CN105751611A - High-strength multilayer plate - Google Patents

High-strength multilayer plate Download PDF

Info

Publication number
CN105751611A
CN105751611A CN201610222000.5A CN201610222000A CN105751611A CN 105751611 A CN105751611 A CN 105751611A CN 201610222000 A CN201610222000 A CN 201610222000A CN 105751611 A CN105751611 A CN 105751611A
Authority
CN
China
Prior art keywords
solid wood
board
plate
parts
batten
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201610222000.5A
Other languages
Chinese (zh)
Other versions
CN105751611B (en
Inventor
许跃跃
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Capital Construction Co. Ltd.
Original Assignee
Jiashan Yuheng Wood Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiashan Yuheng Wood Co Ltd filed Critical Jiashan Yuheng Wood Co Ltd
Priority to CN201610222000.5A priority Critical patent/CN105751611B/en
Publication of CN105751611A publication Critical patent/CN105751611A/en
Application granted granted Critical
Publication of CN105751611B publication Critical patent/CN105751611B/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a high-strength multilayer plate which comprises a first solid board, a second solid board and a solid particle board, wherein a fiber plate is arranged between the first solid board and the solid particle board; the first solid board and the solid particle board are both adhered to the fiber plate; a stainless steel net is arranged on a surface of the fiber plate and is embedded into the solid particle board; a bamboo plate is arranged between the second solid board and the solid particle board; the second solid board and the solid particle board are both adhered to the bamboo plate; battens are arranged on the bamboo plate; the battens and the bamboo plate are integrally arranged; the battens are embedded into the solid particle board and are distributed in a form of Chinese character Tian; carbon fiber rods are arranged in the battens. The high-strength multilayer plate is high in mechanical strength.

Description

A kind of high strength multi-layer plate
Technical field
The present invention relates to a kind of high strength multi-layer plate.
Background technology
Multi-layer sheet is to be peeled into veneer by juggle or become veneer by flitch slicing, then sticks with glue the three layers of agent gluing or the board-like material of multilamellar, typically by odd-level veneer, and makes the orthogonal gluing of machine direction of adjacent layer veneer form.
Multi-layer sheet also makes plywood be one of furniture common used material, and generally its Phaleria macrocarpa plywood dash board and inner plating are symmetrically arranged at central core or the both sides of plate core.Conventional has three-ply board, five-ply board etc..Plywood can improve timber utilization rate, is the main path saving timber.
Multi-layer sheet is one of furniture processing enterprise common used material, is a kind of wood-based plate.One group of veneer is generally by the sheet material of the orthogonal assembly gluing of adjacent layer grain direction, and multi-layer sheet generally its dash board and inner plating are symmetrically arranged at central core or the both sides of plate core.With the veneer after gluing by the crisscross slab being made into of grain direction, when heating or not heating, compacting forms.The number of plies is generally odd number, and minority also has even number.The physics in direction, engineering properties difference are less in length and breadth.Conventional has the multi-layer sheet such as three-ply board, five-ply board.Also the effect materials such as aircraft, boats and ships, train, automobile, building and clad plate case it are available for.
But current multi-layer sheet intensity is not high, it is difficult to meet the demand in market.
Summary of the invention
The technical problem to be solved in the present invention is to provide the high strength multi-layer plate that a kind of mechanical strength is high.
For solving the problems referred to above, the present invention adopts the following technical scheme that
A kind of high strength multi-layer plate, including the first solid wood board, second solid wood board and solid wood granule plate, it is provided with fibre board between described first solid wood board and solid wood granule plate, described first solid wood board and solid wood granule plate all bond with fibre board, described fibre board one side is provided with stainless (steel) wire, described stainless (steel) wire is embedded in solid wood granule plate and arranges, it is provided with bamboo board between described second solid wood board and solid wood granule plate, described second solid wood board and solid wood granule plate all bond with bamboo board, described bamboo board is provided with batten, described batten and bamboo board are that integral type is arranged, described batten is embedded in solid wood granule plate and arranges, described batten is Tian-shaped distribution, it is provided with carbon fiber rod in described batten.
As preferably, described batten bonds with carbon fiber rod, good integrity, connects reliable.
As preferably, melamine impregnated paper is all posted in the front of described first solid wood board and the second solid wood board.
As preferably, described stainless (steel) wire surface is that nickel plating is arranged, it is possible to play good anticorrosion ability.
