CN105774374B - Enamel draws tulle and feels processing method thoroughly

Info

Publication number: CN105774374B
Application number: CN201610278815.5A
Authority: CN
Inventors: 黄灵燕
Original assignee: Individual
Current assignee: Individual
Priority date: 2016-04-28
Filing date: 2016-04-28
Publication date: 2019-02-01
Anticipated expiration: 2036-04-28
Also published as: CN105774374A

Abstract

The present invention relates to a kind of enamel to draw processing technology, and especially a kind of enamel draws tulle and feels processing method thoroughly.Using sense glaze thoroughly upper in saturating sensillary area domain, there is interval in the particle for feeling glaze thoroughly each other, form the method for sense feature thoroughly to carry out the performance of sense characteristic.The above method can be drawn in enamel, make the effect felt, the saturating sense effect of different transparencies can be made according to the size of saturating sense frit particles and spacing, it is drawn by the enamel that the above method is worked it out, not only maintain the effect that original enamel is drawn, it can prevent sense from deforming simultaneously, it is very high to feel glaze stability thoroughly.

Description

Enamel draws tulle and feels processing method thoroughly

Technical field

The present invention relates to a kind of enamel to draw processing technology, and especially a kind of enamel draws tulle and feels processing method thoroughly.

Background technique

Enamel, also known as " Buddhist youth " " method blue " ", also known as cloisonne enamel, is the phonemic loans of a foreign word in fact.One etymology of enamel in The Western Regions Chinese Sui Tang Shigu place name strokes East-Roman-Empire.Byzantine and all embedding glaze handicrafts of enamel that manufacture of ground of West Asia Mediterranean at that time Product Cheng Fu East-Roman-Empire is embedding or Buddhist youth is embedding, the bright machine of Buddhist, is reduced to Fu East-Roman-Empire.Turn sound after there is cloisonne enamel to turn blue, rear be enamel again.1918~ 1956, enamel is synonymous with enamel to be shared.China works out enamelware standard within 1956, and enamel, which changes, is set to enamel, as art The synonym of enamel.

As enamel wires inlay the progress of technique, this artistic expression is applied to and is drawn, therefore forms enamel It draws, enamel, which is drawn, to be completed by glaze filling, thus determines the characteristic of picture, and enamel picture is can not to show half at present The feature of transparence, for example, gauze kerchief, silk etc effect do not exhibit come, which limits enamel draw development and into Step.

Summary of the invention

Tulle, which is drawn, the object of the present invention is to provide a kind of enamel that can show semi-transparency property feels processing method thoroughly.

The technical solution adopted by the present invention to solve the technical problems is: a kind of enamel draws tulle and feels processing method thoroughly, Method is as follows: the first step, while drawing a picture, is sketched the contours of with filamentary silver in the region for needing expression to feel thoroughly and needs to express the area felt thoroughly Domain profile；The glaze of 100 mesh is placed in the water-based glue of 1:100 and is uniformly mixed by second step, and on drawing board basic color into Glaze is drawn a picture on row, and basis of formation is absorbed at picture, and by the water-based glue for being exposed to frit surface；Third step, in the region of filamentary silver There is interval in interior upper sense glaze, the particle for feeling glaze thoroughly, form sense feature thoroughly each other；4th step, with high-density sponge, The moisture for absorbing all glaze is placed in the ventilated environment that temperature is 20-30 degree, naturally dry, until glaze humidity is 20% Until；5th step, with the water-based glue of 30:100, interval sprays at least 4 times on glaze, makes the humidity of glaze in 40-70% Between, it is placed in the ventilated environment that temperature is 20-30 degree, naturally dry, until glaze humidity is 20%；6th step, It is mixed and is painted with the water-based glue of 30:100 with saturating sense glaze on filamentary silver line, form lines of outline, being placed on temperature is 20-30 In the ventilated environment of degree, naturally dry, until glaze humidity is 0；7th step is surface-treated fixed glaze.

The further setting of the present invention are as follows: the distance between described saturating sense frit particles are between 0.001-1mm.

The further setting of the present invention are as follows: the size of the saturating sense frit particles is 80-120 mesh.

The above method can be drawn in enamel, make the effect felt, according to the size and spacing of saturating sense frit particles The saturating sense effect that different transparencies can be made is drawn by the enamel that the above method is worked it out, and is not only maintained original enamel and is drawn Effect, while can prevent sense deform, thoroughly feel glaze stability it is very high.

