CN105819725B - One vegetable oil reclaimed asphalt mixture and preparation method thereof - Google Patents
One vegetable oil reclaimed asphalt mixture and preparation method thereof Download PDFInfo
- Publication number
- CN105819725B CN105819725B CN201610142849.1A CN201610142849A CN105819725B CN 105819725 B CN105819725 B CN 105819725B CN 201610142849 A CN201610142849 A CN 201610142849A CN 105819725 B CN105819725 B CN 105819725B
- Authority
- CN
- China
- Prior art keywords
- component
- plant oil
- vegetable oil
- asphalt
- bitumen regenerant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to technical field of road engineering materials, it is related to vegetable oil reclaimed asphalt mixture and preparation method thereof, vegetable oil reclaimed asphalt mixture includes mineral aggregate, recycling mineral aggregate and vegetable oil regeneration asphalt, the vegetable oil regeneration asphalt includes recycling aged asphalt and plant oil base bitumen regenerant, and the lighter body in the plant oil base bitumen regenerant removes the light-weight plant obtained after impurity oil for waste edible oil.Compared with prior art, reclaimed asphalt mixture and preparation method thereof, mix temperature is low, and mixture service life is long, and pavement performance is good.
Description
Technical field
The present invention relates to technical field of road engineering materials more particularly to a vegetable oil reclaimed asphalt mixture and its systems
Preparation Method.
Background technology
In recent years, pitch regeneration and plant waste oil are recycled as a kind of new technology, are increasingly taken seriously.
The regeneration techniques of bituminous paving are by after pretreating process of the old asphalt pavement by milling, recycling, screening, adopt
Asphalt is mixed and stirred into again by a certain percentage with corresponding regeneration techniques and new pitch ground surface material, enables satisfaction one
Fixed pavement performance and with the technology of its surfacing again.Traditional Applied of Asphalt Pavement Recycle Technique mainly by pitch again
Raw agent carries out mixing and stirring regeneration at a high temperature of being added to old asphalt mixture and being heated to 150 DEG C -180 DEG C with new pitch and mineral aggregate.
At present, plant oil asphalt regeneration techniques are concerned, in order to effectively improve in plant oil asphalt regeneration techniques
Old material ratio, be badly in need of developing a kind of novel compound warm mix regenerative agent, this, which will become, realizes pavement material energy conservation and environmental protection and old
Expect the initiative technology of regeneration.
The Chinese invention patent application of Publication No. CN104788975A discloses a kind of pitch with modified function again
Raw agent and preparation method thereof, it is by lighter body, modified function component, stable equilibrium's component, infiltration enhancing component, discrete sets
Divide and fluidised form adjusts component and is prepared, mass fraction is shared by each component:30~60 parts of lighter body, modified function component
20~35 parts, 5~20 parts of stable equilibrium's component, infiltration 2~15 parts of component of enhancing, 2~10 parts of dispersed component, fluidised form adjusting component
1~10 part.
The Chinese invention patent application of Publication No. CN102585529A discloses a kind of drip prepared using waste edible oil
Green regenerative agent and its preparation process are formed, each component by waste edible oil, plasticizer, stabilizer and age resister through mixed preparing
Content is by weight percentage:Waste edible oil 85%-95%, plasticizer 2%-5%, stabilizer 2%-5%, age resister 1%-
5%.But also comprising many impurity, such as residue in kind in waste edible oil, and these impurity can be to the performance of employing of pitch, such as
Fatigue resistance adversely affects.
Invention content
The purpose of the present invention is exactly to be dripped to overcome the above-mentioned problems of the prior art, and provide a vegetable oil to regenerate
Green mixture and preparation method thereof.The vegetable oil reclaimed asphalt mixture is based on plant oil base bitumen regenerant and is made, plant
Oil base bitumen regenerant is a kind of composite polymer material, can directly, disposably be added to pitch or pitch mixes
It closes in material, realizes the regeneration of pitch or asphalt, and then realize the solid waste utilization and energy-saving and emission-reduction of ground surface material
Double effects.This bitumen regenerant can effectively restore the property indices of pitch and asphalt.
Plant oil base bitumen regenerant in the present invention can realize the regeneration of aged asphalt and old asphalt mixture,
Its aspect ratio can reach 40-50%, and the utilization rate of old material significantly improves, and then realizes solid waste recycling and subtract
The exploitation of few new material, preserves the ecological environment.
The purpose of the present invention can be achieved through the following technical solutions:
First aspect:The present invention provides a vegetable oil base bitumen regenerant.
One vegetable oil base bitumen regenerant including lighter body component, stablizes component and modified component, wherein, institute
Lighter body is stated as light-weight plant oil, the light-weight plant oil is preprocessed by waste edible oil, is obtained after removing impurity.
Waste edible oil is after high temperature, it is not easy to the phenomenon that light composition volatilization occurs, but there are many containing in waste edible oil
Impurity, such as swill, these impurity can cause not the regeneration efficiency of bitumen regenerant and the pavement performance of obtained pitch
Good influence, and after pretreatment so that the impurity in waste edible oil, such as swill are removed so that and it is purified,
So that the pavement performance of regeneration asphalt, such as fatigue resistance, are improved, the regeneration of pitch is really achieved, and pitch regenerates
It is efficient.
Preferably, the pretreatment includes centrifuging and/or filter.
In any of the above-described scheme preferably, the rotating speed of the centrifugation is 8000r/min, centrifugation time 10min.
In any of the above-described scheme preferably, the filtering is carried out by filter paper or strainer.
In any of the above-described scheme preferably, the aperture of the strainer is 0.667mm, and the aperture of filter paper is 90 μm.
In any of the above-described scheme preferably, the plant oil base bitumen regenerant is uniformly dispersed for wherein each component, does not have
There is the uniform compound of isolation lamination.
In any of the above-described scheme preferably, after the plant oil base bitumen regenerant is added in pitch, the plant
Oil base bitumen regenerant is reacted by the crosslinking (hardening) between the stable component and recycling aged asphalt, old with the recycling
Change pitch and form stable spacial framework, by recycling aged asphalt package in a network, keep chemical balance, reduce surface
Tension prevents light, thermal decomposition or oxygenolysis, prevents the lighter body component and recycles the separation of aged asphalt, significantly
Recycling aged asphalt viscosity is reduced, improves processing performance, improves the plasticity of bituminous cements.
In any of the above-described scheme preferably, the stable component includes resin and stearic acid.Resin and stearic acid energy
It crosslinks and reacts with the recycling aged asphalt, finally so that the plant oil base bitumen regenerant and the recycling aging drip
Blueness forms the solidfied material of three-dimensional crosslinking structure, stable structure, and is macroscopically significantly reducing recycling aged asphalt viscosity, improves work
Skill performance improves the plasticity of bituminous cements so that recycling aged asphalt obtains regeneration.
In any of the above-described scheme preferably, in the stable component, resin and stearic mass ratio are 1:1.
But in order to which aged asphalt is removed from old mixture, need to add in a large amount of trichloro ethylene so that aging drips
After blueness regeneration, viscosity can be more relatively low than new pitch, and resin is added in regenerative agent, can increase the viscosity of regeneration asphalt so that its
Viscosity is close to new pitch so that the caking property of regeneration asphalt is close to new pitch.
In any of the above-described scheme preferably, the resin is Petropols, preferably C5 Petropols or C9 oil
Resin.
In any of the above-described scheme preferably, the modified component is used for further improving the pavement performance of regeneration asphalt
And surface characteristic.
In any of the above-described scheme preferably, the modified component includes carbon black and/or lime.Add in lime and/or
Carbon black, is conducive to improve the fatigue resistance and water stability of regeneration asphalt, and then improves the fatigue resistance of reclaimed asphalt mixture
And water stability.Wherein lime can be quick lime or white lime, can achieve the effect that identical.
In any of the above-described scheme preferably, the grain size of the carbon black is 10nm.
Under the action of resin and stearic acid, carbon black or lime can be uniformly dispersed in the light-weight plant oil, and with institute
State the phenomenon that light-weight plant oil, resin, stearic acid form uniform product, be not in laminated segregation.
Certain in order to achieve the effect that, those skilled in the art can select other stable components and modified component, such as
It adds other stable components and/or modified component or replaces aforementioned stable component and/or modified component, and specific grain size can
To be selected or be changed according to actual needs.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 60-90%, stablizes component 5-20%, modified component 5-20%.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 70-90%, stablizes component 5-15%, modified component 5-15%.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 80-90%, stablizes component 5-10%, modified component 5-10%.
Vegetable oil in the plant oil base bitumen regenerant can be such that the asphalitine in recycling aged asphalt obtains well
Dispersion so that regeneration temperature reduces, energy saving, safe operation.
Light-weight plant oil stablizes component and modified component according to more than mass percent proportioning, obtained bitumen regenerant,
With high recycling aged asphalt regeneration efficiency, and the performance of regeneration asphalt can be improved well, and then regeneration is dripped
The performance of green mixture is improved.If the mass percent of light-weight plant oil is more than 90%, the stable component can be caused
And/or the content of modified component is on the low side, and the stability of the bitumen regenerant is caused harmful effect and/or, to regeneration drip
Green modification performance cannot be improved well;And if the content of the light-weight plant oil ingredient is less than 60%, it can cause
When regeneration asphalt, recycling the asphalitine of aged asphalt cannot scatter the bitumen regenerant well, reduce regeneration
Efficiency reduces the utilization rate of old mixture, reduces cost performance.
