CN1057477A - Extreme pressure oil composition for industrial gears - Google Patents
Extreme pressure oil composition for industrial gears Download PDFInfo
- Publication number
- CN1057477A CN1057477A CN 90104292 CN90104292A CN1057477A CN 1057477 A CN1057477 A CN 1057477A CN 90104292 CN90104292 CN 90104292 CN 90104292 A CN90104292 A CN 90104292A CN 1057477 A CN1057477 A CN 1057477A
- Authority
- CN
- China
- Prior art keywords
- oil
- extreme pressure
- additive
- oil composition
- gear oil
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Load extreme pressure oil composition for industrial gears in a kind of is made up of nitrogen sulfate phosphate type extreme pressure/antiwear agents (I), sulfuration hydro carbons extreme pressure agent (II), 124 Triazole amine salt multipurpose (III), antioxidant (IV), anti-emulsifying compound agent (V) and mineral lubricating oils or the lubricated wet goods component of synthin.This gear oil has performances such as good extreme pressure property, resistance to abrasion, thermal oxidation stability, rust-preventing characteristic, erosion resistance and resistance to emulsion, can be used as the lubricant of wheelworks such as iron and steel, mine and Cement industry.
Description
The present invention relates to a kind of middle load extreme pressure oil composition for industrial gears, more particularly, the present invention relates to mix by a certain percentage and the middle load extreme pressure industrial gear oil made from several additives and base oil, it has good extreme pressure property, resistance to abrasion, thermal oxidation stability, rust-preventing characteristic, erosion resistance and resistance to emulsion, can be used as the lubricant of industrial gear devices such as iron and steel, mine and cement.
The middle extreme pressure industrial gear oil that loads is used to load higher, and the industrial gear that flank of tooth stress is bigger is lubricated, requires to have extreme pressure property and resistance to abrasion preferably.Owing to require industrial gear oil that arranged long work-ing life, so thermal oxidation stability preferably must be arranged.Industrial gear oil in use may be subjected to the pollution of water, so require to have rust-preventing characteristic and resistance to emulsion preferably, requires not corrode copper and alloy thereof in addition.Only can not satisfy above-mentioned requirements, so must add multiple suitable additive by base oil.
Early stage extreme pressure industrial gear oil mainly uses sulfide fat oil and organic lead-salt as additive, (sees US2,308 as lead naphthenate, lead stearate etc., 599), lead salt has heavy metal pollution problem, and organometallics also has katalysis to hydrocarbon oxidation, makes the oil product can promote the oxidation.The hydrocarbon oxidation product is a surfactant, makes oil product be easy to emulsification again.In addition, the oil soluble of organic lead-salt is poor, easily separates out precipitation.The sixties begin to occur sulphur phosphorus type extreme pressure industrial gear oil, use phosphoric acid ester (DE1,937,243), phosphorous acid ester and thiophosphite (US3,254,027, BP910,643), alkylphosphonic acid carboxylic acid amine salt (US3,859,218), alkylthio phosphate amine salt (US3,197,405) or the like.Above-mentioned ashless extreme pressure/antiwear agents can partly overcome the shortcoming of organic metal salt, and resistance to abrasion also has further improvement.US3,919,096 propose a kind of extreme pressure oil composition for industrial gears, use sulfide isobutene, dibutyl phosphite and 124 Triazole, the extreme pressure property and the resistance to abrasion of raising oil product.
Extreme pressure oil composition for industrial gears of the present invention uses dialkyl dithiophosphoric acid-formaldehyde-amine condenses to be extreme pressure/antiwear agents, different with the compound that patent noted earlier is used, and the compound use sulfide isobutene of the present invention, dialkyl dithiophosphoric acid-formaldehyde-amine condenses and 124 Triazole fatty amine salt, the extreme pressure property and the resistance to abrasion of oil product have been improved, this and US3,919,096 method is also variant.
The objective of the invention is to propose the extreme pressure oil composition for industrial gears of loading in the different sulphur phosphorus type of a kind of and above-mentioned prior art, have good extreme pressure property, resistance to abrasion, thermal oxidation stability, rust-preventing characteristic, erosion resistance and resistance to emulsion.