As preferably, described stainless (steel) wire is rustless steel seat type net.
As preferably, described fibre board bonds with stainless (steel) wire, connects reliable, Stability Analysis of Structures.
As preferably, described stainless (steel) wire being provided with noise deadener, it is possible to play good soundproof effect.
As preferably, described batten is equal with carbon fiber rod length.
Another technical problem that the invention solves the problems that is for providing the manufacture method of a kind of carbon fiber rod.
For solving the problems referred to above, the present invention adopts the following technical scheme that
It is made up of chopped carbon fiber 26-28 part of proportioning by weight, Merlon 18-20 part, ABS resin 38-40 part, polymethyl methacrylate 10-12 part, SAN resin 6-8 part, Dineodymium trioxide 4-8 part, hollow glass microbead 10-12 part, zirconium oxide bead 15-17 part, maleic acrylic copolymer 9-11 part, POM plastic 12-14 part, acetylene black 8-10 part, nano silicon 7-9 part, Acetylenogen. 10-12 part, cubic boron nitride micropowder 15-17 part and white fused alumina micropowder 10-12 part, comprises the following steps:
1) Merlon 18-20 part, ABS resin 38-40 part, polymethyl methacrylate 10-12 part, SAN resin 6-8 part are poured in vessel together with appropriate moisture, it is then heated to 180 DEG C, heating process is stirred continuously, till solid material melts completely, prepare thick liquid, standby；
2) maleic acrylic copolymer 9-11 part is poured into step 1 together with POM plastic 12-14 part) prepare thick liquid in, and with 150 DEG C heat 12 minutes, prepare mixing thick liquid, standby；
3) Dineodymium trioxide 4-8 part, hollow glass microbead 10-12 part, zirconium oxide bead 15-17 part, acetylene black 8-10 part, nano silicon 7-9 part, Acetylenogen. 10-12 part, cubic boron nitride micropowder 15-17 part are poured in three-dimensional material mixer together with white fused alumina micropowder 10-12 part, it is sufficiently mixed, prepare mixed-powder, standby；
4) by chopped carbon fiber 26-28 part and step 3) prepare mixed-powder together be poured into step 2) prepare mixing thick liquid in, stir, prepare paste, standby；
5) by step 4) prepare paste be poured in injection machine, use injection machine by paste injection and be full of mold cavity, cooling, obtain carbon fiber rod.
The invention have the benefit that and be provided by batten, carbon fiber rod it is provided with in batten, batten is embedded in solid wood granule plate, and batten is Tian-shaped distribution, it is possible not only to so that force structure is more stable, and carbon fiber rod intensity is high, adds stainless (steel) wire, so that the intensity of entirety is greatly promoted.
Accompanying drawing explanation
Fig. 1 is the internal structure schematic diagram of a kind of high strength multi-layer plate of the present invention；
Fig. 2 is the sectional view of the batten of a kind of high strength multi-layer plate of the present invention.
Detailed description of the invention
Embodiment one:
As shown in Figure 1-2, a kind of high strength multi-layer plate, including the first solid wood board 1, second solid wood board 2 and solid wood granule plate 3, it is provided with fibre board 4 between described first solid wood board 1 and solid wood granule plate 3, described first solid wood board 1 and solid wood granule plate 3 all bond with fibre board 4, described fibre board 4 one side is provided with stainless (steel) wire 5, described stainless (steel) wire 5 is embedded in solid wood granule plate 3 and arranges, it is provided with bamboo board 6 between described second solid wood board 2 and solid wood granule plate 3, described second solid wood board 2 and solid wood granule plate 3 all bond with bamboo board 6, described bamboo board 6 is provided with batten 7, described batten 7 is arranged for integral type with bamboo board 6, described batten 7 is embedded in solid wood granule plate 3 and arranges, the distribution in Tian-shaped of described batten 7, it is provided with carbon fiber rod 8 in described batten 7.
Described batten 7 bonds with carbon fiber rod 8, good integrity, connects reliable.
Melamine impregnated paper 9 is all posted in the front of described first solid wood board 1 and the second solid wood board 2.
Described stainless (steel) wire 5 surface is that nickel plating is arranged, it is possible to play good anticorrosion ability.
Described stainless (steel) wire 5 is rustless steel seat type net.
Described fibre board 4 bonds with stainless (steel) wire 5, connects reliable, Stability Analysis of Structures.
