CN105799288A - Anti-static knitted fabric and preparation method thereof - Google Patents
Anti-static knitted fabric and preparation method thereof Download PDFInfo
- Publication number
- CN105799288A CN105799288A CN201610143544.2A CN201610143544A CN105799288A CN 105799288 A CN105799288 A CN 105799288A CN 201610143544 A CN201610143544 A CN 201610143544A CN 105799288 A CN105799288 A CN 105799288A
- Authority
- CN
- China
- Prior art keywords
- fibre
- antistatic
- fiber
- yarn
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-static knitted fabric and a preparation method thereof.An inner layer, a middle layer and an outer layer of the fabric are prepared by compositing different components respectively, wherein the inner layer is prepared from polyvinyl chloride fibers and acrylic fibers, the middle layer is prepared from cellulosic fibers, polyamide fibers and wool blend fibers, and the outer layer is prepared from anti-static fibers, metal blend fibers and protein fibers; the three layers are prepared through the step that the appropriate fabric fibers are selected separately to be composited and then subjected to yarn weaving, the electrical conductivity of the inner layer and the outer layer of the fabric is enhanced, and therefore the static electricity phenomenon generated due to friction of the fabric is prevented from occurring to a great extent; in addition, all the raw material fibers and yarn are finished by adopting a specific finishing solution and then prepared in the preparation process, and therefore the texture, the comfort degree and the anti-static performance of the fabric are further enhanced.
Description
Technical field
The present invention relates to the processing technology of clothing, particularly relate to a kind of Antistatic knitting fabric and preparation method thereof.
Background technology
Raising along with people's living standard, the relaxed and comfortable softness of demand more on clothing, high resilience, extensibility and drapability are good, good permeability, and fashionable, beautiful in colour, the superiority place of these demands knitted fabric clothing just, extensively by the favor of people, namely knitting be utilize knitting needle by yarn bends lopping the fabric overlapped and formed of mutually going here and there, and knitting fabric is different in that from shuttle-woven fabric yarn form in fabric is different.At present, in the products such as knitting fabric is widely used in garment material and lining, home textile, it is subject to liking of consumers in general.But knitting fabric exists a very common problem, there is a puzzlement when people wear off and be easy to exactly produce electrostatic, have impact on the use of people.Generally can carry out reasonably optimizing from aspects such as the material of fabric itself, processing technology for solution the problems referred to above to be designed to deal with.There is no effective fabric composition and corresponding preparation method at present.
Accordingly, it would be desirable to a kind of new technical scheme is to solve the problems referred to above.
Summary of the invention
Goal of the invention: in order to solve the problem existing for prior art, the invention provides a kind of Antistatic knitting fabric of a kind of effective reduction knitting fabric electrostatic phenomenon generation and preparation method thereof.
Technical scheme: for reaching above-mentioned purpose, technical scheme is as follows: a kind of Antistatic knitting fabric, is composited by three layers yarn;Wherein each layer is composited by different fabric components: wherein internal layer is made up of following two composition compound: a1 polyvinyl chloride fibre;B1 acrylic fiber;Middle level is made up of following three kinds of composition compounds: a2 cellulose fibre;B2 nylon fibre;The wool blended fiber of c2;Outer layer is made up of following three kinds of composition compounds: a3 antistatic fibre;B3 metal blend fibre;C3 protein fibre;The weight of described fabric every square metre is 130-220g;The thickness of described fabric is 1.2-2.5mm.
Being more highly preferred to, in described internal layer, a1 polyvinyl chloride fibre and b1 acrylic fiber weight ratio are 4:1.
Being more highly preferred to, described a2 cellulose fibre is mixed with the part by weight of 1:2 by cotton fiber and acetate fiber.
Being more highly preferred to, in described middle level, the weight ratio of a2 cellulose fibre, b2 nylon fibre and the wool blended fiber of c2 is 4:1:3.
Being more highly preferred to, in the wool blended fiber of described c2, the content of Pilus Caprae seu Ovis is not higher than 90%.
