CN105803598A - Synthesis additive for yarn - Google Patents
Synthesis additive for yarn Download PDFInfo
- Publication number
- CN105803598A CN105803598A CN201610281893.0A CN201610281893A CN105803598A CN 105803598 A CN105803598 A CN 105803598A CN 201610281893 A CN201610281893 A CN 201610281893A CN 105803598 A CN105803598 A CN 105803598A
- Authority
- CN
- China
- Prior art keywords
- yarn
- lubricant
- antistatic agent
- synthetic additive
- additive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a synthesis additive for yarn. The synthesis additive is prepared from 1.8-2.4L of an antistatic agent and 1.3-1.8L of a lubricating agent. In order to overcome the defects, the synthesis additive for the yarn will not generate static electricity in the cloth production process, and can improve production efficiency and lower the cost.
Description
Technical field
The present invention relates to synthetic additive technical field, be specifically related to a kind of synthetic additive for yarn.
Background technology
Yarn is the thin thread that fiber is elongated that twisting is spun into by cotton, hair, fiber crops, chemical fibre etc., is typically used as weaving cotton cloth
Raw material, existing producing during cloth, electrostatic can produced, be allowed to when producing cloth be not easy
Shaping, yarn is easily brought together, and affects production efficiency, increases production cost.
Summary of the invention
The present invention solves above-mentioned deficiency, it is provided that a kind of synthetic additive for yarn, be allowed to produce
Do not have the situation of electrostatic during cloth, improve production efficiency, reduce cost.
The technical solution of the present invention: a kind of synthetic additive for yarn, described synthetic additive bag
Include following component, antistatic agent and lubricant；The deal of described each composition is: antistatic agent 1.8L-2.4L, profit
Lubrication prescription 1.3L-1.8L.
As the further optimization of this programme, the deal of described each composition: antistatic agent 1.8L, lubricant 1.3L.
As the further optimization of this programme, the deal of described each composition: antistatic agent 2.4L, lubricant 1.8L.
As the further optimization of this programme, the deal of described each composition: antistatic agent 2.1L, lubricant 1.6L.
As the further optimization of this programme, in 100L hot water, it is firstly added antistatic agent, adds the most again
Enter lubricant, carry out mix and blend.
As the further optimization of this programme, described hot water temperature controls summer between 45 DEG C-52 DEG C, winter
Control between 68 DEG C-74 DEG C.
Use process: the additive of synthesis is by cooling, and the time controls within half an hour, is poured on former afterwards
On material, permeating 24 hours, adding synthetic additive in raw material per ton is 32L.
Beneficial effects of the present invention:
The present invention, by during producing cloth, adds synthetic additive in the feed, when solving to produce
The situation of electrostatic occurs, and then does not haves yarn and be brought together and the quality that affects cloth, be allowed to produce
Cloth out, quality is good, and durable, cost is relatively low, and improves production efficiency.
Detailed description of the invention
All features disclosed in this specification, or disclosed all methods or during step, except mutually
Beyond the feature repelled mutually and/or step, all can combine by any way.
Any feature disclosed in this specification (including any accessory claim, summary), unless especially
Narration, all can be by other equivalences or have the alternative features of similar purpose and replaced.That is, unless chatted especially
Stating, each feature is an example in a series of equivalence or similar characteristics.
Embodiment 1:
Take antistatic agent 1.8L, lubricant 1.3L, in 100L hot water, be firstly added antistatic agent, afterwards
Add lubricant, carry out mix and blend.
The additive of synthesis is by cooling, and the time controls within half an hour, is poured on afterwards on raw material, infiltration
24 hours, adding synthetic additive in raw material per ton was 32L.
Embodiment 2:
Antistatic agent 2.4L, lubricant 1.8L, in 100L hot water, be firstly added antistatic agent, the most again
Add lubricant, carry out mix and blend.
The additive of synthesis is by cooling, and the time controls within half an hour, is poured on afterwards on raw material, infiltration
24 hours, adding synthetic additive in raw material per ton was 32L.
Embodiment 3:
Antistatic agent 2.1L, lubricant 1.6L, in 100L hot water, be firstly added antistatic agent, the most again
Add lubricant, carry out mix and blend.
The additive of synthesis is by cooling, and the time controls within half an hour, is poured on afterwards on raw material, infiltration
24 hours, adding synthetic additive in raw material per ton was 32L.
The present invention all crosses and adds synthetic additive in the feed, it is to avoid the situation of electrostatic occurs in cloth when producing,
Being allowed to the cloth produced, quality is good, durable, and cost is relatively low, and improves production efficiency.
Particular embodiments described above, is entered the purpose of the present invention, technical scheme and beneficial effect
One step describes in detail, be it should be understood that the specific embodiment that the foregoing is only the present invention, not
For limiting the present invention.The present invention expands to any new feature disclosed in this manual or any new group
Close, and the arbitrary new method that discloses or the step of process or any new combination.
Claims (6)
1. the synthetic additive for yarn, it is characterised in that described synthetic additive includes following component, anti-
Electrostatic agent and lubricant；The deal of described each composition is: antistatic agent 1.8L-2.4L, lubricant 1.3L-1.8L.
A kind of synthetic additive for yarn the most according to claim 1, it is characterised in that described each composition
Deal: antistatic agent 1.8L, lubricant 1.3L.
A kind of synthetic additive for yarn the most according to claim 1, it is characterised in that described each composition
Deal: antistatic agent 2.4L, lubricant 1.8L.
A kind of synthetic additive for yarn the most according to claim 1, it is characterised in that described each one-tenth
The deal divided: antistatic agent 2.1L, lubricant 1.6L.
A kind of synthetic additive for yarn the most according to claim 1, it is characterised in that described synthesis
Process is: in 100L hot water, be firstly added antistatic agent, adds lubricant afterwards, is stirred by mixing
Mix.
A kind of synthetic additive for yarn the most according to claim 5, it is characterised in that described hot water temperature
Sky of aestivating controls, between 45 DEG C-52 DEG C, to control winter between 68 DEG C-74 DEG C.