The plant oil base bitumen regenerant (i.e. the first aspect of the present invention) of the present invention, it is nontoxic, pollution-free, non-corrosive,
The phenomenon that being stabilized, will not generating isolation layering, raw material are common, are easy to get, cheap, and old to recycling
Change pitch regeneration effect is good, regeneration efficiency is high, it is environmentally friendly, while there is important economic implications and social effect,
The regenerated pitch of bitumen regenerant of the present invention, especially pavement performance, fatigue resistance and water stability are improved, and then
Improve the pavement performance of reclaimed asphalt mixture, extend Road Service Life.
The bitumen regenerant of the present invention, using the treated light-weight plant oil of waste edible oil as substrate, due to useless food
With oil by high temperature frying, frying etc., volatile component therein is not present already, and the temperature of waste edible oil experience is often high
Commonly used in pitch and mix and stir temperature, this causes during recycling aged asphalt is regenerated, prepare mixture during, it is described light
Matter vegetable oil will not volatilize, and reduce regeneration asphalt premature ageing, so that the service life of reclaimed asphalt mixture extends, and regenerate
It is efficient.
The plant oil base bitumen regenerant of the present invention, moreover it is possible to reduction recycling aged asphalt, which mixes and stirs temperature, can be reduced to 110 DEG C,
Operational hazards are reduced, it is energy saving.
Second aspect:The present invention also provides the preparation methods of a vegetable oil base bitumen regenerant.
The preparation method of plant oil base bitumen regenerant, includes the following steps:
(1) it using waste edible oil as raw material, is pre-processed, isolated light-weight plant oil ingredient;
(2) suitable light-weight plant oil ingredient is weighed, and is uniformly mixed with stablizing component and modified component;
(3) to get to the plant oil base bitumen regenerant after being aged at normal temperatures.
Bitumen regenerant preparation method prepared by the present invention can increase the content of light component in pitch, reduce asphalitine
Content effectively reduces pitch viscosity, restores asphalt performance.
The light-weight plant oil ingredient forms composite material after being mixed and stirred with the stable component and modified component, described compound
Material is plant oil base bitumen regenerant.
Preferably, the pretreatment includes centrifuging and/or filter.
In any of the above-described scheme preferably, the rotating speed of the centrifugation is 8000r/min, centrifugation time 10min.
In any of the above-described scheme preferably, the filtering is carried out by filter paper or strainer.
In any of the above-described scheme preferably, the aperture of the strainer is 0.667mm, and the aperture of filter paper is 90 μm.
In any of the above-described scheme preferably, the centrifugation and/or filtering carry out centrifugal filtration using filter centrifugal,
Centrifugation can be achieved and one step of filtering is completed, it is simple to operate.
In any of the above-described scheme preferably, the waste edible oil is before being centrifuged, being filtered, first by waste edible oil
Precipitation is carried out, to obtain better waste edible oil pretreating effect, the impurity in obtained light-weight plant oil is less, is prepared
Plant oil base bitumen regenerant to recycle aged asphalt regeneration efficiency higher.
In any of the above-described scheme preferably, the precipitation carries out 48~72 hours, preferably 48 hours, 60 hours or 72
Hour.
In any of the above-described scheme preferably, the stable component includes resin and stearic acid.
In any of the above-described scheme preferably, in the stable component, resin and stearic mass ratio are 1:1.
In any of the above-described scheme preferably, the resin is mixed with light-weight plant oil and the modified component
Before, first make its fusing, form fluid, in order to uniformly be mixed with light-weight plant oil and modified component.
In any of the above-described scheme preferably, the resin be Petropols, further preferably C5 Petropols or
C9 Petropols.
In any of the above-described scheme preferably, the modified component includes carbon black and/or lime.Add in lime or charcoal
It is black, be conducive to improve regeneration asphalt fatigue resistance and water stability, and then be turned up reclaimed asphalt mixture fatigue resistance and
Water stability.Wherein lime can be quick lime or white lime, can achieve the effect that identical.
In any of the above-described scheme preferably, the grain size of the carbon black is 10nm.
In any of the above-described scheme preferably, the light-weight plant oil ingredient and stablized component and modified component is old
The change time is 2-5h, further preferably 3-4h.
The present invention is proved by a large number of experiments, and in the digestion time of 2-5h, especially 3-4h, three kinds of substances can be mixed fully
It closes uniform.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient 60-90% stablizes component 5-20%, modified component 5-20%.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient 70-90% stablizes component 5-15%, modified component 5-15%.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 80-90%, stablizes component 5-10%, modified component 5-10%.
Light-weight plant oil stablizes component and modified component according to more than mass percent proportioning, obtained bitumen regenerant,
With high recycling aged asphalt regeneration efficiency, and the performance of regeneration asphalt can be improved well, and then regeneration is dripped
The performance of green mixture is improved.If the mass percent of light-weight plant oil is more than 90%, the stable component can be caused
And/or the content of modified component is on the low side, and the stability of the bitumen regenerant is caused harmful effect and/or, to regeneration drip
Green modification performance cannot be improved well;And if the content of the light-weight plant oil ingredient is less than 60%, it can cause
When regeneration asphalt, recycling the asphalitine of aged asphalt cannot scatter the bitumen regenerant well, reduce regeneration
Efficiency reduces the utilization rate of old mixture, reduces cost performance.
Plant oil base bitumen regenerant described in first aspect present invention has the following advantages:
The plant oil base bitumen regenerant is high to the regeneration efficiency for recycling aged asphalt, and additive amount is recycling aging drip
When 0.06 times green, you can meet the regeneration of recycling aged asphalt, dosage is few.
Preparation method described in second aspect of the present invention effectively solves plant waste oil using vegetable oil as primary raw material
Recycling problem;Bituminous concrete surface is enable to re-use, has achieved the purpose that energy-saving and emission-reduction and waste utilization;Operation letter
Just, it is of low cost, it is easy to implement.
Bitumen regenerant prepared by the preparation method described in second aspect of the present invention so that regenerated in recycling aged asphalt
In the process, during preparing mixture, the light-weight plant oil will not volatilize, and reduce regeneration asphalt premature ageing, and then make
The service life for obtaining reclaimed asphalt mixture extends, and regeneration efficiency is high, moreover it is possible to which reduction recycling aged asphalt, which mixes and stirs temperature, to be reduced to
110 DEG C, operational hazards are reduced, it is energy saving.
The plant oil base bitumen regenerant pitch of first aspect present invention preferably passes through the preparation method described in second aspect
Prepare, but and as limitation, that is to say, that the plant oil base bitumen regenerant of first aspect makes also by other methods
It is standby to obtain.
The third aspect:The present invention also provides a vegetable oil regeneration asphalts.
One vegetable oil regeneration asphalt, is a kind of composite material, and the vegetable oil regeneration asphalt includes recycling aged asphalt
With plant oil base bitumen regenerant, the plant oil base bitumen regenerant includes lighter body component, stablizes component and modification
Component, wherein, the lighter body is light-weight plant oil, and the light-weight plant oil is preprocessed by waste edible oil, goes to clean
It is obtained after matter.
After high temperature the phenomenon that light composition volatilizees will not easily occur for waste edible oil, but containing perhaps in waste edible oil
More impurity, such as swill, these impurity can cause the regeneration efficiency of bitumen regenerant and the pavement performance of obtained pitch
Harmful effect, and after pretreatment so that the impurity in waste edible oil, such as swill are removed so that it obtains pure
Change, so that the pavement performance of regeneration asphalt, such as fatigue resistance, are improved, be really achieved the regeneration of pitch, and pitch is again
Life is efficient.
Preferably, the pretreatment includes centrifuging and/or filter.
In any of the above-described scheme preferably, the rotating speed of the centrifugation is 8000r/min, centrifugation time 10min.
In any of the above-described scheme preferably, the filtering is carried out by filter paper or strainer.
In any of the above-described scheme preferably, the aperture of the strainer is 0.667mm, and the aperture of filter paper is 90 μm.
In any of the above-described scheme preferably, the centrifugation and/or filtering carry out centrifugal filtration using filter centrifugal,
Centrifugation can be achieved and one step of filtering is completed, it is simple to operate.
In any of the above-described scheme preferably, the plant oil base bitumen regenerant is uniformly dispersed for wherein each component, does not have
There is the uniform compound of isolation lamination.
In any of the above-described scheme preferably, after the plant oil base bitumen regenerant is added in pitch, the plant
Oil base bitumen regenerant is reacted by the crosslinking (hardening) between the stable component and recycling aged asphalt, old with the recycling
Change pitch and form stable spacial framework, by recycling aged asphalt package in a network, keep chemical balance, reduce surface
Tension prevents light, thermal decomposition or oxygenolysis, prevents the lighter body component and recycles the separation of aged asphalt, significantly
Recycling aged asphalt viscosity is reduced, improves processing performance, improves the plasticity of bituminous cements.
In any of the above-described scheme preferably, the stable component includes resin and stearic acid.Resin and stearic acid energy
It crosslinks and reacts with the recycling aged asphalt, finally so that the plant oil base bitumen regenerant and the recycling aging drip
Blueness forms the solidfied material of three-dimensional crosslinking structure, stable structure, and is macroscopically significantly reducing recycling aged asphalt viscosity, improves work
Skill performance improves the plasticity of bituminous cements so that recycling aged asphalt obtains regeneration.
