CN105771094B - A kind of multielement compound energy material and its preparation method and application device - Google Patents
A kind of multielement compound energy material and its preparation method and application device Download PDFInfo
- Publication number
- CN105771094B CN105771094B CN201610161856.6A CN201610161856A CN105771094B CN 105771094 B CN105771094 B CN 105771094B CN 201610161856 A CN201610161856 A CN 201610161856A CN 105771094 B CN105771094 B CN 105771094B
- Authority
- CN
- China
- Prior art keywords
- energy
- permanent magnet
- baffler
- magnetic force
- card slot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of multielement compound energy material and its preparation method and application devices, by environment-friendly resin, far-infrared powder, Tourmaline powder, germanite powder, negative ion powder, stone needle powder, volcano stone flour, bamboo charcoal, curing agent, accelerating agent and flexible glue are prepared, it adopts and is prepared manually or machine is prepared, its application apparatus includes energy composite energy body, securing plate, permanent magnet, magnetic force baffler, fixed pedestal, securing plate wraps up permanent magnet to lower half, magnetic force baffler, permanent magnet is adsorbed at the top of magnetic force baffler, magnetic force baffler wraps up permanent magnet to upper half, small card slot on fixed pedestal half wraps up magnetic force baffler upwards, permanent magnet, fixed pedestal wraps up energy composite energy body to upper half, securing plate, permanent magnet, magnetic force baffler.The present invention can be carried out at the same time the physical therapies such as far infrared, anion, Tourmaline, magnetic therapy, stone needle, germanite, promote the volatilization of number Ten microelements by magnetic field effect, human body is allowed to more easily absorb trace element.
Description
Technical field
The present invention relates to healthcare field, specifically a kind of multielement compound energy material and its preparation method and application dress
It sets.
Background technology
Chinese medicine has developed nearly history in 3000, Five elements theory, acupuncture point, the channels and collaterals of Chinese medicine, and magical six art of Chinese medicine
" stone acupuncture needle, needle, moxibustion, medicine, by lifting up, guide ", constitute the main element of Chinese medicine conditioning.Six art Chinese medicine of Chinese medicine is to come the 4th, perform acupunctures with stone needles,
Needle, moxibustion come first 3, illustrate that ancestor is desirable to us and is improved with naturopathy and health of body, ability of having no alternative medication.
With the development of modern science and technology, the equipment facility of three kinds of various simulation stone acupuncture needles, needle, moxibustion therapies emerges one after another, the equipment of most electricity consumptions
1 to 2 kinds can be simulated, non-electric is typically all that far infrared cloth adds block magnet.In recent years by food-safety problem, Chinese medicine plant
Change, (in the world in 30,000,000,000 dollars of Market of Chinese Materia Medica, China only accounts for 5% to chemicalization problem, and Japan, South Korea have seized the world
70% or more the market share of Chinese patent drug, due to the limitation of foreign patent, China's Chinese medicine has been difficult based on international market), allow people
Dare not eat dare not drink, and wipe with being all afraid of, in addition modern society's great work intensity, informationization causes people to enter " lazyboot's epoch " movement
It is fewer and fewer, future belong to green and healthy, naturopathy, simple health epoch.Therefore it needs to develop a kind of new health care
Material and relevant device, to meet the needs of people.
Invention content
The purpose of the present invention is to provide a kind of multielement compound energy material and its preparation method and application devices, with solution
Certainly the problems mentioned above in the background art.
To achieve the above object, the present invention provides the following technical solutions：
A kind of multielement compound energy material, is prepared by the raw material of following mass fraction：Environment-friendly resin 40~50%,
Far-infrared powder 10~14%, Tourmaline powder 10~14%, germanite powder 10~14%, negative ion powder 0.9~1.1%, stone needle powder 4~
6%, volcano stone flour 1.8~2.2%, bamboo charcoal 0.9~1.1%, curing agent 1.8~2.2%, accelerating agent 1.8~2.2%.
