CN105646970A - Non-slip and folding-resistant sole material and preparing method thereof - Google Patents
Non-slip and folding-resistant sole material and preparing method thereof Download PDFInfo
- Publication number
- CN105646970A CN105646970A CN201610037393.2A CN201610037393A CN105646970A CN 105646970 A CN105646970 A CN 105646970A CN 201610037393 A CN201610037393 A CN 201610037393A CN 105646970 A CN105646970 A CN 105646970A
- Authority
- CN
- China
- Prior art keywords
- parts
- sole
- shoe
- folding material
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a non-slip and folding-resistant sole material. The non-slip and folding-resistant sole material is prepared from, by weight, 20-30 parts of butadiene styrene rubber, 20-30 parts of natural rubber, 5-15 parts of PVC resin, 5-12 parts of petroleum resin, 2-5 parts of phenyl salicylate, 5-10 parts of poly(butylene succinate), 1-3 parts of sodium pyrophosphate, 2-5 parts of dimethylsilicone fluid, 0.5-1 part of nanometer titanium oxide, 5-6 parts of calcium stearate, 3-6 parts of N220 carbon black, 1.5-2 parts of an accelerator CZ, 1-2 parts of a coupling agent and 1.5-3.5 parts of an anti-aging agent. The invention discloses a preparing method of the sole material. The sole material is good in non-slip performance, large in elasticity, resistant to folding and good in breathability, and has a certain antibacterial capability. In addition, the method is simple in process, easy to implement and low in cost.
Description
Technical field:
The present invention relates to material for sole of shoe field, be specifically related to a kind of anti-slip folding material for sole of shoe.
Background technology:
Continuous progress along with socioeconomic development and scientific level, people often there has also been more demand for comfortableness and the safety of footwear, such as the requirement of the performances such as the on-slip of footwear, wear-resisting and damping is improved constantly, and the antiskid property of sole directly influences safety when footwear wear, antiskid property is poor, people is easily skidded wrestling when walking, particularly on wet, light, sliding road surface.
The footwear that China is maximum in the world produce and exported country; annual footwear yield accounts for the whole world more than 50%; external in order to protect environment and personal safety to consider in recent years; improve constantly the requirement of footwear standard; and China's footwear outlet has been carried out certain restriction; and the current footwear material of China and technology, the requirement specified with these technology, environmental standard remains in a certain distance. Therefore, the on-slip characteristic of footwear how is improved, it is ensured that the safety of consumer, it has also become the focus that shoe industry and footwear researcher are paid close attention to.
Chinese patent (201410292697.4) discloses a kind of high abrasion anti-slip sole composite, including natural rubber, maleic acid modified natural rubber, butadiene-styrene rubber, Malin's acid modified styrene butadiene rubber, butadiene rubber, white carbon black, terpene resin, phenolic resin, aromatic naphtha, zinc oxide, age resistor, accelerant CZ and sulfur, further butadiene-styrene rubber is modified by maleic anhydride free in Malin's acid modified styrene butadiene rubber, maleic acid modified natural rubber, so that each raw material crosslinked action strengthens, wear-resisting, the slip resistance of material for sole of shoe are improved.
Summary of the invention:
It is an object of the invention to provide a kind of anti-slip folding material for sole of shoe, this material antiskid property is good, elastic big, folding, and good permeability has certain antibacterial ability.
The preparation method that it is a further object to provide this material for sole of shoe, the method technique is simple, it is easy to operation, cost is low.
For achieving the above object, the present invention is by the following technical solutions:
A kind of anti-slip folding material for sole of shoe, with parts by weight, including following components:
Butadiene-styrene rubber 20-30 part, natural rubber 20-30 part,
Polyvinyl chloride resin 5-15 part, Petropols 5-12 part,
Phenyl salicylate 2-5 part, poly butylene succinate 5-10 part,
Sodium pyrophosphate 1-3 part, organic silicone oil 2-5 part,
Nano-titanium oxide 0.5-1 part, calcium stearate 5-6 part,
N220 white carbon black 3-6 part, accelerant CZ 1.5-2 part,
Coupling agent 1-2 part, age resistor 1.5-3.5 part.
Preferred as technique scheme, a kind of anti-slip folding material for sole of shoe, with parts by weight, including following components:
25 parts of butadiene-styrene rubber, natural rubber 28 parts,
Polyvinyl chloride resin 10 parts, Petropols 8 parts,
Phenyl salicylate 4 parts, poly butylene succinate 7 parts,
Sodium pyrophosphate 2.5 parts, organic silicone oil 5 parts,
Nano-titanium oxide 0.8 part, calcium stearate 5 parts,
N220 white carbon black 4 parts, accelerant CZ 1.5 parts,
Coupling agent 1.6 parts, 2 parts of age resistor.