In any of the above-described scheme preferably, in the stable component, resin and stearic mass ratio are 1:1.
But in order to which aged asphalt is removed from old mixture, need to add in a large amount of trichloro ethylene so that aging drips
After blueness regeneration, viscosity can be more relatively low than new pitch, and resin is added in regenerative agent, can increase the viscosity of regeneration asphalt so that its
Viscosity is close to new pitch so that the caking property of regeneration asphalt is close to new pitch.
In any of the above-described scheme preferably, the resin be Petropols, further preferably C5 Petropols or
C9 Petropols.
In any of the above-described scheme preferably, the modified component is used for further improving the pavement performance of regeneration asphalt
And surface characteristic.
In any of the above-described scheme preferably, the modified component includes carbon black and/or lime.Add in lime or charcoal
It is black, be conducive to improve regeneration asphalt fatigue resistance and water stability, and then improve reclaimed asphalt mixture fatigue resistance and
Water stability.Wherein lime can be quick lime or white lime, can achieve the effect that identical.
In any of the above-described scheme preferably, the grain size of the carbon black is 10nm.
Under the action of resin and stearic acid, carbon black or lime can be uniformly dispersed in the light-weight plant oil, and with institute
State the phenomenon that light-weight plant oil, resin, stearic acid form uniform product, be not in laminated segregation.
Certain in order to achieve the effect that, those skilled in the art can select other stable components and modified component, such as
It adds other stable components and/or modified component or replaces aforementioned stable component and/or modified component, and specific grain size can
To be selected or be changed according to actual needs.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 60-90%, stablizes component 5-20%, modified component 5-20%.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 70-90%, stablizes component 5-15%, modified component 5-15%.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 80-90%, stablizes component 5-10%, modified component 5-10%.
In any of the above-described scheme preferably, the mass percent of each component is in the vegetable oil regeneration asphalt, returns
Receive aged asphalt 90-94%, plant oil base bitumen regenerant 6-10%.
In any of the above-described scheme preferably, aged asphalt 91-93%, plant oil base bitumen regenerant 7-9% are recycled.
In any of the above-described scheme preferably, aged asphalt 92%, plant oil base bitumen regenerant 8% are recycled.
Due to the plant oil base bitumen regenerant of first aspect present invention, regeneration efficiency is high, addition recycling aged asphalt
At 0.06 times of quality, you can obtain good regeneration effect.
The vegetable oil regeneration asphalt of the present invention, nontoxic, pollution-free, raw material are common, cheap, environmentally friendly, can
Preferably to restore the properties of pitch, achieve energy-saving and emission reduction purposes simultaneously.The vegetable oil regeneration asphalt can be widely used for
The regions such as urban road, street, airport, harbour and mine.
Vegetable oil regeneration asphalt described in third face of the present invention, regeneration efficiency are high, and old mixture utilization rate is high, change give up into
Treasured, and the performance of regeneration asphalt can be good at being suitable for road close to new pitch or even identical with new pitch, and, compared to
New pitch, light-weight plant oil ingredient therein are not allowed volatile, and regeneration asphalt is non-aging so that road occupation time lengthening,
Energy saving, environmental protection is cost-effective.
Fourth aspect, the present invention also provides a kind of preparation methods of above-mentioned vegetable oil regeneration asphalt, include the following steps:
(1) aged asphalt is received by the way of extraction device extracting to old asphalt mixture;
(2) recycling aged asphalt is heated to mixing and stirring temperature;
(3) plant oil base bitumen regenerant is added in the recycling aged asphalt for having been heated to and mix and stir temperature and mixed
With;
(4) mixture of recycling aged asphalt and plant oil base bitumen regenerant after mixing and stirring, which is put into baking oven, to be sent out
It educates.
Preferably, the temperature of mixing and stirring of the recycling aged asphalt and plant oil base bitumen regenerant is 110-160 DEG C.More
It it is 130-150 DEG C preferably, to mix and stir temperature.Due to the regenerative agent of the present invention, recycling aged asphalt is heated to 110 DEG C,
It can soften asphalitine therein, into fluid state, convenient for being mixed and stirred with plant oil base bitumen regenerant.
In any of the above-described scheme preferably, the recycling aged asphalt and when mixing and stirring of plant oil base bitumen regenerant
Between be 5-60min.Preferably, mixing time 20-40min.
In any of the above-described scheme preferably, the development temperature of the recycling aged asphalt and plant oil base bitumen regenerant
Spend is 110 DEG C -160 DEG C.It after it will recycle aged asphalt and be mixed and stirred with plant oil base bitumen regenerant, is further kept the temperature, is protected
Card pitch mass-energy scatter well so that the favorable regeneration effect of pitch.
In any of the above-described scheme preferably, during the development of the recycling aged asphalt and plant oil base bitumen regenerant
Between be 30-60min.
In any of the above-described scheme preferably, the side of mixing and stirring of the recycling aged asphalt and plant oil base bitumen regenerant
Method is shear agitation, stir speed (S.S.) 2000-10000r/min.Using boxshear apparatus mix and stir at a high speed, stir speed (S.S.) is preferably
4000-6000r/min。
In any of the above-described scheme preferably, the mass percent of each component is in the vegetable oil regeneration asphalt, returns
Receive aged asphalt 90-94%, plant oil base bitumen regenerant 6-10%.It may further be preferable that recycling aged asphalt 91-
93%, plant oil base bitumen regenerant 7-9%.It is further preferred that recycling aged asphalt 92%, plant oil base bitumen regenerant
8%.
In any of the above-described scheme preferably, the preparation method of the plant oil base bitumen regenerant, including following step
Suddenly:
(1) it using waste edible oil as raw material, is pre-processed, isolated light-weight plant oil ingredient;
(2) suitable light-weight plant oil ingredient is weighed, and is uniformly mixed with stablizing component and modified component;
(3) to get to the plant oil base bitumen regenerant after being aged at normal temperatures.
Bitumen regenerant preparation method prepared by the present invention can increase the content of light component in pitch, reduce asphalitine
Content effectively reduces pitch viscosity, restores asphalt performance.
The light-weight plant oil ingredient and stablize component and modified component mix and stir after form composite material, the composite wood
Expect for plant oil base bitumen regenerant.
In any of the above-described scheme preferably, the pretreatment includes centrifuging and/or filter.
In any of the above-described scheme preferably, the rotating speed of the centrifugation is 8000r/min, centrifugation time 10min.
In any of the above-described scheme preferably, the filtering is carried out by filter paper or strainer.
In any of the above-described scheme preferably, the aperture of the strainer is 0.667mm, and the aperture of filter paper is 90 μm.
In any of the above-described scheme preferably, the centrifugation and/or filtering carry out centrifugal filtration using filter centrifugal,
Centrifugation can be achieved and one step of filtering is completed, it is simple to operate.
In any of the above-described scheme preferably, the waste edible oil is before being centrifuged, being filtered, first by waste edible oil
Precipitation is carried out, to obtain better waste edible oil pretreating effect, the impurity in obtained light-weight plant oil is less, is prepared
Plant oil base bitumen regenerant to recycle aged asphalt regeneration efficiency higher.
In any of the above-described scheme preferably, the precipitation carries out 48 hours.
In any of the above-described scheme preferably, the precipitation carries out 60 hours.
In any of the above-described scheme preferably, the precipitation carries out 72 hours.
In any of the above-described scheme preferably, the stable component includes resin and stearic acid.
In any of the above-described scheme preferably, the resin is mixed with light-weight plant oil and the modified component
Before, first make its fusing, form fluid, in order to uniformly be mixed with light-weight plant oil and modified component.
In any of the above-described scheme preferably, the resin is Petropols.
In any of the above-described scheme preferably, the resin is C5 Petropols.
In any of the above-described scheme preferably, the resin is C9 Petropols.
In any of the above-described scheme preferably, the modified component includes carbon black and/or lime.Add in lime or charcoal
It is black, be conducive to improve regeneration asphalt fatigue resistance and water stability, and then be turned up reclaimed asphalt mixture fatigue resistance and
Water stability.Wherein lime can be quick lime or white lime, can achieve the effect that identical.
In any of the above-described scheme preferably, the grain size of the carbon black is 10nm.
In any of the above-described scheme preferably, the light-weight plant oil ingredient and stablized component and modified component is old
The change time is 2-5h.
In any of the above-described scheme preferably, the light-weight plant oil ingredient and stablized component and modified component is old
The change time is 3-4h.
The present invention is proved by a large number of experiments, and in the digestion time of 2-5h, three kinds of substances can be sufficiently mixed uniformly.It is preferred that
, digestion time 3-4h.
The vegetable oil regeneration asphalt preparation method of the present invention, obtained vegetable oil regeneration asphalt, performance is close to new pitch, very
It is extremely identical with new pitch, it can be good at being suitable for road, and, compared to new pitch, light-weight plant oil ingredient therein is not allowed
Volatile, regeneration asphalt is non-aging so that road occupation time lengthening, energy saving, environmental protection are cost-effective.
5th aspect, the present invention also provides a vegetable oil reclaimed asphalt mixtures.