A kind of preparation method of the multielement compound energy material, using in following two preparation methods it is a kind of into
It is prepared by row,
(1) artificial preparation process
1) 1/7 curing agent, 1/7 accelerating agent are added in liquid environment-friendly resin, 2~3min of stirring is poured into mold,
5~15min is stood, pure resin piece is formed；2) while carrying out 1) step, liquid environment-friendly resin is poured into container, successively
Be added far-infrared powder, Tourmaline powder, germanite powder, negative ion powder, stone needle powder, volcano stone flour, with electric blender stirring 9~
11min forms mixes liquid raw material slurry；2) impurity in being starched with the filter filter mixed liquor state raw material of 300~500 mesh；3)
Remaining curing agent, accelerating agent and flexible glue is added in mixes liquid raw material slurry, is stirred for 1~2min；4) by mixes liquid original
Slurry pours into mold, stands 30~60min, and pure resin piece and mixed raw material chip bonding are integrated, and takes out；5) pass through 4~12h
Solidification, hardening, pour into automatic polishing machine, carry out 24~48h polishing, you can；
(2) machine preparation process
1) 1/5 curing agent, 1/5 accelerating agent, flexible glue are added in liquid environment-friendly resin, 2~3min of stirring is poured into certainly
In dynamic centrifugation pelleter；2) centrifugation pelleter is rotated with the speed of 1500 turns/min, rotates 15min, is centrifuged into average 1~5mm
Pure resin sheet material；3) carry out it is above-mentioned 1), 2) step while liquid environment-friendly resin is poured into homogenizer, sequentially add remote
Infrared powder, Tourmaline powder, germanite powder, negative ion powder, stone needle powder, volcano stone flour stir 9~11min, form mixes liquid raw material
Slurry；4) impurity in being starched with the filter filter mixed liquor state raw material of 300~500 mesh；5) it is added in mixes liquid raw material slurry
Remaining curing agent and remaining accelerating agent, are stirred for 2~3min；6) rotation for temporarily only centrifuging pelleter, into mixes liquid
Raw material slurry pour slurry process, according to film-making thickness come determine mixes liquid raw material slurry weight, by liquid mixed raw material slurry pour into from
In heart pelleter；7) centrifugation pelleter is rotated with the speed of 1500 turns/min, rotates 40~60min, is centrifuged into average 2~10mm
Sheet material, pure resin sheet material and mixed raw material sheet material are combined into one；8) soft shape sheet material is taken out from centrifugation pelleter, 20~
60min is sent to and rushes embryo machine and carried out rushing embryo with cutting die, germule is washed into according to the shape of cutting die；9) pass through curing, firmly for 4~12h
Change, germule is sent to vehicle button machine and is modified；10) germule after finishing is poured into automatic polishing machine, carries out the throwing of 24~48h
Light, you can.
A kind of application apparatus of the multielement compound energy material, including energy composite energy body, securing plate, permanent magnet,
Magnetic force baffler, fixed pedestal, the energy composite energy body and securing plate of liquid are integrated molding structure, the energy composite energy body
Middle part lower end is provided with small card slot, and the securing plate partly wraps up permanent magnet, magnetic force baffler, and the permanent magnet is adsorbed on magnetic force resistance
At the top of partition board, the magnetic force baffler wraps up permanent magnet to upper half, and the edge of the fixed pedestal is provided with big card slot, described solid
Determine to be provided with small card slot in the middle part of pedestal, and the small card slot in securing plate is correspondingly arranged with the small card slot in fixed substrate, it is described
Small card slot on fixed pedestal half wraps up magnetic force baffler, permanent magnet upwards, and the big card slot on the fixed pedestal half wraps upwards
Energy composite energy body, securing plate, permanent magnet, magnetic force baffler are wrapped up in, is glued between the fixed pedestal and securing plate or energy composite energy body
Close connection.
As a further solution of the present invention：The energy composite energy body of the liquid instills or is bonded in the kilocalorie of fixed pedestal
In slot, and fixed pedestal half wraps up energy composite energy body, and the energy composite energy body of liquid wraps up permanent magnet and magnetic force baffler, liquid
Big card slot on the full fixed pedestal of energy composite energy body drop.
As a further solution of the present invention：The energy composite energy body correspondence of the liquid drops in or is bonded in fixed pedestal
On, and the energy composite energy body package permanent magnet and magnetic force baffler of liquid, the card slot formed in the middle part of energy composite energy body lower end with it is solid
Determine the corresponding setting of card slot in the middle part of pedestal.
As a further solution of the present invention：The energy composite energy body of the liquid drops on fixed pedestal and one chemical conversion
Type offers card slot on energy composite energy body, and the permanent magnet and magnetic force baffler are arranged in fixed pedestal, the top of permanent magnet
Material bodies are provided with, the material bodies are bonded into one with energy composite energy body, permanent magnet, magnetic force baffler.
As a further solution of the present invention：The energy composite energy body drops in fixed pedestal and integrated molding, recombination energy
It measures body and is equipped with card slot in the middle part of fixed pedestal, the decoration filling plate of liquid is instilled or is bonded in the card slot of fixed pedestal, and is filled
Decorations filling plate wraps up permanent magnet and magnetic force baffler from bottom, the card slot of the full fixed pedestal of decoration filling plate drop of liquid and with it is solid
Determine pedestal to be integrally formed.
As a further solution of the present invention：A perforative connecting hole is respectively arranged in the fixed pedestal both sides.
As further scheme of the invention：It is provided with multiple small card slots, the fixed pedestal in the middle part of the securing plate
Multiple big card slots and small card slot are set, and the small card slot in securing plate is correspondingly arranged with the small deck on fixed pedestal.
