CN105778759A - Asphalt paint for ship anchor chains and preparation method of asphalt paint - Google Patents
Asphalt paint for ship anchor chains and preparation method of asphalt paint Download PDFInfo
- Publication number
- CN105778759A CN105778759A CN201610285080.9A CN201610285080A CN105778759A CN 105778759 A CN105778759 A CN 105778759A CN 201610285080 A CN201610285080 A CN 201610285080A CN 105778759 A CN105778759 A CN 105778759A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- anchor chains
- sufficiently mixed
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses asphalt paint for ship anchor chains and a preparation method of the asphalt paint, and relates to the technical field of marine paint. The asphalt paint comprises, by weight, 40-50 parts of epoxy coal pitch, 10-14 parts of fluorocarbon resin, 10-15 parts of tephra, 8-11 parts of low-density polyethylene, 6-10 parts of disproportionated rosin, 6-10 parts of polyethylene glycol 6000 double-stearate, 5-8 parts of cetanol, 4-6 parts of Portland cement, 4-6 parts of adhesion promoter, 3-5 parts of carbomer resin, 3-5 parts of polyoxyethylene lauryl ether, 2-3 parts of urea, 1-2 parts of glass fiber powder, 1-2 parts of nano aluminum powder, 1-2 parts of sodium hexametaphosphate, 12-17 parts of paraffinic oil and 150-200 parts of water. The asphalt paint has the advantages that paint films with high adhesion force and strength can be formed quickly after the asphalt paint is sprayed onto the ship anchor chains; the paint films have excellent resistance to seawater corrosion, weather and water, and corrosion and damage of seawater and outdoor environment to the anchor chains can be reduced; preparation cost is low, and accordingly, investment is reduced.
Description
Technical field:
The present invention relates to marine paint technical field, be specifically related to a kind of ship anchor chains asphalt caulk and preparation thereof
Method.
Background technology:
Anchor chain is to connect the chain between anchor and hull, is used for transmitting and buffer the external force suffered by boats and ships, also
The frictional force of a part can be produced.Owing to boats and ships are chronically in marine environment, the sea water corrosion to anchor chain
Very serious, on anchor chain, rust staining layer by layer occurs after using a period of time.In order to protect anchor chain structure and prolongation
Its service life, it will usually spray a coating on anchor chain.Although but the anchor chain coating used at present
Anchor chain can be played certain corrosion-resisting function, but force limited, coating easily comes off, thus will be de-
Outside the anchor chain of the part that falls is exposed to.
Summary of the invention:
The technical problem to be solved is to provide one to have excellent resistance to corrosion seawater, weather-proof
Property and resistance to water and the low ship anchor chains asphalt caulk of preparation cost and preparation method thereof.
The technical problem to be solved uses following technical scheme to realize:
A kind of ship anchor chains asphalt caulk, is made up of the raw material of following parts by weight:
Epoxide coal bituminous 40-50 part, fluorocarbon resin 10-15 part, volcanic ash 10-15 part, low density polyethylene
Alkene 8-11 part, disproportionated rosin 6-10 part, polyethylene glycol 6000 double stearate 6-10 part, spermol 5-8
Part, portland cement 4-6 part, adhesion promoter 4-6 part, carbomer 3-5 part, lauryl alcohol polyoxy
Vinyl Ether 3-5 part, carbamide 2-3 part, glass powder 1-2 part, nanometer aluminium powder 1-2 part, sodium hexameta phosphate 1-2
Part, paraffin oil 12-17 part, water 150-200 part.
Described adhesion promoter is made up of the raw material of following parts by weight: terpene resin 10-15 part, activity
Hargil 8-12 part, polyvinyl alcohol 8-12 part, microcrystalline Cellulose 6-10 part, hydroxypropyl guar gum 4-7 part,
Petroleum coke 4-7 part, nanometer titanium dioxide 3-5 part, Oleum Ricini 2-4 part, PEG400 2-4 part, soap
Powder 1-2 part, bone black 1-2 part, ethanol 50-60 part, its preparation method is: first add terpenes in ethanol
Resin, petroleum coke and bone black, after being uniformly dispersed under microwave frequency 2450MHz, power 700W microwave
Process 5min, add polyvinyl alcohol, hydroxypropyl guar gum and PEG400, continue after being sufficiently mixed
Microwave treatment 10min, then sends into spray dryer by mixture, and powder made by the size-reduced machine of gained granule,
It is eventually adding active hargil, microcrystalline Cellulose, nanometer titanium dioxide, Oleum Ricini and soap powder, is sufficiently mixed
Uniformly.