Present composition extreme pressure industrial gear oil additives and basic oil composition are:
Nitrogen sulfate phosphate type extreme pressure/antiwear agents (I) 0.2-1.0m%, better with 0.3-0.5m%;
Sulfur-containing extreme-pressure additive (II) 0.4-2m%, better with 0.5-1.5m%;
124 Triazole amine salt multipurpose additive (III) 0.05-0.5m%, better with 0.1-0.3m%;
Antioxidant addn (IV) 0.1-0.8m%, better with 0.1-0.5m%;
Anti-emulsifying compound agent (V) 0.01-0.3m%, better with 0.03-0.15m%;
The base oil surplus.
The present composition has good extreme pressure property, resistance to abrasion, thermal oxidation stability, rust-preventing characteristic, erosion resistance and resistance to emulsion.Using dialkyl dithiophosphoric acid-formaldehyde-amine condenses is outstanding feature of the present invention as extreme pressure/antiwear agents.
The component of the present composition (I) is 0,0 '-dialkyl dithiophosphoric acid-formaldehyde-fatty amine condensate, wherein the alkyl of thiophosphoric acid is C
4-C
8The straight or branched alkyl, two alkyl are identical or different.Used aliphatic amide is C
4-C
20(C
12-C
18Better) Armeen, secondary amine or acid amides.Component (I) is the inventive method preparation of CN 1033811A by publication number.The Chinese commodity name of this extreme pressure/antiwear agents is called T305, and commodity selling is arranged.Its sulphur content is not less than 10m%, and phosphorus content is not less than 5.5m%, and nitrogen content is not less than 1.0m%.The main effect of component (I) is extreme pressure property and the resistance to abrasion that improves oil product.
The component of the present composition (II) is the sulfuration hydro carbons, and its representational compound is a sulfide isobutene, be to react and get by iso-butylene, single sulfur subchloride, sodium sulphite, and be the preparation of CN 1034714A inventive method by publication number.The Chinese commodity name of this sulfur-containing extreme-pressure additive is called T321, and commodity selling is arranged.Sulfur-containing extreme-pressure additive prevents flank of tooth scratch and gummed, and is effective especially under high speed and shock load condition.
The component of the present composition (III) is the 124 Triazole fatty amine salt, and its structural formula is
, R is C in the formula
8～C
20Alkyl or alkenyl.The Chinese commodity name of this compound is called T406, and commodity selling is arranged.U.S. Pat 4,144,180 reaction product that once proposed 124 Triazole or alkylbenzene triazole and aliphatic amide can improve the terraced nurse of sulphur phosphorus type composite additive and agree rub(bing)test by load, the chemical structure of the reaction product of undeclared 124 Triazole of this patent and aliphatic amide.The present invention has used 124 Triazole fatty amine salt (III), during the compound use of this compound and sulfide isobutene (II), agree can produce synergism in the rub(bing)test at terraced nurse.In addition, component (III) can be improved the rust-preventing characteristic and the erosion resistance of oil product, also has the metal deactivation simultaneously, reduces the katalysis of metal pair hydrocarbon oxidation.
The component of composition of the present invention (IV) is an antioxidant addn, in order to improve the resistance of oxidation of oil product, reduces the increase and the precipitation of oil viscosity in the use and separates out.Component (IV) mainly is a phenol type compound, and as 2,6 ditertiary butyl p cresol, the Chinese commodity name is called T501.Also can use aromatic amine compounds, as phenyl-a-naphthylamine (the Chinese commodity name is called T531) or pentanoic.These antioxidants all have commodity selling.
The component of the present composition (V) is the anti-emulsifying compound agent, in order to improve the resistance to emulsification of oil product.Component (V) is alkylene diamine oxozone trimethylene condenses and C
10-C
20Alkenyl succinic acid is pressed 20-90: mixture 80-10(weight), wherein alkylene base is C
2-C
10The molecular-weight average of condenses is 2,000～10,000.Component (V) is 88108609.6 invention preparation by application number.The now existing commodity of this agent, name is called T1001.
