CN105714618A - 一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒的方法 - Google Patents
一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒的方法 Download PDFInfo
- Publication number
- CN105714618A CN105714618A CN201610062838.2A CN201610062838A CN105714618A CN 105714618 A CN105714618 A CN 105714618A CN 201610062838 A CN201610062838 A CN 201610062838A CN 105714618 A CN105714618 A CN 105714618A
- Authority
- CN
- China
- Prior art keywords
- cyanophyceae
- egg
- garbage
- afterwards
- cellulose
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒的方法，属于日常生活垃圾处理技术领域。本发明以厨房垃圾为原材料，首先将收集得到的厨房垃圾进行晒干、粉碎以及冷却处理，然后放入锅子中，连同草药和水一起进行发酵，之后取蓝藻斩碎，加入纤维素酶进行酶解，将酶解后的蓝藻和厨房垃圾发酵混合物进行混合再次发酵得浆糊状物质，最后利用制得的浆糊状物质进行制作鸡蛋保护壳。本实例证明，本发明解决了厨房垃圾对于环境的污染问题，不仅减少了土地的占用，节约了处理生活垃圾的巨额费用，同时达到了变废为宝的目的，而且制成的鸡蛋保护壳可自行降解，抗冲击能力比较强，能保护鸡蛋，降低了60％以上的鸡蛋损坏率。
Description
技术领域
本发明公开了一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒的方法，属于日常生活垃圾处理技术领域。
背景技术
生活废弃物一般分为可回收的废弃物、不可回收的废弃物及有害废物，这些废弃物对人类生活和环境造成很多危害，例如，它们在运输和露天堆放过程中，有机分解产生恶臭，并向大气释放出大量的氨、硫化物等污染物，其中含有有机挥发气体达100多种，这些释放物中含有许多致癌、致畸物，以及塑料膜、纸屑和粉尘则随风飞扬形成“白色污染”。
而厨房垃圾属于最常见的的废气物，厨房垃圾一般有剩菜、剩饭、蔬菜叶等，每个家庭每天都会产生大量的厨房垃圾，研究显示，我国餐饮企业每年产生的餐厨垃圾已超过3000万吨，数量惊人，但是城市餐厅垃圾处理能力却相对严重落后，这些垃圾如果不及时处理，或者放在垃圾筒里面就好释放大量的二氧化碳，从而进一步促进“温室效应”，如果采用高温焚烧或者卫生填埋，则会造成运行费用极大、环境遭到污染以及土地资源的浪费。
现如今人们对于生活质量的要求越来越高，几乎每个人每天都会吃鸡蛋，特别是小朋友和老人，需要从鸡蛋中摄取大量的蛋白质，因而鸡蛋已经成为人们日常生活中不可或缺的食材，菜场的鸡蛋摊位永远都是络绎不绝，但是鸡蛋很容易破碎，人们买到鸡蛋后一般都很小心谨慎，生怕携带过程中会挤破压碎，回到家还要特意找个安全的地方摆放鸡蛋，非常不方便，另外厂家在运输和搬运过程中由于鸡蛋皮薄而脆，容易破损造成经济损失，现有的鸡蛋保护壳虽然有着一定的保护能力，但是基本都是塑料泡沫做的，除了一般不可以自行降解之外，还经受不起高空衰落，还是会造成鸡蛋的摔坏。
发明内容
