CN105776985A - Preparation method of mulberry twig cement mixed clay - Google Patents
Preparation method of mulberry twig cement mixed clay Download PDFInfo
- Publication number
- CN105776985A CN105776985A CN201610088661.3A CN201610088661A CN105776985A CN 105776985 A CN105776985 A CN 105776985A CN 201610088661 A CN201610088661 A CN 201610088661A CN 105776985 A CN105776985 A CN 105776985A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- mixed
- ramulus mori
- mulberry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of mulberry twig cement mixed clay.The method comprises the following steps that A, mulberry twigs are shredded into shredded mulberry shoots with the length being smaller than 1 millimeter for use; B, mulberry shoots, cement, coal ash, sand and propylene glycol are mixed and stirred to be uniform, and dispersed grinding is performed for 20-30 min to obtain a shredded mulberry twig powder mixture; C, calcium lignosulphonate, a polycarboxylate superplasticizer, methylcellulose and sodium hyaluronate are mixed with water and stirred to be uniform to obtain a water-contained mixture; D, the two mixtures obtained in the step B and the step C are mixed and stirred for 3-5 min, then, pouring is performed, maintenance is performed in the environment under the temperature of 10-27 DEG C, and the maintenance time is not shorter than 7 days.Compared with the prior art, the mulberry twig cement mixed clay is a good material for manufacturing a building product with low weight and high strength.
Description
Technical field
The present invention relates to building material technical field, its preparation method of the mixed earth of especially a kind of Ramulus Mori cement containing Ramulus Mori.
Background technology
Substantial amounts of mulberry has been planted as big province of breeding silkworms in Guangxi, and mulberry is cut down in the summer and cuts down the time with the winter and to cut down substantial amounts of Ramulus Mori, after being taken out by useful Ramulus Mori, also have a large amount of remaining Ramulus Moris can only find suitable use, can only random burn, i.e. contaminated environment, again when waste resource.
Summary of the invention
The preparation method that the technical problem to be solved is to provide the mixed earth of Ramulus Mori cement of a kind of ecology, environmental protection.
This invention address that the technical scheme that technical problem adopts is: the preparation method of the mixed earth of a kind of Ramulus Mori cement, the mixed earth of Ramulus Mori cement is made up of the raw material of following weight portion: Ramulus Mori 5 parts~7 parts, cement 35 parts~55 parts, 15 parts~25 parts of flyash, sand 10 parts~25 parts, propylene glycol 1 part~2 parts, wood calcium 1 part~2 parts, high-efficiency water-reducing agent of poly-carboxylic acid 5 parts~6 parts, methylcellulose 2 parts~3 parts, hyaluronate sodium 1 part~2 parts;
Comprise the following steps:
A, by Ramulus Mori chopping for the length broken mulberry shoot less than 1 millimeter, standby;
B, by broken mulberry shoot, cement, flyash, sand and mixed with propylene glycol and stir, dispersion is ground 20 minutes~30 minutes, obtains broken Ramulus Mori powder mixture;
C, wood calcium, high-efficiency water-reducing agent of poly-carboxylic acid, methylcellulose and hyaluronate sodium are mixed with water, stir, obtain adding aqueous mixtures;
D, two kinds of mixture mixing step B and step C obtained, stir 3 minutes~5 minutes, then pour into a mould, carry out maintenance after building in the environment of 10 DEG C~27 DEG C, and curing time was no less than 7 days.
Owing to have employed technique scheme, the present invention compared with prior art has the advantages that the mechanical external force effect that the mixed earth of this Ramulus Mori cement relies on broken mulberry shoot, cement and other compositions to apply in whipping process, the mixed earth of the Ramulus Mori cement containing uniform micro-bubble formed, namely it is the material manufacturing light-weight building goods, makes again the Ramulus Mori discarded obtain utilization.
Detailed description of the invention
Below in conjunction with example, the invention will be further described:
Embodiment 1:
A kind of preparation method of the mixed earth of Ramulus Mori cement, the mixed earth of this Ramulus Mori cement is made up of the raw material of following weight portion: Ramulus Mori 5 parts, cement 35 parts, 15 parts of flyash, sand 10 parts, propylene glycol 1 part, wood calcium 1 part, high-efficiency water-reducing agent of poly-carboxylic acid 5 parts, methylcellulose 2 parts, hyaluronate sodium 1 part;
Comprise the following steps:
A, by Ramulus Mori chopping for the length broken mulberry shoot less than 1 millimeter, standby;
B, by broken mulberry shoot, cement, flyash, sand and mixed with propylene glycol and stir, dispersion is ground 20 minutes, obtains broken Ramulus Mori powder mixture;
C, wood calcium, high-efficiency water-reducing agent of poly-carboxylic acid, methylcellulose and hyaluronate sodium are mixed with water, stir, obtain adding aqueous mixtures;
D, two kinds of mixture mixing step B and step C obtained, stir 3 minutes, then pour into a mould, carry out maintenance after building in the environment of 10 DEG C~27 DEG C, and curing time was no less than 7 days.
Embodiment 2:
A kind of preparation method of the mixed earth of Ramulus Mori cement, the mixed earth of this Ramulus Mori cement is made up of the raw material of following weight portion: Ramulus Mori 7 parts, cement 55 parts, 25 parts of flyash, sand 25 parts, propylene glycol 2 parts, wood calcium 2 parts, high-efficiency water-reducing agent of poly-carboxylic acid 6 parts, methylcellulose 3 parts, hyaluronate sodium 2 parts;
Comprise the following steps:
A, by Ramulus Mori chopping for the length broken mulberry shoot less than 1 millimeter, standby;
B, by broken mulberry shoot, cement, flyash, sand and mixed with propylene glycol and stir, dispersion is ground 30 minutes, obtains broken Ramulus Mori powder mixture;
C, wood calcium, high-efficiency water-reducing agent of poly-carboxylic acid, methylcellulose and hyaluronate sodium are mixed with water, stir, obtain adding aqueous mixtures;
D, two kinds of mixture mixing step B and step C obtained, stir 5 minutes, then pour into a mould, carry out maintenance after building in the environment of 10 DEG C~27 DEG C, and curing time was no less than 7 days.
Claims (1)
1. the preparation method of the mixed earth of Ramulus Mori cement, it is characterized in that: the mixed earth of Ramulus Mori cement is made up of the raw material of following weight portion: Ramulus Mori 5 parts~7 parts, cement 35 parts~55 parts, 15 parts~25 parts of flyash, sand 10 parts~25 parts, propylene glycol 1 part~2 parts, wood calcium 1 part~2 parts, high-efficiency water-reducing agent of poly-carboxylic acid 5 parts~6 parts, methylcellulose 2 parts~3 parts, hyaluronate sodium 1 part~2 parts;
Comprise the following steps:
A, by Ramulus Mori chopping for the length broken mulberry shoot less than 1 millimeter, standby;
B, by broken mulberry shoot, cement, flyash, sand and mixed with propylene glycol and stir, dispersion is ground 20 minutes~30 minutes, obtains broken Ramulus Mori powder mixture;
C, wood calcium, high-efficiency water-reducing agent of poly-carboxylic acid, methylcellulose and hyaluronate sodium are mixed with water, stir, obtain adding aqueous mixtures;
D, two kinds of mixture mixing step B and step C obtained, stir 3 minutes~5 minutes, then pour into a mould, carry out maintenance after building in the environment of 10 DEG C~27 DEG C, and curing time was no less than 7 days.