CN106381065A - New aqueous antirust coating - Google Patents
New aqueous antirust coating Download PDFInfo
- Publication number
- CN106381065A CN106381065A CN201610759837.3A CN201610759837A CN106381065A CN 106381065 A CN106381065 A CN 106381065A CN 201610759837 A CN201610759837 A CN 201610759837A CN 106381065 A CN106381065 A CN 106381065A
- Authority
- CN
- China
- Prior art keywords
- agent
- defoamer
- rotating speed
- rev
- dispersant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to a coating, and specifically relates to a new aqueous antirust coating. The new aqueous antirust coating is characterized by comprising the following components, according to a weight part ratio, 5-7% of deionized water, 0.1-0.5% of a pH conditioning agent, 0.2-0.8% of a dispersant, 0.1-0.5% of a wetting agent, 0.2-0.8% of an antifoaming agent A, 6-8% of pigment powder of various colors, 2-4% of zinc phosphate, 2-5% of mica powder, 1-3% of barium sulfate, 59.7-78.4% of an antirust emulsion, 4-5.5% of a film-forming auxiliary agent, 0.1-0.5% of an antifoaming agent B, 0.1-0.2% of an antibacterial antiseptic, 0.1-1% of an anti-flash-rust agent, 0.2-1.5% of a nanometer reinforcing agent and 0.5-2% of a thickening agent. The new aqueous antirust coating overcomes defects of performance of a common aqueous antirust coating, and meets the eco-friendly requirements.
Description
Technical field
The invention belongs to a kind of coating is and in particular to a kind of new aqueous rust-proof coatings.
Background technology
With the pay attention to day by day to environmental protection for the people, Environmentally friendly coatings are increasingly paid attention to, and traditional paint is not because
Environmental protection, VOC is exceeded, is gradually restricted.Existing aqueous antirust paint, because rust-proof effect, hardness, adhesive force all do not reach oiliness
The standard of paint.A kind of new aqueous rust-proof coatings of the present invention, can overcome common water borne antirusting paint scarce in aspect of performance
Point, can meet environmental requirement again.
Content of the invention
A kind of new aqueous rust-proof coatings it is characterised in that：Comprise the component of following weight
Deionized water 5%-7%
PH regulator 0.1%-0.5%
Dispersant 0.2%-0.8%
Wetting agent 0.1%-0.5%
Defoamer A 0.2%-0.8%
Various pigments powder 6%-8%
Zinc phosphate 2%-4%
Mica powder 2%-5%
Barium sulfate 1%-3%
Antirust emulsion 59.7%-78.4%
Coalescents 4%-5.5%
Defoamer B 0.1%-0.5%
Sterilization antiseptic 0.1%-0.2%
Anti- flash rusting agent 0.1%-1%
Nanometer strengthener 0.2%-1.5%
Thickening agent 0.5%-2%
Preparation process is：
A：Deionized water is added in reactor, sequentially adds PH regulator, dispersant, wetting agent, defoamer A, control rotating speed
For 900-1000 rev/min, mixing time is 3-5 minute；
B：Rotating speed is adjusted to 1200-1300 rev/min, sequentially adds various pigments powder one or more, zinc phosphate, Muscovitum
Powder, barium sulfate, jitter time is 20-30 minute.Control fineness is 10-30 micron；
C:Rotating speed is adjusted to 400-500 rev/min, sequentially adds antirust emulsion, coalescents, defoamer B, sterilization antiseptic,
Anti- flash rusting agent, nanometer strengthener, thickening agent, jitter time is 10-15 minute.
Preferably technical scheme is：Described PH regulator is AMP-95, and described dispersant is 1124,
Described wetting agent is 407, and described defoamer A is BYK-024, and described various pigments powder is iron oxide red, described antirust emulsion
For btf-717, described defoamer B is tego270, and described sterilization antiseptic is Huffman, and described anti-flash rusting agent is F179, institute
Stating thickening agent is RM2020.
Its preparation process is：
A：Deionized water is added in reactor, sequentially adds PH regulator, dispersant, wetting agent, defoamer（BYK-024）,
Rotating speed is controlled to be 900-1000 rev/min, mixing time is 5 minutes
B：Rotating speed is adjusted to 1200-1300 rev/min, sequentially adds iron oxide red, zinc phosphate, mica powder, barium sulfate, jitter time
For 30 minutes.Fineness is controlled to be 25 microns
C:Rotating speed is adjusted to 400-500 rev/min, sequentially adds antirust emulsion, coalescents, defoamer（tego270）, sterilization
Preservative, anti-flash rusting agent, nanometer strengthener, thickening agent, jitter time is 15 minutes, a kind of new waterborne anti-rust is obtained and applies
Material.
Instant invention overcomes the existing defect that aqueous antirust paint rust-proof effect is poor, hardness, adhesive force is not up to standard, and raw
Not using containing formaldehydes, benzene class component during production. art, environmentally safe, harmless；Green, environmental protection, effect
Fruit achieves well good economic effect.