Compared with prior art, the beneficial effects of the invention are as follows：Material of the present invention is rich in 40 various trace elements, has remote
The energy such as infrared, anion, Tourmaline, magnetic therapy, stone needle, germanite improve effect, simulate stone acupuncture needle art, acupuncture, temperature in six art of Chinese medicine
Three art of moxibustion does not have to water power, and energy consumption, size shape do not change flexibly, can develop the wearable product of serial Chinese medicine, and green
Environmentally friendly, simple and convenient, obvious effect meets following health theory；The fooled acupoint plaster in acupuncture point can be placed directly on to use, can be done
At the wearable protector of Chinese medicine, clothes, it can be placed in pillow, cushion, mattress, bedding, sofa cushion, automobile cushion etc., do not influence original
The use of clothing and article, make former clothing and article upgrade at once have health-care efficacy, be attached on clothes become Chinese medicine conditioning clothing,
Being attached on pillow/neck waist pillow becomes Chinese medicine conditioning pillow, attached become Chinese medicine conditioning chair on the seat, is attached on band and becomes Chinese medicine tune
Manage knapsack, the attached Chinese medicine that becomes in bed improves bed etc.；It being not required in skin contact, alternating floor underwear can generate conditioning effect simultaneously,
It avoids causing skin allergy, itch, environmental and durable, no use cost.
Description of the drawings
Fig. 1 is the structural schematic diagram of the embodiment of the present invention 1.
Fig. 2 is the structural schematic diagram of the embodiment of the present invention 2.
Fig. 3 is the structural schematic diagram of the embodiment of the present invention 3.
Fig. 4 is the structural schematic diagram of the embodiment of the present invention 4.
Fig. 5 is the structural schematic diagram of the embodiment of the present invention 5.
Fig. 6 is the structural schematic diagram of the embodiment of the present invention 6.
Fig. 7 is the structural schematic diagram of the embodiment of the present invention 7.
Fig. 8 is the structural schematic diagram of the embodiment of the present invention 8.
Fig. 9 is the structural schematic diagram of the embodiment of the present invention 9.
Figure 10 is the structural schematic diagram of the embodiment of the present invention 10.
Figure 11 is the structural schematic diagram of the embodiment of the present invention 11.
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment 1
Referring to Fig. 1, in the embodiment of the present invention, the application apparatus of multielement compound energy material, including energy composite energy body
1, securing plate 7, permanent magnet 2, magnetic force baffler 3, fixed pedestal 4, the energy composite energy body 1 and securing plate 7 of liquid are integrated chemical conversion
The middle part lower end of type structure, energy composite energy body 1 is provided with small card slot, and securing plate 7 half wraps up permanent magnet 2, magnetic force baffler 3, forever
Magnet 2 is adsorbed on 3 top of magnetic force baffler, and magnetic force baffler 3 wraps up permanent magnet 2 to upper half, and the edge of fixed pedestal 4 is provided with
The middle part of big card slot, fixed pedestal 4 is provided with small card slot, and the small card slot in securing plate 7 and the small card slot pair in fixed substrate 4
Should be arranged, the small card slot on fixed pedestal 4 half package magnetic force baffler 3, permanent magnet 2 upwards, the big card slot on fixed pedestal 4 to
Upper half wraps up energy composite energy body 1, securing plate 7, permanent magnet 2, magnetic force baffler 3, fixed pedestal 4, magnetic force baffler 3, securing plate 7
Between bond connection.
Energy composite energy body 1 and securing plate 7 are integrated molding structure, are because single energy composite energy body 1 is very crisp fragile
It splits, is easy explosion, breakage in process, causes yield rate low, so having added one layer of securing plate 7；From the angle for saving cost
Degree, do not influence health-care efficacy in advance under, it is possible to reduce the use of 1 raw material of energy composite energy body.
Energy composite energy body 1 is prepared by multielement compound energy material, and multielement compound energy material is by following matter
The raw material of amount score is prepared：Environment-friendly resin 45%, far-infrared powder 12%, Tourmaline powder 12%, germanite powder 12%, anion
Powder 1%, stone needle powder 5%, volcano stone flour 2%, bamboo charcoal 1%, curing agent 2%, accelerating agent 2%, flexible glue 3%.
