CN105733070A - 性能优良的分散剂色母及其制备方法 - Google Patents

性能优良的分散剂色母及其制备方法 Download PDF

Info

Publication number
CN105733070A
CN105733070A CN201410773011.3A CN201410773011A CN105733070A CN 105733070 A CN105733070 A CN 105733070A CN 201410773011 A CN201410773011 A CN 201410773011A CN 105733070 A CN105733070 A CN 105733070A
Authority
CN
China
Prior art keywords
parts
dispersant
color masterbatch
function admirable
dispersing agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410773011.3A
Other languages
English (en)
Inventor
沙作宏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZIBO LONGSHA POLYMER MATERIAL TECHNOLOGY Co Ltd
Original Assignee
ZIBO LONGSHA POLYMER MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZIBO LONGSHA POLYMER MATERIAL TECHNOLOGY Co Ltd filed Critical ZIBO LONGSHA POLYMER MATERIAL TECHNOLOGY Co Ltd
Priority to CN201410773011.3A priority Critical patent/CN105733070A/zh
Publication of CN105733070A publication Critical patent/CN105733070A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种性能优良的分散剂色母及其制备方法，属于化工生产技术领域，由以下重量份数的原料制成：载体40份、无机颜料20份、相容剂10份、聚乙烯蜡20份、分散剂7份、LDPE粉末15份、抗氧剂5份。用LDPE粉末替代聚乙烯蜡，在效果上提高了色母的着色能力及表观质量、降低了成本，同时还具备了良好的物理性能，在色母料中即作为载体有起到分散剂作用，增强了产品的市场竞争力。

Description

性能优良的分散剂色母及其制备方法
技术领域
本发明涉及一种性能优良的分散剂色母及其制备方法，属于化工生产技术领域。
背景技术
目前，色母的主要作用就是用以着色，这样随着技术的发展，现有的色母功效较为单一，而在色母使用的过程中又经常会要求色母再具备其他作用，例如在使用过程中即需要色母的着色能力，同时还需要它具备一些物理性能，在这些要求下，目前的色母就显得不能满足市场的需求。
发明内容
根据现有技术的不足，本发明要解决的技术问题是：提供一种性能优良的分散剂色母，该色母，染色效果好，同时还具备良好的物理性能；同时本制备方法，工艺简单，便于操作。
本发明解决其技术问题所采用的技术方案是：提供一种性能优良的分散剂色母，由以下重量份数的原料制成：
载体40份
无机颜料20份
相容剂10份
聚乙烯蜡20份
分散剂7份
LDPE粉末15份
抗氧剂5份。
所述的载体为线性高密度聚乙烯。
所述的无机颜料酞菁绿或酞菁蓝。
所述的相容剂为醋酸乙烯共聚物。
所述的分散剂低分子量聚乙烯蜡或OP蜡。
所述的抗氧剂为抗氧剂1010。
所述的性能优良的分散剂色母的制备方法，以下步骤：
(1)将LDPE用磨粉机研磨成3微米粉末；
(2)按比例将除聚乙烯蜡除外的原材料投入高速混合机混合至干燥；
(3)将聚乙烯蜡按比例加入以混合干燥的上述原材料中，重新再次进行搅拌，直至粘合均匀，放出晾干；
(4)将晾干后物料投入挤出机中造粒，制得产品。
本发明的有益效果是：用LDPE粉末替代聚乙烯蜡，在效果上提高了色母的着色能力及表观质量、降低了成本，同时还具备了良好的物理性能，在色母料中即作为载体有起到分散剂作用，增强了产品的市场竞争力。
具体实施方式
下面结合实施例对本发明做进一步描述：
实施例1
性能优良的分散剂色母，由以下重量份数的原料制成：
载体40份
无机颜料20份
相容剂10份
聚乙烯蜡20份
分散剂7份
LDPE粉末15份
抗氧剂5份。
所述的载体为线性高密度聚乙烯。
所述的无机颜料酞菁绿或酞菁蓝。
所述的相容剂为醋酸乙烯共聚物。
所述的分散剂低分子量聚乙烯蜡或OP蜡。
所述的抗氧剂为抗氧剂1010。
所述的性能优良的分散剂色母的制备方法，以下步骤：
(1)将LDPE用磨粉机研磨成3微米粉末；
(2)按比例将除聚乙烯蜡除外的原材料投入高速混合机混合至干燥；
(3)将聚乙烯蜡按比例加入以混合干燥的上述原材料中，重新再次进行搅拌，直至粘合均匀，放出晾干；
(4)将晾干后物料投入挤出机中造粒，制得产品。
请提供以下制得的产品即该色母的一些性能检测指标

Claims (7)

1.一种性能优良的分散剂色母，其特征在于由以下重量份数的原料制成：
载体40份
无机颜料20份
相容剂10份
聚乙烯蜡20份
分散剂7份
LDPE粉末15份
抗氧剂5份。
2.根据权利要求1所述的性能优良的分散剂色母，其特征在于所述的载体为线性高密度聚乙烯。
3.根据权利要求1所述的性能优良的分散剂色母，其特征在于所述的无机颜料酞菁绿或酞菁蓝。
4.根据权利要求1所述的性能优良的分散剂色母，其特征在于所述的相容剂为醋酸乙烯共聚物。
5.根据权利要求1所述的性能优良的分散剂色母，其特征在于所述的分散剂低分子量聚乙烯蜡或OP蜡。
6.根据权利要求1所述的性能优良的分散剂色母，其特征在于所述的抗氧剂为抗氧剂1010。
7.根据权利要求1所述的性能优良的分散剂色母的制备方法，其特征在于以下步骤：
(1)将LDPE用磨粉机研磨成3微米粉末；
(2)按比例将除聚乙烯蜡除外的原材料投入高速混合机混合至干燥；
(3)将聚乙烯蜡按比例加入以混合干燥的上述原材料中，重新再次进行搅拌，直至粘合均匀，放出晾干；
(4)将晾干后物料投入挤出机中造粒，制得产品。
CN201410773011.3A 2014-12-12 2014-12-12 性能优良的分散剂色母及其制备方法 Pending CN105733070A (zh)