CN105815854A - Environment-friendly lace shell fabric - Google Patents
Environment-friendly lace shell fabric Download PDFInfo
- Publication number
- CN105815854A CN105815854A CN201610143810.1A CN201610143810A CN105815854A CN 105815854 A CN105815854 A CN 105815854A CN 201610143810 A CN201610143810 A CN 201610143810A CN 105815854 A CN105815854 A CN 105815854A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fiber
- shell fabric
- wool
- spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an environment-friendly lace shell fabric. The environment-friendly lace shell fabric is characterized by comprising an outer layer shell fabric and a lining shell fabric, wherein a layer of SEE ecological cotton is arranged between the outer layer shell fabric and the lining shell fabric. According to the environment-friendly lace shell fabric disclosed by the invention, the SEE ecological cotton is placed between the outer layer shell fabric and the lining shell fabric, so that the shell fabric has the characteristics of being biodegradable, energy-saving, emission-reducing, environment-friendly, ecological and the like, and is an ideal environment-friendly heat preservation shell fabric.
Description
Technical field
The present invention relates to environment-friendly type lace fabric, belong to fabric technical field.
Background technology
Along with the progress in epoch, relevant ecology, environmental protection, the green concept such as nuisanceless will become more and more popular.Pollution-free food has been subjected to the favor of consumer, has the fabric dress ornament of green indignant thought therewith, will be paid high attention to, and DEVELOPMENT PROSPECT is boundless, and exploitation competition of the same trade will present multi-faceted, multi-level.But the heat-insulating property of garment material is general at present, can not meet the demand in epoch.
Summary of the invention
It is an object of the invention to overcome above-mentioned deficiency, it is provided that the environment-friendly type lace fabric of high insulating effect.
The object of the present invention is achieved like this:
A kind of environment-friendly type lace fabric, including outer shell fabric and lining fabric, one layer of SEE ecological cotton it is provided with between described outer shell fabric and lining fabric, described outer shell fabric is provided with upper strata pore, lower floor's pore is offered on described lining fabric, it is connected by spinning threadling between fabric with fabric, the most each fabric block is formed by radial line and parallel intertexture blending, described radial line is viscose rayon, fiber number is 126 ~ 185dtex, it is 34.2 ~ 38.5/cm through density, described parallel is CUP, fiber number is 112 ~ 228dtex, it is 29.8 ~ 43.8/cm through density, it is coated with lace layer on described fabric block；
The manufacture method of this fabric is:
1), yarn variety design:
Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and soft treatment, anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses protease to process, protease consumption is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2), spinning process:
By the super-fine wool fiber of 70% after dyeing, the polyester fiber of 30% passes through and hair → hacking → shredding → carding (becoming bar) → drafting (in the lump, two also) → air spinning → automatic winding, spinning technological process wherein controls relative humidity 50%～55%, temperature 25 DEG C～30 DEG C；
With in hair technique, select NimateCF-5 and crude oil, NimateC602 cationic antistatic agent, with nebulization, add account for gross weight 10% and crude oil and account for the antistatic additive of gross weight 10%, making fiber have the lubricity of excellence, increase the coherent of fiber, antistatic behaviour, improve fiber can cardability, contribute to the full and uniform mixing of different performance fiber；
In carding process, feeding the hair cycle and grasp 50s～60s, sliver exporting speed is less than 100m/min, and shaping grammes per square metre 5g/m, irregular coefficient controls within 2%；
In drawing process, the height that spinning 25/1 is public props up slubbing yarn, parameter 8.2 in the lump, and two rear wool top grammes per square metres control at 4g/m.Selecting import autoleveller draw frame (D45 type), the lower machine uniform coefficient of variation of wool top grammes per square metre is less than 0.5%～1%.In this process, it is necessary to control drafting multiple well, total draft controls 7.8 times, wherein dominant draft 4.58 times, follow-up drawing-off 1.7 times；
3), weaving process:
Warping → gait, plug in reed, inserted sheet → arrow shaft weaving, props up slubbing yarn by the height of 25/1 public on rapier loom, organizes based on the twill of 2/2, use the mode looming weaving of single-warp single-abb, upper machine fabric width is 178cm, and upper machine end count is 225/10cm, and filling density is 216/10cm；
4), postfinishing process:
The fabric that 4th step is made into again by base inspection → mending → reinspection → tape edge → prewashing → fulling → fine purifiation → dehydration → decatizing → porcupine roller fluffing → cropping → raising teasel → wet brush → drying and shaping → hot light → one-tenth inspection makes finished product.
Compared with prior art, the invention has the beneficial effects as follows:
Environment-friendly type lace fabric of the present invention, by increasing SEE ecological cotton between outer shell fabric and lining fabric, uses fabric to have biodegradation, energy-conservation change row, the feature such as environmental and ecological, is a kind of preferable environmental protection thermal fabric.
