CN105820530A - High-toughness fishing net - Google Patents
High-toughness fishing net Download PDFInfo
- Publication number
- CN105820530A CN105820530A CN201610234019.1A CN201610234019A CN105820530A CN 105820530 A CN105820530 A CN 105820530A CN 201610234019 A CN201610234019 A CN 201610234019A CN 105820530 A CN105820530 A CN 105820530A
- Authority
- CN
- China
- Prior art keywords
- fishing net
- superfine
- parts
- calcium carbonate
- high tenacity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-toughness fishing net which is prepared from the following raw materials in parts by weight: 150 to 165 parts of polycarbonate, 15 to 20 parts of superfine light-weight calcium carbonate, 5 to 6 parts of superfine talcum powder, 0.3 to 0.5 part of a titanate coupling agent, 0.6 to 1 part of stearic acid, 1 to 2 parts of castor oil and 0.2 to 0.4 part of carbon nano fibers. According to the high-toughness fishing net, due to premixing modification treatment of the superfine light-weight calcium carbonate and the superfine talcum powder, the fixed performance shortcoming of single ultrafine non-metal powder is effectively overcome due to a difference between different crystal form structures and chemical compositions between two different superfine non-metal powder bodies, so that modified premixed powder with compensatory performance advantages is formed; polycarbonate is used as a main base material, so that the use of additives is reduced; the added carbon nano fibers obviously improve the toughness of the fishing net.
Description
Technical field
The present invention relates to a kind of fishing net, be specially a kind of high tenacity fishing net.
Background technology
Fishing net is used to fishing, and present fishing net mainly nylon material is made, and not enough in terms of intensity, toughness, abrasion resistance, the fishing net intensity made is uneven, affects the quality of fishing net.
Summary of the invention
For solving problem above, the present invention provides following technical scheme:
A kind of high tenacity fishing net, is made up of the raw material of following weight portion: Merlon 150-165, superfine light calcium carbonate 15-20, superfine talcum powder 5-6, titanate coupling agent 0.3-0.5, stearic acid 0.6-1 part, Oleum Ricini 1-2, carbon nano-fiber 0.2-0.4.
Described superfine light calcium carbonate median particle diameter is 0.1-0.3um;
Described superfine talcum powder median particle diameter is 0.3-0.5um;
A kind of high tenacity fishing net, is made up of following steps:
(1) superfine light calcium carbonate and superfine talcum powder being put into blender and carry out premixing, heat while stir, blender rotating speed is 400-450r/min, when temperature reaches 110-120 DEG C, is incubated 3-5 minute;
(2) in blender, add titanate coupling agent, when being continuously heating to 150-160 DEG C, add stearic acid and Oleum Ricini, be incubated and within 5-6 minute, obtain modified premixing flour;
(3) modification premixing flour and Merlon, carbon nano-fiber are added extrusion, molding, establishment in extruder and i.e. obtain described high tenacity fishing net.
Beneficial effect:
Superfine light calcium carbonate and superfine talcum powder are carried out premixing modification by the present invention, utilize between two kinds of ultra-fine non-metallic powders of difference because the difference of different crystalline structures and chemical composition effectively makes up the performance deficiency that single ultra-fine non-metallic powder is intrinsic, form the modified premixing flour that performance is had complementary advantages;Using polycarbonate as main base material, decrease the use of additive, the carbon nano-fiber wherein added significantly improves the toughness of fishing net.
Detailed description of the invention
Embodiment 1
A kind of high tenacity fishing net, is made up of the raw material of following weight portion: Merlon 160, superfine light calcium carbonate 16, superfine talcum powder 5, titanate coupling agent 0.4, stearic acid 0.8 part, Oleum Ricini 1.5, carbon nano-fiber 0.2.
Described superfine light calcium carbonate median particle diameter is 0.2um;
Described superfine talcum powder median particle diameter is 0.4um;
A kind of high tenacity fishing net, is made up of following steps:
(1) superfine light calcium carbonate and superfine talcum powder being put into blender and carry out premixing, heat while stir, blender rotating speed is 450r/min, when temperature reaches 120 DEG C, is incubated 5 minutes;
(2) in blender, add titanate coupling agent, when being continuously heating to 150 DEG C, add stearic acid and Oleum Ricini, be incubated and within 6 minutes, obtain modified premixing flour;
(3) modification premixing flour and Merlon, carbon nano-fiber are added extrusion, molding, establishment in extruder and i.e. obtain described high tenacity fishing net.
Claims (4)
1. a high tenacity fishing net, it is characterised in that be made up of the raw material of following weight portion: Merlon 150-165, superfine light calcium carbonate 15-20, superfine talcum powder 5-6, titanate coupling agent 0.3-0.5, stearic acid 0.6-1 part, Oleum Ricini 1-2, carbon nano-fiber 0.2-0.4.
2. a kind of high tenacity fishing net as claimed in claim 1, it is characterised in that described superfine light calcium carbonate median particle diameter is 0.1-0.3um.
3. a kind of high tenacity fishing net as claimed in claim 1, it is characterised in that described superfine talcum powder median particle diameter is 0.3-0.5um.
4. a kind of high tenacity fishing net as claimed in claim 1, it is characterised in that be made up of following steps:
(1) superfine light calcium carbonate and superfine talcum powder being put into blender and carry out premixing, heat while stir, blender rotating speed is 400-450r/min, when temperature reaches 110-120 DEG C, is incubated 3-5 minute;
(2) in blender, add titanate coupling agent, when being continuously heating to 150-160 DEG C, add stearic acid and Oleum Ricini, be incubated and within 5-6 minute, obtain modified premixing flour;
(3) modification premixing flour and Merlon, carbon nano-fiber are added extrusion, molding, establishment in extruder and i.e. obtain described high tenacity fishing net.