Multielement compound energy material may be used following two preparation methods and be prepared,
(1) artificial preparation process
1) 1/7 curing agent, 1/7 accelerating agent are added in liquid environment-friendly resin, 2~3min of stirring is poured into mold,
15min is stood, pure resin piece is formed；2) while carrying out 1) step, liquid environment-friendly resin is poured into container, is sequentially added
Far-infrared powder, Tourmaline powder, germanite powder, negative ion powder, stone needle powder, volcano stone flour are stirred with hand electric blender
10min forms mixes liquid raw material slurry；2) impurity in being starched with the filter plant filter mixed liquor state raw material of 300~500 mesh；
3) it takes the mixes liquid raw material of 1500g to starch with the measuring cup of 2000mL every time, remaining curing agent, accelerating agent and flexible glue is added, then
2min is stirred with rod；4) mixes liquid raw material slurry is poured into mold, stands 50min, pure resin piece and mixed raw material chip bonding
It is integrated, takes out；5) solidification, the hardening for passing through 10h, pour into automatic polishing machine, carry out polishing for 24 hours, you can；
(2) machine preparation process
1) 1/5 curing agent, 1/5 accelerating agent, flexible glue are added in liquid environment-friendly resin, stirring 3min pours into automatic knob
In button centrifugation pelleter, the weight of resin is determined according to film-making thickness；2) centrifugation pelleter is revolved with the speed of 1500 turns/min
Turn, rotates 15min, be centrifuged into the pure resin sheet material of average 3mm；3) carry out it is above-mentioned 1), 2) step while by liquid environment-friendly resin
It pours into homogenizer, sequentially adds far-infrared powder, Tourmaline powder, germanite powder, negative ion powder, stone needle powder, volcano stone flour, stir
10min is mixed, mixes liquid raw material slurry is formed；4) miscellaneous in being starched with the filter plant filter mixed liquor state raw material of 300~500 mesh
Matter；5) remaining curing agent and remaining accelerating agent is added in mixes liquid raw material slurry, is stirred for 3min；6) temporarily stop automatic knob
The rotation of button centrifugation pelleter pours slurry process into mixes liquid raw material slurry, mixes liquid raw material is determined according to film-making thickness
The weight of slurry pours into liquid mixed raw material slurry in automatic button centrifugation pelleter；7) centrifugation pelleter is with 1500 turns/min's
Speed rotates, and rotates 50min, is centrifuged into the sheet material of average 8mm, pure resin sheet material and mixed raw material sheet material are combined into one；8)
Soft shape sheet material is taken out from centrifugation pelleter, 60min is sent to and rushes embryo machine and carried out rushing embryo with cutting die, is rushed according to the shape of cutting die
At germule；9) solidification, the hardening for passing through 12h, are sent to vehicle button machine by germule and modify；10) germule after finishing is poured into certainly
In dynamic polishing machine, the polishing of 36h is carried out, you can.
Permanent magnet 2 is adsorbed on 3 top of magnetic force baffler, and magnetic force baffler 3 wraps up permanent magnet 2, magnetic force baffler 3 to upper half
It is the resistance magnetic material such as iron-clad, box hat or alloy, is while to reduce cost to enhance magnetic force of the permanent magnet 2 towards one pole of body,
Similar to single side magnetic on the market, make backwards to one pole magnetic force of body it is very weak, avoid backwards to one pole magnetic force of body it is excessive absorption its
Its article.
Energy composite energy body 1 and securing plate 7 are integrated molding structure, and 7 middle part of securing plate is arranged small card slot, securing plate 7 to
Lower half wraps up permanent magnet 2, magnetic force baffler 3, magnetic force baffler 3 in order to promote the magnetic force of permanent magnet 2, and why permanent magnet 2
It is wrapped in energy composite energy body 1 again and 7 inside of securing plate stops magnetic force？A, permanent magnet is in direct contact skin, the surface layer of permanent magnet
It is electroplated layer, electroplated layer is to be not easy to be in direct contact skin using made of a large amount of poisonous and harmful materials；B, permanent magnet surfaces are wrapped up
Act on skin after one layer of thin cloth, electroplated layer (zinc-plated) cracky of permanent magnet aoxidizes after damaged, oxide not only pollution clothes
Also easily cause skin infection；C, permanent magnet exposure is oxidizable in air, loss of excitation is fast, service life is short, waste of resource；D, magnetic exists
Chinese medicine belongs to gold, respectful to drop therefore tremble with fear partially, and long-time service has the side effects such as dizziness, nausea, and energy composite energy body 1 is with a variety of natural micro
Element arrangements synthesize, in addition magnetic forms one complete five-element's energy, since human body is itself is a energy field, multielement is multiple
Closing the energy field that energy magnetic therapy health care material is formed can blend with body energy rapidly, supplement human body positive energy, drive away negative energy；
E, the magnetic field effect that magnetic generates pushes and various trace elements in energy composite energy body 1 is accelerated to blend with absorption of human body, stimulation
Acupuncture point, lively atmosphere blood degrading the channel improve lesions position.