Specific embodiment

A kind of enamel of the present invention draws tulle and feels processing method thoroughly, and method is as follows: the first step, while drawing a picture, with silver Silk is sketched the contours of in the region for needing expression to feel thoroughly to need to express the region contour felt thoroughly；The glaze of 100 mesh is placed on by second step It is uniformly mixed in the water-based glue of 1:100, and basic color carries out upper glaze and draws a picture on drawing board, basis of formation, and will dew at picture It is absorbed in the water-based glue of frit surface；Third step, the upper sense glaze thoroughly in the region of filamentary silver, feel thoroughly the particle of glaze each other it Between exist interval, formed thoroughly sense feature；4th step absorbs the moisture of all glaze with high-density sponge, and being placed on temperature is 20- In 30 degree of ventilated environment, naturally dry, until glaze humidity is 20%；5th step, with the water-based glue of 30:100, Every sprinkling at least 4 times on glaze, make the humidity of glaze between 40-70%, is placed on the ventilated environment that temperature is 20-30 degree It is interior, naturally dry, until glaze humidity is 20%；6th step, on filamentary silver line with thoroughly sense glaze and 30:100 it is aqueous Glue mixing is painted, and lines of outline is formed, and is placed in the ventilated environment that temperature is 20-30 degree, naturally dry, until glaze Until humidity is 0；7th step is surface-treated fixed glaze.

The distance between heretofore described saturating sense frit particles feel frit particles between 0.001-1mm thoroughly certainly The distance between determine the degree felt, apart from smaller, the degree felt thoroughly is more unobvious, and distance is bigger, and the degree felt thoroughly is got over Obviously, transparency as needed carries out the adjusting of spacing, in the same sensillary area, expresses bending using different spacing Fold and other effects can embody the three-dimensional presentation felt thoroughly.

The size of sense frit particles of the present invention is 80-120 mesh, this is intended to embody different art effects Fruit shows the fine and smooth degree felt thoroughly, and the effect that smaller frit particles are shown is finer and smoother, can have more between basic colour glaze Strong stereovision, when especially showing some silk effects, it is necessary to very thin frit particles.

In the present invention, it is placed in the ventilated environment that temperature is 20-30 degree, naturally dry, until glaze humidity is 20%, Be in order to keep frit particles gluing handle can permeate, if dry completely, then go up glue, will lead to it is impermeable, can also Glaze can be caused to deform, therefore to keep such humidity, if humidity is excessively high to will lead between frit particles viscosity not enough, on Glue can make its deformation, and gluing duplicate in this way can guarantee that the fixation of frit particles is very firm, improve the stability of frit particles.

In the present invention for filamentary silver line procedure of processing it is not necessary to, performance thoroughly sense when, be related to two The big form of expression of kind, one is the saturating sense features for having sideline, and one is the saturating sense features without obvious sideline, for the place of filamentary silver Reason is in order to embody apparent sideline, if it is the saturating sense feature without obvious sideline, such as environmental characteristics, it is necessary to be completed thoroughly After sense processing, remove filamentary silver, there are two the effects of filamentary silver, and one is for fixed sense presentation thoroughly, and there are also a kind of effects to be In order to become apparent from its lines clearly, such as when expressing this sense effect of gauze kerchief, it is necessary to filamentary silver and to filamentary silver Processing cooperation.

Obviously, above-described embodiment is just for the sake of clearly illustrating done citing, and does not limit the embodiments. To those of ordinary skill in the art, other various forms of variations or change can also be made on the basis of the above description It is dynamic.There is no necessity and possibility to exhaust all the enbodiments.And obvious variation extended from this or change It moves still in protection scope of the present invention.

Claims

1. a kind of enamel draws tulle feels processing method thoroughly, method is as follows:

The first step sketches the contours of the region wheel that needs to express and feel thoroughly in the region for needing expression to feel thoroughly with filamentary silver while drawing a picture It is wide；

The glaze of 100 mesh is placed in the water-based glue of 1:100 and is uniformly mixed by second step, and basic color carries out on drawing board Upper glaze is drawn a picture, and basis of formation is absorbed at picture, and by the water-based glue for being exposed to frit surface；

Third step, in the region of filamentary silver there is interval in upper sense glaze thoroughly, the particle for feeling glaze thoroughly each other, and it is special to form sense thoroughly Sign；

4th step absorbs the moisture of all glaze with high-density sponge, is placed in the ventilated environment that temperature is 20-30 degree, natural It dries, until glaze humidity is 20%；

5th step, with the water-based glue of 30:100, interval sprinkling at least 4 times on glaze, make the humidity of glaze 40-70% it Between, it is placed in the ventilated environment that temperature is 20-30 degree, naturally dry, until glaze humidity is 20%.

2. enamel described in accordance with the claim 1 draws tulle feels processing method thoroughly, it is characterised in that: the 6th step, on filamentary silver line It is mixed and is painted with the water-based glue of 30:100 with saturating sense glaze, form lines of outline, be placed on the ventilation that temperature is 20-30 degree In environment, naturally dry, until glaze humidity is 0；

7th step is surface-treated fixed glaze.

3. enamel described in accordance with the claim 1 draws tulle feels processing method thoroughly, it is characterised in that: the saturating sense frit particles The distance between 0.001-1mm.

4. enamel described in accordance with the claim 1 draws tulle feels processing method thoroughly, it is characterised in that: the saturating sense frit particles Size be 80-120 mesh.