CN105713543B - A kind of good acrylate structural adhesive of impact resistance - Google Patents
A kind of good acrylate structural adhesive of impact resistance Download PDFInfo
- Publication number
- CN105713543B CN105713543B CN201610273007.XA CN201610273007A CN105713543B CN 105713543 B CN105713543 B CN 105713543B CN 201610273007 A CN201610273007 A CN 201610273007A CN 105713543 B CN105713543 B CN 105713543B
- Authority
- CN
- China
- Prior art keywords
- component
- structural adhesive
- acrylate
- kinds
- impact resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
Claims (8)
- A kind of 1. good acrylate structural adhesive of impact resistance, it is characterised in that its component by component A and B component by volume For 10:1 composition;Wherein described component A includes by weight percentage:Acrylate monomer 30~45%, modified urethane acrylate 10~20%, methacrylic acid 5~10%, toughness reinforcing filler 20~40%, accelerator 1~2% and stabilizer 0.1~0.2%;Described B component includes by weight percentage:Epoxy resin 25~30%, tackifying resin 10~15%, plasticizer 15 ~20%, curing agent 30~40% and filler 4~10%;Wherein, the acrylate monomer described in component A is methyl methacrylate, hydroxyethyl methacrylate or metering system One or more kinds of mixing of sour hydroxypropyl acrylate;Modified urethane acrylate described in component A is by TDI, hydrogenated bisphenol A, PTMG2000, hydroxyethyl methacrylate second Resin made from ester and hydroxy propyl methacrylate synthesis;Epoxy resin described in B component mixes for E-51 epoxy resin or the one or two kinds of of EP828 epoxy resin.
- 2. acrylate structural adhesive according to claim 1, it is characterised in that the toughness reinforcing filler described in component A is ABS, MBS or SBS one or more kinds of mixing.
- 3. acrylate structural adhesive according to claim 1, it is characterised in that the accelerator described in component A is triphen One or more kinds of mixing of base phosphine, N, N- dimethyl-p-toluidines or N, N- dimethyl ortho-aminotoluene.
- 4. acrylate structural adhesive according to claim 1, it is characterised in that the stabilizer described in component A is to benzene Diphenol, tetrasodium ethylenediamine tetraacetate are mixed above to one or both of naphthoquinones.
- 5. acrylate structural adhesive according to claim 1, it is characterised in that the tackifying resin described in B component is poly- One or two kinds of mixing of ethoxylated polyhydric alcohol or PEPA.
- 6. acrylate structural adhesive according to claim 1, it is characterised in that the plasticizer described in B component is benzene first One or two kinds of mixing of acid esters or phthalate.
- 7. acrylate structural adhesive according to claim 1, it is characterised in that the curing agent described in B component is peroxide Change one or two kinds of mixing of benzoyl or lauroyl peroxide.
- 8. acrylate structural adhesive according to claim 1, it is characterised in that the filler described in B component is calcium carbonate Or one or two kinds of mixing of silica flour.