The addition of this adhesion promoter can be effectively improved the paint film adhesive force in metal surface, reduces paint
In use there is the probability of efflorescence and peeling phenomenon in film, and can strengthen paint film as filler
Mechanical performance.
The preparation method of a kind of ship anchor chains asphalt caulk, comprises the steps:
(1) fluorocarbon resin and Low Density Polyethylene are sufficiently mixed, are first heated to 130-140 and are incubated mixing 10
Min, adds disproportionated rosin, adhesion promoter and paraffin oil, continues insulation mixing 10min, to obtain final product
Material I;
(2) in water, the epoxide coal bituminous and double stearate of polyethylene glycol 6000 is added, in micro-after being sufficiently mixed
Microwave treatment 5min under wave frequency 2450MHz, power 700W, is subsequently adding portland cement and Ka Bo
Resin, continues microwave treatment 10min, obtains material II;
(3) in material II add material I, volcanic ash, spermol, polyoxyethylene lauryl ether, carbamide,
Glass powder, nanometer aluminium powder and sodium hexameta phosphate, send in ball mill after being sufficiently mixed, be milled to fineness little
In 50 μm.
The invention has the beneficial effects as follows: the present invention, with epoxide coal bituminous as primary raw material, is aided with fluorocarbon resin
And multiple auxiliary agent prepares ship anchor chains asphalt caulk, this asphalt caulk is sprayed on ship anchor chains and can quickly be formed
The paint film that adhesive force is extremely strong and hardness is big, this paint film has excellent resistance to corrosion seawater, weatherability and water-fast
Property, can alleviate sea water and outdoor environment to the corrosion of anchor chain and loss, and preparation cost is low, thus subtract
Use input less.
Detailed description of the invention:
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be readily apparent from
Solve, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1
(1) 12 parts of fluorocarbon resins and 8 parts of Low Density Polyethylenes are sufficiently mixed, are first heated to 130-140 insulation
Mixing 10min, adds 6 parts of disproportionated rosins, 4 parts of adhesion promoters and 15 parts of paraffin oil, continues insulation
Mixing 10min, obtains material I;
(2) in 150 parts of water, add 40 parts of epoxide coal bituminous and 6 parts of double stearates of polyethylene glycol 6000, fill
Point mixing after under microwave frequency 2450MHz, power 700W microwave treatment 5min, be subsequently adding 5 parts of silicon
Acid salt cement and 3 parts of carbomers, continue microwave treatment 10min, obtain material II;
(3) in material II, material I, 10 parts of volcanic ash, 6 parts of spermols, 5 parts of lauryl alcohol polyethylene glycol oxides are added
Ether, 2 parts of carbamide, 2 parts of glass powder, 1 part of nanometer aluminium powder and 1 part of sodium hexameta phosphate, send into after being sufficiently mixed
In ball mill, it is milled to fineness less than 50 μm.
The preparation of adhesion promoter: first add in 60 parts of ethanol 15 parts of terpene resins, 5 parts of petroleum cokes and
1 part of bone black, after being uniformly dispersed under microwave frequency 2450MHz, power 700W microwave treatment 5min, then
Add 8 parts of polyvinyl alcohol, 4 parts of hydroxypropyl guar gum and 4 parts of PEG400s, continue micro-after being sufficiently mixed
Ripple processes 10min, and then mixture is sent into spray dryer, and powder made by the size-reduced machine of gained granule,
It is eventually adding 8 parts of active hargil, 6 parts of microcrystalline Cellulose, 4 parts of nanometer titanium dioxides, 3 parts of Oleum Ricini and 1 part of fertilizer
Soap powder, is sufficiently mixed uniformly.
Embodiment 2
(1) 15 parts of fluorocarbon resins and 8 parts of Low Density Polyethylenes are sufficiently mixed, are first heated to 130-140 insulation
Mixing 10min, adds 6 parts of disproportionated rosins, 6 parts of adhesion promoters and 12 parts of paraffin oil, continues insulation
Mixing 10min, obtains material I;
(2) in 200 parts of water, add 50 parts of epoxide coal bituminous and 8 parts of double stearates of polyethylene glycol 6000, fill
Point mixing after under microwave frequency 2450MHz, power 700W microwave treatment 5min, be subsequently adding 4 parts of silicon
Acid salt cement and 4 parts of carbomers, continue microwave treatment 10min, obtain material II;
(3) in material II, material I, 15 parts of volcanic ash, 8 parts of spermols, 3 parts of lauryl alcohol polyethylene glycol oxides are added
Ether, 3 parts of carbamide, 1 part of glass powder, 1 part of nanometer aluminium powder and 2 parts of sodium hexameta phosphate, send into after being sufficiently mixed
In ball mill, it is milled to fineness less than 50 μm.
