CN105713335A - Nano modified high-impact-resistance ABS composite plastic - Google Patents
Nano modified high-impact-resistance ABS composite plastic Download PDFInfo
- Publication number
- CN105713335A CN105713335A CN201510594905.0A CN201510594905A CN105713335A CN 105713335 A CN105713335 A CN 105713335A CN 201510594905 A CN201510594905 A CN 201510594905A CN 105713335 A CN105713335 A CN 105713335A
- Authority
- CN
- China
- Prior art keywords
- composite plastic
- impact
- nano
- abs composite
- compatilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses nano modified high-impact-resistance ABS composite plastic, comprising the following components according to parts by weight: 100 parts of ABS, 15-30 parts of nano calcium carbonate, 0.5-1.5 parts of coupling agent, 0.3-1.0 part of surfactant, and 0.2-0.8 part of compatilizer. A preparation method of the nano modified high-impact-resistance ABS composite plastic comprises the following steps: proportionally weighing and mixing the ABS, the nano calcium carbonate, the coupling agent, the surfactant and the compatilizer, stirring well, and extruding with an extruder to obtain the nano modified high-impact-resistance ABS composite plastic. The nano calcium carbonate modified ABS resin has good impact resistance and is useful in the manufacture of automobile rear fenders, instrument panels, radio enclosures, air exhaust pipes, steering wheel speaker covers, grilles, rear guards, upper vent covers, wheel housings, louvers, supports, mirror frames and the like.
Description
Technical field
The present invention relates to a kind of nano modification high-impact ABS composite plastic, belong to modified plastics technical field.
Background technology
ABS resin is one of five big synthetic resin, its impact resistance, thermostability, lower temperature resistance, chemical proofing and excellent electrical properties, also there is the features such as easy processing, product size is stable, lustrous surface property is good, easy application, painted, it is also possible to carry out surface metallization, plating, welding, hot pressing and the secondary operations such as bonding.
The nono calcium carbonate modified ABS resin of the present invention has good shock resistance, can be used for manufacturing rear of vehicle mud plate, instrument board, radio reception hood, air exhaust duct, steering wheel horn cover, grid, rear backplate, upper vent flap, wheelhouse portions, shutter, support, picture frame etc., therefore the present invention's is necessary.
Summary of the invention
The present invention seeks to supplement prior art, and a kind of nano modification high-impact ABS composite plastic is provided.
To achieve these goals, technical scheme is as follows:
A kind of nano modification high-impact ABS composite plastic, it is characterized in that, in parts by weight, the one-tenth of following weight ratio it is grouped into: ABS100 part, nano-calcium carbonate 15-30 part, coupling agent 0.5-1.5 part, surfactant 0.3-1.0 part, compatilizer 0.2-0.8 part..
Described coupling agent is silanes or titanate ester.
Described surfactant is dodecylbenzene sodium sulfonate or quaternary ammonium salt.
Described compatilizer is acrylic type compatilizer.
The preparation method of nano modification high-impact ABS composite plastic, it is characterized in that, comprise the following steps: ABS, nano-calcium carbonate, coupling agent, surfactant, compatilizer example in mass ratio is weighed mixing, stir, then pass through extruder 180-190 DEG C of extrusion, prepare nano modification high-impact ABS composite plastic.
Beneficial effects of the present invention is as follows:
The nono calcium carbonate modified ABS resin of the present invention has good shock resistance, can be used for manufacturing rear of vehicle mud plate, instrument board, radio reception hood, air exhaust duct, steering wheel horn cover, grid, rear backplate, upper vent flap, wheelhouse portions, shutter, support, picture frame etc..
Detailed description of the invention
For the technological means making the present invention realize, creation characteristic, reach purpose and effect and be easy to understand, below in conjunction with specific embodiment, the present invention is expanded on further.
Embodiment 1:
A kind of nano modification high-impact ABS composite plastic, it is characterised in that in parts by weight, the one-tenth of following weight ratio be grouped into: ABS100 part, nano-calcium carbonate 15 parts, coupling agent 0.8 part, 0.8 part of surfactant, compatilizer 0.5 part.
Described coupling agent is titanate ester.
Described surfactant is dodecylbenzene sodium sulfonate.
Described compatilizer is acrylic type compatilizer.