The used base oil of the present invention comprises the mixture of mineral lubricating oils, synthin oil or mineral lubricating oils and synthin oil.Mineral lubricating oils comprises 350SN, 500SN, 650SN neutral oil and 150BS bright stock.Synthin oil mainly is poly-alpha olefins, clorafin condensation oil.The base oil viscosity grade is the N68-N460(GB3141-82 specification).
The present composition has made full use of the synergistic effect between the additive, and olefine sulfide provides extreme pressure property, and sulfuric acid phosphoric acid-formaldehyde-amine condenses provides resistance to abrasion and extreme pressure property, and two doses of compound uses make the present composition have better extreme pressure/resistance to abrasion.Olefine sulfide and the compound use of 124 Triazole amine salt make terraced nurse agree test and significantly improve by load, and this is the important indicator of extreme pressure industrial gear oil specification.Sulphur phosphoric acid-formaldehyde-amine condenses and 124 Triazole fatty amine salt all have long alkyl chain, have the good friction property improved, so the present composition needn't add friction improver in addition.Shielding phenol and aromatic amine are first kind oxidation inhibitor (free radical and peroxylradicals trapping agent), and phosphate sulfur derivatives is second kind antioxidant (peroxide breakdown agent), both compound synergistic effects that produce.The 124 Triazole amine salt has the metal passivation effect, with the compound use of oxidation inhibitor, the resistance of oxidation of oil product is further strengthened.The 124 Triazole amine salt has erosion resistance and rust-preventing characteristic again, thereby the present composition does not need in addition with corrosion inhibitor and rust-preventive agent.Owing to utilize the synergistic effect between the above-mentioned multiple additives, reduced and used the kind number of additive and total additive amount, improved economy and practicality.
Compare with existing extreme pressure industrial gear oil, industrial gear oil compositions of the present invention has following advantage:
1. extreme pressure oil composition for industrial gears of the present invention has good extreme pressure property, resistance to abrasion, thermal oxidation stability, rust-preventing characteristic, erosion resistance and resistance to emulsion, the desired over-all properties of load extreme pressure industrial gear oil in possessing.
2. the nitrogen sulfate phosphate type extreme pressure/antiwear agents that composition of the present invention uses is dialkyl dithiophosphoric acid-formaldehyde-amine condenses, rather than the alkylphosphonic acid carboxylic acid amine salt that often uses at present, alkyl phosphorous acid amine salt or alkylthio phosphate amine salt, this is an outstanding feature of the present invention.
3. the present invention makes full use of the synergistic effect between dialkyl dithiophosphoric acid-formaldehyde-amine condenses, sulfide isobutene, 124 Triazole fatty amine salt, shielding phenol, the aromatic amine, has reduced the kind of using additive and has used lower dosage.For example, general medium duty industrial gear oil composition uses 6-9 kind additive, and total dose is 1.3-3.0m%; The present composition uses 5 kinds of additives, and total dose is that 1.3m% can be by the over-all properties index of medium duty industrial gear oil GB5903 specification.
4. extreme pressure of the present invention industrial gear oil, not only fresh oil has good resistance to emulsion, still has good resistance to emulsion through the oil of oxidation under the severe condition, thereby can prolong the work-ing life of oil product in the presence of water.
Embodiment 1 N220 medium duty industrial gear oil composition
Base oil: 40 parts of (weight) 650SN neutral oils mix with 60 parts of (weight) 150BS bright stocks.
Additive: 0.3m% 0,0 '-normal-butyl, iso-octyl phosphorodithioic acid-formaldehyde-amine condenses (T305) (I); 0.5m% sulfide isobutene (T321) (II); 0.1m% 124 Triazole stearylamine salt (T406) (III); 0.3m% 2,6 ditertiary butyl p cresol (T501) (IV); 0.1m% anti-emulsifying compound agent (T1001) (V).