It is to be bonded together between fixed pedestal 4, magnetic force baffler 3, securing plate 7, this is to accelerate to produce in batches
Journey, the assembled design taken, the independent production of fixed pedestal 4, magnetic force baffler 3 and the independent production of permanent magnet 2, recombination energy
Body 1 and the independent production of securing plate 7 are measured, finally in the unified bonding assembling of maquila, that is, multielement energy composite energy magnetic therapy is completed and protects
The production of strong material.Because of the independent production of fixed pedestal 4, the material of various materials can be used, such as：Resin, plastic cement, timber, jade
Stone, agate, metal etc., convenient for creation at craft work of art, such as：Paint, carve characters, is gold stamping, quarter of stringing paints poem etc., make it
Existing healthcare function, and it is rich in cultural connotation, become the health art art work.
Embodiment 2
Referring to Fig. 2, in the embodiment of the present invention, the application apparatus of multielement compound energy material, energy composite energy body 1 is initially
State is liquid, is instilled in 4 big card slot of fixed pedestal, and permanent magnet 2, magnetic force baffler 3 is fully wrapped around, and big card slot is dripped
It is full, an entirety is formed after solidification.Such mode of production is that first fission combines together again, the independent production of fixed pedestal 4, magnetic force resistance
Partition board 3 and the independent production of permanent magnet 2, after magnetic force baffler 3 and permanent magnet 2 are first bonded in the 4 small card slot in middle part of fixed pedestal, then
Liquid energy composite energy body 1 is instilled in 4 big card slot of fixed pedestal, it is slowly that permanent magnet 2, magnetic force baffler 3 is fully wrapped around, then will
Size card slot drop is full, and such mode of production is manually on the high side, and finished product condition can not be identical, is suitable for small-scale production.
Embodiment 3
Referring to Fig. 3, in the embodiment of the present invention, the application apparatus of multielement compound energy material, 1 middle part of energy composite energy body
Small card slot is set, and small card slot half wraps up permanent magnet 2, magnetic force baffler 3 downwards；Fixed pedestal 4, magnetic force baffler 3, permanent magnet 2,
It is to be bonded together between energy composite energy body 1.
Be provided with big card slot and small card slot on fixed pedestal 4, small card slot upwards half package magnetic force baffler 3, permanent magnet 2,
Energy composite energy body 1 in such mode of production, compared to Figure 1, reduces securing plate 7, reduces one of production process, but increase
The use of 1 raw material of energy composite energy body.
Embodiment 4
Referring to Fig. 4, in the embodiment of the present invention, the application apparatus of multielement compound energy material, 4 middle part of fixed pedestal is set
Card slot is set, card slot is bonded in upper half package magnetic force baffler 3, permanent magnet 2, magnetic force baffler 3 at the top of card slot；Energy composite energy body
The card slot at 1 middle part is the same as the 4 corresponding setting of middle part card slot of fixed pedestal.In such mode of production, energy composite energy body 1 and fixed pedestal
4 areas are that the identical overall dimensions that compare with Fig. 1 are smaller.
Card slot is arranged in 4 middle part of fixed pedestal, and card slot wraps up magnetic force baffler 3, Permanent-magnet layer 2, such producer to upper half
In formula, compared to Figure 1, reduces securing plate 7, reduce one of production process, but increase making for 1 raw material of energy composite energy body
With.
Embodiment 5
Referring to Fig. 5, in the embodiment of the present invention, the application apparatus of multielement compound energy material, energy composite energy body 1 and solid
Determine pedestal 4 and is integrated metaplasia production design；The card slot that energy composite energy body 1 and 4 middle part of fixed pedestal are arranged is hindered to upper half package magnetic force
Partition board 3, permanent magnet 2, material bodies 6, magnetic force baffler 3 are bonded at the top of the card slot at 4 middle part of fixed pedestal, and permanent magnet 2 is adsorbed on
3 top of magnetic force baffler, magnetic force baffler 3 wrap up permanent magnet 2 to upper half, and material bodies 6 are placed in the top of permanent magnet 2；Recombination energy
It is to be bonded together to measure between body 1 and fixed pedestal 4, magnetic force baffler 3, permanent magnet 2, material bodies 6.
Energy composite energy body 1 and fixed pedestal 4 are integrated metaplasia production design, refer to that energy composite energy body 1 and fixed pedestal 4 are initial
State is liquid, refer in process of production, it is another when its semi-solid state wherein one layer is first poured slurry and enters mold
Slurry is poured again and enters mold, and by the waiting of a period of time, two layers of automatic solidification combines together.
Material bodies 6 are placed at the top of permanent magnet, and material bodies 6 independently produce, it can be with 1 material phase of energy composite energy body
Together, can also be the transparent material of other magnetic force such as：Stone needle piece, synthetic material piece etc. or ointment, drug paste, medicine wax etc.,
Convenient for expanding or increasing other effects.
