CN105669149A - Waterproof anti-cracking mortar - Google Patents
Waterproof anti-cracking mortar Download PDFInfo
- Publication number
- CN105669149A CN105669149A CN201410672317.XA CN201410672317A CN105669149A CN 105669149 A CN105669149 A CN 105669149A CN 201410672317 A CN201410672317 A CN 201410672317A CN 105669149 A CN105669149 A CN 105669149A
- Authority
- CN
- China
- Prior art keywords
- kilograms
- waterproof
- organic additive
- mortar
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a waterproof anti-cracking mortar which is prepared from an inorganic cementing material, an organic additive and 180-mesh fine sand, and includes the following components, by weight, 52-65% of the inorganic cementing material, 25-55% of the fine sand in 180-200 meshes, 6-10% of an organic additive, 5-12% of a waterproof powder and the balanced being water. The inorganic cementing material is composed an active blending material and an alkaline activator. The organic additive is a mixture composed of cellulose ether, redispersible latex powder, wood fibers and polypropylene short fibers. The mortar is produced by metering the raw materials according to the preset proportion, blending the raw materials and packaging the product. The waterproof anti-cracking mortar is low in production energy consumption, is low in cost, and is good in waterproof and anti-cracking performance.
Description
Technical field
The present invention relates to a kind of inside and outside wall thermal insulation waterproof anti-crack mortar.
Technical background
Waterproof anti-crack mortar is the satisfied certain deformation of energy and indehiscent mortar that antimitotic agent, waterproof powder, cement and the sand made with polymer emulsion and additive is made by a certain percentage, it solving a great problem-light heat insulation aspect problem of Cracking on the circle of puzzlement building always, it is a kind of tension degree high-quality environment-friendly materials high, easily construction anti-freezing. Flyash etc. are as large industrial residue, and its process and comprehensive utilization have been accompanied and paid close attention to by countries in the world. What produce anticracking grout at present is mainly composed of cement, and cement is high pollution high energy consumption industry.
Summary of the invention
It is an object of the invention to provide a kind of energy consumption low, cost is low, and waterproof is good, Binder Materials-waterproof anti-crack mortar that crack resistance is good.
It is an object of the invention to be realized by following proposal: it is made up of inorganic coagulation material, organic additive, 180 order fine sands, the weight proportion of each component is: inorganic coagulation material 52%～65%, 180-200 order fine sand 25%～55%, organic additive 6%～10%, waterproof powder 5%-12%, surplus is water, described inorganic coagulation material is active admixture, alkali-activator composition, and described organic additive is the mixture of cellulose ether, re-dispersible glue powder, wood fibre polypropene staple.
The production method of waterproof anti-crack mortar, by each raw material by preset blending ratio metering, then by all raw material mix homogeneously, packaging.
The waterproof anti-crack mortar energy consumption of the present invention is low, and cost is low, and the good water proofing property of crack resistance is high.
Detailed description of the invention
Embodiment 1:
Second class powered coal ash 160 kilograms, slag powders 160 kilograms, 24 kilograms of Calx, desulfurated plaster 16 kilograms, 42.5 number cement 40 kilograms, Matrii Sulfas Exsiccatus 12 kilograms, 70-140 order fine sand 600 kilograms, the cellulose ether of 100000 molecular weight 2 kilograms, re-dispersible glue powder 25 kilograms, wood fibre 3 kilograms, 3 millimeters long polypropene staples 1 kilogram, waterproof powder 24 kilograms, hybrid packed.
Embodiment 2:
Second class powered coal ash 120 kg, slag powders 200 kilograms, 20 kilograms of Calx, desulfurated plaster 20 kilograms, 42.5 number cement 40 kilograms, Matrii Sulfas Exsiccatus 10 kilograms, 70-140 order fine sand 600 kilograms, the cellulose ether of 100000 molecular weight 2 kilograms, re-dispersible glue powder 25 kilograms, wood fibre 3 kilograms, 3 millimeters long polypropene staples 1 kilogram, waterproof powder 30 kilograms, hybrid packed.
Embodiment 3:
Second class powered coal ash 160 kilograms, slag powders 160 kilograms, 24 kilograms of Calx, desulfurated plaster 16 kilograms, 42.5 number cement 40 kilograms, Matrii Sulfas Exsiccatus 12 kilograms, 70-140 order fine sand 600 kilograms, the cellulose ether of 100000 molecular weight 2.5 kilograms, re-dispersible glue powder 20 kilograms, wood fibre 2.5 kilograms, 3 millimeters long polypropene staples 1 kilogram, waterproof powder 35 kilograms, hybrid packed.
Embodiment 4:
Second class powered coal ash 110 kilograms, slag powders 160 kilograms, 26 kilograms of Calx, desulfurated plaster 18 kilograms, 42.5 number cement 36 kilograms, Matrii Sulfas Exsiccatus 8 kilograms, 70-140 order fine sand 650 kilograms, the cellulose ether of 100000 molecular weight 2 kilograms, re-dispersible glue powder 30 kilograms, wood fibre 3 kilograms, 3 millimeters long polypropene staples 1 kilogram, waterproof powder 40 kilograms, hybrid packed.
Claims (1)
1. a waterproof anti-crack mortar, it is characterized in that, it is made up of inorganic coagulation material, organic additive, 180 order fine sands, the weight proportion of each component is: inorganic coagulation material 52%～65%, 180-200 order fine sand 25%～55%, organic additive 6%～10%, waterproof powder 5%-12%, surplus is water, described inorganic coagulation material is active admixture, alkali-activator composition, and described organic additive is the mixture of cellulose ether, re-dispersible glue powder, wood fibre polypropene staple.