Described stainless (steel) wire 4 is provided with noise deadener (not shown), it is possible to play good soundproof effect.
Described batten 7 is equal with carbon fiber rod 8 length.
Another technical problem that the invention solves the problems that is for providing the manufacture method of a kind of carbon fiber rod.
For solving the problems referred to above, the present invention adopts the following technical scheme that
It is made up of the chopped carbon fiber 28 parts of proportioning by weight, Merlon 18 parts, ABS resin 38 parts, polymethyl methacrylate 10 parts, SAN resin 6 parts, Dineodymium trioxide 4 parts, hollow glass microbead 10 parts, zirconium oxide bead 15 parts, maleic acrylic copolymer 9 parts, POM plastic 12 parts, acetylene black 8 parts, nano silicon 7 parts, 10 parts of Acetylenogen., cubic boron nitride micropowder 15 parts and white fused alumina micropowder 10 parts, comprises the following steps:
1) Merlon 18 parts, ABS resin 38 parts, polymethyl methacrylate 10 parts, SAN resin 6 parts are poured in vessel together with appropriate moisture, it is then heated to 180 DEG C, heating process is stirred continuously, till solid material melts completely, prepare thick liquid, standby；
2) together with maleic acrylic copolymer 9 parts and POM plastic 12 parts, be poured into step 1) prepare thick liquid in, and with 150 DEG C heat 12 minutes, prepare mixing thick liquid, standby；
3) Dineodymium trioxide 4 parts, hollow glass microbead 10 parts, zirconium oxide bead 15 parts, acetylene black 8 parts, nano silicon 7 parts, 10 parts of Acetylenogen., cubic boron nitride micropowder 15 parts are poured in three-dimensional material mixer together with white fused alumina micropowder 10 parts, it is sufficiently mixed, prepare mixed-powder, standby；
4) by chopped carbon fiber 28 parts and step 3) prepare mixed-powder together be poured into step 2) prepare mixing thick liquid in, stir, prepare paste, standby；
5) by step 4) prepare paste be poured in injection machine, use injection machine by paste injection and be full of mold cavity, cooling, obtain carbon fiber rod.
Embodiment two:
As shown in Figure 1-2, a kind of high strength multi-layer plate, including the first solid wood board 1, second solid wood board 2 and solid wood granule plate 3, it is provided with fibre board 4 between described first solid wood board 1 and solid wood granule plate 3, described first solid wood board 1 and solid wood granule plate 3 all bond with fibre board 4, described fibre board 4 one side is provided with stainless (steel) wire 5, described stainless (steel) wire 5 is embedded in solid wood granule plate 3 and arranges, it is provided with bamboo board 6 between described second solid wood board 2 and solid wood granule plate 3, described second solid wood board 2 and solid wood granule plate 3 all bond with bamboo board 6, described bamboo board 6 is provided with batten 7, described batten 7 is arranged for integral type with bamboo board 6, described batten 7 is embedded in solid wood granule plate 3 and arranges, the distribution in Tian-shaped of described batten 7, it is provided with carbon fiber rod 8 in described batten 7.
Described batten 7 bonds with carbon fiber rod 8, good integrity, connects reliable.
Melamine impregnated paper 9 is all posted in the front of described first solid wood board 1 and the second solid wood board 2.
Described stainless (steel) wire 5 surface is that nickel plating is arranged, it is possible to play good anticorrosion ability.
Described stainless (steel) wire 5 is rustless steel seat type net.
Described fibre board 4 bonds with stainless (steel) wire 5, connects reliable, Stability Analysis of Structures.
Described stainless (steel) wire 4 is provided with noise deadener (not shown), it is possible to play good soundproof effect.
Described batten 7 is equal with carbon fiber rod 8 length.
Another technical problem that the invention solves the problems that is for providing the manufacture method of a kind of carbon fiber rod.
