CN105713575B - Anti-fog agent for wind-screen of automobile and preparation method thereof when a kind of long-acting - Google Patents
Anti-fog agent for wind-screen of automobile and preparation method thereof when a kind of long-acting Download PDFInfo
- Publication number
- CN105713575B CN105713575B CN201610208336.6A CN201610208336A CN105713575B CN 105713575 B CN105713575 B CN 105713575B CN 201610208336 A CN201610208336 A CN 201610208336A CN 105713575 B CN105713575 B CN 105713575B
- Authority
- CN
- China
- Prior art keywords
- modified
- automobile
- wind
- screen
- acting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention belongs to anti-fog agent for wind-screen of automobile preparing technical field, anti-fog agent for wind-screen of automobile and preparation method thereof when specially a kind of long-acting.The antifoggant includes the raw material of following weight/mass percentage composition:Modified manometer silicon dioxide colloidal sol 10 15%, modified polyacrylate solution 1 2%, cetomacrogol 1000 1 3%, OP 10 2 3%, lauryl sodium sulfate 0.5 1%, neopelex 0.5 1%, glycerine 8 10%, propane diols 5 7%, ethanol 15 20%, balance of water, gross mass percentage composition sum are 100%.Modified super hydrophilic nano silicon is employed in this product, its anti-fog effect is greatly enhanced.The preferable modified polypropene acid solution of adhesion is additionally used, super hydrophilic nano-particle and surface active agent composition can be made to be attached on without coming off on glass, so as to enhance the durability of antifogging product, 3 months anti-fog effects can be kept.
Description
Technical field
The invention belongs to anti-fog agent for wind-screen of automobile preparing technical field, when specially a kind of long-acting anti-fog agent for wind-screen of automobile and
Its preparation method.
Background technology
At present, with rapid economic development, the car ownership of China has broken through 100,000,000.Automobile is greatly facilitated
The life of people, but, it also brings a series of traffic safety hidden danger, wherein, into autumn and winter, the fog of vehicle glass
Have become a very important traffic safety problem.And anti-fog agent for wind-screen of automobile, it is mainly used in Automobile and outside car
Antifog work, the condensation that reduction glass, frosting cause because of moisture, reduces the generation of traffic accident.
Glass antidimmer on the market has a large amount in variety at present, is substantially based on organic solvent, common are second
Alcohol, silicone oil, add single surfactant and are made.The shortcoming of this kind of product is inflammable, explosive, particularly in automobile and need
Used in fireproof environment and dangerous big, high cost, it is most important that its antifog time is shorter, and the general antifog time does not surpass
Spend 2 weeks.
Therefore, anti-fog agent for wind-screen of automobile when developing a kind of efficient, long-acting has become the advanced subject of current development.
The content of the invention
The present invention is just being directed to above technical problem, there is provided anti-fog agent for wind-screen of automobile when a kind of long-acting.The vehicle glass is prevented
Mist agent has efficient, lasting anti-fog performance, and environmental protection.
The preparation method of anti-fog agent for wind-screen of automobile when another object of the present invention is to provide a kind of described long-acting.
Concrete technical scheme of the invention is as follows:
Anti-fog agent for wind-screen of automobile when a kind of long-acting, including following weight/mass percentage composition raw material:
In terms of weight/mass percentage composition, 20% nano silicon is contained in described modified manometer silicon dioxide colloidal sol.
The preparation method of anti-fog agent for wind-screen of automobile, comprises the following steps when a kind of long-acting:
(1) raw material, is weighed in proportion, at room temperature, first adds glycerine, propane diols, ethanol, OP-10, poly- second in a reservoir
Glycol and modified polyacrylate solution, then stir;
(2), again to lauryl sodium sulfate is added in the material stirred in container, neopelex changes
Property nano silicon dioxide sol, then water stir, that is, anti-fog agent for wind-screen of automobile when being obtained long-acting.
Described modified manometer silicon dioxide colloidal sol includes the raw material of following weight/mass percentage composition:
The preparation method of modified manometer silicon dioxide colloidal sol comprises the following steps:
(1) each raw material, is weighed in proportion, then in the 250ml there-necked flasks with thermometer and agitator, adds powder
The nano silicon and absolute ethyl alcohol of shape, after being stirred 10 minutes under conditions of 40 DEG C, add vinyl triethoxyl silicon
Oxygen alkane, is again stirring for 30 minutes;
(2), again to sequentially adding maleic anhydride in there-necked flask, acrylic acid, methacrylic acid, hydroxy-ethyl acrylate, fully
After stirring 10 minutes, dibenzoyl peroxide is added, be warming up to boiling;
(3), boiling reaction 3h, is incubated 30 minutes, adds polyvinyl alcohol and sorbierite, and stirring is to being completely dissolved.Make
It is standby to obtain modified manometer silicon dioxide colloidal sol.