Detailed description of the invention
The present invention relates to environment-friendly type lace fabric, including outer shell fabric and lining fabric, one layer of SEE ecological cotton it is provided with between described outer shell fabric and lining fabric, described outer shell fabric is provided with upper strata pore, lower floor's pore is offered on described lining fabric, it is connected by spinning threadling between fabric with fabric, the most each fabric block is formed by radial line and parallel intertexture blending, described radial line is viscose rayon, fiber number is 126 ~ 185dtex, it is 34.2 ~ 38.5/cm through density, described parallel is CUP, fiber number is 112 ~ 228dtex, it is 29.8 ~ 43.8/cm through density, it is coated with lace layer on described fabric block；
The manufacture method of this fabric is:
1), yarn variety design:
Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and soft treatment, anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses protease to process, protease consumption is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2), spinning process:
By the super-fine wool fiber of 70% after dyeing, the polyester fiber of 30% passes through and hair → hacking → shredding → carding (becoming bar) → drafting (in the lump, two also) → air spinning → automatic winding, spinning technological process wherein controls relative humidity 50%～55%, temperature 25 DEG C～30 DEG C；
With in hair technique, select NimateCF-5 and crude oil, NimateC602 cationic antistatic agent, with nebulization, add account for gross weight 10% and crude oil and account for the antistatic additive of gross weight 10%, making fiber have the lubricity of excellence, increase the coherent of fiber, antistatic behaviour, improve fiber can cardability, contribute to the full and uniform mixing of different performance fiber；
In carding process, feeding the hair cycle and grasp 50s～60s, sliver exporting speed is less than 100m/min, and shaping grammes per square metre 5g/m, irregular coefficient controls within 2%；
In drawing process, the height that spinning 25/1 is public props up slubbing yarn, parameter 8.2 in the lump, and two rear wool top grammes per square metres control at 4g/m.Selecting import autoleveller draw frame (D45 type), the lower machine uniform coefficient of variation of wool top grammes per square metre is less than 0.5%～1%.In this process, it is necessary to control drafting multiple well, total draft controls 7.8 times, wherein dominant draft 4.58 times, follow-up drawing-off 1.7 times；
3), weaving process:
Warping → gait, plug in reed, inserted sheet → arrow shaft weaving, props up slubbing yarn by the height of 25/1 public on rapier loom, organizes based on the twill of 2/2, use the mode looming weaving of single-warp single-abb, upper machine fabric width is 178cm, and upper machine end count is 225/10cm, and filling density is 216/10cm；
4), postfinishing process:
The fabric that 4th step is made into again by base inspection → mending → reinspection → tape edge → prewashing → fulling → fine purifiation → dehydration → decatizing → porcupine roller fluffing → cropping → raising teasel → wet brush → drying and shaping → hot light → one-tenth inspection makes finished product.
Claims (1)
1. an environment-friendly type lace fabric, it is characterized in that: include outer shell fabric and lining fabric, one layer of SEE ecological cotton it is provided with between described outer shell fabric and lining fabric, described outer shell fabric is provided with upper strata pore, lower floor's pore is offered on described lining fabric, it is connected by spinning threadling between fabric with fabric, the most each fabric block is formed by radial line and parallel intertexture blending, described radial line is viscose rayon, fiber number is 126 ~ 185dtex, it is 34.2 ~ 38.5/cm through density, described parallel is CUP, fiber number is 112 ~ 228dtex, it is 29.8 ~ 43.8/cm through density, it is coated with lace layer on described fabric block；
The manufacture method of this fabric is:
1), yarn variety design:
Select wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic, to wool fiber, bamboo carbon dacron fiber and acid fiber by polylactic carry out anti pilling process, ferment treatment and soft treatment, anti pilling processes selects phosphate ester antimony oxide mixture as anti pilling agent, phosphate ester antimony oxide amount of mixture is wool fiber weight 1.5-4%, ferment treatment system uses protease to process, protease consumption is the 0.1-0.2% of wool fiber weight, the softening agent that soft treatment is selected is water-soluble organic silicon softening agent, water-soluble organic silicon softening agent consumption is the 6-8% of wool fiber weight；
2), spinning process:
By the super-fine wool fiber of 70% after dyeing, the polyester fiber of 30% passes through and hair → hacking → shredding → carding (becoming bar) → drafting (in the lump, two also) → air spinning → automatic winding, spinning technological process wherein controls relative humidity 50%～55%, temperature 25 DEG C～30 DEG C；
With in hair technique, select NimateCF-5 and crude oil, NimateC602 cationic antistatic agent, with nebulization, add account for gross weight 10% and crude oil and account for the antistatic additive of gross weight 10%, making fiber have the lubricity of excellence, increase the coherent of fiber, antistatic behaviour, improve fiber can cardability, contribute to the full and uniform mixing of different performance fiber；
In carding process, feeding the hair cycle and grasp 50s～60s, sliver exporting speed is less than 100m/min, and shaping grammes per square metre 5g/m, irregular coefficient controls within 2%；
In drawing process, the height that spinning 25/1 is public props up slubbing yarn, parameter 8.2 in the lump, and two rear wool top grammes per square metres control at 4g/m.Selecting import autoleveller draw frame (D45 type), the lower machine uniform coefficient of variation of wool top grammes per square metre is less than 0.5%～1%.In this process, it is necessary to control drafting multiple well, total draft controls 7.8 times, wherein dominant draft 4.58 times, follow-up drawing-off 1.7 times；
3), weaving process:
Warping → gait, plug in reed, inserted sheet → arrow shaft weaving, props up slubbing yarn by the height of 25/1 public on rapier loom, organizes based on the twill of 2/2, use the mode looming weaving of single-warp single-abb, upper machine fabric width is 178cm, and upper machine end count is 225/10cm, and filling density is 216/10cm；
4), postfinishing process:
The fabric that 4th step is made into again by base inspection → mending → reinspection → tape edge → prewashing → fulling → fine purifiation → dehydration → decatizing → porcupine roller fluffing → cropping → raising teasel → wet brush → drying and shaping → hot light → one-tenth inspection makes finished product.