CN105803834A - Cotton-nylon fabric dyeing process - Google Patents
Cotton-nylon fabric dyeing process Download PDFInfo
- Publication number
- CN105803834A CN105803834A CN201610240081.1A CN201610240081A CN105803834A CN 105803834 A CN105803834 A CN 105803834A CN 201610240081 A CN201610240081 A CN 201610240081A CN 105803834 A CN105803834 A CN 105803834A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- washing
- temperature
- jigger
- conducting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a cotton-nylon fabric dyeing process and belongs to the technical field of fabric dyeing. The process comprises the steps of vat distribution, sewing, cool piling, desizing, drying and coiling, pre-setting, detection, weighing, sewing, mercerizing coiling, jig dyeing machine dyeing, washing and half drying, finished product setting, and detection and coiling. Two-bath-process dyeing is adopted in the jig dyeing machine dyeing procedure, wherein the first bath process comprises the steps of supplying materials at normal temperature, adding anhydrous sodium sulphate at 45 DEG C, increasing temperature to 65 DEG C, conducting heat insulation for 0.5-1.5 h, adding soda ash, conducting heat insulation at 65 DEG C for another 1.5 h, then conducting drainage, conducting water input and temperature increase to 90 DEG C for soaping, then cleaning a cloth cover, conducting water input and temperature increase again to 70 DEG C for neutralization and washing, and conducting dyeing after cold water soaking; the second path process comprises the steps of supplying materials at normal temperature, regulating pH value, increasing temperature to 98 DEG C, conducting heat insulation for 1.2 h or more, and taking cloth for sample comparison. A product produced through the dyeing process is high in color fastness and wear resistance, low in shrinkage rate, and high in glossiness and flatness.
Description
Technical field
The present invention discloses the dyeing of a kind of cotton brocade fabric, belongs to the technical field of dyeing fabric.
Background technology
Cotton brocade fabric is the product made as raw material with cotton and chinlon, and the content of cotton is more than 50%.Cotton brocade fabric, after existing dyeing is processed, exists that color fastness is poor, wears no resistance, problem that washing shrinkage is high.
Summary of the invention
It is an object of the invention to provide the dyeing of the cotton brocade fabric that a kind of color fastness is high, wearability is high, washing shrinkage is low.
For reaching above-mentioned purpose, the technical solution adopted in the present invention is:
The dyeing of a kind of cotton brocade fabric, comprises the following steps: joins cylinder → margin to seam → cold dome → desizing and dries clot → pre-setting → check → weigh → margin to seam → mercerising clot → dyeing by jigger → washing and dry half-dried → finished product sizing → check, clot;
Wherein, dyeing by jigger operation uses two bath process;First bath includes room temperature blanking, Matrii Sulfas Exsiccatus is added when 45 DEG C, it is continuously heating to insulation 0.5-1.5 hour when 65 DEG C, then adds soda, draining after then proceeding to be incubated 1.5 hours at 65 DEG C, water inlet is warming up to 90 DEG C and soaps the most again, after soaping, cloth cover is cleaned, be warming up to 70 DEG C followed by water inlet, be neutralized washing, after subcooled water, dye;Second bath includes room temperature blanking, adjusts pH value, is warming up to 98 DEG C and is incubated more than 1.2 hours, takes cloth to sample.
As the further setting of such scheme, in described dyeing by jigger operation, the tension force of dye jigger controls at 1.5-2.5kg/cm2, speed controlling is at 120-140yd/min.
The temperature of described pre-setting operation is 185-195 DEG C, and speed is 40-60m/min.
The temperature that half-dried operation is dried in described washing is 85-95 DEG C, and speed is 50-60m/min.
The temperature of described finished product shaping process is 190-195 DEG C.
The product produced by the dyeing of cotton brocade fabric of the present invention, not only color fastness is high, wearability is high, washing shrinkage is low, and glossiness is good, flatness is high.
Detailed description of the invention
Below by specific embodiment, the invention will be further described, but the present invention is not limited by following example institute.
Embodiment 1
The dyeing of cotton brocade fabric, comprises the following steps: joins cylinder → margin to seam → cold dome → desizing and dries clot → pre-setting → check → weigh → margin to seam → mercerising clot → dyeing by jigger → washing and dry half-dried → finished product sizing → check, clot.
Wherein, dyeing by jigger operation uses two bath process;First bath includes room temperature blanking, Matrii Sulfas Exsiccatus is added when 45 DEG C, it is continuously heating to insulation 1 hour when 65 DEG C, then adds soda, draining after then proceeding to be incubated 1.5 hours at 65 DEG C, water inlet is warming up to 90 DEG C and soaps the most again, after soaping, cloth cover is cleaned, be warming up to 70 DEG C followed by water inlet, be neutralized washing, after subcooled water, dye;Second bath includes room temperature blanking, adjusts pH value, is warming up to 98 DEG C and is incubated more than 1.2 hours, takes cloth to sample.
In above-mentioned dyeing by jigger operation, the tension force of dye jigger controls at 2.0kg/cm2, speed controlling is at 130yd/min.
The temperature of above-mentioned pre-setting operation is 190 DEG C, and speed is 50m/min.
It is 90 DEG C that the temperature of half-dried operation is dried in above-mentioned washing, and speed is 55m/min.
The temperature of above-mentioned finished product shaping process is 192 DEG C.
