CN105778601A - Water-based environment-friendly multicolor special-purposed grounding paint and preparation method thereof - Google Patents
Water-based environment-friendly multicolor special-purposed grounding paint and preparation method thereof Download PDFInfo
- Publication number
- CN105778601A CN105778601A CN201410838066.8A CN201410838066A CN105778601A CN 105778601 A CN105778601 A CN 105778601A CN 201410838066 A CN201410838066 A CN 201410838066A CN 105778601 A CN105778601 A CN 105778601A
- Authority
- CN
- China
- Prior art keywords
- water
- stirring
- aqueous
- background color
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a water-based environment-friendly multicolor special-purposed grounding paint and a preparation method thereof. The paint comprises the following components, in parts by weight: 25-40 parts of synthetic resin emulsion, 30-45 parts of powders, 2-5 parts of auxiliary agents, and 10-20 parts of water. According to the requirement of a formula, water is completely added into a stirring kettle; stirring is carried out with a speed of 300-600r/m; under continuous stirring, the first three of the auxiliary agents are sequentially added into the stirring kettle, and uniform stirring is conducted; after the mixture is uniform, the powders are sequentially added into the stirring kettle according to the sequence specified in the formula; the speed is adjusted to 1200-1600r, and stirring is carried out for 45-60min; after high-speed dispersion, the speed is reduced to 500-600r, and the synthetic resin emulsion is completely added into the stirring kettle; when the synthetic resin emulsion is well mixed, the rest of the auxiliary agents are added; and a thickening agent is added by slow stirring until a needed viscosity is reached. Compared with prior arts, the method provided by the invention has the advantages of low cost and simple procedures. The paint has the advantages of good elasticity, high weatherability and the like.
Description
Technical field
The present invention relates to background color coating, be specifically related to colorful special background color coating of aqueous, environmental protective and preparation method thereof.
Background technology
Multicolor finish is by continuous phase or claims disperse medium, and dispersion phase composition, continuous phase low concentration, low viscosity；Dispersion phase is high concentration then, high viscosity, and containing coloring pigment.Under stirring, the dispersion phase of different colours is dispersed to respectively in continuous phase and forms macroscopic tiny grain bar or grain drips, and then mixes.Also disposable the pigmented base of different colours can be distributed in medium and form multicolor finish.According to biphase character.Multicolor finish can be divided into four classes: oil-in-water type, water-in-oil type, oil oil-in and water-in-water type.Water-in-water type and water paint, this be in aqueous latex paint add can gelation water soluble paint dispersion form.Water type multicolor paint for water drum, is actually a kind of droplet with water emulsion coating and is constituted the dispersion phase of coating, and protection glue solution constitutes the heterogeneous suspended substance of continuous phase.Obtain uniform, stable this suspended substance, be necessary for carrying out that water emulsion coating is added drop-wise to this process in protection glue solution.Do not occur the protection glue solution dilution to water emulsion coating, the condensation of latex paint and pigment to infiltration in protection sol solution etc. in this course simultaneously.Water type multicolor paint for water drum is to have the dispersing droplets of former latex paint proportioning thing wherein, forms protection glue solution continuous phase and is wrapped in the suspended substance of latex paint droplet.Realize the suspended substance of this " water-water "; it is necessary for asking in wink in water emulsion coating being scattered in protection glue solution; one layer of water-fast flexible membrane is formed on the surface being coated with gob; this layer of flexible membrane is except can outside the protection glue component except block film inside courtyard component and film spreads mutually, also prevent from assembling between Paint Drip, condensing.After spraying application, at first the gob that is coated with in wet film still protects the suspended state in aqueous phase, along with the volatilization of moisture in film, is coated with gob and mutually piles up, merges, ultimately form firmly multi-color decorative pattern film.
Patent application 201210178825.3 discloses a kind of water-soluble colorful coating and preparation method thereof.Described water-soluble colorful coating, including dispersion phase and continuous phase, wherein, described dispersion phase includes waterborne film-forming thing, pigment and water；Described continuous phase includes waterborne film-forming material, protection glue and water.This coating coloured silk point is moderate, the pattern effect of different pattern different colours can be obtained by change background color or mould, and processing technology is simple, can extensively replace wallpaper, also can be sprayed on the objects such as body of wall, wood furniture, metal, plastics and form floral designs, reach decorative effect.
