CN105778211A - Antiskid and anti-aging shoe material and production method thereof - Google Patents

Antiskid and anti-aging shoe material and production method thereof Download PDF

Info

Publication number
CN105778211A
CN105778211A CN201610160058.1A CN201610160058A CN105778211A CN 105778211 A CN105778211 A CN 105778211A CN 201610160058 A CN201610160058 A CN 201610160058A CN 105778211 A CN105778211 A CN 105778211A
Authority
CN
China
Prior art keywords
weight portion
aging
district
temperature
skidding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610160058.1A
Other languages
Chinese (zh)
Inventor
魏锋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Yuehu Sponge Composite Plant
Original Assignee
Suzhou Yuehu Sponge Composite Plant
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Yuehu Sponge Composite Plant filed Critical Suzhou Yuehu Sponge Composite Plant
Priority to CN201610160058.1A priority Critical patent/CN105778211A/en
Publication of CN105778211A publication Critical patent/CN105778211A/en
Pending legal-status Critical Current

Abstract

The invention discloses antiskid and anti-aging shoe material and a production method thereof. The antiskid and anti-aging shoe material comprises, by weight, 70-80 parts of polyethylene, 15-20 parts of polyacrylonitrile fibers, 8-11 parts of sec-octyl phenol polyoxyethylene ether, 6-8 parts of magnesium carbonate, 2-4 parts of polymethyl methacrylate, 2-4 parts of polyglycerol fatty acid ester, 2-4 parts of polyoxyethylene rosin ester, 1-2 parts of glutaraldehyde, 0.5-1 part of magnesium zinc ferrite, 0.5-0.8 part of bis(2-chloroethyl)phosphoramidic dichloride, 0.04-0.1 part of nonylphenol ethoxylate and 0.02-0.04 part of pinene.