One vegetable oil reclaimed asphalt mixture, is composite material, and the vegetable oil reclaimed asphalt mixture includes mineral
Gather materials, recycle mineral aggregate and vegetable oil regeneration asphalt, the vegetable oil regeneration asphalt includes recycling aged asphalt and vegetable oil
Base bitumen regenerant, the plant oil base bitumen regenerant include lighter body component, stablize component and modified component,
In, the lighter body is light-weight plant oil, and the light-weight plant oil is preprocessed by waste edible oil, is obtained after removing impurity
It arrives.
After high temperature the phenomenon that light composition volatilizees will not easily occur for waste edible oil, but containing perhaps in waste edible oil
More impurity, such as swill, these impurity can cause the regeneration efficiency of bitumen regenerant and the pavement performance of obtained pitch
Harmful effect, and after pretreatment so that the impurity in waste edible oil, such as swill are removed so that it obtains pure
Change, so that the pavement performance of regeneration asphalt, such as fatigue resistance, are improved, be really achieved the regeneration of pitch, and pitch is again
Life is efficient.
Preferably, the pretreatment includes centrifuging and/or filter.
In any of the above-described scheme preferably, the rotating speed of the centrifugation is 8000r/min, centrifugation time 10min.
In any of the above-described scheme preferably, the filtering is carried out by filter paper or strainer.
In any of the above-described scheme preferably, the aperture of the strainer is 0.667mm, and the aperture of filter paper is 90 μm.
In any of the above-described scheme preferably, the plant oil base bitumen regenerant is uniformly dispersed for wherein each component, does not have
There is the uniform compound of isolation lamination.
In any of the above-described scheme preferably, after the plant oil base bitumen regenerant is added in pitch, the plant
Oil base bitumen regenerant is reacted by the crosslinking (hardening) between the stable component and recycling aged asphalt, old with the recycling
Change pitch and form stable spacial framework, by recycling aged asphalt package in a network, keep chemical balance, reduce surface
Tension prevents light, thermal decomposition or oxygenolysis, prevents the lighter body component and recycles the separation of aged asphalt, significantly
Recycling aged asphalt viscosity is reduced, improves processing performance, improves the plasticity of bituminous cements.
In any of the above-described scheme preferably, the stable component includes resin and stearic acid.Resin and stearic acid energy
It crosslinks and reacts with the recycling aged asphalt, finally so that the plant oil base bitumen regenerant and the recycling aging drip
Blueness forms the solidfied material of three-dimensional crosslinking structure, stable structure, and is macroscopically significantly reducing recycling aged asphalt viscosity, improves work
Skill performance improves the plasticity of bituminous cements so that recycling aged asphalt obtains regeneration.
In any of the above-described scheme preferably, in the stable component, resin and stearic mass ratio are 1:1.
But in order to which aged asphalt is removed from old mixture, need to add in a large amount of trichloro ethylene so that aging drips
After blueness regeneration, adherency can be more relatively low than new pitch, and resin is added in regenerative agent, can increase the viscosity of regeneration asphalt so that its
Viscosity is close to new pitch so that the caking property of regeneration asphalt is close to new pitch.
In any of the above-described scheme preferably, the resin is Petropols.
In any of the above-described scheme preferably, the resin is C5 Petropols.
In any of the above-described scheme preferably, the resin is C9 Petropols.
In any of the above-described scheme preferably, the modified component is used for further improving the pavement performance of regeneration asphalt
And surface characteristic.
In any of the above-described scheme preferably, the modified component includes carbon black and/or lime.Add in lime or charcoal
It is black, be conducive to improve regeneration asphalt fatigue resistance and water stability, and then be turned up reclaimed asphalt mixture fatigue resistance and
Water stability.Wherein lime can be quick lime or white lime, can achieve the effect that identical.
In any of the above-described scheme preferably, the grain size of the carbon black is 10nm.
Under the action of resin and stearic acid, carbon black or lime can be uniformly dispersed in the light-weight plant oil, and with institute
State the phenomenon that light-weight plant oil, resin, stearic acid form uniform product, be not in laminated segregation.
Certain in order to achieve the effect that, those skilled in the art can select other stable components and modified component, such as
It adds other stable components and/or modified component or replaces aforementioned stable component and/or modified component, and specific grain size can
To be selected or be changed according to actual needs.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 60-90%, stablizes component 5-20%, modified component 5-20%.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 70-90%, stablizes component 5-15%, modified component 5-15%.
In any of the above-described scheme preferably, the mass percent of each component in the plant oil base bitumen regenerant
For light-weight plant oil ingredient is 80-90%, stablizes component 5-10%, modified component 5-10%.
In any of the above-described scheme preferably, the mass percent of each component is in the vegetable oil regeneration asphalt, returns
Receive aged asphalt 90-94%, plant oil base bitumen regenerant 6-10%.Preferably, aged asphalt 91-93%, plant are recycled
Oil base bitumen regenerant 7-9%.It is further preferred that recycling aged asphalt 92%, plant oil base bitumen regenerant 8%.
In any of the above-described scheme preferably, the mass percent of each component in the vegetable oil reclaimed asphalt mixture
For mineral aggregate 40-60% recycles mineral aggregate 35-45%, vegetable oil regeneration asphalt 5-15%.
In any of the above-described scheme preferably, the mineral aggregate is alkali aggregate.
In any of the above-described scheme preferably, the mineral aggregate is basalt and/or diabase.
In any of the above-described scheme preferably, the grain size of the mineral aggregate be 26.5-37.5mm, 19.0-26.5mm,
16.0-19.0mm, 13.2-16.0mm, 4.75-9.5mm, 0.15-2.36mm and 0-0.075mm.
In any of the above-described scheme preferably, the mass percent of each grain size mineral aggregate is in the mineral aggregate,
Grain size 26.5-37.5mm is 0-10%, grain size 19.0-26.5mm is 0-10%, grain size 16.0-19.0mm is 0-20%, grain size
13.2-16.0mm is 0-20%, grain size 4.75-9.5mm is 15-50%, grain size 0.15-2.36mm is 40-70%, grain size 0-
0.075mm is 10-15%.
The grading of the mineral aggregate meets《Standard specification for construction and acceptance of highway asphalt pavement》The requirement of (JTG E20-2011),
And it disclosure satisfy that the construction requirements of asphalt highway upper, middle and lower face layer.
The present invention vegetable oil reclaimed asphalt mixture functional effect it is good, pollute small, at low cost, vegetable oil regeneration asphalt
It is mixed and stirred with recycling mineral aggregate, new mineral aggregate, the reclaimed asphalt mixture thus prepared is to have good pavement performance same
When also have good surface characteristic.
The vegetable oil reclaimed asphalt mixture of the present invention, regeneration asphalt therein are non-aging so that the vegetable oil is again
Raw asphalt usage time extends, and energy saving, environmental protection is cost-effective.
Lime or carbon black are added in plant oil base bitumen regenerant, is conducive to improve the fatigue resistance of vegetable oil regeneration asphalt
And water stability, and then the fatigue resistance and water stability of reclaimed asphalt mixture is turned up.
Plant oil base bitumen regenerant prepared by the preparation method of the present invention so that in the recycling regenerated process of aged asphalt
In, prepare mixture during, the light-weight plant oil will not volatilize, reduce regeneration asphalt premature ageing so that again
The service life of raw asphalt extends, and regeneration efficiency is high, moreover it is possible to which reduction recycling aged asphalt, which mixes and stirs temperature, can be reduced to 110
DEG C, operational hazards are reduced, it is energy saving.
6th aspect, the present invention also provides a kind of preparation methods of above-mentioned vegetable oil reclaimed asphalt mixture.
The preparation method of above-mentioned vegetable oil reclaimed asphalt mixture, includes the following steps:
(1) new mineral aggregate and old mineral aggregate are mixed and stirred;
(2) vegetable oil regeneration asphalt and new mineral aggregate, recycling mineral aggregate are mixed and stirred;
The vegetable oil regeneration asphalt includes recycling aged asphalt and plant oil base bitumen regenerant;
The plant oil base bitumen regenerant is light-weight plant oil ingredient, stablizes component and modified component, wherein, it is described light
Matter base oil is light-weight plant oil, and the light-weight plant oil is preprocessed by waste edible oil, is obtained after removing impurity.
Preferably, the preparation method of the vegetable oil regeneration asphalt, includes the following steps:
(1) aged asphalt is received by the way of extraction device extracting to old asphalt mixture;
(2) recycling aged asphalt is heated to mixing and stirring temperature;
(3) plant oil base bitumen regenerant is added in the recycling aged asphalt for having been heated to and mix and stir temperature and mixed
With;
(4) mixture of recycling aged asphalt and plant oil base bitumen regenerant after mixing and stirring, which is put into baking oven, to be sent out
It educates.
Preferably, the temperature of mixing and stirring of the recycling aged asphalt and plant oil base bitumen regenerant is 110-160 DEG C.More
It it is 130-150 DEG C preferably, to mix and stir temperature.Due to the regenerative agent of the present invention, recycling aged asphalt is heated to 110 DEG C,
It can soften asphalitine therein, into fluid state, convenient for being mixed and stirred with plant oil base bitumen regenerant.
In any of the above-described scheme preferably, the recycling aged asphalt and when mixing and stirring of plant oil base bitumen regenerant
Between be 5-60min.Preferably, mixing time 20-40min.
