CN105672041A - Olive cellulose paper and preparation method thereof - Google Patents
Olive cellulose paper and preparation method thereof Download PDFInfo
- Publication number
- CN105672041A CN105672041A CN201510241993.6A CN201510241993A CN105672041A CN 105672041 A CN105672041 A CN 105672041A CN 201510241993 A CN201510241993 A CN 201510241993A CN 105672041 A CN105672041 A CN 105672041A
- Authority
- CN
- China
- Prior art keywords
- component
- paper
- temperature
- olive cellulose
- components
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides olive cellulose paper and a preparation method thereof. The olive cellulose paper is composed of a component A and a component B. The component A is composed of the olive cellulose, water and rosin; and the component B is composed of polyethylene oxide, paraffin, rosin, an emulsifier OP-10, potassium hydroxide and water. The preparation method includes the following steps: 1) placing the components of the component A in a mixing container, stirring and heating the components to 90-100 DEG C, and at the temperature, repeatedly stirring the components for 30-40 min to prepare uniformly-mixed slurry; 2) reducing the temperature of the slurry to 10-20 DEG C, and feeding the slurry to a fourdrinier wire shaping board being 30-40 DEG C in drying temperature through a metering pump to prepare initially-shaped paper; 3) placing the components of the component B in the mixing container, stirring and heating the components to 80-100 DEG C, and at the temperature, repeatedly stirring the components for 20-30 min to prepare transparent glue; and 4) reducing the temperature of the transparent glue to 20-30 DEG C, uniformly spray-coating the initially-shaped paper with the glue with a spray-coating machine to form a glue layer being 0.04-0.06 mm in thickness on the surface of the paper to prepare the olive cellulose paper.
Description
Technical field
The present invention relates to a kind of working and studying paper using with health role, particularly relate to a kind of working and studying olive cellulose paper with health role and preparation method thereof.
Background technology
Paper is that people learn indispensable apparatus in office. But the paper that people use now can give off substantial amounts of waste material in producing preparation process, and environment causes great pollution.
Because the defect that above-mentioned existing study paper in the office exists, the present inventor is based on being engaged in practical experience and the Professional knowledge that this type of product design manufacture is enriched for many years, and coordinate the utilization of scientific principle, actively in addition research and innovation, to founding olive cellulose paper of a kind of new releasable clean air, antiviral, uvioresistant material, the discharge of preparation process no waste mine and preparation method thereof, general existing study paper in the office and preparation method thereof can be improved so that it is have more practicality. Through constantly research, design, and after repeatedly studying sample and improving, finally create the present invention having practical value.
Summary of the invention
Present invention is primarily targeted at, overcome the defect of prior art, and a kind of new releasable clean air, antiviral, uvioresistant material, safe preparation process environmental protection be provided, be unlikely to deform, the olive cellulose paper of variable color and preparation method thereof.
The object of the invention to solve the technical problems realizes by the following technical solutions. According to a kind of olive cellulose paper that the present invention proposes, it is made up of by weight component A and component B, wherein: described component A is made up of olive cellulose 12-14 part, water 100-120 part and Colophonium 7-9 part; Described component B is made up of oxidic polyethylene 15-17 part, paraffin 10-12 part, Colophonium 3-4 part, emulsifier op-10 1-1.4 part, potassium hydroxide 1-1.2 part and water 100-120 part.
The object of the invention to solve the technical problems also realizes by the following technical solutions.According to a kind of method preparing olive cellulose paper that the present invention proposes, comprise the steps of
1) each constituent of component A is placed in mixing container, is stirred and heated to 90-100 DEG C, repeatedly stir 30-40 minute at this temperature, make mixed uniformly slurry;
2) above-mentioned slurry temperature is reduced to 10-20 DEG C, then utilizes dosing pump to be conveyed in the fourdrinier forming plate that baking temperature is 30-40 DEG C, make the paper of just one-step forming;
3) each constituent of component B being placed in mixing container, be stirred and heated to 80-100 DEG C, stirring makes it be sufficiently mixed for 20-30 minute repeatedly at this temperature, makes transparent adhesive tape;
4) temperature of above-mentioned transparent adhesive tape is reduced to 20-30 DEG C, uses flush coater even application to the paper of above-mentioned just one-step forming, form the thick glue-line of 0.04-0.06mm on its surface, namely make desired paper.
The present invention compared with prior art has clear advantage and beneficial effect. By technique scheme, the present invention a kind of olive cellulose paper and preparation method thereof can reach suitable technological progress and practicality, and there is the extensive value in industry, its at least have the advantage that preparation method of the present invention have that technique is simple, with low cost, safety and environmental protection, the feature such as good in economic efficiency, product one olive cellulose paper of the present invention, its color and luster, smoothness and opacity are suitable, and under the high temperature of 200 DEG C, paper is indeformable, invariant color. And its olive cellulose contained can be contacted by finger, by finger skin microcirculation by capillary absorbance, and containing many unsaturated fatty acids in its raw material olive cellulose, it can discharge substantial amounts of physical property biological activity effective ingredient in the environment of the mental activities such as people's study and work, there is the material of the effects such as clean air, antiviral, uvioresistant, antioxidation, elimination free radical, human body is had good health-care effect.
Detailed description of the invention
For further setting forth that the present invention reaches the technological means that predetermined goal of the invention is taked, preferred embodiments below, its detailed description of the invention of a kind of olive cellulose paper and preparation method thereof proposed according to the present invention is described in detail as after.
