire-proof Finishing Agents for Textile is proposed requirements at the higher level, as sleeping suit for children requires that its limited oxygen index (LOI) is more than 25.Fire-proof Finishing Agents for Textile mainly has two approach at present: 1. pair fiber adds flame retardant, suppresses it to burn；2. pair fabric carries out coating or pads flame-proof treatment, by heat insulation, oxygen barrier, stops fuel gas effusion, plays flame retardant effect.But traditional halogen, phosphorous flame-retardant fiber, there is bigger toxicity, fiber burning release poisonous smog, cause " the secondary disaster ", being used alone heat-resistance and flame-retardant fiber spinning, fiber strength is low, and spinnability is poor, coating or pad the fabric of flame-proof treatment, sucting wet air permeability is poor, wears uncomfortable.
Summary of the invention
It is an object of the invention to provide a kind of moisture absorption smooth, comfortable and easy to wear, garment for children flame-retardant yarn possessing permanent fire retardant effect ventilative, soft and preparation method thereof, with the problem solving to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme:
A kind of garment for children flame-retardant yarn, is made up of according to the raw material of mass fraction following:
FRC 40-60 part
Flame-retardant acrylic fibre fiber 10-20 part
Modal fibre 30-40 part
Antistatic fibre 2-5 part.
As the further scheme of the present invention: described FRC fiber number 3.56 dtex, dry strong by 1.5
CN/dtex, wet strong 0.9cN/dtex, LOI
32%。
As the further scheme of the present invention: described flame-retardant acrylic fibre fiber dimensious is 1.56dtex × 38mm, LOI
29%。
As the further scheme of the present invention: described Modal fibre fiber number 1.3dtex, dry strong by 34
CN/dtex, wet strong 19 cN/dtex.
As the further scheme of the present invention: described antistatic fibre is silver chopped fiber, specification 3dtex × 38mm.
The preparation method of described garment for children flame-retardant yarn, comprises the following steps:
A. raw material prepares: by mass fraction by FRC, flame-retardant acrylic fibre fiber, Modal fibre, antistatic fibre mix homogeneously；
B. cotton cleaning process: above-mentioned ready raw material is put into opener shredding, through lapper rolling, prepares lap；
C. carding step: the lap carding machine obtained is carded to bar；
D. mixing in doubling step: use three drawing processes to carry out, prepares ripe bar；
E. Roving Frames: use and space greatly, ripe bar is spun as rove；
F. spinning process: rove is spun into spun yarn, prepared flame-retardant yarn.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention uses multiple fiber blend, and selected fiber does not contains halogen, and between each fiber, character is complementary, good spinnability, and the fabric moisture being made into is breathed freely, soft smooth, comfortable and easy to wear, possesses permanent fire retardant effect, fits entirely into garment for children fire protection flame retarding requirement.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described, it is clear that described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based on the embodiment in the present invention, the every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise, broadly fall into the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of garment for children flame-retardant yarn and preparation method thereof, raw material composition mass fraction is: FRC 40 parts, flame-retardant acrylic fibre fiber 20 parts, Modal fibre 40 parts, antistatic fibre 5 parts.
The preparation method of described flame-retardant yarn, comprises the following steps:
A. raw material prepares: by mass fraction by FRC, flame-retardant acrylic fibre fiber, Modal fibre, antistatic fibre mix homogeneously；
B. cotton cleaning process: above-mentioned ready raw material is put into opener shredding, through lapper rolling, prepares lap；
C. carding step: the lap carding machine obtained is carded to bar；
D. mixing in doubling step: use three drawing processes to carry out, prepares ripe bar；
E. Roving Frames: use and space greatly, ripe bar is spun as rove；
F. spinning process: rove is spun into spun yarn, prepared flame-retardant yarn.
Embodiment 2
In the embodiment of the present invention, a kind of garment for children flame-retardant yarn and preparation method thereof, raw material composition mass fraction is: FRC 50 parts, flame-retardant acrylic fibre fiber 18 parts, Modal fibre 38 parts, antistatic fibre 4 parts.
The preparation method of described flame-retardant yarn, comprises the following steps:
A. raw material prepares: by mass fraction by FRC, flame-retardant acrylic fibre fiber, Modal fibre, antistatic fibre mix homogeneously；
B. cotton cleaning process: above-mentioned ready raw material is put into opener shredding, through lapper rolling, prepares lap；
C. carding step: the lap carding machine obtained is carded to bar；
D. mixing in doubling step: use three drawing processes to carry out, prepares ripe bar；
E. Roving Frames: use and space greatly, ripe bar is spun as rove；
F. spinning process: rove is spun into spun yarn, prepared flame-retardant yarn.
Embodiment 3
In the embodiment of the present invention, a kind of garment for children flame-retardant yarn and preparation method thereof, raw material composition mass fraction is: FRC 55 parts, flame-retardant acrylic fibre fiber 15 parts, Modal fibre 35 parts, antistatic fibre 3 parts.