本发明主要解决的技术问题：针对目前每年产生的厨房垃圾数量惊人，荒弃或者进行焚烧、卫生填埋处理都会给环境以及土地资源带来无法避免的危害，以及如今的鸡蛋容易摔坏，而现有的鸡蛋保护壳虽有一定的保护能力，但材料基本是不可自行降解的，抗压能力也相对比较弱，还是会造成鸡蛋的摔坏的问题，提供了一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒的方法，该方法以厨房垃圾为原材料，首先将收集得到的厨房垃圾进行晒干、粉碎以及冷却处理，然后放入锅子中，连同草药和水一起进行发酵，之后取蓝藻斩碎，加入纤维素酶进行酶解，将酶解后的蓝藻和厨房垃圾发酵混合物进行混合再次发酵得浆糊状物质，最后利用制得的浆糊状物质进行制作鸡蛋保护壳。本发明解决了厨房垃圾对于环境的污染问题，不仅减少了土地的占用，节约了处理生活垃圾的巨额费用，同时达到了变废为宝的目的，而且制成的鸡蛋保护壳可自行降解，抗冲击能力比较强，能保护鸡蛋，降低了60％以上的鸡蛋损坏率。
为了解决上述技术问题，本发明所采用的技术方案是：
（1）将5～10kg回收的厨房垃圾用弱碱废液进行搅拌清洗1～3次，之后均匀平铺在地面上，在太阳光下自然晒干后，放入粉碎机中进行粉碎处理，过100～150目筛，得到厨房垃圾粉末；
（2）将上述得到的厨房垃圾粉末放入蒸汽笼中，向其中通入100～150℃的过热蒸汽，蒸制8～15min后，在18～20℃的室温条件下自然冷却1.5～2.5h；
（3）取10～25g续断、15～20g五倍子，12～18g龙葵和5～10g覆盆子放入气流粉碎机中进行微米级超细粉碎，得到10～15μm草药混合粉末，之后按照固液比为2∶9将草药混合粉末和蒸馏水放入直径为80～100cm的铁锅中，并将上述制得的冷却后的厨房垃圾粉末同时添加到铁锅中，搅拌均匀后盖上锅盖，并用棉被将其包裹住，在35～45℃条件下进行发酵10～15天；
（4）取500～800g新鲜蓝藻，在太阳光下暴晒3～5h，使其自然晾干，之后将晾干后的蓝藻放入粉碎机中进行粉碎处理，然后将粉碎后的蓝藻碎片移入发酵罐中，加入10～15g纤维素酶和2～3L蒸馏水，用搅拌棒均匀搅拌后，用薄膜将发酵罐口密封，在35～45℃下酶解24～36h，使蓝藻软化；
（5）将软化后的蓝藻放入上述步骤（3）中的发酵锅里，用搅拌机在900～1200r/min的转速下高速搅拌20～30min，之后升高温度至40～50℃，盖上锅盖和棉被继续发酵7～14天，得浆糊状混合物；
（6）将得到的浆糊状混合物放入鸡蛋保护盒模具中，之后移入恒温干燥器中，升温至130～150℃进行干燥处理，待其冷却之后，拆除模具，即得一种利用餐厨垃圾添加蓝藻纤维素制备的可降解性鸡蛋保护盒。
本发明的应用方法是：取100～200枚鸡蛋分别依次放入本发明所制得的一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒中，之后再在上面盖上一个同样的鸡蛋保护盒，上下包裹住鸡蛋，使得鸡蛋在运输途中不易被摔坏，抗冲击压比较强，降低了60％以上的鸡蛋损坏率。
本发明的有益效果是：
（1）解决了厨房垃圾对于环境的污染问题，减少了土地的占用，节约了处理生活垃圾的巨额费用，同时达到了变废为宝的目的；
（2）将厨房垃圾生产成高效、环保、绿色的再次可用物，提高了经济收入；
（3）制成的鸡蛋保护壳可自行降解，抗冲击能力比较强，能保护鸡蛋，减少60％以上的鸡蛋损坏率。
具体实施方式
将5～10kg回收的厨房垃圾用弱碱废液进行搅拌清洗1～3次，之后均匀平铺在地面上，在太阳光下自然晒干后，放入粉碎机中进行粉碎处理，过100～150目筛，得到厨房垃圾粉末；将上述得到的厨房垃圾粉末放入蒸汽笼中，向其中通入100～150℃的过热蒸汽，蒸制8～15min后，在18～20℃的室温条件下自然冷却1.5～2.5h；取10～25g续断、15～20g五倍子，12～18g龙葵和5～10g覆盆子放入气流粉碎机中进行微米级超细粉碎，得到10～15μm草药混合粉末，之后按照固液比为2∶9将草药混合粉末和蒸馏水放入直径为80～100cm的铁锅中，并将上述制得的冷却后的厨房垃圾粉末同时添加到铁锅中，搅拌均匀后盖上