CN105645604A - Low-phosphorus scale and corrosion inhibitor - Google Patents
Low-phosphorus scale and corrosion inhibitor Download PDFInfo
- Publication number
- CN105645604A CN105645604A CN201610254561.3A CN201610254561A CN105645604A CN 105645604 A CN105645604 A CN 105645604A CN 201610254561 A CN201610254561 A CN 201610254561A CN 105645604 A CN105645604 A CN 105645604A
- Authority
- CN
- China
- Prior art keywords
- corrosion inhibitor
- low
- acid
- scale
- molybdate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a low-phosphorus scale and corrosion inhibitor which is composed of the following components in percentage by weight: 8-15% of polyaspartic acid, 5-8% of tungstate, 5-8% of molybdate, 8-15% of nitromalonic acid, 20-30% of hydroxyethylidenediphosphonic acid, 4-7% of hydroxy ethidene bis phosphoric acid and the balance of water. The scale and corrosion inhibitor is easy to prepare, and has the advantages of high stability and favorable corrosion and scale inhibition properties.
Description
Technical field
The present invention relates to chemical technology field, be specifically related to a kind of low-phosphorus antiincrustation corrosion inhibitor.
Background technology
Corrosion inhibiter is a kind of when being present in environment (medium) with suitable concentration and form, it is possible to prevent or slow down the chemical substance of corrosion or the mixture of several chemical substance. In industry, the utilization of recirculated water is conducive to saving the cost of enterprise, improve the benefit of enterprise, but recirculated water in use there will be two problems, the evaporation of moisture when one, causes crystallization and the precipitation of salt, and modal have the incrustation scale such as calcium carbonate, calcium silicates, the existence of incrustation scale greatly reduces heat transfer efficiency, it two is the electrochemical corrosion corrosiveness to equipment of recirculated water, and this corrosion is fatal, gently then more exchange device; Heavy then injure human life, currently mainly adopt anti-incrustation corrosion inhibitor to be added in recirculated water, reduce the appearance of incrustation scale. But the composition of anti-incrustation corrosion inhibitor at present on the market is single, and scale removal effect is bad, particularly with the treatment effect of modal calcium carbonate etc. bad, this is the deficiencies in the prior art.
Summary of the invention
For above-mentioned the deficiencies in the prior art, the technical problem to be solved in the present invention is to provide a kind of new low-phosphorus antiincrustation corrosion inhibitor, and its scale inhibitor is effective, stability is strong.
The present invention adopts the technical scheme that:
A kind of low-phosphorus antiincrustation corrosion inhibitor, is made up of following component by weight percentage:
Poly-aspartate 8-15%
Tungstates 5-8%
Molybdate 5-8%
Nitro malonic acid 8-15%
Hydroxy ethylene diphosphonic acid 20-30%
1-hydroxy ethylidene-1,1-diphosphonic acid 4-7%
Surplus is water.
Described tungstates is sodium tungstate.
Described molybdate is sodium molybdate.
The invention have the advantage that
1, the anti-incrustation corrosion inhibitor of the present invention is without toxic compounds and inorganic phosphate, low stain, is beneficial to environmental conservation;
2, the anti-incrustation corrosion inhibitor of the present invention is easily prepared, good stability, has good inhibition and scale-inhibiting properties.
Detailed description of the invention
Below embodiments of the invention are described in detail, so that advantages and features of the invention can be easier to be readily appreciated by one skilled in the art, thus protection scope of the present invention being made apparent clear and definite defining.
Embodiment 1
A kind of low-phosphorus antiincrustation corrosion inhibitor, is made up of following component by weight percentage:
Poly-aspartate 8%
Sodium tungstate 5%
Sodium molybdate 5%
Nitro malonic acid 8%
Hydroxy ethylene diphosphonic acid 20%
1-hydroxy ethylidene-1,1-diphosphonic acid 4%
Surplus is water.
Embodiment 2
A kind of low-phosphorus antiincrustation corrosion inhibitor, is made up of following component by weight percentage:
Poly-aspartate 11.5%
Sodium tungstate 6.5%
Sodium molybdate 6.5%
Nitro malonic acid 11.5%
Hydroxy ethylene diphosphonic acid 25%
1-hydroxy ethylidene-1,1-diphosphonic acid 5.5%
Surplus is water.
Embodiment 3
A kind of low-phosphorus antiincrustation corrosion inhibitor, is made up of following component by weight percentage:
Poly-aspartate 15%
Sodium tungstate 8%
Sodium molybdate 8%
Nitro malonic acid 15%
Hydroxy ethylene diphosphonic acid 30%
1-hydroxy ethylidene-1,1-diphosphonic acid 7%
Surplus is water.
Former water calcium hardness (with calcium carbonate) 300mg/L, add the anti-incrustation corrosion inhibitor of the embodiment of the present invention 2 preparation of 40mg/L, by detect heat exchanger monitor carbon steel experiment tube corrosion rate to be 0.01031mm/a, rustless steel experiment tube corrosion rate be 0.000112mm/a, pyrite experiment tube corrosion rate are 0.0000937mm/a, dirtiness resistance is/1.05 �� 10-4m2��K/W��
Claims (3)
1. a low-phosphorus antiincrustation corrosion inhibitor, it is characterised in that be made up of following component by weight percentage:
Poly-aspartate 8-15%
Tungstates 5-8%
Molybdate 5-8%
Nitro malonic acid 8-15%
Hydroxy ethylene diphosphonic acid 20-30%
1-hydroxy ethylidene-1,1-diphosphonic acid 4-7%
Surplus is water.
2. low-phosphorus antiincrustation corrosion inhibitor according to claim 1, it is characterised in that described tungstates is sodium tungstate.
3. low-phosphorus antiincrustation corrosion inhibitor according to claim 1, it is characterised in that described molybdate is sodium molybdate.