Embodiment 6
Referring to Fig. 6, in the embodiment of the present invention, the application apparatus of multielement compound energy material, energy composite energy body 1 and solid
Determine pedestal 4 to be the integrated design；Energy composite energy body 1 and the middle part of fixed pedestal 4 set card slot to upper half package magnetic force baffler 3, forever
Magnet 2, magnetic force baffler 3 are bonded at the top of the card slot of middle part, and permanent magnet 2 is adsorbed on 3 top of magnetic force baffler, magnetic force baffler 3
Permanent magnet 2 is wrapped up to upper half, energy reinforcing plate 9 is placed in the top of permanent magnet 2；9 original state of energy reinforcing plate is liquid, is instilled
4 middle part card slot of energy composite energy body 1 and fixed pedestal, permanent magnet 2, magnetic force baffler 3 is fully wrapped around, and card slot is dripped completely, Gu
An entirety is formed after change.
Energy reinforcing plate 9 is placed in the top of permanent magnet, can be identical with 1 material of energy composite energy body, can also improve formula,
Increase other substances, such as Chinese medicine, remedies, beneficial element, minerals, to promote and reinforce effect.
Embodiment 7
Referring to Fig. 7, in the embodiment of the present invention, the application apparatus of multielement compound energy material, energy composite energy body 1 and solid
Determine pedestal 4 to be the integrated design；Energy composite energy body 1 and 4 middle part of fixed pedestal set card slot to lower half package permanent magnet 2, magnetic force resistance
Partition board 3, decoration filling plate 5, permanent magnet 2 are bonded in card slot bottom, and permanent magnet 2 is adsorbed on 3 top of magnetic force baffler, magnetic force barrier
Plate 3 wraps up permanent magnet 2 to upper half, and decoration filling plate 5 is placed in the bottom of magnetic force baffler 3；Energy composite energy body 1 and fixed pedestal 4,
It is to be bonded together between magnetic force baffler 3, permanent magnet 2, decoration filling plate 5.
It is to be bonded in one between energy composite energy body 1 and fixed pedestal 4, magnetic force baffler 3, permanent magnet 2, decoration filling plate 5
It rises.It is to set card slot below energy composite energy body 1 and fixed pedestal 4 that this mode of production compares with Fig. 6, by magnetic force baffler 3, forever
After magnet 2 is packed into card slot, blocked with decoration filling plate 5.Because of the 5 independent production of decoration filling plate, various materials can be used
Material, such as：Resin, plastic cement, timber, jade, agate, metal etc., convenient for creation at craft work of art, such as：Paint, carve characters,
Gold stamping, quarter paints poem etc., assigns cultural connotation.
Embodiment 8
Referring to Fig. 8, in the embodiment of the present invention, the application apparatus of multielement compound energy material, energy composite energy body 1 and solid
Determine pedestal 4 to be the integrated design；Energy composite energy body 1 and 4 middle part of fixed pedestal set card slot to lower half package permanent magnet 2, magnetic force resistance
Partition board 3, decoration filling plate 5, permanent magnet 2 are bonded in card slot bottom, and permanent magnet 2 is adsorbed on 3 top of magnetic force baffler, magnetic force barrier
Plate 3 wraps up permanent magnet 2 to upper half, and decoration filling plate 5 is placed in the bottom of magnetic force baffler 3；Decoration filling 5 original state of plate is liquid
State instills energy composite energy body 1 and 4 middle part card slot of fixed pedestal, and permanent magnet 2, magnetic force baffler 3 is fully wrapped around, and by card slot
Drop is full, and an entirety is formed after solidification.
Decoration filling 5 original state of plate is liquid, energy composite energy body 1 and 4 middle part card slot of fixed pedestal is instilled, by permanent magnet
2, magnetic force baffler 3 is fully wrapped around, and card slot is dripped to full, one entirety of formation after solidification.Compared with the mode of production of Fig. 7,
Production is slower, can be few with material selection, and appearance can be slightly different, but good integrity, firm.
Embodiment 9
Referring to Fig. 9, in the embodiment of the present invention, the application apparatus of multielement compound energy material, energy composite energy body 1 and plus
Solid plate 4 is integrated molding structure, and energy composite energy body 1 and 7 middle part of securing plate are provided with card slot, and securing plate 7 is wrapped up forever to lower half
Magnet 2, magnetic force baffler 3, permanent magnet 2 are adsorbed on 3 top of magnetic force baffler, and magnetic force baffler 3 wraps up permanent magnet 2 to upper half；
Fixed pedestal 4 is provided with big card slot and small card slot, and the small card slot at middle part half wraps up magnetic force baffler 3, permanent magnet 2, kilocalorie upwards
Slot wraps up energy composite energy body 1, securing plate 7, permanent magnet 2, magnetic force baffler 3 to upper half；Fixed pedestal 4, adds magnetic force baffler 3
It is to be bonded together between solid plate 7；A connecting hole 8 for running through entire gasket is respectively arranged in 4 both sides of fixed pedestal, to facilitate one
Sheet is connected between a independent more devices.
