CN105755352A - High-temperature-resistant automobile accessory alloy steel material and preparation method thereof - Google Patents

High-temperature-resistant automobile accessory alloy steel material and preparation method thereof Download PDF

Info

Publication number
CN105755352A
CN105755352A CN201610200199.1A CN201610200199A CN105755352A CN 105755352 A CN105755352 A CN 105755352A CN 201610200199 A CN201610200199 A CN 201610200199A CN 105755352 A CN105755352 A CN 105755352A
Authority
CN
China
Prior art keywords
parts
alloy steel
steel material
high temperature
temperature resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610200199.1A
Other languages
Chinese (zh)
Inventor
岳胜桥
龚达锦
吴海峰
郑福新
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU RUIXIN AUTO PARTS CO Ltd
Original Assignee
SUZHOU RUIXIN AUTO PARTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU RUIXIN AUTO PARTS CO Ltd filed Critical SUZHOU RUIXIN AUTO PARTS CO Ltd
Priority to CN201610200199.1A priority Critical patent/CN105755352A/en
Publication of CN105755352A publication Critical patent/CN105755352A/en
Pending legal-status Critical Current

Abstract

The invention discloses a high-temperature-resistant automobile accessory alloy steel material and a preparation method thereof.The method includes the steps of putting 100-120 parts of iron, 0.8-1.2 parts of carbon, 0.03-0.05 part of zirconium, 0.02-0.08 part of germaniumc, 0.04-0.07 part of stibium, 1-1.5 parts of aluminum, 1-2 parts of silicon, 0.5-1 part of copper, 0.1-0.6 part of phosphorus, 0.04-0.06 part of potassium, 0.9-1.2 parts of tin, 0.03-0.05 part of cobalt and 0.5-0.9 part of barium into a medium-frequency induction furnace in proportion to be molten, heating to 1400 DEG C at the speed of 50 DEG C per minute, getting the materials out of the furnace to be cast, conducting quenching at the temperature of 900 DEG C for 1 hour, getting the materials out of the furnace to be air-cooled, conducting tempering at the temperature of 300 DEG C for 1 hour, and getting the materials out of the furnace to be air-cooled to prepare the high-temperature-resistant automobile accessory alloy steel material.The alloy steel material is excellent in corrosion resistance and suitable for application and popularization and has wide market value.

