CN105679398A - Macromolecule electric power compound grease - Google Patents
Macromolecule electric power compound grease Download PDFInfo
- Publication number
- CN105679398A CN105679398A CN201610107789.XA CN201610107789A CN105679398A CN 105679398 A CN105679398 A CN 105679398A CN 201610107789 A CN201610107789 A CN 201610107789A CN 105679398 A CN105679398 A CN 105679398A
- Authority
- CN
- China
- Prior art keywords
- parts
- electric power
- macromolecule
- compound grease
- stearate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses macromolecule electric power compound grease, belonging to the technical field of power industry and solving the problems of poor high-temperature performance, easiness in flowing in a high temperature and easiness in crack in a low temperature of existing electric power compound grease. The macromolecule electric power compound grease comprises the following constituents based on weight: 200-300 parts of base oil, 40-60 parts of stearate, 10-20 parts of 12-hydroxystearic acid, 2-3 parts of amination bentonite, 40-50 parts of di-iso-octyl sebacate, 0.5-1 part of superfine graphite powder, 1-2 parts of zinc dimethyldithiocarbamate, 0.1-0.2 part of butylated hydroxytoluene, 2-5 parts of dodecencylsuccinic acid, 3-6 parts of zinc naphthenate, 0.1-0.3 part of diphenylamine, 1-3 parts of tricresyl phosphate and 0.6-1.3 parts of conductive polymer. The macromolecule electric power compound grease can be widely used for a substation and a power distribution station, and the running safety of a power grid is greatly improved.
Description
Technical field
The present invention relates to a kind of macromolecule electric force compounded grease, belong to power industry technologies field.
Background technology
Electric force compounded grease, also known as conductive paste, is the neutral conductive dressing that a kind of electrical contact performance is good. it is applicable to high and low voltage electrical equipment busbar shiplap joint place's contact surface and various electrical connector place, contact resistance can be made to be decreased obviously, thus greatly reducing electric energy loss. therefore electric force compounded grease can be widely applied to electric substation, bus in distribution substation and bus, on the contact surface of bus and the sub-junction of appliance terminal and the contact surface of switch contact, identical and different metal materials electric conductor (copper and copper, copper and aluminum, aluminum and aluminum) connection also can use, replace and be better than being fastenedly connected contact surface ward off stannum, silver plating process, can effectively reduce contact resistance, thus reducing temperature rise, improve the purpose of bus junction electric conductivity, enhance the safety of operation of power networks, save substantial amounts of electric energy loss, the face that also can avoid contact with produces electrochemical corrosion.
Summary of the invention
It is an object of the invention to provide a kind of macromolecule electric force compounded grease, have high temperature resistant, antioxidation, anticorrosion, the effect such as antirust, and physicochemical property is stable, high temperature does not trickle, low temperature does not chap.
Described macromolecule electric force compounded grease, is made up of the raw material of following weight portion:
Base oil 200-300 part, stearate 40-60 part, 12-hydroxyl stearate 10-20 part, amination bentonite 2-3 part, Plexol 201 40-50 part, superfine graphite powder 0.5-1 part, PZ 1-2 part, ditertbutylparacresol 0.1-0.2 part, dodecenylsuccinic acid 2-5 part, zinc naphthenate 3-6 part, diphenylamines 0.1-0.3 part, tricresyl phosphate 1-3 part, conducting polymer 0.6-1.3 part.
Preferred macromolecule electric force compounded grease, is made up of the raw material of following weight portion:
Base oil 265 parts, stearate 56 parts, 12-hydroxyl stearate 14 parts, amination bentonite 2.5 parts, Plexol 201 45 parts, 0.8 part of superfine graphite powder, PZ 1.5 parts, ditertbutylparacresol 0.15 part, dodecenylsuccinic acid 4 parts, zinc naphthenate 5 parts, diphenylamines 0.2 part, tricresyl phosphate 2 parts, conducting polymer 1 part.
Described conducting polymer is the one in p-methyl benzenesulfonic acid doped conductive polyaniline, DBSA doped conductive polyaniline.
