CN105778702A - High-strength abrasion-resistant corrosion-resistant paint - Google Patents
High-strength abrasion-resistant corrosion-resistant paint Download PDFInfo
- Publication number
- CN105778702A CN105778702A CN201610182730.7A CN201610182730A CN105778702A CN 105778702 A CN105778702 A CN 105778702A CN 201610182730 A CN201610182730 A CN 201610182730A CN 105778702 A CN105778702 A CN 105778702A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- rosin
- modified polyurethane
- epoxy resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength abrasion-resistant corrosion-resistant paint, prepared from the following raw materials: rosin phenolic resin, modified polyurethane, styrene-acrylic emulsion, polyvinyl chloride resin, epoxy resin, rosin resin, epoxy resin, alkyd resin, butyl acetate, aluminium hydroxide, bentonite, barite powder, mica powder, zeolite powder, chlorinated paraffin, calcium ferrite, hexamethyl cellulose, citric acid and a curing agent. The high-strength abrasion-resistant corrosion-resistant paint has high strength, and good abrasion resistance and corrosion resistance.
Description
Technical field
The present invention relates to paint field, particularly relate to a kind of high-strength abrasion-proof anti-corrosion paint.
Background technology
Paint is that one can firmly cover body surface, plays the chemical mixture coating of protection, decoration, mark and other specific uses.According to the classification of the chemical products that the modern times pass through, coating belongs to fine chemical product.The whitewashing of modern paint not only can spread out of one pungent taste later, and can be not easy to do in the regular hour, and very poor in viscosity, whitewashes on metal, and react with metal makes burning get rusty.
The low rustproof property that wears no resistance of paint intensity of the prior art is low, it is impossible to meet the demand in actual production.
Summary of the invention
For solving the technical problem existed in background technology, the present invention proposes a kind of high-strength abrasion-proof anti-corrosion paint, and intensity high-wearing feature is good, and rustproof property is strong.
A kind of high-strength abrasion-proof anti-corrosion paint that the present invention proposes, its raw material includes by weight: rosin phenolic resin 25-45 part, modified polyurethane 2-9 part, styrene-acrylic emulsion 3-9 part, Corvic 1-5 part, epoxy resin 3-9 part, rosin resin 4-12 part, epoxy resin 2-8 part, alkyd resin 1-5 part, butyl acetate 3-5 part, aluminium hydroxide 2-6 part, bentonite 3-5 part, blanc fixe 1-4 part, mica powder 2-6 part, zeolite powder 1-4 part, chlorinated paraffin 2-6 part, calcium ferrite 2-8 part, hexamethyl cellulose 3-6 part, citric acid 1-4 part, firming agent 2-5 part.
Preferably, modified polyurethane is prepared by following technique: by nano silicon, n-butyl acetate and propylene glycol methyl ether acetate mix homogeneously, is then placed in dispersion machine and disperses 20-40min, then grinds 40-60min and obtains the material a of 0.05-0.1mm;By acrylate and material a mix homogeneously, it is then placed in high speed dispersor and disperses 20-30min, then pass through sand mill and carry out sand milling 40-50min, obtain the modified polyurethane of 15-25 μm.
Preferably, the weight ratio of nano silicon, n-butyl acetate, propylene glycol methyl ether acetate and acrylate is 5-15:2-6:1-5:3-5.
Preferably, the weight ratio of rosin phenolic resin, modified polyurethane, styrene-acrylic emulsion, Corvic, epoxy resin, rosin resin, epoxy resin, alkyd resin and butyl acetate is 25-45:2-9:3-9:1-5:3-9:4-12:2-8:1-5:3-5.
Preferably, the cellulosic weight ratio of rosin phenolic resin, modified polyurethane, aluminium hydroxide, bentonite, blanc fixe, mica powder, zeolite powder, chlorinated paraffin, calcium ferrite and hexamethyl is 28-42:3-8:3-5:3.5-4.5:2-3:3-5:2-3:3-5:3-7:4-5.
Preferably, the weight ratio of nano silicon, n-butyl acetate, propylene glycol methyl ether acetate, acrylate, rosin phenolic resin and alkyd resin is 5-15:2-6:1-5:3-5:28-42:2-4.
Preferably, its raw material includes by weight: rosin phenolic resin 28-42 part, modified polyurethane 3-8 part, styrene-acrylic emulsion 4-8 part, Corvic 2-4 part, epoxy resin 4-8 part, rosin resin 6-10 part, epoxy resin 3-7 part, alkyd resin 2-4 part, butyl acetate 3.5-4.5 part, aluminium hydroxide 3-5 part, bentonite 3.5-4.5 part, blanc fixe 2-3 part, mica powder 3-5 part, zeolite powder 2-3 part, chlorinated paraffin 3-5 part, calcium ferrite 3-7 part, hexamethyl cellulose 4-5 part, citric acid 2-3 part, firming agent 3-4 part.