锅盖，并用棉被将其包裹住，在35～45℃条件下进行发酵10～15天；取500～800g新鲜蓝藻，在太阳光下暴晒3～5h，使其自然晾干，之后将晾干后的蓝藻放入粉碎机中进行粉碎处理，然后将粉碎后的蓝藻碎片移入发酵罐中，加入10～15g纤维素酶和2～3L蒸馏水，用搅拌棒均匀搅拌后，用薄膜将发酵罐口密封，在35～45℃下酶解24～36h，使蓝藻软化；将软化后的蓝藻放入上述的发酵锅里，用搅拌机在900～1200r/min的转速下高速搅拌20～30min，之后升高温度至40～50℃，盖上锅盖和棉被继续发酵7～14天，得浆糊状混合物；将得到的浆糊状混合物放入鸡蛋保护盒模具中，之后移入恒温干燥器中，升温至130～150℃进行干燥处理，待其冷却之后，拆除模具，即得一种利用餐厨垃圾添加蓝藻纤维素制备的可降解性鸡蛋保护盒。
实例1
将5g回收的厨房垃圾用弱碱废液进行搅拌清洗1次，之后均匀平铺在地面上，在太阳光下自然晒干后，放入粉碎机中进行粉碎处理，过100目筛，得到厨房垃圾粉末；将上述得到的厨房垃圾粉末放入蒸汽笼中，向其中通入100℃的过热蒸汽，蒸制8min后，在18℃的室温条件下自然冷却1.5h；取10g续断、15g五倍子，12g龙葵和5g覆盆子放入气流粉碎机中进行微米级超细粉碎，得到10μm草药混合粉末，之后按照固液比为2∶9将草药混合粉末和蒸馏水放入直径为80cm的铁锅中，并将上述制得的冷却后的厨房垃圾粉末同时添加到铁锅中，搅拌均匀后盖上锅盖，并用棉被将其包裹住，在35℃条件下进行发酵10天；取500g新鲜蓝藻，在太阳光下暴晒3h，使其自然晾干，之后将晾干后的蓝藻放入粉碎机中进行粉碎处理，然后将粉碎后的蓝藻碎片移入发酵罐中，加入10g纤维素酶和2L蒸馏水，用搅拌棒均匀搅拌后，用薄膜将发酵罐口密封，在35℃下酶解24h，使蓝藻软化；将软化后的蓝藻放入上述的发酵锅里，用搅拌机在900r/min的转速下高速搅拌20min，之后升高温度至40℃，盖上锅盖和棉被继续发酵7天，得浆糊状混合物；将得到的浆糊状混合物放入鸡蛋保护盒模具中，之后移入恒温干燥器中，升温至130℃进行干燥处理，待其冷却之后，拆除模具，即得一种利用餐厨垃圾添加蓝藻纤维素制备的可降解性鸡蛋保护盒。
本实例方法独特新颖，使用时，取100枚鸡蛋分别依次放入本发明所制得的一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒中，之后再在上面盖上一个同样的鸡蛋保护盒，上下包裹住鸡蛋，使得鸡蛋在运输途中不易被摔坏，抗冲击压比较强，降低了60％的鸡蛋损坏率。
实例2
将8kg回收的厨房垃圾用弱碱废液进行搅拌清洗2次，之后均匀平铺在地面上，在太阳光下自然晒干后，放入粉碎机中进行粉碎处理，过130目筛，得到厨房垃圾粉末；将上述得到的厨房垃圾粉末放入蒸汽笼中，向其中通入130℃的过热蒸汽，蒸制12min后，在19℃的室温条件下自然冷却2h；取20g续断、18g五倍子，15g龙葵和8g覆盆子放入气流粉碎机中进行微米级超细粉碎，得到13μm草药混合粉末，之后按照固液比为2∶9将草药混合粉末和蒸馏水放入直径为90cm的铁锅中，并将上述制得的冷却后的厨房垃圾粉末同时添加到铁锅中，搅拌均匀后盖上锅盖，并用棉被将其包裹住，在40℃条件下进行发酵13天；取650g新鲜蓝藻，在太阳光下暴晒4h，使其自然晾干，之后将晾干后的蓝藻放入粉碎机中进行粉碎处理，然后将粉碎后的蓝藻碎片移入发酵罐中，加入13g纤维素酶和2.5L蒸馏水，用搅拌棒均匀搅拌后，用薄膜将发酵罐口密封，在40℃下酶解32h，使蓝藻软化；将软化后的蓝藻放入上述的发酵锅里，用搅拌机在1100r/min的转速下高速搅拌25min，之后升高温度至45℃，盖上锅盖和棉被继续发酵10天，得浆糊状混合物；将得到的浆糊状混合物放入鸡蛋保护盒模具中，之后移入恒温干燥器中，升温至140℃进行干燥处理，待其冷却之后，拆除模具，即得一种利用餐厨垃圾添加蓝藻纤维素制备的可降解性鸡蛋保护盒。