In any of the above-described scheme preferably, the development temperature of the recycling aged asphalt and plant oil base bitumen regenerant
Spend is 110 DEG C -160 DEG C.It after it will recycle aged asphalt and be mixed and stirred with plant oil base bitumen regenerant, is further kept the temperature, is protected
Card pitch mass-energy scatter well so that the favorable regeneration effect of pitch.
In any of the above-described scheme preferably, during the development of the recycling aged asphalt and plant oil base bitumen regenerant
Between be 30-60min.
In any of the above-described scheme preferably, the side of mixing and stirring of the recycling aged asphalt and plant oil base bitumen regenerant
Method is shear agitation, stir speed (S.S.) 2000-10000r/min.Using boxshear apparatus mix and stir at a high speed, stir speed (S.S.) is preferably
4000-6000r/min。
In any of the above-described scheme preferably, the mass percent of each component is in the vegetable oil regeneration asphalt, returns
Receive aged asphalt 90-94%, plant oil base bitumen regenerant 6-10%.Preferably, aged asphalt 91-93%, plant are recycled
Oil base bitumen regenerant 7-9%.It is further preferred that recycling aged asphalt 92%, plant oil base bitumen regenerant 8%.
In any of the above-described scheme preferably, the preparation method of the plant oil base bitumen regenerant, including following step
Suddenly:
(1) it using waste edible oil as raw material, is pre-processed, isolated light-weight plant oil ingredient;
(2) suitable light-weight plant oil ingredient is weighed, and is uniformly mixed with stablizing component and modified component;
(3) to get to the plant oil base bitumen regenerant after being aged at normal temperatures.
Bitumen regenerant preparation method prepared by the present invention can increase the content of light component in pitch, reduce asphalitine
Content effectively reduces pitch viscosity, restores asphalt performance.
The light-weight plant oil ingredient and stablize component and modified component mix and stir after form composite material, the composite wood
Expect for plant oil base bitumen regenerant.
In any of the above-described scheme preferably, the pretreatment includes centrifuging and/or filter.
In any of the above-described scheme preferably, the rotating speed of the centrifugation is 8000r/min, centrifugation time 10min.
In any of the above-described scheme preferably, the filtering is carried out by filter paper or strainer.
In any of the above-described scheme preferably, the aperture of the strainer is 0.667mm, and the aperture of filter paper is 90 μm.
In any of the above-described scheme preferably, the centrifugation and/or filtering carry out centrifugal filtration using filter centrifugal,
Centrifugation can be achieved and one step of filtering is completed, it is simple to operate.
In any of the above-described scheme preferably, the waste edible oil is before being centrifuged, being filtered, first by waste edible oil
Precipitation is carried out, to obtain better waste edible oil pretreating effect, the impurity in obtained light-weight plant oil is less, is prepared
Plant oil base bitumen regenerant to recycle aged asphalt regeneration efficiency higher.
In any of the above-described scheme preferably, the precipitation carries out 48 hours.
In any of the above-described scheme preferably, the precipitation carries out 60 hours.
In any of the above-described scheme preferably, the precipitation carries out 72 hours.
In any of the above-described scheme preferably, the stable component includes resin and stearic acid.
In any of the above-described scheme preferably, in the stable component, resin and stearic mass ratio are 1:1.
In any of the above-described scheme preferably, the resin is mixed with light-weight plant oil and the modified component
Before, first make its fusing, form fluid, in order to uniformly be mixed with light-weight plant oil and modified component.
In any of the above-described scheme preferably, the resin is Petropols.
In any of the above-described scheme preferably, the resin is C5 Petropols.
In any of the above-described scheme preferably, the resin is C9 Petropols.
In any of the above-described scheme preferably, the modified component includes carbon black and/or lime.Add in lime or charcoal
It is black, be conducive to improve regeneration asphalt fatigue resistance and water stability, and then be turned up reclaimed asphalt mixture fatigue resistance and
Water stability.Wherein lime can be quick lime or white lime, can achieve the effect that identical.
In any of the above-described scheme preferably, the grain size of the carbon black is 10nm.
In any of the above-described scheme preferably, the light-weight plant oil ingredient and stablized component and modified component is old
The change time is 2-5h.
In any of the above-described scheme preferably, the light-weight plant oil ingredient and stablized component and modified component is old
The change time is 3-4h.
The present invention is proved by a large number of experiments, and in the digestion time of 2-5h, three kinds of substances can be sufficiently mixed uniformly.It is preferred that
, digestion time 3-4h.
In any of the above-described scheme preferably, the temperature of mixing and stirring of the mineral aggregate and vegetable oil regeneration asphalt is 120-
170℃。
In any of the above-described scheme preferably, it is 140-150 DEG C to mix and stir temperature.
In any of the above-described scheme preferably, the mixing time of the mineral aggregate and vegetable oil regeneration asphalt is 50-
120s.Preferably, mixing time 80-100s.
The preparation method of the vegetable oil reclaimed asphalt mixture of the present invention, by the way that plant oil base bitumen regenerant is directly added
It is added in recycling aged asphalt, is prepared into vegetable oil regeneration asphalt, then the vegetable oil regeneration asphalt is directly appended to a deciding grade and level
In the mineral aggregate matched, vegetable oil reclaimed asphalt mixture is formed, the preparation method is simple, and cost control is good, reaches energy saving
The effect of emission reduction, and the vegetable oil reclaimed asphalt mixture has good pavement performance.
Description of the drawings
Fig. 1 is the stability result of the plant oil base bitumen regenerant in embodiment 1.1-1.13.
Specific embodiment
The present invention is described in detail with specific embodiment below in conjunction with the accompanying drawings.
Embodiment 1.1
One vegetable oil base bitumen regenerant is combined by light-weight plant oil ingredient, stable component, modified component,
Described in light-weight plant oil be the filtrate for obtaining waste edible oil after centrifuging, filtering, during centrifugation and filtering, institute
It states centrifugal filtration and filter centrifugal may be used, described is 8000r/min, centrifugation time 10min.The filtering is to pass through filter
Paper or strainer, the aperture of strainer is 0.667mm, and the aperture of filter paper is 90 μm.
The plant oil base bitumen regenerant is uniformly dispersed for wherein each component, does not isolate the uniform mixing of lamination
Object.
In this example, it is C5 Petropols and stearic acid to stablize component, and C5 Petropols form fluid through fusing in advance, with
Just it can be uniformly mixed with light-weight plant oil and modified component, conducive to uniform plant oil base bitumen regenerant is prepared.
In this example, modified component is carbon black.The grain size of the carbon black is 10nm.
In the plant oil base bitumen regenerant of the present embodiment, the mass percent of light-weight plant oil ingredient is 60%, is stablized
The mass percent of component respectively accounts for 10% for 20%, C5 Petropols and stearic acid, and the mass percent of carbon black is 20%.
By taking 10000g recycles aged asphalt as an example, the preparation method of above-mentioned plant oil base bitumen regenerant is as follows:
1) using waste edible oil as raw material, first precipitation 48 hours to waste edible oil centrifuged using filter centrifugal
Filter, the rotating speed of centrifugation are 8000r/min, centrifugation time 10min, isolated light-weight plant oil ingredient;
2) light-weight plant oil is weighed, and the light-weight plant oil ingredient weighed is poured into container, it is and described steady
Determine component and modified component mixing, can select to sequentially add stable component and modified component;
3) it is aged 2 hours at normal temperatures to get to the plant oil base bitumen regenerant.
The plant oil base bitumen regenerant that need to be prepared is to recycle 0.06 times of aged asphalt, i.e. 600g.Plant oil base pitch
In regenerative agent, the mass percent of light-weight plant oil ingredient is 60%, i.e. 360g;The mass percent for stablizing component is 20%,
That is 120g (C5 Petropols 60g, stearic acid 60g), the mass percent of anti-strip component is 20%, i.e. 120g.
Embodiment 1.2
One vegetable oil base bitumen regenerant, it is substantially the same manner as Example 1, unlike, the plant oil base of the present embodiment
In bitumen regenerant, the mass percent of light-weight plant oil ingredient is 70%, and the mass percent for stablizing component is 15%, anti-stripping
The mass percent for falling component is 15%.
In the preparation process of the plant oil base bitumen regenerant, equally by taking 10000g recycles aged asphalt as an example, need to make
Standby plant oil base bitumen regenerant is to recycle 0.07 times of aged asphalt, i.e. 700g.In plant oil base bitumen regenerant, lightweight
The mass percent of vegetable oil component is 70%, i.e. 490g;The mass percent for stablizing component is 15%, i.e. 105g (stearic acid
With each 52.5g of C5 Petropols), the mass percent of carbon black (as modified component, also serving as anti-strip component) is 15%, i.e.,
105g。
In the present embodiment, the digestion time that mixes and stirs of lightweight oil ingredient, stable component and modified component is 3h, and waste edible oil is first
Precipitation 60 hours.
Embodiment 1.3
One vegetable oil base bitumen regenerant, it is substantially the same manner as Example 1, unlike, the plant oil base of the present embodiment
In bitumen regenerant, the mass percent of light-weight plant oil ingredient is 80%, and the mass percent for stablizing component is 10%, anti-stripping
The mass percent for falling component is 10%.