Described modified polyacrylate solution is by the 8% of acrylic acid-maleic acid acid anhydride-methacrylic acid copolymer
Solution.The preparation method of modified polyacrylate solution is:In there-necked flask, acrylic acid 2g, maleic anhydride 3g, methyl-prop are added
Olefin(e) acid 3g, water 92g, potassium peroxydisulfate 0.5g, 3h is reacted in 85 DEG C, that is, modified polyacrylate solution is obtained, and is modified in the solution
Weight/mass percentage composition shared by polyacrylate is 8%, and the solution has good tack and film forming.
The positive effect of the present invention is embodied in:
(1), anti-fog duration can reach 3 months, be in all antifogging products the duration it is most long.Due to using
Be modified super hydrophilic nano silicon, greatly enhances its anti-fog effect.
(2), as a result of the preferable modified polypropene acid solution of adhesion, super hydrophilic nano-particle and surface can be made
Active agent component is attached on without coming off on glass, so as to more enhance the durability of antifogging product.Can keep preventing for 3 months
Fog effect, is that antifog persistence is best in all antifogging products.
(3), environmental protection of the present invention, pollution-free, easy to clean, it is corrosion-free to glass.
Specific embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, with reference to specific embodiment pair
The present invention is described in further detail, but this scope for being interpreted as above-mentioned theme of the invention should not be only limitted into following implementations
Example.
First, modified manometer silicon dioxide colloidal sol includes the raw material of following weight/mass percentage composition in following instance:
The preparation method of modified manometer silicon dioxide colloidal sol comprises the following steps:
(1) each raw material, is weighed in proportion, then in the 250ml there-necked flasks with thermometer and agitator, adds powder
The nano silicon and absolute ethyl alcohol of shape, after being stirred 10 minutes under conditions of 40 DEG C, add vinyl triethoxyl silicon
Oxygen alkane, is again stirring for 30 minutes;
(2), again to sequentially adding maleic anhydride in there-necked flask, acrylic acid, methacrylic acid, hydroxy-ethyl acrylate, fully
After stirring 10 minutes, dibenzoyl peroxide is added, be warming up to boiling;
(3), boiling reaction 3h, is incubated 30 minutes, adds polyvinyl alcohol and sorbierite, and stirring is to being completely dissolved.Make
It is standby to obtain modified manometer silicon dioxide colloidal sol.
Modified polyacrylate solution is formed by acrylic acid-maleic acid acid anhydride-methacrylic acid copolymer in following instance
8% solution.The preparation method of modified polyacrylate solution is:In there-necked flask, acrylic acid 2g, maleic anhydride are added
3g, methacrylic acid 3g, water 92g, potassium peroxydisulfate 0.5g react 3h in 85 DEG C, that is, modified polyacrylate solution is obtained.
Embodiment 1:
Described anti-fog agent for wind-screen of automobile, its raw material for including following weight/mass percentage composition:
Modified manometer silicon dioxide colloidal sol (20% liquid) refers to using the formula and preparation method of specific embodiment kind
Weight/mass percentage composition in the modified manometer silicon dioxide colloidal sol for preparing shared by modified manometer silicon dioxide is 20%.Below
It is same.
Described anti-fog agent for wind-screen of automobile its specific preparation process is:
(1) glycerine 8g, propane diols 5g, ethanol 15g, OP-10 emulsifying agent 2g, poly- second, at room temperature, are first added in a reservoir
Glycol 1g.Modified polyacrylate solution 1g, stirs
(2), again to addition lauryl sodium sulfate 0.5g, neopelex 0.5g, nanometer titanium dioxide in container
Ludox 10g, water 57g, then stirs, that is, glass antidimmer when being obtained long-acting.
(3) this product, is applied to glass surface with 2mL/m2, then the glass there is lasting anti-fog effect.
Embodiment 2:
Anti-fog agent for wind-screen of automobile when a kind of long-acting, its raw material for including following weight/mass percentage composition:
Gross mass percentage composition sum is 100%.Modified manometer silicon dioxide colloidal sol (20% liquid) refers to using specific
Modified manometer silicon dioxide institute in the modified manometer silicon dioxide colloidal sol that the formula and preparation method of implementation method kind are prepared
The weight/mass percentage composition for accounting for is 20%.