Description

A kind of footwear material anti-skidding, anti-aging and preparation method thereof
Technical field
The invention belongs to footwear material field, particularly to a kind of footwear material anti-skidding, anti-aging and preparation method thereof.
Background technology
The quality of material for sole of shoe is in addition to non-skid property, and it is elastic and wearability is also the biggest of decision shoes comfort level Influence factor, material for sole of shoe reaches certain skidproof effect by suppressing lines on sole at present, but this lines Often it is smoothed because of the constantly friction after wearing a period of time between shoes and ground, does not still have anti-skidding effect, additionally Wear sole and have obvious sense of discomfort, walk the most painstaking.
Polyethylene (being called for short PE) is the aggregated prepared a kind of thermoplastic resin of ethene, and polyethylene odorless, nontoxic, feel is seemingly Wax, has excellent resistance to low temperature, and chemical stability is good, is resistant to the erosion of most of soda acid.
Summary of the invention
For above-mentioned demand, invention especially provides a kind of footwear material anti-skidding, anti-aging and preparation method thereof.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of footwear material anti-skidding, anti-aging, is made up of the component comprising following weight portion:
Polyethylene 70-80 part,
Polyacrylonitrile fibre 15-20 part,
Secondary octyl phenol polyethenoxy ether 8-11 part,
Magnesium carbonate 6-8 part,
Polymethyl methacrylate 2-4 part,
Polyglyceryl fatty acid ester 2-4 part,
Polyoxylethylene abietate 2-4 part,
Glutaraldehyde 1-2 part,
MgZn ferrite 0.5-1 part,
Double (2-chloroethyl) dichlor-phosphoryl amine 0.5-0.8 part,
Poly-ethylene oxide nonyl phenol 0.04-0.1 part,
Firpene 0.02-0.04 part.
Described component also includes paraffin 0-1 weight portion.
Described component also includes polyoxyethylene oleic acid ester 0-0.5 weight portion.
A kind of preparation method of footwear material anti-skidding, anti-aging, the method comprises the following steps:
(1) polyethylene 70-80 weight portion, magnesium carbonate 6-8 weight portion, polymethyl methacrylate 2-4 weight portion, polyglycereol are weighed Fatty acid ester 2-4 weight portion, polyoxylethylene abietate 2-4 weight portion, glutaraldehyde 1-2 weight portion, MgZn ferrite 0.5-1 weight Amount part, double (2-chloroethyl) dichlor-phosphoryl amine 0.5-0.8 weight portion, poly-ethylene oxide nonyl phenol 0.04-0.1 weight portion, firpene 0.02-0.04 weight portion, paraffin 0-1 weight portion and polyoxyethylene oleic acid ester 0-0.5 weight portion, stir at 50-60 DEG C;
(2) said components is added pusher stirrer for mixing uniform, adds secondary octyl phenol polyethenoxy ether 8-11 weight portion, Adding in double screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 15-20 weight portion, melt, Extrusion, dry, pelletizing, obtain footwear material anti-skidding, anti-aging.
The each zone temperatures of described double screw extruder is: district's temperature 170-180 DEG C, two district's temperature 190-210 DEG C, 3rd district Temperature 220-230 DEG C, four district's temperature 200-210 DEG C, five district's temperature 170-180 DEG C.
Compared with prior art, it has the beneficial effect that the present invention
(1) the footwear material anti-skidding, anti-aging that the present invention prepares is with polyethylene as primary raw material, by adding polyacrylonitrile fibre, secondary OPEO, magnesium carbonate, polymethyl methacrylate, polyglyceryl fatty acid ester, polyoxylethylene abietate, penta 2 Aldehyde, MgZn ferrite, double (2-chloroethyl) dichlor-phosphoryl amine, poly-ethylene oxide nonyl phenol and firpene, prepared is anti-skidding, anti-aging Footwear material has good mechanical strength, remains to keep good mechanical property when temperature is relatively low.
(2) the footwear material anti-skidding, anti-aging of the present invention has good surface abrasion resistance, and has the longer use longevity Life.
(3) the footwear material anti-skidding, anti-aging of the present invention, its preparation method is simple, it is easy to industrialized production.
Detailed description of the invention
Below in conjunction with embodiment, the present invention is further illustrated.
Embodiment 1
(1) polyethylene 70kg, magnesium carbonate 6kg, polymethyl methacrylate 2kg, polyglyceryl fatty acid ester 2kg, rosin acid are weighed Polyoxyethylene ester 2kg, glutaraldehyde 1kg, MgZn ferrite 0.5kg, double (2-chloroethyl) dichlor-phosphoryl amine 0.5kg, poly-ethylene oxide Nonyl phenol 0.04kg and firpene 0.02kg, stirs at 50 DEG C;
(2) said components is added pusher stirrer for mixing uniform, add secondary octyl phenol polyethenoxy ether 8kg, add double In screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 15kg, melts, extrudes, is dried, cuts Grain, obtains footwear material anti-skidding, anti-aging.
The each zone temperatures of described double screw extruder is: district's temperature 170 DEG C, two district's temperature 190 DEG C, three district's temperature 220 DEG C, four district's temperature 200 DEG C, five district's temperature 170 DEG C.
The performance test results preparing footwear material anti-skidding, anti-aging is as shown in table 1.
Embodiment 2
(1) polyethylene 70kg, magnesium carbonate 6kg, polymethyl methacrylate 2kg, polyglyceryl fatty acid ester 2kg, rosin acid are weighed Polyoxyethylene ester 2kg, glutaraldehyde 1kg, MgZn ferrite 0.5kg, double (2-chloroethyl) dichlor-phosphoryl amine 0.5kg, poly-ethylene oxide Nonyl phenol 0.04kg, firpene 0.02kg, paraffin 1kg and polyoxyethylene oleic acid ester 0.5kg, stir at 50 DEG C;
(2) said components is added pusher stirrer for mixing uniform, add secondary octyl phenol polyethenoxy ether 8kg, add double In screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 15kg, melts, extrudes, is dried, cuts Grain, obtains footwear material anti-skidding, anti-aging.
The each zone temperatures of described double screw extruder is: district's temperature 170 DEG C, two district's temperature 190 DEG C, three district's temperature 220 DEG C, four district's temperature 200 DEG C, five district's temperature 170 DEG C.
The performance test results preparing footwear material anti-skidding, anti-aging is as shown in table 1.
Embodiment 3