In the preparation process of the plant oil base bitumen regenerant, equally by taking 10000g recycles aged asphalt as an example, need to make
Standby plant oil base bitumen regenerant is to recycle 0.08 times of aged asphalt, i.e. 800g.In plant oil base bitumen regenerant, lightweight
The mass percent of vegetable oil component is 80%, i.e. 640g;The mass percent for stablizing component is 10%, i.e. 180g (C5 oil
Resin and each 90g of stearic acid), the mass percent of carbon black is 10%, i.e. 180g.
In the present embodiment, the digestion time that mixes and stirs of lightweight oil ingredient, stable component and modified component is 4h, and waste edible oil is first
Precipitation 72 hours.
Embodiment 1.4
One vegetable oil base bitumen regenerant, it is substantially the same manner as Example 1, unlike, the plant oil base of the present embodiment
In bitumen regenerant, the mass percent of light-weight plant oil ingredient is 90%, and the mass percent for stablizing component is 5%, anti-stripping
The mass percent for falling component is 5%.
In the preparation process of the plant oil base bitumen regenerant, equally, by taking 10000g recycles aged asphalt as an example, need to make
Standby plant oil base bitumen regenerant is to recycle 0.09 times of aged asphalt, i.e. 900g.In plant oil base bitumen regenerant, lightweight
The mass percent of vegetable oil component is 90%, i.e. 810g;The mass percent for stablizing component is 5%, i.e. 45g (C5 oil trees
Fat and each 22.5g of stearic acid), the mass percent of carbon black is 5%, i.e. 45g.
In the present embodiment, the digestion time that mixes and stirs of lightweight oil ingredient, stable component and modified component is 5h.
Embodiment 1.5
One vegetable oil base bitumen regenerant, it is essentially identical with above-described embodiment, unlike, the modified component is stone
Ash.Lime can be quick lime or white lime.
Identical method can be selected in the preparation method of the plant oil base bitumen regenerant.
Embodiment 1.6
One vegetable oil base bitumen regenerant, it is essentially identical with above-described embodiment, unlike, the modified component is charcoal
Black and lime, and carbon black is identical with the additive amount of lime.Lime can be quick lime or white lime.
Identical method can be selected in the preparation method of the plant oil base bitumen regenerant.
Embodiment 1.7
One vegetable oil base bitumen regenerant, it is essentially identical with above-described embodiment, unlike, stablize in component, it is stearic
Acid accounts for 60%, C5 Petropols 40%.
Identical method can be selected in the preparation method of the plant oil base bitumen regenerant.
Embodiment 1.8
One vegetable oil base bitumen regenerant, it is essentially identical with above-described embodiment, unlike, stablize component as tristearin
Acid.
Identical method can be selected in the preparation method of the plant oil base bitumen regenerant.
Embodiment 1.9
One vegetable oil base bitumen regenerant, it is essentially identical with above-described embodiment, unlike, stablize component C5 oil trees
Fat.
Identical method can be selected in the preparation method of the plant oil base bitumen regenerant.
Embodiment 1.10
One vegetable oil base bitumen regenerant, it is essentially identical with above-described embodiment, unlike, stablize component C9 oil trees
Fat.
Identical method can be selected in the preparation method of the plant oil base bitumen regenerant.
Embodiment 1.11
One vegetable oil base bitumen regenerant, it is essentially identical with above-described embodiment, unlike, the plant oil base pitch
The preparation of regenerative agent is without precipitation.
Embodiment 1.12
One vegetable oil base bitumen regenerant, it is essentially identical with above-described embodiment, unlike, the plant oil base pitch
The preparation of regenerative agent is without centrifugal filtration.
Embodiment 1.13
One vegetable oil base bitumen regenerant, it is essentially identical with above-described embodiment, unlike, the plant oil base pitch
The preparation of regenerative agent is without ageing.
Embodiment 2.1
One vegetable oil regeneration asphalt, is composite material, and the vegetable oil regeneration asphalt includes recycling aged asphalt and plant
Object oil base bitumen regenerant.Light-weight plant oil 80%, stable component 10%, modified component in the plant oil base bitumen regenerant
10%.
For preparing 10000g vegetable oil regeneration asphalts, the mass percent that need to recycle aged asphalt is 94%, i.e.,
9400g, it is 6% that need to prepare plant oil base bitumen regenerant mass percent, i.e. 600g.Preparing plant oil base bitumen regenerant
During, light-weight plant oil ingredient 480g is needed, stablizes component 60g (C5 Petropols and each 30g of stearic acid), modified component
(carbon black, grain size 10nm) 60g.
The preparation method of above-mentioned vegetable oil regeneration asphalt is as follows:
(1) aged asphalt is recycled in a manner of extracting from old asphalt mixture;
(2) recycling aged asphalt is heated to mixing and stirring temperature;
(3) plant oil base bitumen regenerant is added in the recycling aged asphalt for having been heated to and mix and stir temperature and mixed
With;
(4) mixture of recycling aged asphalt and plant oil base bitumen regenerant after mixing and stirring, which is put into baking oven, to be sent out
It educates.
Recycling aged asphalt and plant oil base bitumen regenerant mix and stir temperature be 115 DEG C, mixing time 50min;It returns
The developmental temperature for receiving aged asphalt and plant oil base bitumen regenerant is 115 DEG C, development time 30min.Using boxshear apparatus into
Row mixes and stirs at a high speed, stir speed (S.S.) 4000r/min.
Embodiment 2.2
One vegetable oil regeneration asphalt, it is essentially identical with embodiment 2.1, unlike, equally, to prepare 10000g plants
For oil regeneration pitch, the mass percent that need to recycle aged asphalt is 93%, i.e. 9300g, need to prepare plant oil base pitch again
Raw agent mass percent is 7%, i.e. 700g.During plant oil base bitumen regenerant is prepared, light-weight plant oil ingredient is needed
560g stablizes component 70g (C5 Petropols and each 35g of stearic acid), modified component (carbon black, grain size 10nm) 70g.
The preparation method of above-mentioned vegetable oil regeneration asphalt is as follows:
(1) aged asphalt is recycled in a manner of extracting from old asphalt mixture;
(2) recycling aged asphalt is heated to mixing and stirring temperature;
(3) plant oil base bitumen regenerant is added in the recycling aged asphalt for having been heated to and mix and stir temperature and mixed
With;
(4) mixture of recycling aged asphalt and plant oil base bitumen regenerant after mixing and stirring, which is put into baking oven, to be sent out
It educates.
Recycling aged asphalt and plant oil base bitumen regenerant mix and stir temperature be 130 DEG C, mixing time 60min;It returns
The developmental temperature for receiving aged asphalt and plant oil base bitumen regenerant is 130 DEG C, development time 40min.Using boxshear apparatus into
Row mixes and stirs at a high speed, stir speed (S.S.) 4000r/min.
Embodiment 2.3
One vegetable oil regeneration asphalt, it is essentially identical with embodiment 2.1, unlike, equally to prepare 10000g plants
For oil regeneration pitch, the mass percent that need to recycle aged asphalt is 92%, i.e. 9200g, need to prepare plant oil base pitch again
Raw agent mass percent is 8%, i.e. 800g.During plant oil base bitumen regenerant is prepared, light-weight plant oil ingredient is needed
640g stablizes component 80g (C5 Petropols and each 35g of stearic acid), modified component (carbon black, grain size 10nm) 80g.
The preparation method of above-mentioned vegetable oil regeneration asphalt is as follows:
(1) aged asphalt is recycled in a manner of extracting from old asphalt mixture;
(2) recycling aged asphalt is heated to mixing and stirring temperature;
(3) plant oil base bitumen regenerant is added in the recycling aged asphalt for having been heated to and mix and stir temperature and mixed
With;
(4) mixture of recycling aged asphalt and plant oil base bitumen regenerant after mixing and stirring, which is put into baking oven, to be sent out
It educates.
Recycling aged asphalt and plant oil base bitumen regenerant mix and stir temperature be 145 DEG C, mixing time 70min;It returns
The developmental temperature for receiving aged asphalt and plant oil base bitumen regenerant is 145 DEG C, development time 50min.Using boxshear apparatus into
Row mixes and stirs at a high speed, stir speed (S.S.) 4000r/min.
Embodiment 2.4
One vegetable oil regeneration asphalt, it is essentially identical with embodiment 2.1, unlike, equally to prepare 10000g plants
For oil regeneration pitch, the mass percent that need to recycle aged asphalt is 91%, i.e. 9100g, need to prepare plant oil base pitch again
Raw agent mass percent is 9%, i.e. 900g.During plant oil base bitumen regenerant is prepared, light-weight plant oil ingredient is needed
720g stablizes component 90g (C5 Petropols and each 35g of stearic acid), modified component (carbon black, grain size 10nm) 90g.
The preparation method of above-mentioned vegetable oil regeneration asphalt is as follows:
(1) aged asphalt is recycled in a manner of extracting from old asphalt mixture;
(2) recycling aged asphalt is heated to mixing and stirring temperature;
(3) plant oil base bitumen regenerant is added in the recycling aged asphalt for having been heated to and mix and stir temperature and mixed
With;
(4) mixture of recycling aged asphalt and plant oil base bitumen regenerant after mixing and stirring, which is put into baking oven, to be sent out
It educates.
Recycling aged asphalt and plant oil base bitumen regenerant mix and stir temperature be 160 DEG C, mixing time 80min;It returns
The developmental temperature for receiving aged asphalt and plant oil base bitumen regenerant is 160 DEG C, development time 60min.Using boxshear apparatus into
Row mixes and stirs at a high speed, stir speed (S.S.) 4000r/min.