The preparation method of nano modification high-impact ABS composite plastic, it is characterized in that, comprise the following steps: ABS, nano-calcium carbonate, coupling agent, surfactant, compatilizer example in mass ratio is weighed mixing, stir, then pass through extruder 180-190 DEG C of extrusion, prepare nano modification high-impact ABS composite plastic.
The nono calcium carbonate modified ABS resin of the present invention has good shock resistance, can be used for manufacturing rear of vehicle mud plate, instrument board, radio reception hood, air exhaust duct, steering wheel horn cover, grid, rear backplate, upper vent flap, wheelhouse portions, shutter, support, picture frame etc..
Embodiment 2:
A kind of nano modification high-impact ABS composite plastic, it is characterised in that in parts by weight, the one-tenth of following weight ratio be grouped into: ABS100 part, nano-calcium carbonate 20 parts, coupling agent 0.8 part, 0.6 part of surfactant, compatilizer 0.5 part..
Described coupling agent is silanes.
Described surfactant is dodecylbenzene sodium sulfonate.
Described compatilizer is acrylic type compatilizer.
The preparation method of nano modification high-impact ABS composite plastic, it is characterized in that, comprise the following steps: ABS, nano-calcium carbonate, coupling agent, surfactant, compatilizer example in mass ratio is weighed mixing, stir, then pass through extruder 180-190 DEG C of extrusion, prepare nano modification high-impact ABS composite plastic.
The nono calcium carbonate modified ABS resin of the present invention has good shock resistance, can be used for manufacturing rear of vehicle mud plate, instrument board, radio reception hood, air exhaust duct, steering wheel horn cover, grid, rear backplate, upper vent flap, wheelhouse portions, shutter, support, picture frame etc..
Embodiment 3:
A kind of nano modification high-impact ABS composite plastic, it is characterised in that in parts by weight, the one-tenth of following weight ratio be grouped into: ABS100 part, nano-calcium carbonate 25 parts, coupling agent 1.2 parts, 0.5 part of surfactant, compatilizer 0.5 part.
Described coupling agent is titanate ester.
Described surfactant is dodecylbenzene sodium sulfonate.
Described compatilizer is acrylic type compatilizer.
The preparation method of nano modification high-impact ABS composite plastic, it is characterized in that, comprise the following steps: ABS, nano-calcium carbonate, coupling agent, surfactant, compatilizer example in mass ratio is weighed mixing, stir, then pass through extruder 180-190 DEG C of extrusion, prepare nano modification high-impact ABS composite plastic.
The nono calcium carbonate modified ABS resin of the present invention has good shock resistance, can be used for manufacturing rear of vehicle mud plate, instrument board, radio reception hood, air exhaust duct, steering wheel horn cover, grid, rear backplate, upper vent flap, wheelhouse portions, shutter, support, picture frame etc..
The ultimate principle of the present invention and principal character and advantages of the present invention have more than been shown and described.Skilled person will appreciate that of the industry; the present invention is not restricted to the described embodiments; described in above-described embodiment and description is that principles of the invention is described; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements both fall within the claimed scope of the invention.Claimed scope is defined by appending claims and equivalent thereof.
Claims (5)
1. a nano modification high-impact ABS composite plastic, it is characterized in that, in parts by weight, the one-tenth of following weight ratio it is grouped into: ABS100 part, nano-calcium carbonate 15-30 part, coupling agent 0.5-1.5 part, surfactant 0.3-1.0 part, compatilizer 0.2-0.8 part.
2. nano modification high-impact ABS composite plastic according to claim 1, it is characterised in that described coupling agent is silanes or titanate ester.
3. nano modification high-impact ABS composite plastic according to claim 1, it is characterised in that described surfactant is dodecylbenzene sodium sulfonate or quaternary ammonium salt.
4. nano modification high-impact ABS composite plastic according to claim 1, it is characterised in that described compatilizer is acrylic type compatilizer.
5. the preparation method of a nano modification high-impact ABS composite plastic as claimed in claim 1, it is characterized in that, comprise the following steps: ABS, nano-calcium carbonate, coupling agent, surfactant, compatilizer example in mass ratio is weighed mixing, stir, then pass through extruder 180-190 DEG C of extrusion, prepare nano modification high-impact ABS composite plastic.