(1) polyethylene 80kg, magnesium carbonate 8kg, polymethyl methacrylate 4kg, polyglyceryl fatty acid ester 4kg, rosin acid are weighed Polyoxyethylene ester 4kg, glutaraldehyde 2kg, MgZn ferrite 1kg, double (2-chloroethyl) dichlor-phosphoryl amine 0.8kg, poly-ethylene oxide nonyl Base phenol 0.1kg, firpene 0.04kg, paraffin 1kg and polyoxyethylene oleic acid ester 0.5kg, stir at 60 DEG C;
(2) said components is added pusher stirrer for mixing uniform, add secondary octyl phenol polyethenoxy ether 11kg, add double In screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 20kg, melts, extrudes, is dried, cuts Grain, obtains footwear material anti-skidding, anti-aging.
The each zone temperatures of described double screw extruder is: district's temperature 180 DEG C, two district's temperature 210 DEG C, three district's temperature 230 DEG C, four district's temperature 210 DEG C, five district's temperature 180 DEG C.
The performance test results preparing footwear material anti-skidding, anti-aging is as shown in table 1.
Embodiment 4
(1) polyethylene 80kg, magnesium carbonate 8kg, polymethyl methacrylate 4kg, polyglyceryl fatty acid ester 4kg, rosin acid are weighed Polyoxyethylene ester 2kg, glutaraldehyde 2kg, MgZn ferrite 0.5kg, double (2-chloroethyl) dichlor-phosphoryl amine 0.8kg, poly-ethylene oxide Nonyl phenol 0.1kg, firpene 0.04kg, paraffin 1kg and polyoxyethylene oleic acid ester 0.5kg, stir at 60 DEG C;
(2) said components is added pusher stirrer for mixing uniform, add secondary octyl phenol polyethenoxy ether 11kg, add double In screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 20kg, melts, extrudes, is dried, cuts Grain, obtains footwear material anti-skidding, anti-aging.
The each zone temperatures of described double screw extruder is: district's temperature 180 DEG C, two district's temperature 210 DEG C, three district's temperature 230 DEG C, four district's temperature 210 DEG C, five district's temperature 180 DEG C.
The performance test results preparing footwear material anti-skidding, anti-aging is as shown in table 1.
Embodiment 5
(1) polyethylene 75kg, magnesium carbonate 7kg, polymethyl methacrylate 3kg, polyglyceryl fatty acid ester 3kg, rosin acid are weighed Polyoxyethylene ester 3kg, glutaraldehyde 1.5kg, MgZn ferrite 1kg, double (2-chloroethyl) dichlor-phosphoryl amine 0.6kg, poly-ethylene oxide Nonyl phenol 0.07kg, firpene 0.03kg, paraffin 0.5kg and polyoxyethylene oleic acid ester 0.2kg, stir at 55 DEG C;
(2) said components is added pusher stirrer for mixing uniform, add secondary octyl phenol polyethenoxy ether 9kg, add double In screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 18kg, melts, extrudes, is dried, cuts Grain, obtains footwear material anti-skidding, anti-aging.
The each zone temperatures of described double screw extruder is: district's temperature 175 DEG C, two district's temperature 200 DEG C, three district's temperature 225 DEG C, four district's temperature 205 DEG C, five district's temperature 175 DEG C.
The performance test results preparing footwear material anti-skidding, anti-aging is as shown in table 1.
Comparative example 1
(1) polyethylene 80kg, magnesium carbonate 8kg, polymethyl methacrylate 4kg, polyglyceryl fatty acid ester 4kg, rosin acid are weighed Polyoxyethylene ester 4kg, glutaraldehyde 2kg, double (2-chloroethyl) dichlor-phosphoryl amine 0.8kg, poly-ethylene oxide nonyl phenol 0.1kg, pinane Alkene 0.04kg, paraffin 1kg and polyoxyethylene oleic acid ester 0.5kg, stir at 60 DEG C;
(2) said components is added pusher stirrer for mixing uniform, add secondary octyl phenol polyethenoxy ether 11kg, add double In screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 20kg, melts, extrudes, is dried, cuts Grain, obtains footwear material anti-skidding, anti-aging.
The each zone temperatures of described double screw extruder is: district's temperature 180 DEG C, two district's temperature 210 DEG C, three district's temperature 230 DEG C, four district's temperature 210 DEG C, five district's temperature 180 DEG C.
The performance test results preparing footwear material anti-skidding, anti-aging is as shown in table 1.
Comparative example 2
(1) polyethylene 80kg, magnesium carbonate 8kg, polymethyl methacrylate 4kg, polyglyceryl fatty acid ester 4kg, glutaraldehyde are weighed 2kg, MgZn ferrite 1kg, double (2-chloroethyl) dichlor-phosphoryl amine 0.8kg, poly-ethylene oxide nonyl phenol 0.1kg, firpene 0.04kg, paraffin 1kg and polyoxyethylene oleic acid ester 0.5kg, stir at 60 DEG C;
(2) said components is added pusher stirrer for mixing uniform, add secondary octyl phenol polyethenoxy ether 11kg, add double In screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 20kg, melts, extrudes, is dried, cuts Grain, obtains footwear material anti-skidding, anti-aging.
The each zone temperatures of described double screw extruder is: district's temperature 180 DEG C, two district's temperature 210 DEG C, three district's temperature 230 DEG C, four district's temperature 210 DEG C, five district's temperature 180 DEG C.
The performance test results preparing footwear material anti-skidding, anti-aging is as shown in table 1.
Comparative example 3
(1) polyethylene 80kg, magnesium carbonate 8kg, polymethyl methacrylate 4kg, polyglyceryl fatty acid ester 4kg, rosin acid are weighed Polyoxyethylene ester 4kg, glutaraldehyde 2kg, MgZn ferrite 1kg, double (2-chloroethyl) dichlor-phosphoryl amine 0.8kg, poly-ethylene oxide nonyl Base phenol 0.1kg, paraffin 1kg and polyoxyethylene oleic acid ester 0.5kg, stir at 60 DEG C;
(2) said components is added pusher stirrer for mixing uniform, add secondary octyl phenol polyethenoxy ether 11kg, add double In screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 20kg, melts, extrudes, is dried, cuts Grain, obtains footwear material anti-skidding, anti-aging.
The each zone temperatures of described double screw extruder is: district's temperature 180 DEG C, two district's temperature 210 DEG C, three district's temperature 230 DEG C, four district's temperature 210 DEG C, five district's temperature 180 DEG C.
Table 1
Test event Hardness (HW, degree) Tearing toughness (KN/m)
Embodiment 1 77 33
Embodiment 2 78 35
Embodiment 3 84 39
Embodiment 4 85 41
Embodiment 5 87 45
Comparative example 1 48 15
Comparative example 2 45 17
Comparative example 3 50 13
The invention is not restricted to embodiment here, those skilled in the art are according to the announcement of the present invention, without departing from scope Improvement and the amendment made all should be within protection scope of the present invention.