For solving the problems referred to above, the present invention adopts the following technical scheme that
It is made up of the chopped carbon fiber 26 parts of proportioning by weight, Merlon 20 parts, ABS resin 40 parts, polymethyl methacrylate 12 parts, SAN resin 8 parts, Dineodymium trioxide 8 parts, hollow glass microbead 12 parts, zirconium oxide bead 17 parts, maleic acrylic copolymer 11 parts, POM plastic 14 parts, acetylene black 10 parts, nano silicon 9 parts, 12 parts of Acetylenogen., cubic boron nitride micropowder 17 parts and white fused alumina micropowder 12 parts, comprises the following steps:
1) Merlon 20 parts, ABS resin 40 parts, polymethyl methacrylate 12 parts, SAN resin 8 parts are poured in vessel together with appropriate moisture, it is then heated to 180 DEG C, heating process is stirred continuously, till solid material melts completely, prepare thick liquid, standby；
2) together with maleic acrylic copolymer 11 parts and POM plastic 14 parts, be poured into step 1) prepare thick liquid in, and with 150 DEG C heat 12 minutes, prepare mixing thick liquid, standby；
3) Dineodymium trioxide 8 parts, hollow glass microbead 12 parts, zirconium oxide bead 17 parts, acetylene black 10 parts, nano silicon 9 parts, 12 parts of Acetylenogen., cubic boron nitride micropowder 17 parts are poured in three-dimensional material mixer together with white fused alumina micropowder 12 parts, it is sufficiently mixed, prepare mixed-powder, standby；
4) by chopped carbon fiber 26 parts and step 3) prepare mixed-powder together be poured into step 2) prepare mixing thick liquid in, stir, prepare paste, standby；
5) by step 4) prepare paste be poured in injection machine, use injection machine by paste injection and be full of mold cavity, cooling, obtain carbon fiber rod.
Embodiment three:
As shown in Figure 1-2, a kind of high strength multi-layer plate, including the first solid wood board 1, second solid wood board 2 and solid wood granule plate 3, it is provided with fibre board 4 between described first solid wood board 1 and solid wood granule plate 3, described first solid wood board 1 and solid wood granule plate 3 all bond with fibre board 4, described fibre board 4 one side is provided with stainless (steel) wire 5, described stainless (steel) wire 5 is embedded in solid wood granule plate 3 and arranges, it is provided with bamboo board 6 between described second solid wood board 2 and solid wood granule plate 3, described second solid wood board 2 and solid wood granule plate 3 all bond with bamboo board 6, described bamboo board 6 is provided with batten 7, described batten 7 is arranged for integral type with bamboo board 6, described batten 7 is embedded in solid wood granule plate 3 and arranges, the distribution in Tian-shaped of described batten 7, it is provided with carbon fiber rod 8 in described batten 7.
Described batten 7 bonds with carbon fiber rod 8, good integrity, connects reliable.
Melamine impregnated paper 9 is all posted in the front of described first solid wood board 1 and the second solid wood board 2.
Described stainless (steel) wire 5 surface is that nickel plating is arranged, it is possible to play good anticorrosion ability.
Described stainless (steel) wire 5 is rustless steel seat type net.
Described fibre board 4 bonds with stainless (steel) wire 5, connects reliable, Stability Analysis of Structures.
Described stainless (steel) wire 4 is provided with noise deadener (not shown), it is possible to play good soundproof effect.
Described batten 7 is equal with carbon fiber rod 8 length.
Another technical problem that the invention solves the problems that is for providing the manufacture method of a kind of carbon fiber rod.
For solving the problems referred to above, the present invention adopts the following technical scheme that
It is made up of the chopped carbon fiber 27 parts of proportioning by weight, Merlon 19 parts, ABS resin 39 parts, polymethyl methacrylate 11 parts, SAN resin 7 parts, Dineodymium trioxide 6 parts, hollow glass microbead 11 parts, zirconium oxide bead 16 parts, maleic acrylic copolymer 10 parts, POM plastic 13 parts, acetylene black 9 parts, nano silicon 8 parts, 11 parts of Acetylenogen., cubic boron nitride micropowder 16 parts and white fused alumina micropowder 11 parts, comprises the following steps:
1) Merlon 19 parts, ABS resin 39 parts, polymethyl methacrylate 11 parts, SAN resin 7 parts are poured in vessel together with appropriate moisture, it is then heated to 180 DEG C, heating process is stirred continuously, till solid material melts completely, prepare thick liquid, standby；
2) together with maleic acrylic copolymer 10 parts and POM plastic 13 parts, be poured into step 1) prepare thick liquid in, and with 150 DEG C heat 12 minutes, prepare mixing thick liquid, standby；
3) Dineodymium trioxide 6 parts, hollow glass microbead 11 parts, zirconium oxide bead 16 parts, acetylene black 9 parts, nano silicon 8 parts, 11 parts of Acetylenogen., cubic boron nitride micropowder 16 parts are poured in three-dimensional material mixer together with white fused alumina micropowder 11 parts, it is sufficiently mixed, prepare mixed-powder, standby；
4) by chopped carbon fiber 27 parts and step 3) prepare mixed-powder together be poured into step 2) prepare mixing thick liquid in, stir, prepare paste, standby；
5) by step 4) prepare paste be poured in injection machine, use injection machine by paste injection and be full of mold cavity, cooling, obtain carbon fiber rod.