Preferably, its raw material includes by weight: rosin phenolic resin 35 parts, modified polyurethane 5.5 parts, styrene-acrylic emulsion 6 parts, Corvic 3 parts, epoxy resin 6 parts, rosin resin 8 parts, epoxy resin 4 parts, alkyd resin 3 parts, butyl acetate 4 parts, aluminium hydroxide 4 parts, bentonite 4 parts, blanc fixe 2.5 parts, mica powder 4 parts, zeolite powder 2.5 parts, chlorinated paraffin 4 parts, calcium ferrite 5 parts, hexamethyl cellulose 4.5 parts, citric acid 2.5 parts, 3.5 parts of firming agent.
A kind of high-strength abrasion-proof anti-corrosion paint of the present invention, its raw material includes rosin phenolic resin, modified polyurethane, styrene-acrylic emulsion, Corvic, epoxy resin, rosin resin, epoxy resin, alkyd resin, butyl acetate, aluminium hydroxide, bentonite, blanc fixe, mica powder, zeolite powder, chlorinated paraffin, calcium ferrite, hexamethyl cellulose, citric acid and firming agent.The rosin phenolic resin wherein added and modified polyurethane are major ingredient, and by adding styrene-acrylic emulsion, Corvic, epoxy resin, rosin resin, epoxy resin, alkyd resin and the butyl acetate supporting material as major ingredient, and the proportioning that conservative control is each other, it is effectively increased the intensity of major ingredient, wear-resisting and rustproof property;The aluminium hydroxide, bentonite, blanc fixe, mica powder, zeolite powder, chlorinated paraffin, calcium ferrite, hexamethyl cellulose, citric acid and the firming agent that add are as filler and auxiliary agent, and the proportioning of control and rosin phenolic resin, modified polyurethane so that the good anti-corrosion ability of paint intensity high-wearing feature of the present invention is strong;Modified polyurethane is with nano silicon, n-butyl acetate, propylene glycol methyl ether acetate and acrylate for raw material, the modified polyurethane obtained by nano-silicon dioxide modified polyurethane can be effectively increased intensity and the wearability of present invention paint, and the proportioning of the raw material with rosin phenolic resin and alkyd resin by controlling modified polyurethane, further increase intensity and the anti-wear performance of present invention paint;The citric acid added is as anti-corrosion adding material, it is possible to be effectively improved the rustproof property of present invention paint.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in detail; it is understood that; embodiment is served only for the present invention is described, rather than is used for limiting the invention, any make on basis of the present invention amendment, equivalent replacement etc. is all in protection scope of the present invention.
Embodiment 1
A kind of high-strength abrasion-proof anti-corrosion paint that the present invention proposes, its raw material includes by weight: rosin phenolic resin 35 parts, modified polyurethane 5.5 parts, styrene-acrylic emulsion 6 parts, Corvic 3 parts, epoxy resin 6 parts, rosin resin 8 parts, epoxy resin 4 parts, alkyd resin 3 parts, butyl acetate 4 parts, aluminium hydroxide 4 parts, bentonite 4 parts, blanc fixe 2.5 parts, mica powder 4 parts, zeolite powder 2.5 parts, chlorinated paraffin 4 parts, calcium ferrite 5 parts, hexamethyl cellulose 4.5 parts, citric acid 2.5 parts, 3.5 parts of firming agent.
Modified polyurethane is prepared by following technique: by weight by 10 parts of nano silicons, 4 parts of n-butyl acetates and 3 parts of propylene glycol methyl ether acetate mix homogeneously, is then placed in dispersion machine and disperses 30min, then grinds 50min and obtains the material a of 0.075mm;By 4 parts of acrylate and material a mix homogeneously, it is then placed in high speed dispersor and disperses 25min, then pass through sand mill and carry out sand milling 45min, obtain the modified polyurethane of 20 μm.
Embodiment 2
A kind of high-strength abrasion-proof anti-corrosion paint that the present invention proposes, its raw material includes by weight: rosin phenolic resin 25 parts, modified polyurethane 9 parts, styrene-acrylic emulsion 3 parts, Corvic 5 parts, epoxy resin 3 parts, rosin resin 12 parts, epoxy resin 2 parts, alkyd resin 5 parts, butyl acetate 3 parts, aluminium hydroxide 6 parts, bentonite 3 parts, blanc fixe 4 parts, mica powder 2 parts, zeolite powder 4 parts, chlorinated paraffin 2 parts, calcium ferrite 8 parts, hexamethyl cellulose 3 parts, citric acid 4 parts, 2 parts of firming agent.