The preparation method of described flame-retardant yarn, comprises the following steps:
A. raw material prepares: by mass fraction by FRC, flame-retardant acrylic fibre fiber, Modal fibre, antistatic fibre mix homogeneously；
B. cotton cleaning process: above-mentioned ready raw material is put into opener shredding, through lapper rolling, prepares lap；
C. carding step: the lap carding machine obtained is carded to bar；
D. mixing in doubling step: use three drawing processes to carry out, prepares ripe bar；
E. Roving Frames: use and space greatly, ripe bar is spun as rove；
F. spinning process: rove is spun into spun yarn, prepared flame-retardant yarn.
Embodiment 4
In the embodiment of the present invention, a kind of garment for children flame-retardant yarn and preparation method thereof, raw material composition mass fraction is: FRC 60 parts, flame-retardant acrylic fibre fiber 10 parts, Modal fibre 30 parts, antistatic fibre 2 parts.
The preparation method of described flame-retardant yarn, comprises the following steps:
A. raw material prepares: by mass fraction by FRC, flame-retardant acrylic fibre fiber, Modal fibre, antistatic fibre mix homogeneously；
B. cotton cleaning process: above-mentioned ready raw material is put into opener shredding, through lapper rolling, prepares lap；
C. carding step: the lap carding machine obtained is carded to bar；
D. mixing in doubling step: use three drawing processes to carry out, prepares ripe bar；
E. Roving Frames: use and space greatly, ripe bar is spun as rove；
F. spinning process: rove is spun into spun yarn, prepared flame-retardant yarn.
Embodiment 5
In the embodiment of the present invention, a kind of garment for children flame-retardant yarn, it is made up of according to the raw material of mass fraction following:
FRC 45 parts
Flame-retardant acrylic fibre fiber 12 parts
Modal fibre 32 parts
Antistatic fibre 3 parts.
The preparation method of described flame-retardant yarn, comprises the following steps:
A. raw material prepares: by mass fraction by FRC, flame-retardant acrylic fibre fiber, Modal fibre, antistatic fibre mix homogeneously；
B. cotton cleaning process: above-mentioned ready raw material is put into opener shredding, through lapper rolling, prepares lap；
C. carding step: the lap carding machine obtained is carded to bar；
D. mixing in doubling step: use three drawing processes to carry out, prepares ripe bar；
E. Roving Frames: use and space greatly, ripe bar is spun as rove；
F. spinning process: rove is spun into spun yarn, prepared flame-retardant yarn.
Embodiment 6
In the embodiment of the present invention, a kind of garment for children flame-retardant yarn, it is made up of according to the raw material of mass fraction following:
FRC 55 parts
Flame-retardant acrylic fibre fiber 18 parts
Modal fibre 38 parts
Antistatic fibre 4 parts.
The preparation method of described flame-retardant yarn, comprises the following steps:
A. raw material prepares: by mass fraction by FRC, flame-retardant acrylic fibre fiber, Modal fibre, antistatic fibre mix homogeneously；
B. cotton cleaning process: above-mentioned ready raw material is put into opener shredding, through lapper rolling, prepares lap；
C. carding step: the lap carding machine obtained is carded to bar；
D. mixing in doubling step: use three drawing processes to carry out, prepares ripe bar；
E. Roving Frames: use and space greatly, ripe bar is spun as rove；
F. spinning process: rove is spun into spun yarn, prepared flame-retardant yarn.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, and without departing from the spirit or essential characteristics of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter from the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is limited by claims rather than described above, it is intended that all changes fallen in the implication of equivalency and scope of claim included in the present invention.
In addition, it is to be understood that, although this specification is been described by according to embodiment, but the most each embodiment only comprises an independent technical scheme, this narrating mode of description is only for clarity sake, description should can also be formed, through appropriately combined, other embodiments that it will be appreciated by those skilled in the art that as an entirety, the technical scheme in each embodiment by those skilled in the art.
Claims (6)
1. a garment for children flame-retardant yarn, it is characterised in that be made up of according to the raw material of mass fraction following:
FRC 40-60 part
Flame-retardant acrylic fibre fiber 10-20 part
Modal fibre 30-40 part
Antistatic fibre 2-5 part.
Garment for children flame-retardant yarn the most according to claim 1, it is characterised in that described is fire-retardant viscous
Glue fiber fiber number 3.56dtex, dry strong 1.5cN/dtex, wet strong 0.9cN/dtex, LOI 32%.
Garment for children flame-retardant yarn the most according to claim 1, it is characterised in that described fire-retardant nitrile
Synthetic fibre fiber dimensious is 1.56dtex × 38mm, LOI 29%.
Garment for children flame-retardant yarn the most according to claim 1, it is characterised in that described Modal
Fibre number 1.3dtex, dry strong 34cN/dtex, wet strong 19cN/dtex.
Garment for children flame-retardant yarn the most according to claim 1, it is characterised in that described antistatic
Fiber is silver chopped fiber, specification 3dtex × 38mm.
6. a preparation method for the garment for children flame-retardant yarn as described in claim 1-5 is arbitrary, its feature
It is, comprises the following steps:
A. raw material prepares: by mass fraction by FRC, flame-retardant acrylic fibre fiber, Modal fibre, anti-
Electrostatic fibre mix homogeneously；
B. cotton cleaning process: above-mentioned ready raw material is put into opener shredding, through lapper rolling, prepares
Lap；
C. carding step: the lap carding machine obtained is carded to bar；
D. mixing in doubling step: use three drawing processes to carry out, prepares ripe bar；
E. Roving Frames: use and space greatly, ripe bar is spun as rove；
F. spinning process: rove is spun into spun yarn, prepared flame-retardant yarn.