Preferred as technique scheme, described butadiene-styrene rubber is emulsion polymerized styrene butadiene rubber, and wherein the weight percent content of butadiene is 25.5%, and cinnamic weight percent content is 74.5%.
Preferred as technique scheme, in described natural rubber, 90-95% is rubber hydrocarbon.
Preferred as technique scheme, described Petropols are C5 Petropols, and its softening point is 110-115 DEG C.
Preferred as technique scheme, the size of described nano-titanium oxide is 10-30nm.
Preferred as technique scheme, described coupling agent is the mixture of silane coupler, titanate coupling agent, and the two volume ratio is 3:1.
The preparation method of a kind of anti-slip folding material for sole of shoe, comprises the following steps:
(1) butadiene-styrene rubber, natural rubber, polyvinyl chloride resin, Petropols, phenyl salicylate, poly butylene succinate are joined in banbury, banburying 3-5min, continuously add sodium pyrophosphate, organic silicone oil, nano-titanium oxide, calcium stearate, N220 white carbon black, coupling agent, age resistor, banburying 10-20min, then proceeds in opening rubber mixing machine, adds accelerant CZ, begin to pratise, begin to pratise after end, naturally cool to room temperature, obtain mixed material;
(2) the mixing logistics that step (1) obtains being vulcanized by vulcanizing press, sulfuration naturally cools to room temperature, obtains anti-slip folding material for sole of shoe after terminating.
Preferred as technique scheme, in step (1), described in the temperature begun to pratise be 50 �� 5 DEG C, the time begun to pratise is 300-330s.
Preferred as technique scheme, in step (2), the temperature of described sulfuration is 160 �� 5 DEG C, and the time of sulfuration is 180-200s.
The method have the advantages that
The addition of C5 Petropols reduces the strand free volume in rubber, make that chain is intersegmental, between filler and between segment and filler friction increase, so that the material for sole of shoe skid resistance of preparation is greatly improved, and C5 Petropols are fine with the compatibility of each rubber, on its processing characteristics without impact;
Phenyl salicylate, poly butylene succinate addition the elasticity of material for sole of shoe is greatly improved, macromolecular chain is wound around mutually, and wearability is greatly improved, and phenyl salicylate can absorb ultraviolet light, it is possible to be effectively improved the anti-ultraviolet function of material for sole of shoe.
Detailed description of the invention:
In order to be better understood from the present invention, the present invention is further described by the examples below, and embodiment is served only for explaining the present invention, and the present invention will not constitute any restriction.
Embodiment 1
A kind of anti-slip folding material for sole of shoe, with parts by weight, including following components:
20 parts of butadiene-styrene rubber, natural rubber 20 parts,
Polyvinyl chloride resin 5 parts, Petropols 5 parts,
Phenyl salicylate 2 parts, poly butylene succinate 5 parts,
Sodium pyrophosphate 1 part, organic silicone oil 2 parts,
Nano-titanium oxide 0.5 part, calcium stearate 5 parts,
N220 white carbon black 3 parts, accelerant CZ 1.5 parts,
Coupling agent 1 part, 1.5 parts of age resistor.
Its preparation method comprises the following steps:
(1) butadiene-styrene rubber, natural rubber, polyvinyl chloride resin, Petropols, phenyl salicylate, poly butylene succinate are joined in banbury, banburying 3min, continuously add sodium pyrophosphate, organic silicone oil, nano-titanium oxide, calcium stearate, N220 white carbon black, coupling agent, age resistor, banburying 10min, then proceeds in opening rubber mixing machine, adds accelerant CZ, begin to pratise, begin to pratise after end, naturally cool to room temperature, obtain mixed material;
(2) the mixing logistics that step (1) obtains being vulcanized by vulcanizing press, sulfuration naturally cools to room temperature, obtains anti-slip folding material for sole of shoe after terminating.
Embodiment 2
A kind of anti-slip folding material for sole of shoe, with parts by weight, including following components:
30 parts of butadiene-styrene rubber, natural rubber 30 parts,
Polyvinyl chloride resin 15 parts, Petropols 12 parts,
Phenyl salicylate 5 parts, poly butylene succinate 10 parts,
Sodium pyrophosphate 3 parts, organic silicone oil 5 parts,
Nano-titanium oxide 1 part, calcium stearate 6 parts,
N220 white carbon black 6 parts, accelerant CZ 2 parts,
Coupling agent 2 parts, 3.5 parts of age resistor.