本实例方法独特新颖，使用时，取150枚鸡蛋分别依次放入本发明所制得的一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒中，之后再在上面盖上一个同样的鸡蛋保护盒，上下包裹住鸡蛋，使得鸡蛋在运输途中不易被摔坏，抗冲击压比较强，降低了65％的鸡蛋损坏率。
实例3
将10kg回收的厨房垃圾用弱碱废液进行搅拌清洗3次，之后均匀平铺在地面上，在太阳光下自然晒干后，放入粉碎机中进行粉碎处理，过150目筛，得到厨房垃圾粉末；将上述得到的厨房垃圾粉末放入蒸汽笼中，向其中通入150℃的过热蒸汽，蒸制15min后，在20℃的室温条件下自然冷却2.5h；取25g续断、20g五倍子，18g龙葵和10g覆盆子放入气流粉碎机中进行微米级超细粉碎，得到15μm草药混合粉末，之后按照固液比为2∶9将草药混合粉末和蒸馏水放入直径为100cm的铁锅中，并将上述制得的冷却后的厨房垃圾粉末同时添加到铁锅中，搅拌均匀后盖上锅盖，并用棉被将其包裹住，在45℃条件下进行发酵15天；取800g新鲜蓝藻，在太阳光下暴晒5h，使其自然晾干，之后将晾干后的蓝藻放入粉碎机中进行粉碎处理，然后将粉碎后的蓝藻碎片移入发酵罐中，加入15g纤维素酶和3L蒸馏水，用搅拌棒均匀搅拌后，用薄膜将发酵罐口密封，在45℃下酶解36h，使蓝藻软化；将软化后的蓝藻放入上述的发酵锅里，用搅拌机在1200r/min的转速下高速搅拌30min，之后升高温度至50℃，盖上锅盖和棉被继续发酵14天，得浆糊状混合物；将得到的浆糊状混合物放入鸡蛋保护盒模具中，之后移入恒温干燥器中，升温至150℃进行干燥处理，待其冷却之后，拆除模具，即得一种利用餐厨垃圾添加蓝藻纤维素制备的可降解性鸡蛋保护盒。
本实例方法独特新颖，使用时，取200枚鸡蛋分别依次放入本发明所制得的一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒中，之后再在上面盖上一个同样的鸡蛋保护盒，上下包裹住鸡蛋，使得鸡蛋在运输途中不易被摔坏，抗冲击压比较强，降低了70％的鸡蛋损坏率。
Claims (1)
1.一种餐厨垃圾添加蓝藻纤维素制备可降解性鸡蛋保护盒的方法，其特征在于具体操作步骤为：
（1）将5～10kg回收的厨房垃圾用弱碱废液进行搅拌清洗1～3次，之后均匀平铺在地面上，在太阳光下自然晒干后，放入粉碎机中进行粉碎处理，过100～150目筛，得到厨房垃圾粉末；
（2）将上述得到的厨房垃圾粉末放入蒸汽笼中，向其中通入100～150℃的过热蒸汽，蒸制8～15min后，在18～20℃的室温条件下自然冷却1.5～2.5h；
（3）取10～25g续断、15～20g五倍子，12～18g龙葵和5～10g覆盆子放入气流粉碎机中进行微米级超细粉碎，得到10～15μm草药混合粉末，之后按照固液比为2∶9将草药混合粉末和蒸馏水放入直径为80～100cm的铁锅中，并将上述制得的冷却后的厨房垃圾粉末同时添加到铁锅中，搅拌均匀后盖上锅盖，并用棉被将其包裹住，在35～45℃条件下进行发酵10～15天；
（4）取500～800g新鲜蓝藻，在太阳光下暴晒3～5h，使其自然晾干，之后将晾干后的蓝藻放入粉碎机中进行粉碎处理，然后将粉碎后的蓝藻碎片移入发酵罐中，加入10～15g纤维素酶和2～3L蒸馏水，用搅拌棒均匀搅拌后，用薄膜将发酵罐口密封，在35～45℃下酶解24～36h，使蓝藻软化；
（5）将软化后的蓝藻放入上述步骤（3）中的发酵锅里，用搅拌机在900～1200r/min的转速下高速搅拌20～30min，之后升高温度至40～50℃，盖上锅盖和棉被继续发酵7～14天，得浆糊状混合物；
（6）将得到的浆糊状混合物放入鸡蛋保护盒模具中，之后移入恒温干燥器中，升温至130～150℃进行干燥处理，待其冷却之后，拆除模具，即得一种利用餐厨垃圾添加蓝藻纤维素制备的可降解性鸡蛋保护盒。