Embodiment 10
Referring to Fig. 10, in the embodiment of the present invention, the application apparatus of multielement compound energy material, 1 He of energy composite energy body
Securing plate 7 is integrated molding structure, and multiple small card slots are arranged in 7 middle part of securing plate, and securing plate 7 wraps up permanent magnet 2, magnetic to lower half
Mechanical resistance partition board 3, permanent magnet 2 are adsorbed on 3 top of magnetic force baffler, and magnetic force baffler 3 wraps up permanent magnet 2 to upper half；Fixed pedestal 4
Multiple big card slots and small card slot are set, and the small card slot at middle part half wraps up magnetic force baffler 3, permanent magnet 2, the big card slot in outside upwards
To upper half package energy composite energy body 1, securing plate 7, permanent magnet 2, magnetic force baffler 3；Fixed pedestal 4, is reinforced magnetic force baffler 3
To be bonded together between plate 7, such mode of production be in order to produce the multielement energy composite energy Magnetotherapeutic health material of bulk,
Such as：Floor, cushion, mattress, massage cushion etc..
Embodiment 11
Please refer to Fig.1 1, in the embodiment of the present invention, the application apparatus of multielement compound energy material, 1 He of energy composite energy body
Fixed pedestal 4 is integrated metaplasia production design；Energy composite energy body 1 and the middle part of fixed pedestal 4 set card slot to upper half package permanent magnet 2,
Material bodies 6, permanent magnet 2 are bonded at the top of the card slot of middle part, and material bodies 6 are placed in the top of permanent magnet 2；Energy composite energy body 1 and fixation
It is to be bonded together between pedestal 4, permanent magnet 2, material bodies 6.
Energy composite energy body 1 and 4 middle part of fixed pedestal set card slot and wrap up permanent magnet 2, material bodies 6, the production with Fig. 5 to upper half
Mode compares, and cancels magnetic force baffler 3.
It is obvious to a person skilled in the art that invention is not limited to the details of the above exemplary embodiments, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, the present embodiments are to be considered as illustrative and not restrictive, and the scope of the present invention is by appended power
Profit requires rather than above description limits, it is intended that all by what is fallen within the meaning and scope of the equivalent requirements of the claims
Variation is included within the present invention.Any reference signs in the claims should not be construed as limiting the involved claims.
Claims (9)
1. a kind of multielement compound energy material, which is characterized in that be prepared by the raw material of following mass fraction：Environment-friendly resin
40~50%, far-infrared powder 10~14%, Tourmaline powder 10~14%, germanite powder 10~14%, negative ion powder 0.9~1.1%,
Stone needle powder 4~6%, volcano stone flour 1.8~2.2%, bamboo charcoal 0.9~1.1%, curing agent 1.8~2.2%, accelerating agent 1.8~
2.2%.
2. a kind of preparation method of multielement compound energy material as described in claim 1, which is characterized in that use following two
It is a kind of in kind preparation method to be prepared,
(1) artificial preparation process
1) 1/7 curing agent, 1/7 accelerating agent are added in liquid environment-friendly resin, 2~3min of stirring is poured into mold, stands 5
~15min forms pure resin piece；2) while carrying out 1) step, liquid environment-friendly resin is poured into container, is sequentially added remote
Infrared powder, Tourmaline powder, germanite powder, negative ion powder, stone needle powder, volcano stone flour stir 9~11min with electric blender, are formed
Mixes liquid raw material is starched；2) impurity in being starched with the filter filter mixed liquor state raw material of 300~500 mesh；3) in mixes liquid
Remaining curing agent, accelerating agent and flexible glue is added in raw material slurry, is stirred for 1~2min；4) mixes liquid raw material slurry is poured into mould
In tool, 30~60min is stood, pure resin piece and mixed raw material chip bonding are integrated, and are taken out；5) pass through curing, firmly for 4~12h
Change, pour into automatic polishing machine, carries out the polishing of 24~48h, you can；
(2) machine preparation process
1) in liquid environment-friendly resin be added 1/5 curing agent, 1/5 accelerating agent, flexible glue, stirring 2~3min pour into automatically from
In heart pelleter；2) centrifugation pelleter is rotated with the speed of 1500 turns/min, rotates 15min, is centrifuged into the pure of average 1~5mm
Resin sheet；3) carry out it is above-mentioned 1), 2) step while liquid environment-friendly resin is poured into homogenizer, sequentially add far infrared
Powder, Tourmaline powder, germanite powder, negative ion powder, stone needle powder, volcano stone flour stir 9~11min, form mixes liquid raw material slurry；
4) impurity in being starched with the filter filter mixed liquor state raw material of 300~500 mesh；5) it is added in mixes liquid raw material slurry remaining
Curing agent and remaining accelerating agent, be stirred for 2~3min；6) rotation for temporarily only centrifuging pelleter, into mixes liquid raw material
Slurry pours slurry process, and the weight of mixes liquid raw material slurry is determined according to film-making thickness, and liquid mixed raw material slurry is poured into centrifugation system
In piece machine；7) centrifugation pelleter is rotated with the speed of 1500 turns/min, rotates 40~60min, is centrifuged into the piece of average 2~10mm
Material, pure resin sheet material and mixed raw material sheet material are combined into one；8) soft shape sheet material is taken out from centrifugation pelleter, 20~
60min is sent to and rushes embryo machine and carried out rushing embryo with cutting die, germule is washed into according to the shape of cutting die；9) pass through curing, firmly for 4~12h
Change, germule is sent to vehicle button machine and is modified；10) germule after finishing is poured into automatic polishing machine, carries out the throwing of 24~48h
Light, you can.