Being more highly preferred to, in described outer layer, the weight ratio of a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre is 3:1:4.
Being more highly preferred to, described a3 antistatic fibre is surfactant addition type fiber.
Being more highly preferred to, described c3 protein fibre is the one in wool fiber, mulberry silk fiber, rabbit fur fibre.
The preparation method of above-mentioned a kind of Antistatic knitting fabric, all carried out a prefinishing before carrying out ectonexine monolayer yarn and three layers yarn compound, specific as follows:
(1) it is placed in internal layer raw material a1 polyvinyl chloride fibre with b1 acrylic fiber in the water of the glacial acetic acid that with the addition of 8% to soak to take out after 30-40min and is dried to 9 one-tenth and dry carries out yarn;
(2) outer layer a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre are placed in the mixed solution that mass ratio is the penetrating agent of 1:3:20, chitosan and water immersion 20-40min, are dried to 9 one-tenth after taking-up and dry carry out yarn;
(3) by be placed in the aqueous solution that with the addition of softening agent, enzyme, penetrating agent before three layers yarn compound to soak take out natural air drying after 1-2h after carry out composite yarn again and knit.
Further, in described step (3) addition of softening agent be 1%, the addition of enzyme be 2%, the addition of penetrating agent be 1%.
Beneficial effect: a kind of Antistatic knitting fabric provided by the present invention and preparation method thereof, in fabric, China and foreign countries' three layers is composited by different components respectively, and wherein internal layer is made up of polyvinyl chloride fibre and acrylic fiber;Middle level is made up of cellulose fibre, nylon fibre and wool blended fiber;Outer layer is made up of antistatic fibre, metal blend fibre and protein fibre;Three layers selects suitable fabric fibre to carry out compound respectively, then carries out yarn and knit and form, and enhances the electric conductivity of fabric ectonexine, largely reduces the generation of its electrostatic phenomenon produced due to friction;Various raw fibres and yarn are adopted specific finisher solution to be prepared after arranging by this external preparation process, further enhancing the texture comfort level of fabric and antistatic property.
Detailed description of the invention
Embodiment 1:
A kind of Antistatic knitting fabric, is composited by three layers yarn;Wherein each layer is composited by different fabric components: wherein internal layer is made up of following two composition compound: a1 polyvinyl chloride fibre;B1 acrylic fiber;Middle level is made up of following three kinds of composition compounds: a2 cellulose fibre;B2 nylon fibre;The wool blended fiber of c2;Outer layer is made up of following three kinds of composition compounds: a3 antistatic fibre;B3 metal blend fibre;C3 protein fibre;The weight of described fabric every square metre is 130g;The thickness of described fabric is 1.2mm.
Wherein, in described internal layer, a1 polyvinyl chloride fibre and b1 acrylic fiber weight ratio are 4:1;In middle level, the weight ratio of a2 cellulose fibre, b2 nylon fibre and the wool blended fiber of c2 is 4:1:3;In outer layer, the weight ratio of a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre is 3:1:4;Described a2 cellulose fibre is mixed with the part by weight of 1:2 by cotton fiber and acetate fiber;In the wool blended fiber of described c2, the content of Pilus Caprae seu Ovis is not higher than 90%;Described a3 antistatic fibre is surfactant addition type fiber;Described c3 protein fibre is wool fiber.
The preparation method of above-mentioned a kind of Antistatic knitting fabric, all carried out a prefinishing before carrying out ectonexine monolayer yarn and three layers yarn compound, specific as follows:
(1) it is placed in internal layer raw material a1 polyvinyl chloride fibre with b1 acrylic fiber in the water of the glacial acetic acid that with the addition of 8% to soak to take out after 30min and is dried to 9 one-tenth and dry carries out yarn;
(2) outer layer a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre are placed in the mixed solution that mass ratio is the penetrating agent of 1:3:20, chitosan and water immersion 20min, are dried to 9 one-tenth after taking-up and dry carry out yarn;
(3) by be placed in the aqueous solution that with the addition of softening agent, enzyme, penetrating agent before three layers yarn compound to soak take out natural air drying after 1h after carry out composite yarn again and knit, wherein the addition of softening agent be 1%, the addition of enzyme be 2%, the addition of penetrating agent be 1%.
