CN105821276A - Metal ceramic material - Google Patents
Metal ceramic material Download PDFInfo
- Publication number
- CN105821276A CN105821276A CN201610347096.8A CN201610347096A CN105821276A CN 105821276 A CN105821276 A CN 105821276A CN 201610347096 A CN201610347096 A CN 201610347096A CN 105821276 A CN105821276 A CN 105821276A
- Authority
- CN
- China
- Prior art keywords
- parts
- nbc
- aln
- component
- preservative
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a metal ceramic material. The metal ceramic material comprises the following components in parts by weight: 10-35 parts of AlN, 20-30 parts of Al2O3, 10-20 parts of Al, 5-20 parts of Cu, 2-5 parts of NbC, 3-12 parts of Cr3C2, 5-15 parts of Co, 2-10 parts of Mn, 3-10 parts of Ni, 0.1-0.3 part of a dispersing agent, 0.2-0.4 part of antiseptic, 0.3-0.5 part of preservative, and 0.2-0.4 part of an antifoaming agent. The metal ceramic material is excellent in heat conductivity and low in thermal expansivity, and resists high temperature, corrosion and wear.
Description
Technical field
Present invention relates particularly to a kind of cermet material.
Background technology
Ceramic-metal composite is by one or more ceramic phases and metal phase or alloy (being also matrix) institute group
The composite become.Ceramic phase in ceramic metal is to have high-melting-point, the oxide of high rigidity or infusible compound, metal phase
Mainly transition elements (ferrum, cobalt, nickel, chromium, tungsten, molybdenum etc.) and alloy thereof.Different according to each composition phase percentage, gold
Belong to pottery to be divided into pottery as substrate with metal for substrate two class.Ceramic base ceramic metal mainly has following a few class: 1. aoxidize
Thing based ceramic metal, with aluminium oxide, zirconium oxide, magnesium oxide, beryllium oxide etc. as matrix, is composited with tungsten, chromium or cobalt, tool
Have high temperature resistant, resist chemical, heat conductivity are good, mechanical strength high, can be used as the earthenware of guided missile nozzle insert, smelting metal
Crucible and metal cutting tool;2. carbide-base ceramics, with titanium carbide, carborundum, tungsten carbide etc. as matrix, with metallic cobalt,
The metal composite such as nickel, chromium, tungsten, molybdenum form, and have high rigidity, high-wearing feature, the feature such as high temperature resistant, be used for manufacturing cutting tool,
High-temperature bearing, sealing ring, pick up a die sleeve and turbine blade;3. nitride based ceramic metal, with titanium nitride, boron nitride, silicon nitride
It is matrix with tantalum nitride, there is superhard, shaking property of heat resistanceheat resistant and good high temperature creep, apply less.But current metal pottery
Porcelain poor thermal conductivity, coefficient of thermal expansion height, non-refractory, the most corrosion-resistant and abrasion.
Summary of the invention
Heat conductivity is good, coefficient of thermal expansion is low, high temperature resistant, corrosion-resistant and anti abrasive metal providing one for the purpose of the present invention
Ceramic material.
Technology and method in order to solve the employing of the above-mentioned problem present invention are as follows:
A kind of cermet material, including the component of following weight: AlN, 10-35 parts;Al2O3, 20-30 part;Al,
10-20 part;Cu, 5-20 part;NbC, 2-5 part;Cr3C2, 3-12 part;Co, 5-15 part;Mn, 2-10 part;Ni, 3-10 part;Dispersion
Agent, 0.1-0.3 part;Antifungus agent, 0.2-0.4 part;Preservative, 0.3-0.5 part;Defoamer, 0.2-0.4 part.
Further, including the component of following weight: AlN, 10 parts;Al2O3, 20 parts;Al, 10 parts;Cu, 5 parts;
NbC, 2 parts;Cr3C2, 3 parts;Co, 5 parts;Mn, 2 parts;Ni, 3 parts;Dispersant, 0.1 part;Antifungus agent, 0.2 part;Preservative, 0.3 part;
Defoamer, 0.2 part.