Description

A kind of high temperature resistant vehicle accessory alloy steel material and preparation method thereof
Technical field
The invention belongs to auto parts manufacturing technology field, be specifically related to a kind of high temperature resistant vehicle accessory alloy steel material and preparation method thereof.
Background technology
Automobile has the part of more than 90% to be metal parts, and the drawback of metal parts is exactly easily be corroded, and the corrosion of auto parts is mainly atmospheric corrosion, belongs to electrochemical corrosion, is modal in metal erosion.According to statistics, in metal erosion, atmospheric corrosion accounts for more than half, and most parts of automobile are all directly and atmosphere.So-called atmospheric corrosion refers to metal rust corrosion under the effect of humid air at normal temperatures.When being substantially free of moisture in an atmosphere, due to the effect of oxygen in air, even if metal surface at room temperature also can be made to produce moisture film one layer very thin, corrosion carries out in moisture film.In air, not only metal can be corrosive by oxygen, even the gas such as carbon dioxide, copper dioxide or the impurity such as dust, salt all can accelerate electrochemical corrosion and make metal damage.
As the part of automobile, not only structural strength with functionally have higher requirement, no less important in machining simultaneously, such requirement is not only and is met the primary condition that automobile uses, and is also the safe and reliable guarantee increased the service life simultaneously.
In prior art, the steel of production auto parts machinery are common middle low content steel alloy, and because these automobile metal accessories are functionally usually moving component frequently in use, wear rate is significantly high, changes frequently, adds maintenance cost；Searching out a kind of raising hardness and anti-wear performance, the steel alloy of the middle low content that piece surface heat resistance is high is extremely important with regard to what show simultaneously.
Summary of the invention
Goal of the invention: a kind of high temperature resistant vehicle accessory alloy steel material and preparation method thereof is provided.
Technical scheme:
A kind of high temperature resistant vehicle accessory alloy steel material, it is to use following Material synthesis:
Ferrum 100～120 parts, 0.8～1.2 part of carbon, zirconium 0.03～0.05 part, 0.02～0.08 part of germanium, 0.04～0.07 part of antimony, 1～1.5 part of aluminum, silicon 1～2 part, copper 0.5～1 part, 0.1～0.6 part of phosphorus, 0.04～0.06 part of potassium, 0.9～1.2 part of stannum, cobalt 0.03～0.05 part, barium 0.5～0.9 part.
Preferred as the present invention, it is to use following Material synthesis:
Ferrum 110 parts, 1 part of carbon, zirconium 0.04 part, 0.05 part of germanium, 0.06 part of antimony, 1.3 parts of aluminum, silicon 1.5 parts, copper 0.8 part, 0.4 part of phosphorus, 0.05 part of potassium, 1 part of stannum, cobalt 0.04 part, barium 0.7 part.
Preferred as the present invention, it is to use following Material synthesis:
Ferrum 100 parts, 0.8 part of carbon, zirconium 0.03 part, 0.02 part of germanium, 0.04 part of antimony, 1 part of aluminum, silicon 1 part, copper 0.5 part, 0.1 part of phosphorus, 0.04 part of potassium, 0.9 part of stannum, cobalt 0.03 part, barium 0.5 part.
Preferred as the present invention, it is to use following Material synthesis:
Ferrum 120 parts, 1.2 parts of carbon, zirconium 0.05,0.08 part of germanium, 0.07 part of antimony, 1.5 parts of aluminum, silicon 2 parts, copper 1 part, 0.6 part, 0.06 part of potassium, 1.2 parts of stannum, cobalt 0.05 part, barium 0.9 part.
The preparation method of above-mentioned high temperature resistant vehicle accessory alloy steel material, comprises the steps:
(1) all raw materials are put in proportion in intermediate frequency furnace and melt；
(2) 1100～1150 DEG C it are warming up to, tapping casting；
(3) Quenching Treatment: hardening heat is 500～550 DEG C, insulation 2～3h, air cooling of coming out of the stove,
(4) temper: temperature is 200～250 DEG C, is incubated 2～5h, air cooling of coming out of the stove, namely obtains high temperature resistant vehicle accessory alloy steel material.
In step (2), programming rate is the speed of 80 DEG C/min.
In step (3), described hardening heat is 550 DEG C.
In step (4), described temperature is 220 DEG C.
Beneficial effect: the corrosion resistance of high temperature resistant vehicle accessory alloy steel material prepared by the present invention is good, has stronger resistance to elevated temperatures, suitable popularization and application, there is wide market value.
Detailed description of the invention
According to following embodiment, it is possible to be more fully understood that the present invention.But, as it will be easily appreciated by one skilled in the art that the content described by embodiment is merely to illustrate the present invention, and should without the present invention described in detail in restriction claims.
Embodiment 1:
(1) ferrum 110 parts, 1 part of carbon, zirconium 0.04 part, 0.05 part of germanium, 0.06 part of antimony, 1.3 parts of aluminum, silicon 1.5 parts, copper 0.8 part, 0.4 part of phosphorus, 0.05 part of potassium, 1 part of stannum, cobalt 0.04 part, barium 0.7 part are put in proportion in intermediate frequency furnace and melt；
(2) 1100 DEG C it are warming up to, tapping casting；
(3) Quenching Treatment: hardening heat is 500 DEG C, insulation 2h, air cooling of coming out of the stove,
(4) temper: temperature is 200 DEG C, is incubated 2h, air cooling of coming out of the stove, namely obtains high temperature resistant vehicle accessory alloy steel material.
Embodiment 2:
(1) by Material synthesis:
Ferrum 100 parts, 0.8 part of carbon, zirconium 0.03 part, 0.02 part of germanium, 0.04 part of antimony, 1 part of aluminum, silicon 1 part, copper 0.5 part, 0.1 part of phosphorus, 0.04 part of potassium, 0.9 part of stannum, cobalt 0.03 part, barium 0.5 part put in proportion in intermediate frequency furnace and melt；
(2) 1120 DEG C it are warming up to, tapping casting；
(3) Quenching Treatment: hardening heat is 520 DEG C, insulation 2.5h, air cooling of coming out of the stove,
(4) temper: temperature is 230 DEG C, is incubated 3h, air cooling of coming out of the stove, namely obtains high temperature resistant vehicle accessory alloy steel material.
Embodiment 3:
(1) by ferrum 120 parts, 1.2 parts of carbon, zirconium 0.05,0.08 part of germanium, 0.07 part of antimony, 1.5 parts of aluminum, silicon 2 parts, copper 1 part, 0.6 part, 0.06 part of potassium, 1.2 parts of stannum, cobalt 0.05 part, barium 0.9 part puts in proportion in intermediate frequency furnace and melts；
(2) 1150 DEG C it are warming up to, tapping casting；
(3) Quenching Treatment: hardening heat is 550 DEG C, insulation 3h, air cooling of coming out of the stove,
(4) temper: temperature is 250 DEG C, is incubated 5h, air cooling of coming out of the stove, namely obtains high temperature resistant vehicle accessory alloy steel material.