3. a kind of application apparatus of multielement compound energy material as described in claim 1, which is characterized in that including liquid
Energy composite energy body (1), securing plate (7), permanent magnet (2), magnetic force baffler (3), fixed pedestal (4), the energy composite energy body of liquid
(1) and securing plate (7) is integrated molding structure, and the middle part lower end of the energy composite energy body (1) is provided with small card slot, described to add
Solid plate (7) half wraps up permanent magnet (2), magnetic force baffler (3), and the permanent magnet (2) is adsorbed at the top of magnetic force baffler (3), institute
Magnetic force baffler (3) is stated to upper half package permanent magnet (2), the edge of the fixed pedestal (4) is provided with big card slot, the fixation
Small card slot is provided in the middle part of pedestal (4), and the small card slot in securing plate (7) is corresponding with the small card slot in fixed substrate (4) sets
It sets, the small card slot on the fixed pedestal (4) half wraps up magnetic force baffler (3), permanent magnet (2), the fixed pedestal (4) upwards
On big card slot half package energy composite energy body (1), securing plate (7), permanent magnet (2), magnetic force baffler (3) upwards, the fixation
Connection is bonded between pedestal (4) and securing plate (7) or energy composite energy body (1), the energy composite energy body (1) is compound by multielement
Energy material is prepared.
4. the application apparatus of multielement compound energy material according to claim 3, which is characterized in that the liquid is answered
It closes energy body (1) to instill or be bonded in the big card slot of fixed pedestal (4), and fixed pedestal (4) half wraps up energy composite energy body
(1), energy composite energy body (1) drop of energy composite energy body (1) the package permanent magnet (2) and magnetic force baffler (3) of liquid, liquid is full solid
Determine the big card slot on pedestal (4).
5. the application apparatus of multielement compound energy material according to claim 3, which is characterized in that the liquid is answered
Close energy body (1) correspondence drops in or is bonded on fixed pedestal (4), and liquid energy composite energy body (1) package permanent magnet (2) and
Magnetic force baffler (3), the card slot of energy composite energy body (1) lower end middle part formation is corresponding with the card slot in the middle part of fixed pedestal (4) to be set
It sets.
6. the application apparatus of multielement compound energy material according to claim 3, which is characterized in that the liquid is answered
Conjunction energy body (1) drops on fixed pedestal (4) and integrated molding, and card slot, the permanent magnet are offered on energy composite energy body (1)
(2) and magnetic force baffler (3) setting is in fixed pedestal (4), and material bodies (6), the material are provided at the top of permanent magnet (2)
Body (6) is bonded into one with energy composite energy body (1), permanent magnet (2), magnetic force baffler (3).
7. the application apparatus of multielement compound energy material according to claim 3, which is characterized in that the energy composite energy
Body (1) drops in fixed pedestal (4) and integrated molding, and energy composite energy body (1) is equipped with card slot, liquid with fixed pedestal (4) middle part
Decoration filling plate (5) instill or be bonded in the card slot of fixed pedestal (4), and decorate filling plate (5) from bottom wrap up permanent magnetism
Body (2) and magnetic force baffler (3), the decoration filling plate (5) of liquid drip the card slot of full fixed pedestal (4) and with fixed pedestal (4)
It is integrally formed.
8. the application apparatus of multielement compound energy material according to claim 3, which is characterized in that the fixed pedestal
(4) a perforative connecting hole (8) is respectively arranged in both sides.
9. the application apparatus of multielement compound energy material according to claim 3, which is characterized in that the securing plate
(7) middle part is provided with multiple small card slots, and multiple big card slots and small card slot is arranged in the fixed pedestal (4), and in securing plate (7)
Small card slot is correspondingly arranged with the small deck on fixed pedestal (4).