CN105734536A - 一种铝合金镀镍电镀液 - Google Patents
一种铝合金镀镍电镀液 Download PDFInfo
- Publication number
- CN105734536A CN105734536A CN201410750495.XA CN201410750495A CN105734536A CN 105734536 A CN105734536 A CN 105734536A CN 201410750495 A CN201410750495 A CN 201410750495A CN 105734536 A CN105734536 A CN 105734536A
- Authority
- CN
- China
- Prior art keywords
- aluminum alloy
- electroplating liquid
- acid
- alloy nickel
- plating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种铝合金镀镍电镀液，每kg电镀液由下述原料组成：硼酸20-40，乙酸2-10，硫酸铵10-30，磷酸20-40，磷酸三钠10-30，氟化氢铵20-40，硫脲2-8，水为余量；本发明产品可以在铝基材表面形成一层附着良好的薄砂面，并能有效控制化学镀镍的速度和保护基材不被过腐蚀，具有良好的经济价值，适合广泛推广应用。
Description
技术领域
本发明涉及铝合金表面电镀技术领域，尤其是一种铝合金镀镍电镀液。
背景技术
铝合金是工业中应用最广泛的一类有色金属结构材料，在航空、航天、汽车、机械制造、船舶及化学工业中已大量应用。工业经济的飞速发展，对铝合金焊接结构件的需求日益增多，使铝合金的焊接性研究也随之深入。但是铝合金由于表面较柔软，如不对铝合金表面进行处理，直接进行加工使用，不仅影响其使用寿命，还影响其美观，化学镀镍层具有优秀的均匀性、硬度、耐磨和耐蚀性等综合物理化学性能，该项技术已经得到广泛应用，目前几乎难以找到一个工业不采用化学镀镍技术，把这一技术引用到铝合金材料上，来增加铝合金的力学性能和寿命，是提高铝合金产品价值的重要途径。因此，研发一种铝合金镀液，解决这一问题成为十分必要的事情。
发明内容
本发明的目的就是针对铝合金材料表面容易被刮伤，需要在其表面制备镀层来改善铝合金制品的性能，延其使用寿命的问题，提供一种铝合金镀镍电镀液。
本发明的一种铝合金镀镍电镀液，每kg电镀液由下述原料组成：
硼酸20-40g乙酸2-10g
硫酸铵10-30g磷酸20-40g
磷酸三钠10-30g氟化氢铵20-40g
硫脲2-8g水余量。
本发明的一种铝合金镀镍电镀液，其优选配方每kg电镀液由下述原料组成：
硼酸25-35g乙酸4-8g
硫酸铵15-25g磷酸28-32g
磷酸三钠15-25g氟化氢铵25-35g
硫脲4-6g水余量。
用本发明产品进行铝合金镀镍的工艺流程如下：（1）在45-50℃下将经过预处理的铝合金放入含有十二烷基苯磺酸钠、偏硅酸钠、乙二胺四乙酸的溶液中浸泡5min；（2）将铝合金基材进行抛光处理后放入硝酸和氟化氢溶液20-40s；（3）将铝合金基材放入本品电镀液中进行化学镀镍。
本发明产品可以在铝基材表面形成一层附着良好的薄砂面，并能有效控制化学镀镍的速度和保护基材不被过腐蚀，具有良好的经济价值，适合广泛推广应用。
具体实施方式
实施例1
一种铝合金镀镍电镀液，每kg电镀液由下述原料组成：
硼酸30g乙酸6g
硫酸铵20g磷酸30g
磷酸三钠20g氟化氢铵30g
硫脲5g水余量。
实施例2
一种铝合金镀镍电镀液，每kg电镀液由下述原料组成：
硼酸35g乙酸4g
硫酸铵25g磷酸32g
磷酸三钠15g氟化氢铵35g
硫脲4g水余量。
实施例3
一种铝合金镀镍电镀液，每kg电镀液由下述原料组成：
硼酸25g乙酸8g
硫酸铵15g磷酸28g
磷酸三钠25g氟化氢铵25g
硫脲6g水余量。
Claims (2)
1.一种铝合金镀镍电镀液，其特征在于每kg电镀液由下述原料组成：
硼酸20-40g乙酸2-10g
硫酸铵10-30g磷酸20-40g
磷酸三钠10-30g氟化氢铵20-40g
硫脲2-8g水余量。
2.根据权利要求1所述的一种铝合金镀镍电镀液，其特征在于每kg电镀液由下述原料组成：
硼酸25-35g乙酸4-8g
硫酸铵15-25g磷酸28-32g
磷酸三钠15-25g氟化氢铵25-35g
硫脲4-6g水余量。