Claims (8)

1. a high temperature resistant vehicle accessory alloy steel material, it is characterised in that it is to use following Material synthesis:
Ferrum 100 ~ 120 parts, 0.8 ~ 1.2 part of carbon, zirconium 0.03 ~ 0.05 part, 0.02 ~ 0.08 part of germanium, 0.04 ~ 0.07 part of antimony, 1 ~ 1.5 part of aluminum, silicon 1 ~ 2 part, copper 0.5 ~ 1 part, 0.1 ~ 0.6 part of phosphorus, 0.04 ~ 0.06 part of potassium, 0.9 ~ 1.2 part of stannum, cobalt 0.03 ~ 0.05 part, barium 0.5 ~ 0.9 part.
2. high temperature resistant vehicle accessory alloy steel material according to claim 1, it is characterised in that it is to use following Material synthesis:
Ferrum 110 parts, 1 part of carbon, zirconium 0.04 part, 0.05 part of germanium, 0.06 part of antimony, 1.3 parts of aluminum, silicon 1.5 parts, copper 0.8 part, 0.4 part of phosphorus, 0.05 part of potassium, 1 part of stannum, cobalt 0.04 part, barium 0.7 part.
3. high temperature resistant vehicle accessory alloy steel material according to claim 1, it is characterised in that it is to use following Material synthesis:
Ferrum 100 parts, 0.8 part of carbon, zirconium 0.03 part, 0.02 part of germanium, 0.04 part of antimony, 1 part of aluminum, silicon 1 part, copper 0.5 part, 0.1 part of phosphorus, 0.04 part of potassium, 0.9 part of stannum, cobalt 0.03 part, barium 0.5 part.
4. high temperature resistant vehicle accessory alloy steel material according to claim 1, it is characterised in that it is to use following Material synthesis:
Ferrum 120 parts, 1.2 parts of carbon, zirconium 0.05,0.08 part of germanium, 0.07 part of antimony, 1.5 parts of aluminum, silicon 2 parts, copper 1 part, 0.6 part, 0.06 part of potassium, 1.2 parts of stannum, cobalt 0.05 part, barium 0.9 part.
5. the preparation method of high temperature resistant vehicle accessory alloy steel material described in any one of claim 1 ~ 4, it is characterised in that comprise the steps:
(1) all raw materials are put in proportion in intermediate frequency furnace and melt；
(2) 1100 ~ 1150 DEG C it are warming up to, tapping casting；
(3) Quenching Treatment: hardening heat is 500 ~ 550 DEG C, insulation 2 ~ 3h, air cooling of coming out of the stove,
(4) temper: temperature is 200 ~ 250 DEG C, is incubated 2 ~ 5h, air cooling of coming out of the stove, namely obtains high temperature resistant vehicle accessory alloy steel material.
6. the preparation method of high temperature resistant vehicle accessory alloy steel material according to claim 5, it is characterised in that in step (2), programming rate is the speed of 80 DEG C/min.
7. the preparation method of high temperature resistant vehicle accessory alloy steel material according to claim 5, it is characterised in that in step (3), described hardening heat is 550 DEG C.
8. the preparation method of high temperature resistant vehicle accessory alloy steel material according to claim 5, it is characterised in that in step (4), described temperature is 220 DEG C.
CN201610200199.1A 2016-03-31 2016-03-31 High-temperature-resistant automobile accessory alloy steel material and preparation method thereof Pending CN105755352A (en)