Experimental example:
Using the high strength multi-layer plate of the present invention as experimental group, existing common multi-layer sheet as a control group, existing import multi-layer sheet as a control group two, to test, concrete outcome is as shown in the table:
By 3 groups of experiments are detected, the high strength multi-layer plate of experimental group is high with existing common and import multi-layer sheet phase specific strength.
The invention have the benefit that and be provided by batten, carbon fiber rod it is provided with in batten, batten is embedded in solid wood granule plate, and batten is Tian-shaped distribution, it is possible not only to so that force structure is more stable, and carbon fiber rod intensity is high, adds stainless (steel) wire, so that the intensity of entirety is greatly promoted.
Typical case:
Lee, it is Kai Liaoyijian Furniture Factory at home, and bought substantial amounts of multi-layer sheet making furniture, owing to order volume is bigger, multi-layer sheet has been used up substantially, but Lee suffers the complaint of client when being ready for again buying multiple-plate, timber intensity owing to making furniture is inadequate, cause that furniture damages soon, then Lee just attempts introducing the multi-layer sheet of other brands, but problem does not have solution always, after Lee employs the high strength multi-layer plate of the present invention, find that the furniture made is very firm, then Lee has just introduced the high strength multi-layer plate of the present invention in a large number.
The above, be only the specific embodiment of the present invention, but protection scope of the present invention be not limited thereto, any change expected without creative work or replacement, all should be encompassed within protection scope of the present invention.

Claims (8)

  1. null1. a high strength multi-layer plate，It is characterized in that: include the first solid wood board、Second solid wood board and solid wood granule plate，It is provided with fibre board between described first solid wood board and solid wood granule plate，Described first solid wood board and solid wood granule plate all bond with fibre board，Described fibre board one side is provided with stainless (steel) wire，Described stainless (steel) wire is embedded in solid wood granule plate and arranges，It is provided with bamboo board between described second solid wood board and solid wood granule plate，Described second solid wood board and solid wood granule plate all bond with bamboo board，Described bamboo board is provided with batten，Described batten and bamboo board are that integral type is arranged，Described batten is embedded in solid wood granule plate and arranges，Described batten is Tian-shaped distribution，It is provided with carbon fiber rod in described batten，Described carbon fiber rod is by chopped carbon fiber 26-28 part of proportioning by weight、Merlon 18-20 part、ABS resin 38-40 part、Polymethyl methacrylate 10-12 part、SAN resin 6-8 part、Dineodymium trioxide 4-8 part、Hollow glass microbead 10-12 part、Zirconium oxide bead 15-17 part、Maleic acrylic copolymer 9-11 part、POM plastic 12-14 part、Acetylene black 8-10 part、Nano silicon 7-9 part、Acetylenogen. 10-12 part、Cubic boron nitride micropowder 15-17 part and white fused alumina micropowder 10-12 part composition.
  2. 2. high strength multi-layer plate as claimed in claim 1, it is characterised in that: described batten and carbon fiber rod bonding.
  3. 3. high strength multi-layer plate as claimed in claim 2, it is characterised in that: melamine impregnated paper is all posted in the front of described first solid wood board and the second solid wood board.
  4. 4. high strength multi-layer plate as claimed in claim 3, it is characterised in that: described stainless (steel) wire surface is that nickel plating is arranged.
  5. 5. high strength multi-layer plate as claimed in claim 4, it is characterised in that: described stainless (steel) wire is rustless steel seat type net.
  6. 6. high strength multi-layer plate as claimed in claim 5, it is characterised in that: described fibre board and stainless (steel) wire bonding.
  7. 7. high strength multi-layer plate as claimed in claim 6, it is characterised in that: described stainless (steel) wire is provided with noise deadener.
  8. 8. high strength multi-layer plate as claimed in claim 7, it is characterised in that: described batten is equal with carbon fiber rod length.
CN201610222000.5A 2016-04-11 2016-04-11 A kind of high strength multi-layer plate Expired - Fee Related CN105751611B (en)