Claims (5)

1. a footwear material anti-skidding, anti-aging, it is characterised in that be made up of the component comprising following weight portion:
Polyethylene 70-80 part,
Polyacrylonitrile fibre 15-20 part,
Secondary octyl phenol polyethenoxy ether 8-11 part,
Magnesium carbonate 6-8 part,
Polymethyl methacrylate 2-4 part,
Polyglyceryl fatty acid ester 2-4 part,
Polyoxylethylene abietate 2-4 part,
Glutaraldehyde 1-2 part,
MgZn ferrite 0.5-1 part,
Double (2-chloroethyl) dichlor-phosphoryl amine 0.5-0.8 part,
Poly-ethylene oxide nonyl phenol 0.04-0.1 part,
Firpene 0.02-0.04 part.
Footwear material the most anti-skidding, anti-aging, it is characterised in that described component also includes paraffin 0-1 weight Part.
Footwear material the most anti-skidding, anti-aging, it is characterised in that described component also includes oleic acid polyoxyethylene Ester 0-0.5 weight portion.
4. the preparation method of a footwear material anti-skidding, anti-aging, it is characterised in that the method comprises the following steps:
(1) polyethylene 70-80 weight portion, magnesium carbonate 6-8 weight portion, polymethyl methacrylate 2-4 weight portion, polyglycereol are weighed Fatty acid ester 2-4 weight portion, polyoxylethylene abietate 2-4 weight portion, glutaraldehyde 1-2 weight portion, MgZn ferrite 0.5-1 weight Amount part, double (2-chloroethyl) dichlor-phosphoryl amine 0.5-0.8 weight portion, poly-ethylene oxide nonyl phenol 0.04-0.1 weight portion, firpene 0.02-0.04 weight portion, paraffin 0-1 weight portion and polyoxyethylene oleic acid ester 0-0.5 weight portion, stir at 50-60 DEG C;
(2) said components is added pusher stirrer for mixing uniform, adds secondary octyl phenol polyethenoxy ether 8-11 weight portion, Adding in double screw extruder, the side loading mouth at double screw extruder adds polyacrylonitrile fibre 15-20 weight portion, melt, Extrusion, dry, pelletizing, obtain footwear material anti-skidding, anti-aging.
The preparation method of footwear material anti-skidding, anti-aging the most according to claim 4, it is characterised in that described twin-screw extrusion The each zone temperatures of machine is: district's temperature 170-180 DEG C, two district's temperature 190-210 DEG C, three district's temperature 220-230 DEG C, four district's temperature 200-210 DEG C, five district's temperature 170-180 DEG C.
CN201610160058.1A 2016-03-21 2016-03-21 Antiskid and anti-aging shoe material and production method thereof Pending CN105778211A (en)