Its preparation method comprises the following steps:
(1) butadiene-styrene rubber, natural rubber, polyvinyl chloride resin, Petropols, phenyl salicylate, poly butylene succinate are joined in banbury, banburying 5min, continuously add sodium pyrophosphate, organic silicone oil, nano-titanium oxide, calcium stearate, N220 white carbon black, coupling agent, age resistor, banburying 20min, then proceeds in opening rubber mixing machine, adds accelerant CZ, begin to pratise, begin to pratise after end, naturally cool to room temperature, obtain mixed material;
(2) the mixing logistics that step (1) obtains being vulcanized by vulcanizing press, sulfuration naturally cools to room temperature, obtains anti-slip folding material for sole of shoe after terminating.
Embodiment 3
A kind of anti-slip folding material for sole of shoe, with parts by weight, including following components:
22 parts of butadiene-styrene rubber, natural rubber 22 parts,
Polyvinyl chloride resin 7 parts, Petropols 7 parts,
Phenyl salicylate 3 parts, poly butylene succinate 6 parts,
Sodium pyrophosphate 1.5 parts, organic silicone oil 3 parts,
Nano-titanium oxide 0.6 part, calcium stearate 5.2 parts,
N220 white carbon black 4 parts, accelerant CZ 1.6 parts,
Coupling agent 1.2 parts, 2 parts of age resistor.
Its preparation method comprises the following steps:
(1) butadiene-styrene rubber, natural rubber, polyvinyl chloride resin, Petropols, phenyl salicylate, poly butylene succinate are joined in banbury, banburying 4min, continuously add sodium pyrophosphate, organic silicone oil, nano-titanium oxide, calcium stearate, N220 white carbon black, coupling agent, age resistor, banburying 12min, then proceeds in opening rubber mixing machine, adds accelerant CZ, begin to pratise, begin to pratise after end, naturally cool to room temperature, obtain mixed material;
(2) the mixing logistics that step (1) obtains being vulcanized by vulcanizing press, sulfuration naturally cools to room temperature, obtains anti-slip folding material for sole of shoe after terminating.
Embodiment 4
A kind of anti-slip folding material for sole of shoe, with parts by weight, including following components:
24 parts of butadiene-styrene rubber, natural rubber 24 parts,
Polyvinyl chloride resin 9 parts, Petropols 8 parts,
Phenyl salicylate 3.5 parts, poly butylene succinate 7 parts,
Sodium pyrophosphate 2 parts, organic silicone oil 3.5 parts,
Nano-titanium oxide 0.7 part, calcium stearate 5.4 parts,
N220 white carbon black 4.5 parts, accelerant CZ 1.7 parts,
Coupling agent 1.4 parts, 2.5 parts of age resistor.
Its preparation method comprises the following steps:
(1) butadiene-styrene rubber, natural rubber, polyvinyl chloride resin, Petropols, phenyl salicylate, poly butylene succinate are joined in banbury, banburying 3min, continuously add sodium pyrophosphate, organic silicone oil, nano-titanium oxide, calcium stearate, N220 white carbon black, coupling agent, age resistor, banburying 14min, then proceeds in opening rubber mixing machine, adds accelerant CZ, begin to pratise, begin to pratise after end, naturally cool to room temperature, obtain mixed material;
(2) the mixing logistics that step (1) obtains being vulcanized by vulcanizing press, sulfuration naturally cools to room temperature, obtains anti-slip folding material for sole of shoe after terminating.
Embodiment 5
A kind of anti-slip folding material for sole of shoe, with parts by weight, including following components:
26 parts of butadiene-styrene rubber, natural rubber 26 parts,
Polyvinyl chloride resin 11 parts, Petropols 10 parts,
Phenyl salicylate 4 parts, poly butylene succinate 8 parts,
Sodium pyrophosphate 2.5 parts, organic silicone oil 4 parts,
Nano-titanium oxide 0.8 part, calcium stearate 5.6 parts,
N220 white carbon black 5 parts, accelerant CZ 1.8 parts,
Coupling agent 1.6 parts, 3 parts of age resistor.
Its preparation method comprises the following steps:
(1) butadiene-styrene rubber, natural rubber, polyvinyl chloride resin, Petropols, phenyl salicylate, poly butylene succinate are joined in banbury, banburying 4min, continuously add sodium pyrophosphate, organic silicone oil, nano-titanium oxide, calcium stearate, N220 white carbon black, coupling agent, age resistor, banburying 16min, then proceeds in opening rubber mixing machine, adds accelerant CZ, begin to pratise, begin to pratise after end, naturally cool to room temperature, obtain mixed material;
(2) the mixing logistics that step (1) obtains being vulcanized by vulcanizing press, sulfuration naturally cools to room temperature, obtains anti-slip folding material for sole of shoe after terminating.