After dye, fabric is after tested, and color fastness reaches 3 grades, within washing shrinkage 3%, and fastness to rubbing: dry and wet rubs 3 grades, acid, alkali perspiration fastness 3-4 level.
Embodiment 2
The dyeing of cotton brocade fabric, comprises the following steps: joins cylinder → margin to seam → cold dome → desizing and dries clot → pre-setting → check → weigh → margin to seam → mercerising clot → dyeing by jigger → washing and dry half-dried → finished product sizing → check, clot.
Wherein, dyeing by jigger operation uses two bath process;First bath includes room temperature blanking, Matrii Sulfas Exsiccatus is added when 45 DEG C, it is continuously heating to insulation 0.5 hour when 65 DEG C, then adds soda, draining after then proceeding to be incubated 1.5 hours at 65 DEG C, water inlet is warming up to 90 DEG C and soaps the most again, after soaping, cloth cover is cleaned, be warming up to 70 DEG C followed by water inlet, be neutralized washing, after subcooled water, dye;Second bath includes room temperature blanking, adjusts pH value, is warming up to 98 DEG C and is incubated more than 1.2 hours, takes cloth to sample.
In above-mentioned dyeing by jigger operation, the tension force of dye jigger controls at 1.5kg/cm2, speed controlling is at 120yd/min.
The temperature of above-mentioned pre-setting operation is 185 DEG C, and speed is 40m/min.
It is 85 DEG C that the temperature of half-dried operation is dried in above-mentioned washing, and speed is 50m/min.
The temperature of above-mentioned finished product shaping process is 190 DEG C.
After dye, fabric is after tested, and color fastness reaches 3 grades, within washing shrinkage 3%, and fastness to rubbing: dry and wet rubs 3 grades, acid, alkali perspiration fastness 3-4 level.
Embodiment 3
The dyeing of cotton brocade fabric, comprises the following steps: joins cylinder → margin to seam → cold dome → desizing and dries clot → pre-setting → check → weigh → margin to seam → mercerising clot → dyeing by jigger → washing and dry half-dried → finished product sizing → check, clot.
Wherein, dyeing by jigger operation uses two bath process;First bath includes room temperature blanking, Matrii Sulfas Exsiccatus is added when 45 DEG C, it is continuously heating to insulation 1.5 hours when 65 DEG C, then adds soda, draining after then proceeding to be incubated 1.5 hours at 65 DEG C, water inlet is warming up to 90 DEG C and soaps the most again, after soaping, cloth cover is cleaned, be warming up to 70 DEG C followed by water inlet, be neutralized washing, after subcooled water, dye;Second bath includes room temperature blanking, adjusts pH value, is warming up to 98 DEG C and is incubated more than 1.2 hours, takes cloth to sample.
In above-mentioned dyeing by jigger operation, the tension force of dye jigger controls at 2.5kg/cm2, speed controlling is at 140yd/min.
The temperature of above-mentioned pre-setting operation is 195 DEG C, and speed is 60m/min.
It is 95 DEG C that the temperature of half-dried operation is dried in above-mentioned washing, and speed is 60m/min.
The temperature of above-mentioned finished product shaping process is 195 DEG C.
After dye, fabric is after tested, and color fastness reaches 3 grades, within washing shrinkage 3%, and fastness to rubbing: dry and wet rubs 3 grades, acid, alkali perspiration fastness 3-4 level.
Above-described embodiment is only used for illustrating the inventive concept of the present invention, rather than the restriction to rights protection of the present invention, all changes utilizing this design that the present invention carries out unsubstantiality, all should fall into protection scope of the present invention.
Claims (5)
1. the dyeing of a cotton brocade fabric, it is characterised in that comprise the following steps: join cylinder → margin to seam → cold dome → desizing and dry clot → pre-setting → check → weigh → margin to seam → mercerising clot → dyeing by jigger → washing and dry half-dried → finished product sizing → check, clot;
Wherein, dyeing by jigger operation uses two bath process;First bath includes room temperature blanking, Matrii Sulfas Exsiccatus is added when 45 DEG C, it is continuously heating to insulation 0.5-1.5 hour when 65 DEG C, then adds soda, draining after then proceeding to be incubated 1.5 hours at 65 DEG C, water inlet is warming up to 90 DEG C and soaps the most again, after soaping, cloth cover is cleaned, be warming up to 70 DEG C followed by water inlet, be neutralized washing, after subcooled water, dye;Second bath includes room temperature blanking, adjusts pH value, is warming up to 98 DEG C and is incubated more than 1.2 hours, takes cloth to sample.
2. the dyeing of cotton brocade fabric as claimed in claim 1, it is characterised in that: in described dyeing by jigger operation, the tension force of dye jigger controls at 1.5-2.5kg/cm2, speed controlling is at 120-140yd/min.
3. the dyeing of cotton brocade fabric as claimed in claim 1, it is characterised in that: the temperature of described pre-setting operation is 185-195 DEG C, and speed is 40-60m/min.
4. the dyeing of cotton brocade fabric as claimed in claim 1, it is characterised in that: the temperature that half-dried operation is dried in described washing is 85-95 DEG C, and speed is 50-60m/min.
5. the dyeing of cotton brocade fabric as claimed in claim 1, it is characterised in that: the temperature of described finished product shaping process is 190-195 DEG C.