The additive of above-mentioned percentage composition and above-mentioned base oil (surplus) 50～60 ℃ of stirring and dissolving, are added 10PPM dimethyl silicone oil kilfoam then.Processed oil viscosity (40 ℃ of ν) is 265mm
2/ S, its performance meets medium duty industrial gear oil standard GB5903-86, and is as shown in table 1.
Embodiment 2 N220 medium duty industrial gear oil compositions (different) with the base oil of example 1.
Base oil: clay-filtered (viscosity ν is 504mm for 40 ℃ through 5m% for 52 parts of (weight) No. 35 poly alpha olefine synthetic oil stills Residual oils
2/ S) and 48 parts (weight) No. 15 pressed oils (viscosity ν is 154mm for 40 ℃ through clay-filtered
2/ S) mix.
Additive and consumption are with embodiment 1.Processed oil viscosity ν is 260mm for 40 ℃
2/ S, its performance meets medium duty industrial gear oil standard GB5903-86, and is as shown in table 1.
Embodiment 3 N320 medium duty industrial gear oil compositions.
Base oil: clay-filtered (viscosity ν is 504mm for 40 ℃ through 5m% for 77 parts of (weight) No. 35 poly alpha olefine synthetic oil stills Residual oils
2/ S) and 23 parts (weight) No. 15 pressed oils (viscosity ν is 154mm for 40 ℃ through clay-filtered
2/ S), mix.
Additive and consumption are with example 1.Processed oil viscosity ν is 377mm for 40 ℃
2/ S, its performance meets medium duty industrial gear oil standard GB5903-86, and is as shown in table 1.
Embodiment 4 N220 medium duty industrial gear oil compositions (base oil is different with embodiment 1 and embodiment 2).
Base oil: clay-filtered (viscosity ν is 504mm for 40 ℃ through 5m% for 45 parts of (weight) No. 35 poly alpha olefine synthetic oil stills Residual oils
2/ S) mix with 55 parts of (weight) 500SN neutral oils.
Additive: 0.33m%0,0 '-normal-butyl, iso-octyl phosphorodithioic acid-formaldehyde-amine condenses (T305) (I); 0.53m% sulfo-iso-butylene (T321) (II); 0.1m% 124 Triazole stearylamine salt (T406) (III); 0.3m%2,6-ditertbutylparacresol (T501) (IV); 0.05m% anti-emulsifying compound agent (T1001) (V).
The additive of above-mentioned percentage composition and above-mentioned base oil (surplus) 50～60 ℃ of stirring and dissolving, are added 5PPm dimethyl silicone oil kilfoam then.Processed oil viscosity ν is 218mm for 40 ℃
2Its performance of/S meets medium duty industrial gear oil standard GB5903-86, and is as shown in table 1.
Embodiment 5 N220 medium duty industrial gear oil compositions.
Base oil: with embodiment 1.
Additive: 0.33m% 0,0 '-normal-butyl, iso-octyl phosphorodithioic acid-formaldehyde-amine condenses (T305) (I); 0.57m% sulfide isobutene (T321) (II); 0.11m% 124 Triazole stearylamine salt (406) (III); 0.14m% 2,6 ditertiary butyl p cresol (T501) (IV); 0.05m% anti-emulsifying compound agent (T1001) (V).
The additive of above-mentioned percentage composition and above-mentioned base oil (surplus) 50～60 ℃ of dissolvings, are added 5PPm dimethyl silicone oil kilfoam then.Processed oil viscosity ν is 257mm for 40 ℃
2/ S, its performance meets medium duty industrial gear oil standard GB5903-86, and is as shown in table 1.
Embodiment 6 N220 medium duty industrial gear oil compositions.
Base oil: with embodiment 1.
Additive: 0.5m% 0,0 '-normal-butyl, iso-octyl phosphorodithioic acid-formaldehyde-amine condenses (T305) (I); 1m% sulfide isobutene (T321) (II); 0.2m% 124 Triazole stearylamine salt (T406) (III); 0.2m% 2,6 ditertiary butyl p cresol (T501) (IV); 0.13m% anti-emulsifying compound agent (T1001) (V).
