CN105694293A - Environment-friendly plastic composition for cables - Google Patents
Environment-friendly plastic composition for cables Download PDFInfo
- Publication number
- CN105694293A CN105694293A CN201610213684.2A CN201610213684A CN105694293A CN 105694293 A CN105694293 A CN 105694293A CN 201610213684 A CN201610213684 A CN 201610213684A CN 105694293 A CN105694293 A CN 105694293A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- filler
- plastics composite
- friendly cable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environment-friendly plastic composition for cables. The plastic composition comprises the following components in parts by weight: 100 parts of polyvinyl chloride powder, 35-45 parts of trioctyl trimellitate, 9-13 parts of chlorinated paraffin 70, 3-5 parts of filler, 20-30 parts of nitrile-butadiene rubber, 10-12 parts of calcium carbonate and 0.5-1 part of stearate. The environment-friendly plastic composition for cables adopts environment-friendly raw materials which have wide sources, can not generate toxic gas, wastewater or other harmful substances in the production process, does not influence good health of the operating personnel, can effectively protect the environment, and is free from the restriction of the regions.
Description
Technical field
The present invention relates to modified plastics plastic cement field, particularly relate to a kind of environment-friendly cable plastics composite。
Background technology
Plastics are mainly made up of synthetic resin, which determine plastic material key property。Electric wire common plastics has polyethylene, crosslinked polyethylene, polrvinyl chloride, polypropylene, polyolefin, fluoroplastics, nylon etc.。Polrvinyl chloride has good physical and mechanical property and excellent processing performance, is the 20th century maximum plastics of consumption, is also predominating insulation and the sheath material of low tension wire cable。Existing electric wire plastic raw materials is toxic, can produce the harmful substance such as poison, waste water in process of production, pollute the environment, and destroys health。
Summary of the invention
The technical problem that present invention mainly solves is to provide a kind of environment-friendly cable plastics composite, protects environment, to human body non-hazardous。
For solving above-mentioned technical problem, the technical scheme that the present invention adopts is: provide a kind of environment-friendly cable plastics composite, including component have polyvinyl chloride powder, trioctyl trimellitate (TOTM), chlorinated paraffin 70, filler, nitrile rubber, calcium carbonate and hard acid ester, described environment-friendly cable plastics composite with parts by weight, including component have: polrvinyl chloride 100 parts, trioctyl trimellitate (TOTM) 35-45 part, chlorinated paraffin 709-13 part, filler 3-5 part, nitrile rubber 20-30 part, calcium carbonate 10-12 part, hard acid ester 0.5-1 part。
In a preferred embodiment of the present invention, the molecular weight of described chlorinated paraffin 70 is 1000-1200。
In a preferred embodiment of the present invention, described filler is one or more in Kaolin, kieselguhr, Pulvis Talci。
In a preferred embodiment of the present invention, described environment-friendly cable plastics composite with parts by weight, including component have: polrvinyl chloride 100 parts, trioctyl trimellitate (TOTM) 40 parts, chlorinated paraffin 7011 parts, filler 4 parts, nitrile rubber 25 parts, calcium carbonate 11 parts, hard acid ester 0.7 part。
The invention has the beneficial effects as follows: the environment-friendly cable plastics composite of the present invention, selection is feature of environmental protection raw material, wide material sources; the harmful substance such as poison, waste water will not be produced in process of production; healthy nothing impact on operator, it is possible to effectively protect environment, without geographical restrictions。
Detailed description of the invention
Technical scheme in the embodiment of the present invention will be clearly and completely described below, it is clear that described embodiment is only a part of embodiment of the present invention, rather than whole embodiments。Based on the embodiment in the present invention, all other embodiments that those of ordinary skill in the art obtain under not making creative work premise, broadly fall into the scope of protection of the invention。