Embodiment 2:
A kind of Antistatic knitting fabric, is composited by three layers yarn;Wherein each layer is composited by different fabric components: wherein internal layer is made up of following two composition compound: a1 polyvinyl chloride fibre;B1 acrylic fiber;Middle level is made up of following three kinds of composition compounds: a2 cellulose fibre;B2 nylon fibre;The wool blended fiber of c2;Outer layer is made up of following three kinds of composition compounds: a3 antistatic fibre;B3 metal blend fibre;C3 protein fibre;The weight of described fabric every square metre is 220g;The thickness of described fabric is 2.5mm.
Wherein, in described internal layer, a1 polyvinyl chloride fibre and b1 acrylic fiber weight ratio are 4:1;In middle level, the weight ratio of a2 cellulose fibre, b2 nylon fibre and the wool blended fiber of c2 is 4:1:3;In outer layer, the weight ratio of a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre is 3:1:4;Described a2 cellulose fibre is mixed with the part by weight of 1:2 by cotton fiber and acetate fiber;In the wool blended fiber of described c2, the content of Pilus Caprae seu Ovis is not higher than 90%;Described a3 antistatic fibre is surfactant addition type fiber;Described c3 protein fibre is mulberry silk fiber.
The preparation method of above-mentioned a kind of Antistatic knitting fabric, all carried out a prefinishing before carrying out ectonexine monolayer yarn and three layers yarn compound, specific as follows:
(1) it is placed in internal layer raw material a1 polyvinyl chloride fibre with b1 acrylic fiber in the water of the glacial acetic acid that with the addition of 8% to soak to take out after 40min and is dried to 9 one-tenth and dry carries out yarn;
(2) outer layer a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre are placed in the mixed solution that mass ratio is the penetrating agent of 1:3:20, chitosan and water immersion 40min, are dried to 9 one-tenth after taking-up and dry carry out yarn;
(3) by be placed in the aqueous solution that with the addition of softening agent, enzyme, penetrating agent before three layers yarn compound to soak take out natural air drying after 2h after carry out composite yarn again and knit, wherein the addition of softening agent be 1%, the addition of enzyme be 2%, the addition of penetrating agent be 1%.
Embodiment 3:
A kind of Antistatic knitting fabric, is composited by three layers yarn;Wherein each layer is composited by different fabric components: wherein internal layer is made up of following two composition compound: a1 polyvinyl chloride fibre;B1 acrylic fiber;Middle level is made up of following three kinds of composition compounds: a2 cellulose fibre;B2 nylon fibre;The wool blended fiber of c2;Outer layer is made up of following three kinds of composition compounds: a3 antistatic fibre;B3 metal blend fibre;C3 protein fibre;The weight of described fabric every square metre is 180g;The thickness of described fabric is 1.8mm.
Wherein, in described internal layer, a1 polyvinyl chloride fibre and b1 acrylic fiber weight ratio are 4:1;In middle level, the weight ratio of a2 cellulose fibre, b2 nylon fibre and the wool blended fiber of c2 is 4:1:3;In outer layer, the weight ratio of a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre is 3:1:4;Described a2 cellulose fibre is mixed with the part by weight of 1:2 by cotton fiber and acetate fiber;In the wool blended fiber of described c2, the content of Pilus Caprae seu Ovis is not higher than 90%;Described a3 antistatic fibre is surfactant addition type fiber;Described c3 protein fibre is rabbit fur fibre.