But multicolor finish is along with the maturation of technology, the stability of product is become better and better, popularization and the dynamics of use in market are increasing, practice and construction in the middle of exist some problems also outstanding day by day out, after construction completes, except marmorean phase knowledge and magnanimity, it is more and more higher that to external world water-fast weather-proof also requires that, it is directed to colorful resistance to water-white problem, we develop a kind of existing elongation percentage, having again water-fast, the coating of weatherability is as colorful priming color so that it is resistance to water-white problem is eased.
Summary of the invention
Defect that the purpose of the present invention is contemplated to overcome above-mentioned prior art to exist and provide that a kind of cost is low, operation simple, the colorful special background color coating of aqueous, environmental protective of good springiness, resistance to water-white and preparation method thereof.
The purpose of the present invention can be achieved through the following technical solutions: a kind of colorful special background color coating of aqueous, environmental protective, it is characterised in that this coating includes the component of following weight portion: resins synthesis emulsion 25～40, powder body 30-45, auxiliary agent 2-5, water 10-20.
Described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity is at 200～1000Pa s, and testing conditions is: 3#.30rpm, 25 DEG C.His its existing good elongation percentage of this emulsion, and stain resistance has again good weatherability.
Described resins synthesis emulsion is made by the following method: by weight percentage, commercially available emulsion is added 80%, water 14%, cellulose 0.1%, coalescents 3.2%, propylene glycol 2.0%, adhesion promoter 0.2%, defoamer 0.1%, thickening agent 0.3% and progressive dose 0.1% stir at normal temperatures a kind of is with granular cream liquid to be resins synthesis emulsion.
Described powder body includes the component of following weight portion: rutile-type exterior wall titanium dioxide (1250 order) 15～25, Kaolin (1250 order) 5～15, sericite (1250 order) 1～8, triple superphosphate (1250 order) 5～10；The particle diameter of described powder body is.
Described powder body includes the component of following weight portion: rutile-type exterior wall titanium dioxide 17.5, Kaolin 10, sericite 5, triple superphosphate 8.
Described auxiliary agent includes the component of following weight portion: coalescents is with 0.8, and propylene glycol is with 1, and wetting agent consumption 0.2, nertralizer is with 0.2, and antibacterial is with 0.5, and defoamer is with 0.3, and thickening agent is with 1.
The preparation method of the colorful special background color coating of a kind of aqueous, environmental protective, it is characterised in that the method comprises the following steps:
(1) first all being put in stirred tank by water by recipe requirements, 300-600 rev/min is stirred；
(2) it is kept stirring for and by the stirred tank of input successively of first three in auxiliary agent, stirs；
(3) to be mixed uniformly after powder body is sequentially added in stirred tank according to formula order, speed is transferred to 1200-1600 and turns, carry out the stirring of 45-60 minute；
(4) when, after high speed dispersion, being down to low speed 500-600 and turn, resins synthesis emulsion is all added in stirred tank；
(5) resins synthesis emulsion is stirring evenly and then adding into remainder auxiliary agent；
(6) slowly stirring addition thickening agent is transferred to required viscosity again.
Adding auxiliary agent according to formula can make auxiliary agent be fully utilized, and will not be neutralized each other.Need to carry out high speed dispersion after powder body adds, can disperse when speed is inadequate to be fully that product produces precipitation.
Compared with prior art, the invention have the advantages that
(1) this product has good resistance to water；
(2) not only there is extensibility but also there is stain resistance；
(3) cost of raw material of product can be reduced；
(4) reduce aberration and construction connects a batch problem.
Detailed description of the invention
Below embodiments of the invention being elaborated, the present embodiment is carried out under premised on technical solution of the present invention, gives detailed embodiment and concrete operating process, but protection scope of the present invention is not limited to following embodiment.