Specific embodiment：
A kind of new aqueous rust-proof coatings it is characterised in that：Comprise the component of following weight
Deionized water 7%
PH regulator（AMP-95） 0.2%
Dispersant（1124） 0.5%
Wetting agent（407） 0.1%
Defoamer A（BYK-024） 0.2%
Iron oxide red： 8%
Zinc phosphate 4%
Mica powder 5%
Barium sulfate 2%
Antirust emulsion (btf-717) 65%
Coalescents 5.3%
Defoamer B（tego270） 0.1%
Sterilization antiseptic（Huffman） 0.1%
Anti- flash rusting agent（F179） 0.5%
Nanometer strengthener 1%
Thickening agent（RM2020） 1%
Step
A：Deionized water is added in reactor, sequentially adds PH regulator, dispersant, wetting agent, defoamer A, control rotating speed
For 1000 revs/min, mixing time is 5 minutes
B：Rotating speed is adjusted to 1200 revs/min, sequentially adds iron oxide red, zinc phosphate, mica powder, barium sulfate, jitter time is 30
Minute.Fineness is controlled to be 25 microns
C:Rotating speed is adjusted to 500 revs/min, sequentially adds antirust emulsion, coalescents, defoamer B, sterilization antiseptic, anti-sudden strain of a muscle
Rust agent, nanometer strengthener, thickening agent, jitter time is 15 minutes, and a kind of new aqueous rust-proof coatings are obtained.
The above, a kind of only embodiment of aqueous rust-proof coatings of the present invention, not it is used for limiting present invention enforcement
Scope.So all, to make a formal request shape described in scope, structure, feature and spirit and do according to the present invention be all equivalent variations or modification,
Making a formal request within the scope of the claims of the present invention all should be included in.
Claims (3)
1. a kind of new aqueous rust-proof coatings it is characterised in that：Comprise the component of following weight：
Deionized water 5%-7%
PH regulator 0.1%-0.5%
Dispersant 0.2%-0.8%
Wetting agent 0.1%-0.5%
Defoamer A 0.2%-0.8%
Various pigments powder 6%-8%
Zinc phosphate 2%-4%
Mica powder 2%-5%
Barium sulfate 1%-3%
Antirust emulsion 59.7%-78.4%
Coalescents 4%-5.5%
Defoamer B 0.1%-0.5%
Sterilization antiseptic 0.1%-0.2%
Anti- flash rusting agent 0.1%-1%
Nanometer strengthener 0.2%-1.5%
Thickening agent 0.5%-2%
Preparation process is：
A：Deionized water is added in reactor, sequentially adds PH regulator, dispersant, wetting agent, defoamer A, control rotating speed
For 900-1000 rev/min, mixing time is 3-5 minute；
B：Rotating speed is adjusted to 1200-1300 rev/min, sequentially adds various pigments powder one or more, zinc phosphate, Muscovitum
Powder, barium sulfate, jitter time is 20-30 minute, and control fineness is 10-30 micron；
C:Rotating speed is adjusted to 400-500 rev/min, sequentially adds antirust emulsion, coalescents, defoamer B, sterilization antiseptic,
Anti- flash rusting agent, nanometer strengthener, thickening agent, jitter time is 10-15 minute.
2. a kind of new aqueous rust-proof coatings according to claim 1 it is characterised in that：Described PH regulator is
AMP-95, described dispersant is 1124, and described wetting agent is 407, and described defoamer A is BYK-024, and described various pigments powder is
Iron oxide red, described antirust emulsion is btf-717, and described defoamer B is tego270, and described sterilization antiseptic is Huffman, described
Anti- flash rusting agent is F179, and described thickening agent is RM2020
Its preparation process is：
A：Deionized water is added in reactor, sequentially adds PH regulator, dispersant, wetting agent, defoamer A（BYK-024）,
Rotating speed is controlled to be 900-1000 rev/min, mixing time is 5 minutes
B：Rotating speed is adjusted to 1200-1300 rev/min, sequentially adds iron oxide red, zinc phosphate, mica powder, barium sulfate, jitter time
For 30 minutes, fineness is controlled to be 25 microns;
C:Rotating speed is adjusted to 400-500 rev/min, sequentially adds antirust emulsion, coalescents, defoamer（tego270）, sterilize anti-
Rotten agent, anti-flash rusting agent, nanometer strengthener, thickening agent, jitter time is 15 minutes, and a kind of new aqueous rust-proof coatings are obtained.
3. a kind of new aqueous rust-proof coatings according to claim 2 it is characterised in that：
Comprise the component of following weight
Deionized water 7%
PH regulator（AMP-95） 0.2%
Dispersant（1124） 0.5%
Wetting agent（407） 0.1%
Defoamer A（BYK-024） 0.2%
Iron oxide red： 8%
Zinc phosphate 4%
Mica powder 5%
Barium sulfate 2%
Antirust emulsion (btf-717) 65%
Coalescents 5.3%
Defoamer B（tego270） 0.1%
Sterilization antiseptic（Huffman） 0.1%
Anti- flash rusting agent（F179） 0.5%
Nanometer strengthener 1%
Thickening agent（RM2020） 1%.