Preparation method in the example is identical with example 1.
Embodiment 3:
A kind of long-acting automobile glass antidimmer, its raw material for including following weight/mass percentage composition:
Modified manometer silicon dioxide colloidal sol (20% liquid) refers to using the formula and preparation method of specific embodiment kind
Weight/mass percentage composition in the modified manometer silicon dioxide colloidal sol for preparing shared by modified manometer silicon dioxide is 20%.
Preparation method in the example is with example 1.
Contrast experiment, influence experiment of the test modified manometer silicon dioxide in the antifoggant to anti-fog effect:
Based on embodiment 1, all parameters and step with it is consistent in embodiment 1, only change modified nano-silica
The addition of SiClx, influence of the measurement modified manometer silicon dioxide to anti-fog effect, design parameter is as shown in the table:
Table 1 adds influence of the modified manometer silicon dioxide to anti-fog effect
Add influence experiment of the modified polyacrylate solution to anti-fog effect:
Based on embodiment 1, all parameters and step with it is consistent in embodiment 1, only change modified polyacrylic acid
The addition of ester solution, influence of the measurement modified polyacrylate solution to anti-fog effect, design parameter is as shown in the table:
Table 2:Modified polyacrylate solution is added on antifog persistent influence
As seen from the above table, rational adding proportion can make antifog effect more longlasting.
Claims (4)
1. anti-fog agent for wind-screen of automobile when a kind of long-acting, it is characterised in that the raw material including following weight/mass percentage composition:
Modified manometer silicon dioxide colloidal sol 10-15%
Modified polyacrylate solution 1-2%
Cetomacrogol 1000 1-3%
OP-10 2-3%
Lauryl sodium sulfate 0.5-1%
Neopelex 0.5-1%
Glycerine 8-10%
Propane diols 5-7%
Ethanol 15-20%
Balance of water, gross mass percentage composition sum is 100%;
Described modified manometer silicon dioxide colloidal sol includes the raw material of following weight/mass percentage composition:
Nano silicon 18-25%
Maleic anhydride 0.5-1%
Acrylic acid 1-2%
Methacrylic acid 0.5-1%
Hydroxy-ethyl acrylate 0.5-1%
Vinyl triethoxyl siloxanes 0.2-0.5%
Polyvinyl alcohol 0.1-0.3%
Sorbierite 0.3-0.6%
Dibenzoyl peroxide 0.1%
Absolute ethyl alcohol surplus
Gross mass percentage composition sum is 100%;
The preparation method of wherein modified manometer silicon dioxide colloidal sol comprises the following steps:
(1) each raw material, is weighed in proportion, then in the 250ml there-necked flasks with thermometer and agitator, adds powder shaped
Nano silicon and absolute ethyl alcohol, under conditions of 40 DEG C after stirring 10 minutes, add vinyl triethoxyl silica
Alkane, is again stirring for 30 minutes;
(2), again to maleic anhydride is sequentially added in there-necked flask, acrylic acid, methacrylic acid, hydroxy-ethyl acrylate is sufficiently stirred for
After 10 minutes, dibenzoyl peroxide is added, be warming up to boiling;
(3), boiling reaction 3h, is incubated 30 minutes, adds polyvinyl alcohol and sorbierite, and stirring is to being completely dissolved;It is prepared into
To modified manometer silicon dioxide colloidal sol.
2. anti-fog agent for wind-screen of automobile when according to claim 1 long-acting, it is characterised in that:Described modified nano-silica
The weight/mass percentage composition of nano silicon is 20% in Ludox.
3. anti-fog agent for wind-screen of automobile when according to claim 1 long-acting, it is characterised in that:Described modified polyacrylate
Solution is formed by polyacrylic-maleic acid anhydride-methacrylic acid copolymer, the quality hundred wherein shared by modified polyacrylate
Content is divided to be 8%.
4. the preparation method of anti-fog agent for wind-screen of automobile when long-acting as described in any one claim in a kind of 1-3 such as claim,
It is characterized in that comprising the following steps:
(1) raw material, is weighed in proportion, at room temperature, first adds glycerine, propane diols, ethanol, OP-10, polyethylene glycol in a reservoir
With modified polyacrylate solution, then stir;
(2), again to lauryl sodium sulfate is added in the material stirred in container, neopelex is modified to receive
Rice silicon dioxide gel and water, then stir, that is, anti-fog agent for wind-screen of automobile when being obtained long-acting.