Modified polyurethane is prepared by following technique: by weight by 5 parts of nano silicons, 6 parts of n-butyl acetates and 1 part of propylene glycol methyl ether acetate mix homogeneously, is then placed in dispersion machine and disperses 40min, then grinds 40min and obtains the material a of 0.1mm;By 3 parts of acrylate and material a mix homogeneously, it is then placed in high speed dispersor and disperses 30min, then pass through sand mill and carry out sand milling 40min, obtain the modified polyurethane of 25 μm.
Embodiment 3
A kind of high-strength abrasion-proof anti-corrosion paint that the present invention proposes, its raw material includes by weight: rosin phenolic resin 45 parts, modified polyurethane 2 parts, styrene-acrylic emulsion 9 parts, Corvic 1 part, epoxy resin 9 parts, rosin resin 4 parts, epoxy resin 8 parts, alkyd resin 1 part, butyl acetate 5 parts, aluminium hydroxide 2 parts, bentonite 5 parts, blanc fixe 1 part, mica powder 6 parts, zeolite powder 1 part, chlorinated paraffin 6 parts, calcium ferrite 2 parts, hexamethyl cellulose 6 parts, citric acid 1 part, 5 parts of firming agent.
Modified polyurethane is prepared by following technique: by weight by 15 parts of nano silicons, 2 parts of n-butyl acetates and 5 parts of propylene glycol methyl ether acetate mix homogeneously, is then placed in dispersion machine and disperses 20min, then grinds 60min and obtains the material a of 0.05mm;By 5 parts of acrylate and material a mix homogeneously, it is then placed in high speed dispersor and disperses 20min, then pass through sand mill and carry out sand milling 50min, obtain the modified polyurethane of 15 μm.
Embodiment 4
A kind of high-strength abrasion-proof anti-corrosion paint that the present invention proposes, its raw material includes by weight: rosin phenolic resin 28 parts, modified polyurethane 8 parts, styrene-acrylic emulsion 4 parts, Corvic 4 parts, epoxy resin 4 parts, rosin resin 10 parts, epoxy resin 3 parts, alkyd resin 4 parts, butyl acetate 3.5 parts, aluminium hydroxide 5 parts, bentonite 3.5 parts, blanc fixe 3 parts, mica powder 3 parts, zeolite powder 3 parts, chlorinated paraffin 3 parts, calcium ferrite 7 parts, hexamethyl cellulose 4 parts, citric acid 3 parts, 3 parts of firming agent.
Modified polyurethane is prepared by following technique: by weight by 8 parts of nano silicons, 5 parts of n-butyl acetates and 2 parts of propylene glycol methyl ether acetate mix homogeneously, is then placed in dispersion machine and disperses 35min, then grinds 45min and obtains the material a of 0.09mm;By 3.5 parts of acrylate and material a mix homogeneously, it is then placed in high speed dispersor and disperses 28min, then pass through sand mill and carry out sand milling 42min, obtain the modified polyurethane of 22 μm.
Embodiment 5
A kind of high-strength abrasion-proof anti-corrosion paint that the present invention proposes, its raw material includes by weight: rosin phenolic resin 42 parts, modified polyurethane 3 parts, styrene-acrylic emulsion 8 parts, Corvic 2 parts, epoxy resin 8 parts, rosin resin 6 parts, epoxy resin 7 parts, alkyd resin 2 parts, butyl acetate 4.5 parts, aluminium hydroxide 3 parts, bentonite 4.5 parts, blanc fixe 2 parts, mica powder 5 parts, zeolite powder 2 parts, chlorinated paraffin 5 parts, calcium ferrite 3 parts, hexamethyl cellulose 5 parts, citric acid 2 parts, 4 parts of firming agent.
Modified polyurethane is prepared by following technique: by weight by 12 parts of nano silicons, 3 parts of n-butyl acetates and 4 parts of propylene glycol methyl ether acetate mix homogeneously, is then placed in dispersion machine and disperses 25min, then grinds 55min and obtains the material a of 0.06mm;By 4.5 parts of acrylate and material a mix homogeneously, it is then placed in high speed dispersor and disperses 22min, then pass through sand mill and carry out sand milling 48min, obtain the modified polyurethane of 18 μm.