The auxiliary agent adopted in following example is:
Coalescents CS-25, propylene glycol BS-12, wetting agent RA-80, nertralizer DA-59, antibacterial FA-34, defoamer XA-26, thickening agent ZA-48.
Embodiment 1
A kind of preparation method of the colorful special background color coating of aqueous, environmental protective, the method comprises the following steps:
(1) first all being put in stirred tank by water 15kg by recipe requirements, 300 revs/min are stirred；
(2) it is kept stirring for and CS-250.8kg, BS-121kg, RA-800.2kg are put in stirred tank successively, stirring；
(3) to be mixed uniformly after by powder body: rutile-type exterior wall titanium dioxide 17.5kg, Kaolin 10kg, sericite 5kg, triple superphosphate 8kg is sequentially added in stirred tank according to formula order, and speed is transferred to 1200 turns, carries out the stirring of 45 minutes；
(4) when, after high speed dispersion, being down to low speed 500 turns, resins synthesis emulsion 30kg is all added in stirred tank；Described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity, at 200～1000 (4#.30rpm, 25 degree), has excellent elongation percentage, and the emulsion 15% being equipped with silicon third has weatherability, resistance to water and stain resistance.Described resins synthesis emulsion is made by the following method: by weight percentage, commercially available emulsion is added 80%, water 14%, cellulose 0.1%, coalescents 3.2%, propylene glycol 2.0%, adhesion promoter 0.2%, defoamer 0.1%, thickening agent 0.3% and progressive dose 0.1% stir at normal temperatures a kind of is with granular cream liquid to be resins synthesis emulsion.
(5) resins synthesis emulsion is stirring evenly and then adding into remainder auxiliary agent: DA-590.2kg, FA-340.5kg, XA-260.3kg, ZA-481kg；
(6) slowly stirring addition thickening agent is transferred to required viscosity again.
Embodiment 2
A kind of preparation method of the colorful special background color coating of aqueous, environmental protective, the method comprises the following steps:
(1) first all being put in stirred tank by water 10kg by recipe requirements, 300 revs/min are stirred；
(2) it is kept stirring for and CS-250.3kg, BS-120.5kg, RA-800.2kg are put in stirred tank successively, stirring；
(3) to be mixed uniformly after by powder body: rutile-type exterior wall titanium dioxide 15kg, Kaolin 5kg, sericite 9kg, triple superphosphate 5kg is sequentially added in stirred tank according to formula order, and speed is transferred to 1500 turns, carries out the stirring of 50 minutes；
(4) when, after high speed dispersion, being down to low speed 500-600 and turn, resins synthesis emulsion 25kg is all added in stirred tank；Described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity, at 200～1000 (4#.30rpm, 25 degree), has excellent elongation percentage, and the emulsion 15% being equipped with silicon third has weatherability, resistance to water and stain resistance.Described resins synthesis emulsion is made by the following method: by weight percentage, commercially available emulsion is added 80%, water 14%, cellulose 0.1%, coalescents 3.2%, propylene glycol 2.0%, adhesion promoter 0.2%, defoamer 0.1%, thickening agent 0.3% and progressive dose 0.1% stir at normal temperatures a kind of is with granular cream liquid to be resins synthesis emulsion.
(5) resins synthesis emulsion is stirring evenly and then adding into remainder auxiliary agent: DA-590.1kg, FA-340.4kg, XA-260.1kg, ZA-480.5kg；
(6) slowly stirring addition thickening agent is transferred to required viscosity again.
Embodiment 3
A kind of preparation method of the colorful special background color coating of aqueous, environmental protective, the method comprises the following steps:
(1) first all being put in stirred tank by water 20kg by recipe requirements, 600 revs/min are stirred；
(2) it is kept stirring for and CS-250.8kg, BS-121kg, RA-800.2kg are put in stirred tank successively, stirring；
(3) to be mixed uniformly after by powder body: rutile-type exterior wall titanium dioxide 20kg, Kaolin 15kg, sericite 8kg, triple superphosphate 2kg is sequentially added in stirred tank according to formula order, and speed is transferred to 1600 turns, carries out the stirring of 60 minutes；
(4) when, after high speed dispersion, being down to low speed 500-600 and turn, resins synthesis emulsion 40kg is all added in stirred tank；Described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity, at 200～1000 (4#.30rpm, 25 degree), has excellent elongation percentage, and the emulsion 15% being equipped with silicon third has weatherability, resistance to water and stain resistance.Described resins synthesis emulsion is made by the following method: by weight percentage, commercially available emulsion is added 80%, water 14%, cellulose 0.1%, coalescents 3.2%, propylene glycol 2.0%, adhesion promoter 0.2%, defoamer 0.1%, thickening agent 0.3% and progressive dose 0.1% stir at normal temperatures a kind of is with granular cream liquid to be resins synthesis emulsion.