Embodiment 2.5
One vegetable oil regeneration asphalt, unlike embodiment 2.1, light-weight plant oil in plant oil base bitumen regenerant
90%th, stablize component 5%, modified component 5%.
When preparing the vegetable oil regeneration asphalt, that recycles aged asphalt and plant oil base bitumen regenerant mixes and stirs temperature
It is 110 DEG C, mixing time 60min;The developmental temperature for recycling aged asphalt and plant oil base bitumen regenerant is 110 DEG C, hair
The time is educated for 30min.Using boxshear apparatus mix and stir at a high speed, stir speed (S.S.) 4000r/min.
Embodiment 2.6
One vegetable oil regeneration asphalt, unlike embodiment 2.1, light-weight plant oil in plant oil base bitumen regenerant
70%th, stablize component 15%, modified component 15%.
When preparing the vegetable oil regeneration asphalt, that recycles aged asphalt and plant oil base bitumen regenerant mixes and stirs temperature
It is 120 DEG C, mixing time 60min;The developmental temperature for recycling aged asphalt and plant oil base bitumen regenerant is 120 DEG C, hair
The time is educated for 30min.Using boxshear apparatus mix and stir at a high speed, stir speed (S.S.) 4000r/min.
Embodiment 2.7
One vegetable oil regeneration asphalt, unlike embodiment 2.1, light-weight plant oil in plant oil base bitumen regenerant
60%th, stablize component 20%, modified component 20%.
When preparing the vegetable oil regeneration asphalt, that recycles aged asphalt and plant oil base bitumen regenerant mixes and stirs temperature
It is 150 DEG C, mixing time 60min;The developmental temperature for recycling aged asphalt and plant oil base bitumen regenerant is 110 DEG C, hair
The time is educated for 30min.Using boxshear apparatus mix and stir at a high speed, stir speed (S.S.) 4000r/min.
Embodiment 2.8
One vegetable oil regeneration asphalt and preparation method thereof, it is essentially identical with above-described embodiment, unlike, the modification
Component is lime.
Embodiment 2.9
One vegetable oil regeneration asphalt and preparation method thereof, it is essentially identical with above-described embodiment, unlike, the modification
Component is carbon black and lime, and carbon black is identical with the additive amount of lime.
Embodiment 2.10
One vegetable oil regeneration asphalt and preparation method thereof, it is essentially identical with above-described embodiment, unlike, stablize component
In, stearic acid accounts for 60%, C5 Petropols 40%.
Embodiment 2.11
One vegetable oil regeneration asphalt and preparation method thereof, it is essentially identical with above-described embodiment, unlike, stablize component
For stearic acid.
Embodiment 2.12
One vegetable oil regeneration asphalt and preparation method thereof, it is essentially identical with above-described embodiment, unlike, stablize component
C5 Petropols.
Embodiment 2.13
One vegetable oil regeneration asphalt and preparation method thereof, it is essentially identical with above-described embodiment, unlike, stablize component
For C9 Petropols.
Embodiment 3.1
One vegetable oil reclaimed asphalt mixture, is composite material, and the vegetable oil reclaimed asphalt mixture includes new ore deposit
Matter gathers materials, recycles mineral aggregate and vegetable oil regeneration asphalt.Described vegetable oil regeneration asphalt and preparation method thereof is embodiment
One kind in 2.1-2.13, including recycling aged asphalt and plant oil base bitumen regenerant.The plant oil base bitumen regenerant
And preparation method thereof to be a kind of in embodiment 1.1-1.10, including lightweight oil ingredient, stablize component and modified component.
In the present embodiment, mineral aggregate is basalt.
The mass percent of each grain size mineral aggregate is in the mineral aggregate, and grain size 26.5-37.5mm is 0-10%, grain
Diameter 19.0-26.5mm is 0-10%, grain size 16.0-19.0mm is 0-20%, grain size 13.2-16.0mm is 0-20%, grain size
4.75-9.5mm is 15-50%, grain size 0.15-2.36mm is 40-70%, grain size 0-0.075mm is 10-15%.
For preparing 10000g vegetable oil reclaimed asphalt mixtures, the mass percent for needing new mineral aggregate is 60%,
That is 6000g;The mass percent that mineral aggregate need to be recycled is 35%, i.e. 3500g;The quality hundred of vegetable oil regeneration asphalt need to be prepared
Divide than being 5%, i.e. 500g.
The preparation method of above-mentioned vegetable oil reclaimed asphalt mixture is as follows:
(1) new mineral aggregate and old mineral aggregate are mixed and stirred in proportion;
(2) vegetable oil regeneration asphalt and new mineral aggregate, recycling mineral aggregate are mixed at a certain temperature by a certain percentage
And certain time.
Mineral aggregate, vegetable oil regeneration asphalt mix and stir temperature as 130 DEG C, mixing time 90s.
Embodiment 3.2
One vegetable oil reclaimed asphalt mixture, it is essentially identical with embodiment 3.1, unlike, in the present embodiment, mineral
Gather materials for basalt.
For preparing 10000g vegetable oil reclaimed asphalt mixtures, the mass percent for needing new mineral aggregate is 50%,
That is 5000g;The mass percent that mineral aggregate need to be recycled is 40%, i.e. 4000g;The quality hundred of vegetable oil regeneration asphalt need to be prepared
Divide than being 10%, i.e. 1000g.
The preparation method of above-mentioned vegetable oil reclaimed asphalt mixture is identical with embodiment 3.1
Embodiment 3.3
One vegetable oil reclaimed asphalt mixture, it is essentially identical with embodiment 3.1, unlike, in the present embodiment, mineral
Gather materials for basalt.
For preparing 10000g vegetable oil reclaimed asphalt mixtures, the mass percent for needing new mineral aggregate is 40%,
That is 4000g;The mass percent that mineral aggregate need to be recycled is 45%, i.e. 4500g;The quality hundred of vegetable oil regeneration asphalt need to be prepared
Divide than being 15%, i.e. 1500g.
The preparation method of above-mentioned vegetable oil reclaimed asphalt mixture is identical with embodiment 3.1.
Embodiment 3.4
One vegetable oil reclaimed asphalt mixture, unlike the embodiments above, mineral aggregate is dripped with plant oil regeneration
Green temperature of mixing and stirring is 120 DEG C, mixing time 120s.
Embodiment 3.5
One vegetable oil reclaimed asphalt mixture, unlike the embodiments above, mineral aggregate is dripped with plant oil regeneration
Green temperature of mixing and stirring is 140 DEG C, mixing time 100s.
Embodiment 3.6
One vegetable oil reclaimed asphalt mixture, unlike the embodiments above, mineral aggregate is dripped with plant oil regeneration
Green temperature of mixing and stirring is 150 DEG C, mixing time 80s.
Embodiment 3.7
One vegetable oil reclaimed asphalt mixture, unlike the embodiments above, mineral aggregate is dripped with plant oil regeneration
Green temperature of mixing and stirring is 170 DEG C, mixing time 50s.
Embodiment 3.8
One vegetable oil reclaimed asphalt mixture, it is unlike the embodiments above, used regenerative agent be without
The vegetable oil of precipitation.
Embodiment 3.9
One vegetable oil reclaimed asphalt mixture, it is unlike the embodiments above, used regenerative agent be without
The vegetable oil of centrifugal filtration.
Embodiment 3.10
One vegetable oil reclaimed asphalt mixture, it is unlike the embodiments above, used regenerative agent be without
The vegetable oil of ageing.
The performance test results of plant oil base bitumen regenerant prepared by embodiment 1.1 to embodiment 1.13 such as 1 institute of table
Show.
The performance test results of 1 plant oil base bitumen regenerant of table
The stability result of plant oil base bitumen regenerant in embodiment 1.1-1.13 is as shown in Figure 1, can be with from Fig. 1
Find out, the stability of vegetable oil regenerative agent is very good, can stablize preservation, is not in the phenomenon that isolation is layered.
Foundation《Highway engineering pitch and Asphalt Mixture Experiment regulation》(JTJ E20-2011) is to embodiment 2.1 to implementation
Vegetable oil regeneration asphalt prepared by example 2.13 carries out the performance tests such as needle penetration, ductility, softening point, viscosity, and test result is such as
Shown in table 2.
The performance test results of 2 vegetable oil regeneration asphalt of table
From Table 2, it can be seen that the regenerated vegetable oil regeneration asphalt of plant oil base bitumen regenerant of the present invention, each side
Face performance is very close with new pitch, illustrates, recycling aged asphalt regeneration effect is very good.And vegetable oil regeneration asphalt is anti-
Fatigability and water stability are significantly larger than new pitch, and the fatigue resistance and water stability for illustrating vegetable oil regeneration asphalt compare new pitch
Fortunately, non-aging, service life is long.
On the other hand, during regeneration asphalt, the additive amount of plant oil base bitumen regenerant is considerably less, even less than plants
The 10% of object oil regeneration pitch illustrates that plant oil base bitumen regenerant is very high to the regeneration efficiency for recycling aged asphalt, sexual valence
Than very high.
Vegetable oil reclaimed asphalt mixture prepared by embodiment 3.1 to embodiment 3.7 is subjected to high temperature dynamic stability, low
Warm cracking resistance and freeze-thaw split test, test result are as shown in table 3.From the point of view of test result, vegetable oil reclaimed asphalt mixture
High temperature stability performance, crack resistance at low-temperature and water stability can effectively be restored.