Further, including the component of following weight: AlN, 35 parts;Al2O3, 30 parts;Al, 20 parts;Cu, 20 parts;
NbC, 5 parts;Cr3C2, 12 parts;Co, 15 parts;Mn, 10 parts;Ni, 10 parts;Dispersant, 0.3 part;Antifungus agent, 0.4 part;Preservative,
0.5 part;Defoamer, 0.4 part.
Further, including the component of following weight: AlN, 25 parts;Al2O3, 25 parts;Al, 15 parts;Cu, 10 parts;
NbC, 3 parts;Cr3C2, 8 parts;Co, 10 parts;Mn, 6 parts;Ni, 7 parts;Dispersant, 0.2 part;Antifungus agent, 0.3 part;Preservative, 0.4
Part;Defoamer, 0.3 part.
Further, its preparation method comprises the steps:
(1) by component dispensing, the raw material prepared addition tumbling ball mill is carried out wet grinding;
(2) ball milling is to after the stipulated time, is filtered by slip, uses spray dryer to carry out atomization drying granulation;
(3) by after compressing for pellet, put in defat pressurization all-in-one oven and be sintered, can be prepared by.
The invention have the benefit that, compared to traditional SiC ceramic material, AlN pottery has lower thermal expansion
Coefficient, high thermal conductivity and good mechanical property, finished product bending strength is high, and hardness, toughness are high;Furthermore adding Cr can be significantly
Improve corrosion resistance and the thermostability of pottery;Add Cu can dispersion-strengtherning pottery Binder Phase, improve intensity;Adding Mn can
Strengthening Binder Phase, improves the intensity of pottery;Add Cr3C2The obdurability of pottery can be improved, reduce coefficient of friction, improve wear-resisting
Property;Add NbC and can improve the rigid of pottery.
Detailed description of the invention
Experimental example 1:
A kind of cermet material, including the component of following weight: AlN, 10 parts;Al2O3, 20 parts;Al, 10 parts;Cu,
5 parts;NbC, 2 parts;Cr3C2, 3 parts;Co, 5 parts;Mn, 2 parts;Ni, 3 parts;Dispersant, 0.1 part;Antifungus agent, 0.2 part;Preservative,
0.3 part;Defoamer, 0.2 part.
Its preparation method comprises the steps:
(1) by component dispensing, the raw material prepared addition tumbling ball mill is carried out wet grinding;
(2) ball milling is to after the stipulated time, is filtered by slip, uses spray dryer to carry out atomization drying granulation;
(3) by after compressing for pellet, put in defat pressurization all-in-one oven and be sintered, can be prepared by.
Experimental example 2:
A kind of cermet material,
Component including following weight: AlN, 35 parts;Al2O3, 30 parts;Al, 20 parts;Cu, 20 parts;NbC, 5 parts;
Cr3C2, 12 parts;Co, 15 parts;Mn, 10 parts;Ni, 10 parts;Dispersant, 0.3 part;Antifungus agent, 0.4 part;Preservative, 0.5 part;Froth breaking
Agent, 0.4 part.
Its preparation method comprises the steps:
(1) by component dispensing, the raw material prepared addition tumbling ball mill is carried out wet grinding;
(2) ball milling is to after the stipulated time, is filtered by slip, uses spray dryer to carry out atomization drying granulation;
(3) by after compressing for pellet, put in defat pressurization all-in-one oven and be sintered, can be prepared by.
Experimental example 3:
A kind of cermet material, including the component of following weight: AlN, 25 parts;Al2O3, 25 parts;Al, 15 parts;Cu,
10 parts;NbC, 3 parts;Cr3C2, 8 parts;Co, 10 parts;Mn, 6 parts;Ni, 7 parts;Dispersant, 0.2 part;Antifungus agent, 0.3 part;Anticorrosion
Agent, 0.4 part;Defoamer, 0.3 part.