Embodiment 1
A kind of olive cellulose paper, it is made up of by weight component A and component B, wherein: described component A is made up of olive cellulose 12g, water 100g and Colophonium 7g; Described component B is made up of oxidic polyethylene 15g, paraffin 10g, Colophonium 3g, emulsifier op-10 1g, potassium hydroxide 1g and water 100g. The method of the olive cellulose paper that preparation is described, comprises the steps of
1) each constituent of component A is placed in mixing container, is stirred and heated to 90 DEG C, repeatedly stir 30 minutes at this temperature, make mixed uniformly slurry;
2) above-mentioned slurry temperature is reduced to 10 DEG C, in then utilize dosing pump to be conveyed to fourdrinier forming plate that baking temperature is 30 DEG C, makes the paper of just one-step forming;
3) each constituent of component B being placed in mixing container, be stirred and heated to 80 DEG C, stirring makes it be sufficiently mixed in 20 minutes repeatedly at this temperature, makes transparent adhesive tape;
4) temperature of above-mentioned transparent adhesive tape is reduced to 20 DEG C, uses flush coater even application to the paper of above-mentioned just one-step forming, form the thick glue-line of 0.04mm on its surface, namely make desired paper.
Embodiment 2
A kind of olive cellulose paper, it is made up of by weight component A and component B, wherein: described component A is made up of olive cellulose 13g, water 110g and Colophonium 8g;Described component B is made up of oxidic polyethylene 16g, paraffin 11g, Colophonium 3.5g, emulsifier op-10 1.2g, potassium hydroxide 1.1g and water 110g.
The method of the olive cellulose paper that preparation is described, comprises the steps of
1) each constituent of component A is placed in mixing container, is stirred and heated to 95 DEG C, repeatedly stir 35 minutes at this temperature, make mixed uniformly slurry;
2) above-mentioned slurry temperature is reduced to 15 DEG C, in then utilize dosing pump to be conveyed to fourdrinier forming plate that baking temperature is 35 DEG C, makes the paper of just one-step forming;
3) each constituent of component B being placed in mixing container, be stirred and heated to 90 DEG C, stirring makes it be sufficiently mixed in 25 minutes repeatedly at this temperature, makes transparent adhesive tape;
4) temperature of above-mentioned transparent adhesive tape is reduced to 25 DEG C, uses flush coater even application to the paper of above-mentioned just one-step forming, form the thick glue-line of 0.05mm on its surface, namely make desired paper.
Embodiment 3
A kind of olive cellulose paper, it is made up of by weight component A and component B, wherein: described component A is made up of olive cellulose 14g, water 120g and Colophonium 9g; Described component B is made up of oxidic polyethylene 17g, paraffin 12g, Colophonium 4g, emulsifier op-10 1.4g, potassium hydroxide 1.2g and water 120g.
The method of the olive cellulose paper that preparation is described, comprises the steps of
1) each constituent of component A is placed in mixing container, is stirred and heated to 100 DEG C, repeatedly stir 40 minutes at this temperature, make mixed uniformly slurry;
2) above-mentioned slurry temperature is reduced to 20 DEG C, in then utilize dosing pump to be conveyed to fourdrinier forming plate that baking temperature is 40 DEG C, makes the paper of just one-step forming;
3) each constituent of component B being placed in mixing container, be stirred and heated to 100 DEG C, stirring makes it be sufficiently mixed in 30 minutes repeatedly at this temperature, makes transparent adhesive tape;
4) temperature of above-mentioned transparent adhesive tape is reduced to 30 DEG C, uses flush coater even application to the paper of above-mentioned just one-step forming, form the thick glue-line of 0.06mm on its surface, namely make desired paper.
The above, it it is only presently preferred embodiments of the present invention, not the present invention is done any pro forma restriction, although the present invention is disclosed above with preferred embodiment, but it is not limited to the present invention, any those skilled in the art, without departing within the scope of technical solution of the present invention, when the technology contents of available the disclosure above makes a little change or is modified to the Equivalent embodiments of equivalent variations, in every case it is the content without departing from technical solution of the present invention, the technical spirit of the foundation present invention is to any simple modification made for any of the above embodiments, equivalent variations and modification, all still fall within the scope of technical solution of the present invention.
Claims (2)
1. an olive cellulose paper, it is characterised in that it is made up of by weight component A and component B, wherein:
Described component A is made up of olive cellulose 12-14 part, water 100-120 part and Colophonium 7-9 part;
Described component B is made up of oxidic polyethylene 15-17 part, paraffin 10-12 part, Colophonium 3-4 part, emulsifier op-10 1-1.4 part, potassium hydroxide 1-1.2 part and water 100-120 part.
2. the method preparing olive cellulose paper described in claim 1, raw material calculates by weight, it is characterised in that comprise the steps of
1) each constituent of component A is placed in mixing container, is stirred and heated to 90-100 DEG C, repeatedly stir 30-40 minute at this temperature, make mixed uniformly slurry;
2) above-mentioned slurry temperature is reduced to 10-20 DEG C, then utilizes dosing pump to be conveyed in the fourdrinier forming plate that baking temperature is 30-40 DEG C, make the paper of just one-step forming;
3) each constituent of component B being placed in mixing container, be stirred and heated to 80-100 DEG C, stirring makes it be sufficiently mixed for 20-30 minute repeatedly at this temperature, makes transparent adhesive tape;
4) temperature of above-mentioned transparent adhesive tape is reduced to 20-30 DEG C, uses flush coater even application to the paper of above-mentioned just one-step forming, form the thick glue-line of 0.04-0.06mm on its surface, namely make desired paper.