(5) resins synthesis emulsion is stirring evenly and then adding into remainder auxiliary agent: DA-590.2kg, FA-340.5kg, XA-260.3kg, ZA-482kg；
(6) slowly stirring addition thickening agent is transferred to required viscosity again.
The performance of the coating obtained by above-described embodiment is as follows:
| Embodiment 1 | Embodiment 2 | Embodiment 3 | |
| Hot strength | 1.5 | 1.2 | 1.3 |
| Anti-aging test | 500 pass through | 500 pass through | 500 pass through |
| Abrasion resistance | Pass through for 2000 times | Pass through for 2000 times | Pass through for 2000 times |
| Resistance to water-white | 96H is without exception | 96H is without exception | 96H is without exception |
Claims (7)
1. the colorful special background color coating of aqueous, environmental protective, it is characterised in that this coating includes the component of following weight portion: resins synthesis emulsion 25～40, powder body 30-45, auxiliary agent 2-5, water 10-20.
2. the colorful special background color coating of aqueous, environmental protective according to claim 1, it is characterised in that described resins synthesis emulsion particle diameter is at 0.1-0.2 micron, and viscosity is at 200～1000Pa s, and testing conditions is: 3#.30rpm, 25 DEG C.
3. the colorful special background color coating of aqueous, environmental protective according to claim 1 and 2, it is characterized in that, described resins synthesis emulsion is made by the following method: by weight percentage, by acrylic acid pure-acrylic emulsion 80%, water 14%, cellulose 0.1%, coalescents 3.2%, propylene glycol 2.0%, adhesion promoter 0.2%, defoamer 0.1%, thickening agent 0.3% and progressive dose 0.1% stir at normal temperatures a kind of is with granular cream liquid to be resins synthesis emulsion.
4. the colorful special background color coating of aqueous, environmental protective according to claim 1, it is characterised in that described powder body includes the component of following weight portion: rutile-type exterior wall titanium dioxide 15～25, Kaolin 5～15, sericite 1～8, triple superphosphate 5～10；The particle diameter of described powder body is 1250 orders.
5. the colorful special background color coating of aqueous, environmental protective according to claim 4, it is characterised in that described powder body includes the component of following weight portion: rutile-type exterior wall titanium dioxide 17.5, Kaolin 10, sericite 5, triple superphosphate 8.
6. the colorful special background color coating of aqueous, environmental protective according to claim 1, it is characterised in that described auxiliary agent includes the component of following weight portion: coalescents is with 0.8, propylene glycol with 1, wetting agent consumption 0.2, nertralizer is with 0.2, dispersant is with 0.5, and defoamer is with 0.3, and thickening agent is with 1.
7. the preparation method of the colorful special background color coating of aqueous, environmental protective as claimed in claim 1, it is characterised in that the method comprises the following steps:
(1) first all being put in stirred tank by water by recipe requirements, 300-600 rev/min is stirred；
(2) it is kept stirring for and by the stirred tank of input successively of first three in auxiliary agent, stirs；
(3) to be mixed uniformly after powder body is sequentially added in stirred tank according to formula order, speed is transferred to 1200-1600 and turns, carry out the stirring of 45-60 minute；
(4) when, after high speed dispersion, being down to low speed 500-600 and turn, resins synthesis emulsion is all added in stirred tank；
(5) resins synthesis emulsion is stirring evenly and then adding into remainder auxiliary agent；
(6) slowly stirring addition thickening agent is transferred to required viscosity again.