The preparation method of above-mentioned a kind of Antistatic knitting fabric, all carried out a prefinishing before carrying out ectonexine monolayer yarn and three layers yarn compound, specific as follows:
(1) it is placed in internal layer raw material a1 polyvinyl chloride fibre with b1 acrylic fiber in the water of the glacial acetic acid that with the addition of 8% to soak to take out after 35min and is dried to 9 one-tenth and dry carries out yarn;
(2) outer layer a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre are placed in the mixed solution that mass ratio is the penetrating agent of 1:3:20, chitosan and water immersion 30min, are dried to 9 one-tenth after taking-up and dry carry out yarn;
(3) by be placed in the aqueous solution that with the addition of softening agent, enzyme, penetrating agent before three layers yarn compound to soak take out natural air drying after 1.5h after carry out composite yarn again and knit, wherein the addition of softening agent be 1%, the addition of enzyme be 2%, the addition of penetrating agent be 1%.
Should be understood that, above detailed description of the invention is merely to illustrate the present invention rather than restriction the scope of the present invention, after having read the present invention, the amendment of the various equivalent form of values of the present invention is all fallen within the application claims limited range by those skilled in the art.
Claims (10)
1. an Antistatic knitting fabric, it is characterised in that be composited by three layers yarn;Wherein each layer is composited by different fabric components: wherein internal layer is made up of following two composition compound: a1 polyvinyl chloride fibre;B1 acrylic fiber;Middle level is made up of following three kinds of composition compounds: a2 cellulose fibre;B2 nylon fibre;The wool blended fiber of c2;Outer layer is made up of following three kinds of composition compounds: a3 antistatic fibre;B3 metal blend fibre;C3 protein fibre;The weight of described fabric every square metre is 130-220g;The thickness of described fabric is 1.2-2.5mm.
2. a kind of Antistatic knitting fabric according to claim 1, it is characterised in that: in described internal layer, a1 polyvinyl chloride fibre and b1 acrylic fiber weight ratio are 4:1.
3. a kind of Antistatic knitting fabric according to claim 1, it is characterised in that: described a2 cellulose fibre is mixed with the part by weight of 1:2 by cotton fiber and acetate fiber.
4. a kind of Antistatic knitting fabric according to claim 1, it is characterised in that: in described middle level, the weight ratio of a2 cellulose fibre, b2 nylon fibre and the wool blended fiber of c2 is 4:1:3.
5. a kind of Antistatic knitting fabric according to claim 1, it is characterised in that: in the wool blended fiber of described c2, the content of Pilus Caprae seu Ovis is not higher than 90%.
6. a kind of Antistatic knitting fabric according to claim 1, it is characterised in that: in described outer layer, the weight ratio of a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre is 3:1:4.
7. a kind of Antistatic knitting fabric according to claim 1, it is characterised in that: described a3 antistatic fibre is surfactant addition type fiber.
8. a kind of Antistatic knitting fabric according to claim 1, it is characterised in that: described c3 protein fibre is the one in wool fiber, mulberry silk fiber, rabbit fur fibre.
9. the preparation method of a kind of Antistatic knitting fabric as claimed in claim 1, it is characterised in that all carried out a prefinishing before carrying out ectonexine monolayer yarn and three layers yarn compound, specific as follows:
(1) it is placed in internal layer raw material a1 polyvinyl chloride fibre with b1 acrylic fiber in the water of the glacial acetic acid that with the addition of 8% to soak to take out after 30-40min and is dried to 9 one-tenth and dry carries out yarn;
(2) outer layer a3 antistatic fibre, b3 metal blend fibre and c3 protein fibre are placed in the mixed solution that mass ratio is the penetrating agent of 1:3:20, chitosan and water immersion 20-40min, are dried to 9 one-tenth after taking-up and dry carry out yarn;
(3) by be placed in the aqueous solution that with the addition of softening agent, enzyme, penetrating agent before three layers yarn compound to soak take out natural air drying after 1-2h after carry out composite yarn again and knit.
10. the preparation method of a kind of Antistatic knitting fabric according to claim 8, it is characterised in that: in described step (3) addition of softening agent be 1%, the addition of enzyme be 2%, the addition of penetrating agent be 1%.