CN105665927A - 一种高氮奥氏体不锈钢焊接接头保护方法 - Google Patents

一种高氮奥氏体不锈钢焊接接头保护方法 Download PDF

Info

Publication number
CN105665927A
CN105665927A CN201610185790.4A CN201610185790A CN105665927A CN 105665927 A CN105665927 A CN 105665927A CN 201610185790 A CN201610185790 A CN 201610185790A CN 105665927 A CN105665927 A CN 105665927A
Authority
CN
China
Prior art keywords
welding
stainless steel
austenitic stainless
argon
nitrogen austenitic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610185790.4A
Other languages
English (en)
Inventor
杜劭峰
赵文军
王宇琪
杨炙坤
邝玉林
王小龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Inner Mongolia First Machinery Group Corp
Original Assignee
Inner Mongolia First Machinery Group Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Inner Mongolia First Machinery Group Corp filed Critical Inner Mongolia First Machinery Group Corp
Priority to CN201610185790.4A priority Critical patent/CN105665927A/zh
Publication of CN105665927A publication Critical patent/CN105665927A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种高氮奥氏体不锈钢焊接接头保护方法，解决了目前焊接方法在焊接时产生大量密集氮气孔，造成接头性能下降的问题。在采用高能束激光电弧复合焊接时，在原有氩气-二氧化碳混合气体保护气外再另外增加纯氩气进行气体保护，氩气-二氧化碳混合气体和纯氩气在焊接时同时通到焊接熔池里。焊接时，纯氩气流量采用40L/Min。本发明能有效防止高氮奥氏体不锈钢焊接中焊缝产生大量气孔的焊接保护工艺，确保焊接接头机械性能的同时，提高高氮奥氏体不锈钢的焊接性。

Description

一种高氮奥氏体不锈钢焊接接头保护方法
技术领域
本发明涉及一种焊接保护方法，具体涉及一种用于高氮奥氏体不锈钢激光电弧复合焊接时接头的保护方法。
背景技术
作为一种资源节约型不锈钢，高氮奥氏体不锈钢的研究和应用正在不断研究和推广。高氮奥氏体不锈钢焊接中接头极易产生气孔，尤其是采用高能束激光电弧复合焊接时，由于极快的焊接速度和冷却速度，焊缝中的氮气来不及溢出，极易在焊缝表面和内部产生大量密集氮气孔，造成接头性能下降，外观质量差，严重制约了新技术的应用。
发明内容
本发明通过在常规高氮奥氏体不锈钢激光电弧复合焊接工艺基础上进行改进，解决了目前焊接方法在焊接时产生大量密集氮气孔，造成接头性能下降的问题。
本发明是由以下技术方案实现的：
一种高氮奥氏体不锈钢焊接接头保护方法，在采用高能束激光电弧复合焊接时，在原有氩气-二氧化碳混合气体保护气外再另外增加纯氩气进行气体保护，氩气-二氧化碳混合气体和纯氩气在焊接时同时通到焊接熔池里。
焊接时，纯氩气流量采用40L/Min。
本发明能有效防止高氮奥氏体不锈钢焊接中焊缝产生大量气孔的焊接保护工艺，确保焊接接头机械性能的同时，提高高氮奥氏体不锈钢的焊接性。
附图说明
图1是本发明方法实施例图。
具体实施方式
本发明是一种高氮奥氏体不锈钢焊接接头保护方法，在采用高能束激光电弧复合焊接时，在原有氩气-二氧化碳混合气体保护气外再另外增加纯氩气进行气体保护，氩气-二氧化碳混合气体和纯氩气在焊接时同时通到焊接熔池里。焊接时，纯氩气流量采用40L/Min。
实施例
如图1所示，在激光电弧焊复合头4外部，与激光束2和焊枪1同轴增加一路保护气排装置3，保护气排装置3通入纯氩，与激光电弧复合焊接系统预留的电磁阀连接，实现焊接同步控制，即在原有氩气-二氧化碳混合气体保护气外再另外增加氩气进行气体保护，氩气流量40L/Min，其余采用原有工艺参数，焊后有效克服了焊接气孔的产生。
下面是8mm高氮钢激光电弧复合焊工艺：
焊接方式为高能束激光-电弧复合热源焊接，焊接母材厚度为8mm，Y型坡口，钝边高度4mm，根部间隙0.5mm，坡口角度30°，施焊时电弧在前，激光在后，光丝距3mm。填充的焊接材料是HCr20Ni10Mn7Mo焊丝，直径1.2mm；电弧焊接参数是：焊接电流240A，焊接电压26V，干伸长为15mm，焊枪与工件夹角为60°，焊接速度V＝0.8m/min，电弧保护气95％Ar+5％CO2，流量30L/min。；激光焊接参数是：激光使用连续波形，激光功率2.0kW，1s上升和1s下降过程，离焦-1mm，激光喷嘴高度25mm，激光保护气为压缩空气，保护气排装置氩气流量40L/min。焊板完全焊透。焊接区域温度15-18度。焊接后经射线无损检测，焊缝等级I级，气孔倾向显著降低。
本发明通过在焊枪旁边另外增加一路保护气排，通入纯氩气进行辅助保护，克服了高氮奥氏体不锈钢在激光电弧复合焊接时的严重气孔倾向，达到接头少无气孔、组织均匀稳定，焊接合格率高的目的，解决了高氮奥氏体不锈钢激光电弧复合焊接在我国装甲车辆行业的工程化推广应用问题。

Claims (2)

1.一种高氮奥氏体不锈钢焊接接头保护方法，其特征是：在采用高能束激光电弧复合焊接时，在原有氩气-二氧化碳混合气体保护气外再另外增加纯氩气进行气体保护，氩气-二氧化碳混合气体和纯氩气在焊接时同时通到焊接熔池里。
2.根据权利要求1所述的一种高氮奥氏体不锈钢焊接接头保护方法，其特征是：焊接时，纯氩气流量采用40L/Min。
CN201610185790.4A 2016-03-30 2016-03-30 一种高氮奥氏体不锈钢焊接接头保护方法 Pending CN105665927A (zh)