Embodiment 6
A kind of anti-slip folding material for sole of shoe, with parts by weight, including following components:
28 parts of butadiene-styrene rubber, natural rubber 28 parts,
Polyvinyl chloride resin 13 parts, Petropols 11 parts,
Phenyl salicylate 4.5 parts, poly butylene succinate 9 parts,
Sodium pyrophosphate 3 parts, organic silicone oil 4.5 parts,
Nano-titanium oxide 0.9 part, calcium stearate 5.8 parts,
N220 white carbon black 5.5 parts, accelerant CZ 1.9 parts,
Coupling agent 1.8 parts, 3.5 parts of age resistor.
Its preparation method comprises the following steps:
(1) butadiene-styrene rubber, natural rubber, polyvinyl chloride resin, Petropols, phenyl salicylate, poly butylene succinate are joined in banbury, banburying 5min, continuously add sodium pyrophosphate, organic silicone oil, nano-titanium oxide, calcium stearate, N220 white carbon black, coupling agent, age resistor, banburying 18min, then proceeds in opening rubber mixing machine, adds accelerant CZ, begin to pratise, begin to pratise after end, naturally cool to room temperature, obtain mixed material;
(2) the mixing logistics that step (1) obtains being vulcanized by vulcanizing press, sulfuration naturally cools to room temperature, obtains anti-slip folding material for sole of shoe after terminating.
Claims (10)
1. an anti-slip folding material for sole of shoe, it is characterised in that with parts by weight, including following components:
Butadiene-styrene rubber 20-30 part, natural rubber 20-30 part,
Polyvinyl chloride resin 5-15 part, Petropols 5-12 part,
Phenyl salicylate 2-5 part, poly butylene succinate 5-10 part,
Sodium pyrophosphate 1-3 part, organic silicone oil 2-5 part,
Nano-titanium oxide 0.5-1 part, calcium stearate 5-6 part,
N220 white carbon black 3-6 part, accelerant CZ 1.5-2 part,
Coupling agent 1-2 part, age resistor 1.5-3.5 part.
2. a kind of anti-slip folding material for sole of shoe as claimed in claim 1, it is characterised in that with parts by weight, including following components:
25 parts of butadiene-styrene rubber, natural rubber 28 parts,
Polyvinyl chloride resin 10 parts, Petropols 8 parts,
Phenyl salicylate 4 parts, poly butylene succinate 7 parts,
Sodium pyrophosphate 2.5 parts, organic silicone oil 5 parts,
Nano-titanium oxide 0.8 part, calcium stearate 5 parts,
N220 white carbon black 4 parts, accelerant CZ 1.5 parts,
Coupling agent 1.6 parts, 2 parts of age resistor.
3. a kind of anti-slip folding material for sole of shoe as claimed in claim 1, it is characterised in that described butadiene-styrene rubber is emulsion polymerized styrene butadiene rubber, and wherein the weight percent content of butadiene is 25.5%, and cinnamic weight percent content is 74.5%.
4. a kind of anti-slip folding material for sole of shoe as claimed in claim 1, it is characterised in that in described natural rubber, 90-95% is rubber hydrocarbon.
5. a kind of anti-slip folding material for sole of shoe as claimed in claim 1, it is characterised in that described Petropols are C5 Petropols, and its softening point is 110-115 DEG C.
6. a kind of anti-slip folding material for sole of shoe as claimed in claim 1, it is characterised in that the size of described nano-titanium oxide is 10-30nm.
7. a kind of anti-slip folding material for sole of shoe as claimed in claim 1, it is characterised in that described coupling agent is the mixture of silane coupler, titanate coupling agent, and the two volume ratio is 3:1.
8. the preparation method of a kind of anti-slip folding material for sole of shoe as described in as arbitrary in claim 1 to 7, it is characterised in that comprise the following steps:
(1) butadiene-styrene rubber, natural rubber, polyvinyl chloride resin, Petropols, phenyl salicylate, poly butylene succinate are joined in banbury, banburying 3-5min, continuously add sodium pyrophosphate, organic silicone oil, nano-titanium oxide, calcium stearate, N220 white carbon black, coupling agent, age resistor, banburying 10-20min, then proceeds in opening rubber mixing machine, adds accelerant CZ, begin to pratise, begin to pratise after end, naturally cool to room temperature, obtain mixed material;
(2) the mixing logistics that step (1) obtains being vulcanized by vulcanizing press, sulfuration naturally cools to room temperature, obtains anti-slip folding material for sole of shoe after terminating.
9. the preparation method of a kind of anti-slip folding material for sole of shoe as claimed in claim 8, it is characterised in that in step (1), described in the temperature begun to pratise be 50 �� 5 DEG C, the time begun to pratise is 300-330s.
10. the preparation method of a kind of anti-slip folding material for sole of shoe as claimed in claim 8, it is characterised in that in step (2), the temperature of described sulfuration is 160 �� 5 DEG C, and the time of sulfuration is 180-200s.