The above; it is only the present invention preferably detailed description of the invention; but protection scope of the present invention is not limited thereto; any those familiar with the art is in the technical scope that the invention discloses; it is equal to replacement according to technical scheme and inventive concept thereof or is changed, all should be encompassed within protection scope of the present invention.
Claims (8)
1. a high-strength abrasion-proof anti-corrosion paint, it is characterized in that, its raw material includes by weight: rosin phenolic resin 25-45 part, modified polyurethane 2-9 part, styrene-acrylic emulsion 3-9 part, Corvic 1-5 part, epoxy resin 3-9 part, rosin resin 4-12 part, epoxy resin 2-8 part, alkyd resin 1-5 part, butyl acetate 3-5 part, aluminium hydroxide 2-6 part, bentonite 3-5 part, blanc fixe 1-4 part, mica powder 2-6 part, zeolite powder 1-4 part, chlorinated paraffin 2-6 part, calcium ferrite 2-8 part, hexamethyl cellulose 3-6 part, citric acid 1-4 part, firming agent 2-5 part.
2. high-strength abrasion-proof anti-corrosion according to claim 1 paint, it is characterized in that, modified polyurethane is prepared by following technique: by nano silicon, n-butyl acetate and propylene glycol methyl ether acetate mix homogeneously, it is then placed in dispersion machine and disperses 20-40min, then grind 40-60min and obtain the material a of 0.05-0.1mm;By acrylate and material a mix homogeneously, it is then placed in high speed dispersor and disperses 20-30min, then pass through sand mill and carry out sand milling 40-50min, obtain the modified polyurethane of 15-25 μm.
3. high-strength abrasion-proof anti-corrosion according to claim 1 and 2 paint, it is characterised in that the weight ratio of nano silicon, n-butyl acetate, propylene glycol methyl ether acetate and acrylate is 5-15:2-6:1-5:3-5.
4. the high-strength abrasion-proof anti-corrosion paint according to any one of claim 1-3, it is characterized in that, the weight ratio of rosin phenolic resin, modified polyurethane, styrene-acrylic emulsion, Corvic, epoxy resin, rosin resin, epoxy resin, alkyd resin and butyl acetate is 25-45:2-9:3-9:1-5:3-9:4-12:2-8:1-5:3-5.
5. the high-strength abrasion-proof anti-corrosion paint according to any one of claim 1-4, it is characterized in that, the cellulosic weight ratio of rosin phenolic resin, modified polyurethane, aluminium hydroxide, bentonite, blanc fixe, mica powder, zeolite powder, chlorinated paraffin, calcium ferrite and hexamethyl is 28-42:3-8:3-5:3.5-4.5:2-3:3-5:2-3:3-5:3-7:4-5.
6. the high-strength abrasion-proof anti-corrosion paint according to any one of claim 1-5, it is characterized in that, the weight ratio of nano silicon, n-butyl acetate, propylene glycol methyl ether acetate, acrylate, rosin phenolic resin and alkyd resin is 5-15:2-6:1-5:3-5:28-42:2-4.
7. the high-strength abrasion-proof anti-corrosion paint according to any one of claim 1-6, it is characterized in that, its raw material includes by weight: rosin phenolic resin 28-42 part, modified polyurethane 3-8 part, styrene-acrylic emulsion 4-8 part, Corvic 2-4 part, epoxy resin 4-8 part, rosin resin 6-10 part, epoxy resin 3-7 part, alkyd resin 2-4 part, butyl acetate 3.5-4.5 part, aluminium hydroxide 3-5 part, bentonite 3.5-4.5 part, blanc fixe 2-3 part, mica powder 3-5 part, zeolite powder 2-3 part, chlorinated paraffin 3-5 part, calcium ferrite 3-7 part, hexamethyl cellulose 4-5 part, citric acid 2-3 part, firming agent 3-4 part.
8. the high-strength abrasion-proof anti-corrosion paint according to any one of claim 1-7, it is characterized in that, its raw material includes by weight: rosin phenolic resin 35 parts, modified polyurethane 5.5 parts, styrene-acrylic emulsion 6 parts, Corvic 3 parts, epoxy resin 6 parts, rosin resin 8 parts, epoxy resin 4 parts, alkyd resin 3 parts, butyl acetate 4 parts, aluminium hydroxide 4 parts, bentonite 4 parts, blanc fixe 2.5 parts, mica powder 4 parts, zeolite powder 2.5 parts, chlorinated paraffin 4 parts, calcium ferrite 5 parts, hexamethyl cellulose 4.5 parts, citric acid 2.5 parts, 3.5 parts of firming agent.