Embodiment one:
A kind of environment-friendly cable plastics composite is provided, including component have polyvinyl chloride powder, trioctyl trimellitate (TOTM), chlorinated paraffin 70, filler, nitrile rubber, calcium carbonate and hard acid ester, described environment-friendly cable plastics composite with parts by weight, including component have: polrvinyl chloride 100 parts, trioctyl trimellitate (TOTM) 40 parts, chlorinated paraffin 7011 parts, filler 4 parts, nitrile rubber 25 parts, calcium carbonate 11 parts, hard acid ester 0.7 part。The molecular weight of described chlorinated paraffin 70 is 1100。Described filler is Kaolin and kieselguhr mixture。
Embodiment two:
A kind of environment-friendly cable plastics composite is provided, including component have polyvinyl chloride powder, trioctyl trimellitate (TOTM), chlorinated paraffin 70, filler, nitrile rubber, calcium carbonate and hard acid ester, described environment-friendly cable plastics composite with parts by weight, including component have: polrvinyl chloride 100 parts, trioctyl trimellitate (TOTM) 35 parts, chlorinated paraffin 7013 parts, filler 3 parts, nitrile rubber 30 parts, calcium carbonate 10 parts, hard acid ester 0.5 part。The molecular weight of described chlorinated paraffin 70 is 1000。Described filler is Kaolin and talc mixture。
Embodiment three:
A kind of environment-friendly cable plastics composite is provided, including component have polyvinyl chloride powder, trioctyl trimellitate (TOTM), chlorinated paraffin 70, filler, nitrile rubber, calcium carbonate and hard acid ester, described environment-friendly cable plastics composite with parts by weight, including component have: polrvinyl chloride 100 parts, trioctyl trimellitate (TOTM) 45 parts, chlorinated paraffin 709 parts, filler 5 parts, nitrile rubber 20 parts, calcium carbonate 12 parts, hard acid ester 1 part。The molecular weight of described chlorinated paraffin 70 is 1200。Described filler is kieselguhr and talc mixture。
The invention has the beneficial effects as follows: what described environment-friendly cable plastics composite was selected is feature of environmental protection raw material; wide material sources, will not produce the harmful substance such as poison, waste water in process of production, the healthy nothing impact on operator; can effectively protect environment, without geographical restrictions
What one, described environment-friendly cable plastics composite was selected is feature of environmental protection raw material, wide material sources, it is possible to effectively protect environment, without geographical restrictions；
Two, described environment-friendly cable plastics composite will not produce the harmful substance such as poison, waste water in process of production, the healthy nothing impact on operator。
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every equivalent structure utilizing description of the present invention to make or equivalence flow process conversion; or directly or indirectly it is used in other relevant technical field, all in like manner include in the scope of patent protection of the present invention。
Claims (4)
1. an environment-friendly cable plastics composite, it is characterized in that, including component have polyvinyl chloride powder, trioctyl trimellitate (TOTM), chlorinated paraffin 70, filler, nitrile rubber, calcium carbonate and hard acid ester, described environment-friendly cable plastics composite with parts by weight, including component have: polrvinyl chloride 100 parts, trioctyl trimellitate (TOTM) 35-45 part, chlorinated paraffin 709-13 part, filler 3-5 part, nitrile rubber 20-30 part, calcium carbonate 10-12 part, hard acid ester 0.5-1 part。
2. environment-friendly cable plastics composite according to claim 1, it is characterised in that the molecular weight of described chlorinated paraffin 70 is 1000-1200。
3. environment-friendly cable plastics composite according to claim 1, it is characterised in that described filler is one or more in Kaolin, kieselguhr, Pulvis Talci。
4. environment-friendly cable plastics composite according to claim 1, it is characterized in that, described environment-friendly cable plastics composite with parts by weight, including component have: polrvinyl chloride 100 parts, trioctyl trimellitate (TOTM) 40 parts, chlorinated paraffin 7011 parts, filler 4 parts, nitrile rubber 25 parts, calcium carbonate 11 parts, hard acid ester 0.7 part。