Above-mentioned additive and base oil 50～60 ℃ of stirring and dissolving, are added 10PPm dimethyl silicone oil kilfoam then.Processed oil viscosity ν is 252mm for 40 ℃
2/ S, its performance meets medium duty industrial gear oil standard GB5903-86, and is as shown in table 1.
Embodiment 7 N220 medium duty industrial gear oil compositions.
Base oil: with embodiment 1.
Additive: 0.5m% 0,0 '-normal-butyl, iso-octyl phosphorodithioic acid-formaldehyde-amine condenses (T305) (I); 1.5m% sulfide isobutene (T321) (II), 0.3m% 124 Triazole stearylamine salt (T406) (III); 0.1m% phenyl-a-naphthylamine (IV); 0.15m% anti-emulsifying compound agent (T1001) (V).
Modulator approach is with embodiment 6, and processed oil viscosity ν is 250mm for 40 ℃
2/ S, load gear oil standard GB5903-86 was as shown in table 1 during its performance met.
Embodiment 8
This embodiment explanation still has good resistance to emulsion after the extreme pressure oil composition for industrial gears oxidation of the present invention.
Medium duty industrial gear oil with embodiment 1,2,3 and 5, through the GB5004 oxidation test, promptly the oil after 95 ℃ of atmospheric oxidations in following 312 hours carries out demulsibility test (GB8022-87 standard) again, test shows that the resistance to emulsion of oil after the oxidation is still fine, as shown in table 2.
Table 2
| Fresh oil | Oil after the GB5004 oxidation test | |||||
| W/O V% | Total free-water ml | Emulsion layer ml | W/O V% | Total free-water ml | Emulsion layer ml | |
| The oil of the oily embodiment 5 of the oily embodiment 3 of the oily embodiment 2 of embodiment 1 | 0.9 0.8 0.8 0.9 | 84.4 83.9 83.5 84.5 | 0 0 0 0 | 1.1 0.8 0.8 1.0 | 80.4 84.4 82.3 82.9 | 0.4 0 0.07 vestiges |
Embodiment 9
Present embodiment be by three kinds of tests illustrate 0,0 '-normal-butyl, iso-octyl phosphorodithioic acid-formaldehyde-stearylamine condenses (I) has good extreme pressure property and resistance to abrasion, and is as shown in table 3.
It is a kind of test of measuring the lubricating oil supporting capacity that terraced nurse is agree test, and its friction member is ring and piece, abrading the crest of phenomenon for passing through load not occur.
The FZG test is a kind of gear testing machine test, measures the lubricating oil supporting capacity abrasive crest not occur for passing through load.
The tetra-ball machine test of quoting in the table 3 is a kind of test method of measuring the abrasion resistance of lubricating oil.
The data of table 3 show dialkyl dithiophosphoric acid-formaldehyde-amine condenses (I) are added in sulfur-bearing and the sulphur phosphorus composite additive, have all improved willing test of terraced nurse and FZG test by load, have reduced wearing and tearing.
(notes):
(1) Containing Sulfur alkene, 124 Triazole stearylamine salt, corrosion inhibitor.
(2) contain sulfo-triphenylphosphate, antioxidant, corrosion inhibitor.
(3) base oil with example 1 is identical.
(4) mineral lubricating oils, 40 ℃ of 47mm of ν
2/ S.
Embodiment 10
Present embodiment shows 124 Triazole fatty amine salt (III) and the compound use of olefine sulfide (II), agree demonstrate synergistic effect in the test at terraced nurse, and is as shown in table 4.
The synergistic effect of additive is meant the weighted mean of total effect of the compound use of two or more additives greater than the independent effect of these additives.124 Triazole amine salt (III) and the compound use of olefine sulfide (II), terraced nurse agree significantly improve by load, demonstrate synergistic effect, and additive amount is reduced.
