CN105669112A - 一种含有尼龙纤维的抗裂砂浆 - Google Patents
一种含有尼龙纤维的抗裂砂浆 Download PDFInfo
- Publication number
- CN105669112A CN105669112A CN201410672323.5A CN201410672323A CN105669112A CN 105669112 A CN105669112 A CN 105669112A CN 201410672323 A CN201410672323 A CN 201410672323A CN 105669112 A CN105669112 A CN 105669112A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- nylon fiber
- containing nylon
- polyoxyethylene ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含有尼龙纤维的抗裂砂浆，其是由下述重量份的原料制得：尼龙纤维3-8、仲醇聚氧乙烯醚0.4-0.6、环氧硬脂酸辛酯2-4、硅酸盐水泥60-100、硅灰石粉4-10、羟丙基甲基纤维素醚5-8、氯化钙2-5、尿素3-8、六偏磷酸钠3-8、可分散性乳胶粉7-12、脱硫石膏7-12、玻化微珠70-85、硅酸铝3-8、甲酸钙3-8、葡萄糖酸钠3-8、氯化石蜡3-8、浓度为15-20%的双氧水7-9、填充料8-12、氧化石蜡皂0.1-0.2，适量水。
Description
技术领域
本发明涉及保温砂浆领域，确切地说是一种含有尼龙纤维的抗裂砂浆。
背景技术
保温砂浆是指由阻隔型保温材料和砂浆材料混合而成的，用于构筑建筑表面保温层的一种建筑材料。聚酰胺纤维是第一个合成高分子聚合物商业化之合成纤维制品﹐其为在1937年由美国杜邦公司卡罗瑟斯研究发明聚六甲基己二酰胺(即尼龙六六酰)﹐因而开启了合成纤维的第一页﹐其至今仍是聚酰胺纤维的代表。
发明内容
本发明的目的在于提供一种含有尼龙纤维的抗裂砂浆。
上述目的通过以下方案实现：
一种含有尼龙纤维的抗裂砂浆，其是由下述重量份的原料制得其是由下述重量份的原料制得：尼龙纤维3-8，仲醇聚氧乙烯醚0.4-0.6，环氧硬脂酸辛酯2-4，硅酸盐水泥60-100，硅灰石粉4-10，羟丙基甲基纤维素醚5-8、氯化钙2-5、尿素3-8、六偏磷酸钠3-8、可分散性乳胶粉7-12，脱硫石膏7-12、玻化微珠70-85、硅酸铝3-8、甲酸钙3-8，葡萄糖酸钠3-8，氯化石蜡3-8，浓度为15-20%的双氧水7-9,填充料8-12，氧化石蜡皂0.1-0.2，适量水。
本发明的有益效果为：本发明防水抗裂效果好，加入双氧水，是的本发明微膨胀，保温性能优异，容重低。
具体实施方式
一种含有尼龙纤维的抗裂砂浆，其是由下述重量kg的原料制得：尼龙纤维4，仲醇聚氧乙烯醚0.5，环氧硬脂酸辛酯2，硅酸盐水泥85，硅灰石粉8，羟丙基甲基纤维素醚6、氯化钙2、尿素2、六偏磷酸钠2、可分散性乳胶粉12，脱硫石膏12、玻化微珠85、硅酸铝2、甲酸钙2，葡萄糖酸钠2，氯化石蜡1，浓度为15-20%的双氧水9,填充料12，氧化石蜡皂0.2，适量水；
填充料由下列重量kg的原料制成：硅藻土22、膨胀蛭石粉15，萤石矿渣粉8，环氧大豆油2，氮化铝粉末4、脂肪醇聚氧乙烯醚2，硅烷偶联剂KH5501.8，丙烯酸丁酯4,重钙粉2，3-氨丙基三甲氧基硅烷2.5、二缩三丙二醇二丙烯酸酯3、硬脂酸2；
填充料的制备方法是将硅藻土、膨胀蛭石粉、萤石矿渣粉混匀，放入煅烧炉中在700℃下煅烧3小时，冷却，放入12%氢氧化钠溶液中浸泡7小时，过滤取出，去离子水洗涤，烘干，再与其它剩余原料混合均匀后，即得。
所述的一种含有尼龙纤维的抗裂砂浆，制备方法为：
将全部原料混匀后，380转/分钟匀速搅拌25分钟，包装后即得。
Claims (1)
1.一种含有尼龙纤维的抗裂砂浆，其特征在于：其是由下述重量份的原料制得：尼龙纤维3-8，仲醇聚氧乙烯醚0.4-0.6，环氧硬脂酸辛酯2-4，硅酸盐水泥60-100，硅灰石粉4-10，羟丙基甲基纤维素醚5-8、氯化钙2-5、尿素3-8、六偏磷酸钠3-8、可分散性乳胶粉7-12，脱硫石膏7-12、玻化微珠70-85、硅酸铝3-8、甲酸钙3-8，葡萄糖酸钠3-8，氯化石蜡3-8，浓度为15-20%的双氧水7-9,填充料8-12，氧化石蜡皂0.1-0.2，适量水；填充料由下列重量份的原料制成：硅藻土18-22、膨胀蛭石粉10-15，萤石矿渣粉5-8，环氧大豆油3-8，氮化铝粉末2-4、脂肪醇聚氧乙烯醚3-8，硅烷偶联剂KH5501.5-3，丙烯酸丁酯2-4,重钙粉3-8，3-氨丙基三甲氧基硅烷2-3、二缩三丙二醇二丙烯酸酯2-3、硬脂酸3-8。