Described base oil viscosity under 100 DEG C of conditions is 6-36mm2/s。
Compared with prior art, the invention has the beneficial effects as follows:
Macromolecule electric force compounded grease of the present invention has high temperature resistant, low temperature resistant, antioxidation, anticorrosion, the effect such as antirust, product adhesive force of the present invention is strong, high temperature does not trickle, low temperature does not chap, physicochemical property is stable, dropping point is high, still can keep good thixotropy when temperature reaches 330 DEG C, there is original shape, and do not trickle. The present invention has high conduction performance, can effectively reduce contact resistance more than 90%, reduces temperature rise more than 80%, considerably reduces electric energy loss, and long product lifecycle, can effectively reduce use cost. The composite can be widely applied to electric substation and distribution substation, greatly improve the safety of operation of power networks.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention will be further described.
Embodiment 1
Described macromolecule electric force compounded grease, is made up of the raw material of following weight portion:
Base oil 200 parts, stearate 40 parts, 12-hydroxyl stearate 10 parts, amination bentonite 2 parts, Plexol 201 40 parts, 0.5 part of superfine graphite powder, PZ 1 part, ditertbutylparacresol 0.1 part, dodecenylsuccinic acid 2 parts, zinc naphthenate 3 parts, diphenylamines 0.1 part, tricresyl phosphate 1 part, DBSA doped conductive polyaniline 0.6 part.
Described base oil viscosity under 100 DEG C of conditions is 6mm2/s
Embodiment 2
Described macromolecule electric force compounded grease, is made up of the raw material of following weight portion:
Base oil 300 parts, stearate 60 parts, 12-hydroxyl stearate 20 parts, amination bentonite 3 parts, Plexol 201 50 parts, 1 part of superfine graphite powder, PZ 2 parts, ditertbutylparacresol 0.2 part, dodecenylsuccinic acid 5 parts, zinc naphthenate 6 parts, diphenylamines 0.3 part, tricresyl phosphate 3 parts, DBSA doped conductive polyaniline 1.3 parts.
Described base oil viscosity under 100 DEG C of conditions is 36mm2/s
Embodiment 3
Described macromolecule electric force compounded grease, is made up of the raw material of following weight portion:
Base oil 265 parts, stearate 56 parts, 12-hydroxyl stearate 14 parts, amination bentonite 2.5 parts, Plexol 201 45 parts, 0.8 part of superfine graphite powder, PZ 1.5 parts, ditertbutylparacresol 0.15 part, dodecenylsuccinic acid 4 parts, zinc naphthenate 5 parts, diphenylamines 0.2 part, tricresyl phosphate 2 parts, p-methyl benzenesulfonic acid doped conductive polyaniline 1 part.
Described base oil viscosity under 100 DEG C of conditions is 22mm2/s。
Claims (4)
1. a macromolecule electric force compounded grease, it is characterised in that be made up of the raw material of following weight portion:
Base oil 200-300 part, stearate 40-60 part, 12-hydroxyl stearate 10-20 part, amination bentonite 2-3 part, Plexol 201 40-50 part, superfine graphite powder 0.5-1 part, PZ 1-2 part, ditertbutylparacresol 0.1-0.2 part, dodecenylsuccinic acid 2-5 part, zinc naphthenate 3-6 part, diphenylamines 0.1-0.3 part, tricresyl phosphate 1-3 part, conducting polymer 0.6-1.3 part.
2. macromolecule electric force compounded grease according to claim 1, it is characterised in that be made up of the raw material of following weight portion:
Base oil 265 parts, stearate 56 parts, 12-hydroxyl stearate 14 parts, amination bentonite 2.5 parts, Plexol 201 45 parts, 0.8 part of superfine graphite powder, PZ 1.5 parts, ditertbutylparacresol 0.15 part, dodecenylsuccinic acid 4 parts, zinc naphthenate 5 parts, diphenylamines 0.2 part, tricresyl phosphate 2 parts, conducting polymer 1 part.
3. macromolecule electric force compounded grease according to claim 1 and 2, it is characterised in that: described conducting polymer is the one in p-methyl benzenesulfonic acid doped conductive polyaniline, DBSA doped conductive polyaniline.
4. macromolecule electric force compounded grease according to claim 3, it is characterised in that: described base oil viscosity under 100 DEG C of conditions is 6-36mm2/s。