(notes) (1) mineral lubricating oils, 40 ℃ of 360mm of ν
2/ S
Embodiment 11
This embodiment explanation, 124 Triazole fatty amine salt (III) can improve the rust-preventing characteristic and the erosion resistance of oil product.
Base oil: with example 2.
With 0,0 '-normal-butyl, iso-octyl phosphorodithioic acid-formaldehyde-amine condenses (T305) (I); Sulfo-iso-butylene (T321) (II); 124 Triazole stearylamine salt (T406) (III) and 2, independent or compound being added in the base oil of 6-ditertbutylparacresol (T501) (IV), press the B method (synthetic sea water) of SY2674 and survey rust-preventing characteristic, press the GB5096 method and survey copper corrosion performance down at 121 ℃, the result is as shown in table 5.
Table 5
| Extreme pressure industrial gear oil formula | Corrosion test (synthetic sea water) | 121 ℃ of 3h levels of copper corrosion |
| N220 base oil (same) with example 1 | Heavily become rusty | 11 |
| 0.5m%T321 (II)+N220 base oil | Heavily become rusty | 11～12 |
| 0.3m%T305 (I)+N220 base oil | Light variable color | 22 |
| 0.3m%T501 (IV)+N220 base oil | Heavily become rusty | 11 |
| 0.5m%T321 (II)+0.3m%T305 (I)+0.3m% T501 (IV)+N220 base oil | In～heavily become rusty | 23 |
| 0.5m%T321 (II)+0.3m%T305 (I)+0.3m% T501 (IV)+0.1m%T406 (III)+N220 base oil | Rustless | 12 |
Claims (7)
1, a kind of middle load extreme pressure oil composition for industrial gears of being made up of base oil and additive is characterized in that in base oil and additive various doses component and content is:
Nitrogen sulfate phosphate type extreme pressure/antiwear agents (I) 0.2～1.0m%, better with 0.3～0.5m%;
Sulfur-containing extreme-pressure additive (II) 0.4～2.0m%, better with 0.5～1.5m%;
124 Triazole amine salt multipurpose additive (III) 0.05～0.5m%, better with 0.1～0.3m%;
Antioxidant addn (IV) 0.1～0.8m%, better with 0.1～0.5m%;
Anti-emulsifying compound agent (V) 0.01～0.3m%, better with 0.03～0.15m%;
The base oil surplus.
2, according to the described gear oil composition of claim 1, it is characterized in that nitrogen sulfate phosphate type extreme pressure/antiwear agents (I) be 0,0 '-dialkyl dithiophosphoric acid-formaldehyde-fatty amine condensate, the alkyl of thiophosphoric acid wherein is C
4～C
8The straight or branched alkyl, two alkyl are identical or different, and its aliphatic amide is C
4～C
20Armeen, secondary amine or acid amides.
3,, it is characterized in that sulfur-containing extreme-pressure additive (II) is the sulfuration hydrocarbon compound according to the described gear oil composition of claim 1.
4, according to the described gear oil composition of claim 1, it is characterized in that 124 Triazole amine salt multipurpose additive (III) is the 124 Triazole fatty amine salt, the aliphatics substituting group in its fatty amine salt is C
8～C
20Alkyl or alkenyl.
5, according to the described gear oil composition of claim 1, it is characterized in that antioxidant addn (IV) can be selected from phenol type antioxidant and aromatic amine type oxidation inhibitor, phenol type antioxidant such as 2,6 ditertiary butyl p cresol, aromatic amine type oxidation inhibitor such as phenyl-a-naphthylamine or pentanoic.
6,, it is characterized in that anti-emulsifying compound agent (V) is alkylene diamine oxozone trimethylene condenses and C according to the described gear oil composition of claim 1
10～C
20Alkenyl succinic acid is by 20～90: mixture 80～10(weight ratio), alkylene base wherein are C
2～C
10, the molecular-weight average of condenses is 2,000～10,000.
7,, it is characterized in that base oil can be selected from the mixture of mineral lubricating oils, synthin oil or mineral lubricating oils and synthin oil according to the described gear oil composition of claim 1.