Its preparation method comprises the steps:
(1) by component dispensing, the raw material prepared addition tumbling ball mill is carried out wet grinding;
(2) ball milling is to after the stipulated time, is filtered by slip, uses spray dryer to carry out atomization drying granulation;
(3) by after compressing for pellet, put in defat pressurization all-in-one oven and be sintered, can be prepared by.
Experimental example:
Carry out existing SiC ceramic material and this cermet material testing comparison, the results are shown in Table one.
Comparison result tested by table one
Material | Density | Hardness | Bending strength | Thermal coefficient of expansion |
SiC ceramic material | 3.22g/cm3 | 76HRA | 750N/mm2 | 3.8 |
Cermet material | 5.83g/cm3 | 94HRA | 913N/mm2 | 3.13 |
As can be seen here, this cermet material has higher hardness and bending strength compared to existing SiC ceramic material,
And thermal coefficient of expansion is less, there is the preferably suitability.
The invention have the benefit that, compared to traditional SiC ceramic material, AlN pottery has lower thermal expansion
Coefficient, high thermal conductivity and good mechanical property, finished product bending strength is high, and hardness, toughness are high;Furthermore adding Cr can be significantly
Improve corrosion resistance and the thermostability of pottery;Add Cu can dispersion-strengtherning pottery Binder Phase, improve intensity;Adding Mn can
Strengthening Binder Phase, improves the intensity of pottery;Add Cr3C2The obdurability of pottery can be improved, reduce coefficient of friction, improve wear-resisting
Property;Add NbC and can improve the rigid of pottery.
The above, the only detailed description of the invention of the present invention, but protection scope of the present invention is not limited thereto, and any
The change expected without creative work or replacement, all should contain within protection scope of the present invention, therefore, and the present invention's
Protection domain should be as the criterion with the protection domain that claims are limited.
Claims (5)
1. a cermet material, it is characterised in that include the component of following weight: AlN, 10-35 parts;Al2O3,
20-30 part;Al, 10-20 part;Cu, 5-20 part;NbC, 2-5 part;Cr3C2, 3-12 part;Co, 5-15 part;Mn, 2-10 part;Ni, 3-
10 parts;Dispersant, 0.1-0.3 part;Antifungus agent, 0.2-0.4 part;Preservative, 0.3-0.5 part;Defoamer, 0.2-0.4 part.
Cermet material the most according to claim 1, it is characterised in that include the component of following weight:
AlN, 10 parts;Al2O3, 20 parts;Al, 10 parts;Cu, 5 parts;NbC, 2 parts;Cr3C2, 3 parts;Co, 5 parts;Mn, 2 parts;Ni, 3 parts;Point
Powder, 0.1 part;Antifungus agent, 0.2 part;Preservative, 0.3 part;Defoamer, 0.2 part.
Cermet material the most according to claim 2, it is characterised in that include the component of following weight:
AlN, 35 parts;Al2O3, 30 parts;Al, 20 parts;Cu, 20 parts;NbC, 5 parts;Cr3C2, 12 parts;Co, 15 parts;Mn, 10 parts;Ni, 10
Part;Dispersant, 0.3 part;Antifungus agent, 0.4 part;Preservative, 0.5 part;Defoamer, 0.4 part.
Cermet material the most according to claim 3, it is characterised in that include the component of following weight:
AlN, 25 parts;Al2O3, 25 parts;Al, 15 parts;Cu, 10 parts;NbC, 3 parts;Cr3C2, 8 parts;Co, 10 parts;Mn, 6 parts;Ni, 7 parts;
Dispersant, 0.2 part;Antifungus agent, 0.3 part;Preservative, 0.4 part;Defoamer, 0.3 part.
Cermet material the most according to claim 1, it is characterised in that its preparation method comprises the steps:
(1) by component dispensing, the raw material prepared addition tumbling ball mill is carried out wet grinding;
(2) ball milling is to after the stipulated time, is filtered by slip, uses spray dryer to carry out atomization drying granulation;
(3) by after compressing for pellet, put in defat pressurization all-in-one oven and be sintered, can be prepared by.