The pavement performance test result of 3 vegetable oil reclaimed asphalt mixture of table
From table 3 it is observed that the performance of vegetable oil reclaimed asphalt mixture is much better than the mixed of new pitch preparation
Material, especially fatigue resistance and water stability are closed, illustrates the regenerated plant oil regeneration of plant oil base bitumen regenerant of the present invention
Pitch helps to improve the pavement performance of reclaimed asphalt mixture, especially fatigue resistance and water stability.
Waste edible oil (without the waste vegetable oil of centrifugal filtration), the light-weight plant oil and mineral obtained by centrifugal filtration
Bitumen regenerant regeneration efficiency that matter oil (aromatic naphtha, furfural oil) single-factor variable is prepared, the ageing resistance of regeneration asphalt,
Fatigue resistance, water stability comparison are as shown in table 4.
Table 4 is by centrifugal filtration, the regeneration effect without centrifugal filtration vegetable oil and mineral oil
From table 4, it can be seen that bitumen regenerant (this that the light-weight plant oil obtained by centrifugal filtration is prepared
The plant oil base bitumen regenerant provided is provided) other two kinds are significantly larger than to the rate of producing effects again for recycling aged asphalt, and it is anti-ageing
The property changed, fatigue resistance and water stability are far better than other two kinds.
It is resin, stearic acid, resin and stearic acid to stablize component, by the comparison to regenerative agent uniformity, adds resin
And stearic acid, the obtained uniformity of plant oil base bitumen regenerant are best.
Waste edible oil without precipitation directly with stablizing component, modified component mixes, waste edible oil elder generation precipitation 48 hours or more
It is to stablize component, modified component mixing, it is steady to obtained regeneration heroic lovers of plant oil base bitumen regenerant, fatigue resistance, water
Qualitatively correction data is as shown in table 4.
As can be known from Table 4, after waste edible oil precipitation 48, then the light-weight plant oil that centrifugal filtration obtains is more conducive to the plant
Uniform, the stabilization of oil base bitumen regenerant, regeneration efficiency higher, the fatigue resistance of regeneration asphalt, water stability are more preferable.
It will be apparent to those skilled in the art that vegetable oil regeneration asphalt of the present invention and preparation method thereof includes above-mentioned hair
The arbitrary combination of the invention content and specific embodiment part of bright specification, as space is limited and for make specification concise without
Each scheme that these combinations are formed is described one by one.All within the spirits and principles of the present invention, it is any modification for being made, equivalent
Replace, improve etc., it should all be included in the protection scope of the present invention.
Claims (28)
- A 1. vegetable oil reclaimed asphalt mixture, which is characterized in that including mineral aggregate, recycling mineral aggregate and vegetable oil again Raw pitch, the vegetable oil regeneration asphalt include recycling aged asphalt and plant oil base bitumen regenerant, the plant oil base drip Green regenerative agent includes lighter body component, stablizes component and modified component, and the lighter body is light-weight plant oil, described Light-weight plant oil is preprocessed by waste edible oil, is obtained after removing impurity, and the stable component includes resin and stearic acid, described Modified component includes carbon black and/or lime.
- 2. vegetable oil reclaimed asphalt mixture according to claim 1, which is characterized in that it is described pretreatment include from The heart and/or filtering.
- 3. vegetable oil reclaimed asphalt mixture according to claim 1, which is characterized in that in the stable component, Resin and stearic mass ratio are 1:1.
- 4. vegetable oil reclaimed asphalt mixture according to claim 1, which is characterized in that the resin is oil tree Fat.
- 5. vegetable oil reclaimed asphalt mixture according to claim 1, which is characterized in that the plant oil base pitch The mass percent of each component is in regenerative agent, and light-weight plant oil ingredient is 60-90%, stablizes component 5-20%, modified component 5-20%.
- 6. vegetable oil reclaimed asphalt mixture according to claim 5, which is characterized in that the plant oil base pitch The mass percent of each component is in regenerative agent, and light-weight plant oil ingredient is 70-90%, stablizes component 5-15%, modified component 5-15%.
- 7. vegetable oil reclaimed asphalt mixture according to claim 6, which is characterized in that the plant oil base pitch The mass percent of each component is in regenerative agent, and light-weight plant oil ingredient is 80-90%, stablizes component 5-10%, modified component 5-10%.
- 8. vegetable oil reclaimed asphalt mixture according to claim 1, which is characterized in that the plant oil regeneration drip The mass percent of each component is in blueness, recycles aged asphalt 90-94%, plant oil base bitumen regenerant 6-10%.
- 9. vegetable oil reclaimed asphalt mixture according to claim 8, which is characterized in that the plant oil regeneration drip The mass percent of each component is in blueness, recycles aged asphalt 91-93%, plant oil base bitumen regenerant 7-9%.
- 10. vegetable oil reclaimed asphalt mixture according to claim 9, which is characterized in that the plant oil regeneration The mass percent of each component is in pitch, recycles aged asphalt 92%, plant oil base bitumen regenerant 8%.
- 11. vegetable oil reclaimed asphalt mixture according to claim 1, which is characterized in that the plant oil regeneration The mass percent of each component is in asphalt, mineral aggregate 40-60%, recycles mineral aggregate 35-45%, vegetable oil is again Raw pitch 5-15%.
- 12. vegetable oil reclaimed asphalt mixture according to claim 1, which is characterized in that the mineral aggregate or It is basalt and/or diabase to recycle mineral aggregate.
- 13. the preparation method of a vegetable oil reclaimed asphalt mixture, which is characterized in that include the following steps:(1) new mineral aggregate and recycling mineral aggregate are mixed and stirred;(2) vegetable oil regeneration asphalt and new mineral aggregate, recycling mineral aggregate are mixed and stirred, obtains the mixing of vegetable oil regeneration asphalt Material;The vegetable oil regeneration asphalt includes recycling aged asphalt and plant oil base bitumen regenerant;The plant oil base bitumen regenerant is light-weight plant oil ingredient, stablizes component and modified component, the lighter body For light-weight plant oil, the light-weight plant oil is preprocessed by waste edible oil, is obtained after removing impurity;The stable component includes resin and stearic acid, and the modified component includes carbon black and/or lime.
- 14. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 13, which is characterized in that described The preparation method of vegetable oil regeneration asphalt, includes the following steps:(1) aged asphalt is recycled by the way of extraction device extracting to old asphalt mixture;(2) recycling aged asphalt is heated to mixing and stirring temperature;(3) plant oil base bitumen regenerant is added in the recycling aged asphalt for having been heated to and mix and stir temperature and mixed and stirred;(4) mixture of recycling aged asphalt and plant oil base bitumen regenerant after mixing and stirring, which is put into baking oven, develops.
- 15. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 14, which is characterized in that described Recycling aged asphalt and the temperature of mixing and stirring of plant oil base bitumen regenerant are 110-160 DEG C, mixing time 20-40min.
- 16. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 14, which is characterized in that described The developmental temperature for recycling aged asphalt and plant oil base bitumen regenerant is 110 DEG C -160 DEG C, development time 30-60min.
- 17. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 14, which is characterized in that described The mass percent of each component is in vegetable oil regeneration asphalt, recycles aged asphalt 90-94%, plant oil base bitumen regenerant 6- 10%.
- 18. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 17, which is characterized in that described The mass percent of each component is in vegetable oil regeneration asphalt, recycles aged asphalt 91-93%, plant oil base bitumen regenerant 7- 9%.
- 19. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 18, which is characterized in that described The mass percent of each component is in vegetable oil regeneration asphalt, recycles aged asphalt 92%, plant oil base bitumen regenerant 8%.
- 20. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 13, which is characterized in that described The preparation method of plant oil base bitumen regenerant, includes the following steps:(1) it using waste edible oil as raw material, is centrifuged or is filtered, isolated light-weight plant oil ingredient;(2) suitable light-weight plant oil ingredient is weighed, and is uniformly mixed with stablizing component and modified component;(3) to get to the plant oil base bitumen regenerant after being aged at normal temperatures.
- 21. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 20, which is characterized in that described Before resin is mixed with light-weight plant oil and the modified component, first make its fusing, form fluid.
- 22. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 20, which is characterized in that described Light-weight plant oil ingredient is 2-5h with the digestion time for stablizing component and modified component.
- 23. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 22, which is characterized in that described Light-weight plant oil ingredient is 3-4h with the digestion time for stablizing component and modified component.
- 24. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 13, which is characterized in that described Resin and stearic mass ratio are 1:1.
- 25. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 13, which is characterized in that described Resin is Petropols.
- 26. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 13, which is characterized in that described The mass percent of each component is in plant oil base bitumen regenerant, and light-weight plant oil ingredient is 60-90%, stablizes component 5- 20%th, modified component 5-20%.
- 27. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 26, which is characterized in that described The mass percent of each component is in plant oil base bitumen regenerant, and light-weight plant oil ingredient is 70-90%, stablizes component 5- 15%th, modified component 5-15%.
- 28. the preparation method of vegetable oil reclaimed asphalt mixture according to claim 27, which is characterized in that described The mass percent of each component is in plant oil base bitumen regenerant, and light-weight plant oil ingredient is 80-90%, stablizes component 5- 10%th, modified component 5-10%.