The preparation of adhesion promoter: first add in 50 parts of ethanol 10 parts of terpene resins, 4 parts of petroleum cokes and
2 parts of bone black, after being uniformly dispersed under microwave frequency 2450MHz, power 700W microwave treatment 5min, then
Add 8 parts of polyvinyl alcohol, 6 parts of hydroxypropyl guar gum and 3 parts of PEG400s, continue micro-after being sufficiently mixed
Ripple processes 10min, and then mixture is sent into spray dryer, and powder made by the size-reduced machine of gained granule,
It is eventually adding 8 parts of active hargil, 6 parts of microcrystalline Cellulose, 3 parts of nanometer titanium dioxides, 4 parts of Oleum Ricini and 2 parts of fertilizer
Soap powder, is sufficiently mixed uniformly.
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.One's own profession
Skilled person will appreciate that of industry, the present invention is not restricted to the described embodiments, above-described embodiment and explanation
The principle that the present invention is simply described described in book, without departing from the spirit and scope of the present invention,
The present invention also has various changes and modifications, and these changes and improvements both fall within claimed invention model
In enclosing.Claimed scope is defined by appending claims and equivalent thereof.
Claims (3)
1. a ship anchor chains asphalt caulk, it is characterised in that be made up of the raw material of following parts by weight:
Epoxide coal bituminous 40-50 part, fluorocarbon resin 10-15 part, volcanic ash 10-15 part, low density polyethylene
Alkene 8-11 part, disproportionated rosin 6-10 part, polyethylene glycol 6000 double stearate 6-10 part, spermol 5-8
Part, portland cement 4-6 part, adhesion promoter 4-6 part, carbomer 3-5 part, lauryl alcohol polyoxy
Vinyl Ether 3-5 part, carbamide 2-3 part, glass powder 1-2 part, nanometer aluminium powder 1-2 part, sodium hexameta phosphate 1-2
Part, paraffin oil 12-17 part, water 150-200 part.
Ship anchor chains asphalt caulk the most according to claim 1, it is characterised in that described adhesive force
Accelerator is made up of the raw material of following parts by weight: terpene resin 10-15 part, active hargil 8-12 part,
Polyvinyl alcohol 8-12 part, microcrystalline Cellulose 6-10 part, hydroxypropyl guar gum 4-7 part, petroleum coke 4-7 part,
Nanometer titanium dioxide 3-5 part, Oleum Ricini 2-4 part, PEG400 2-4 part, soap powder 1-2 part, bone black
1-2 part, ethanol 50-60 part, its preparation method is: first add in ethanol terpene resin, petroleum coke and
Bone black, after being uniformly dispersed under microwave frequency 2450MHz, power 700W microwave treatment 5min, then add
Enter polyvinyl alcohol, hydroxypropyl guar gum and PEG400, after being sufficiently mixed, continue microwave treatment 10min,
Then mixture is sent into spray dryer, and the size-reduced machine of gained granule is made powder, is eventually adding activity
Hargil, microcrystalline Cellulose, nanometer titanium dioxide, Oleum Ricini and soap powder, be sufficiently mixed uniformly.
3. the preparation method of a ship anchor chains asphalt caulk, it is characterised in that comprise the steps:
(1) fluorocarbon resin and Low Density Polyethylene are sufficiently mixed, are first heated to 130-140 and are incubated mixing 10
Min, adds disproportionated rosin, adhesion promoter and paraffin oil, continues insulation mixing 10min, to obtain final product
Material I;
(2) in water, the epoxide coal bituminous and double stearate of polyethylene glycol 6000 is added, in micro-after being sufficiently mixed
Microwave treatment 5min under wave frequency 2450MHz, power 700W, is subsequently adding portland cement and Ka Bo
Resin, continues microwave treatment 10min, obtains material II;
(3) in material II add material I, volcanic ash, spermol, polyoxyethylene lauryl ether, carbamide,
Glass powder, nanometer aluminium powder and sodium hexameta phosphate, send in ball mill after being sufficiently mixed, be milled to fineness little
In 50 μm.