Background technology
Water is the blood of industry, at present, in the bigger industry of the such water consumption of industrial or agricultural, water saving is a bigger problem, existing reasonable method is exactly recycle cooling water, but because the water quality difference of the water that industry is discharged makes these water directly not to be recycled, must could be applied to again produce through after a series for the treatment of processes.
Industrial circulating cooling water system can run into some problems when the cycle for the treatment of water coolant, such as fouling in the industrial circulating cooling water system, corrosion and microorganism harm etc.Existing solution to the problems described above mainly is to add anti-incrustation corrosion inhibitor in recirculating cooling water system.Anti-incrustation corrosion inhibitor generally adopts polyphosphoric acid, organic phosphoric acid, contains the sulfonic group multipolymer, with the zinc salt compound prescription.Organophosphorus is widely used in the prescription of anti-incrustation corrosion inhibitor of process water because scale inhibition effect is good.
For general scale inhibitor agent prescription, water quality difference according to system, can there be bigger difference in its corrosion inhibition and scale-inhibiting properties, in low cycles of concentration circulating water system, because hardness in the water, basicity are all lower, the fouling tendency of recirculated water is lower, corrodes byer force relatively, requires the scale inhibitor agent prescription that corrosion mitigating effect preferably will be arranged; And in the high concentration multiple circulating water system, be non-adding in the circulating water system that acid regulates especially, because the increase of water quality calcium hardness and basicity, the deposition tendency increases, and corrode faintly, requires the scale inhibitor agent prescription must have good scale-inhibiting properties at this moment.
Summary of the invention
The object of the invention provides a kind of composite scale-inhibiting corrosion inhibitor, can be applicable to the circulating water system of industries such as chemical industry, chemical fertilizer, electric power, weaving, because the variation of the water quality of every profession and trade, the present invention can be adapted to the corrosion mitigating effect of low cycles of concentration, can scale-inhibiting properties preferably be arranged at high concentration multiple again.
Technical scheme of the present invention is:
A kind of composite scale-inhibiting corrosion inhibitor is characterized in that, comprises following main ingredient:
2-phosphonate group-1,2,4-tricarboxylic acid, hydroxy ethylene diphosphonic acid, acrylic terpolymer, benzotriazole, zinc chloride, poly-epoxy succinic acid.
Preferably, the weight part of described each main ingredient is:
Preferably, described acrylic terpolymer is vinylformic acid/Propylene glycol monoacrylate/2-methyl-2-acrylamido propane sulfonic acid terpolymer.
Preferably, described composite scale-inhibiting corrosion inhibitor is applicable to the more natural gas conditioning treatment plant of high rigidity, high basicity, high-temperature and calcium ions, magnesium ion and sulfate ion, chemical plant recirculating cooling water system, and described composite scale-inhibiting corrosion inhibitor also is applicable to industry recirculating cooling water systems such as the chemical fertilizer, electric power, weaving of high rigidity, high basicity, high-temperature.
Preferably, be standard with the calcium hardness, calcium hardness is during less than 200mg/L in the 1L recirculated cooling water, and described composite scale-inhibiting corrosion inhibitor injected volume remains when calcium hardness is 200~400mg/L in 40~60mg/L1L recirculated cooling water, and described composite scale-inhibiting corrosion inhibitor injected volume keeps 60~80mg/L; Calcium hardness is during greater than 400mg/L in the 1L recirculated cooling water, and described composite scale-inhibiting corrosion inhibitor injected volume remains 80~90mg/L.
2-phosphonate group-1,2, the 4-tricarboxylic acid, phosphorus content is low, has good anticorrosion-antiscaling property, the organic phosphoric acid that is better than using always, special scale-inhibiting properties at high temperature is much better than organic phosphoric acid commonly used, can improve the solubleness of zinc, and the oxidation susceptibility of anti-chlorine is good, composite synergetic property is good, also is the good stable agent of zinc salt.Hydroxy ethylene diphosphonic acid, phosphorus content is low, is a kind of organic phosphine acids anti-incrustation corrosion inhibitor, can form stable complex compound with multiple metal ions such as iron, copper, zinc, the oxide compound on energy dissolution of metals surface.Still can play good corrosion-mitigation scale-inhibition effect under 250 ℃, still very stable under high pH value, facile hydrolysis is not difficult for decomposing under the general light and heat condition.Resistance to acids and bases, anti-oxychlorination performance are good than other organic phospho acid.Can belong to ion with underwater gold, especially form six annulus inner complexs with calcium ion, thereby have scale inhibition effect and the tangible molten limit effect of tool preferably, when with the compound use by a certain percentage of other component of the present invention, show desirable synergistic effect.Vinylformic acid/Propylene glycol monoacrylate/2-methyl-2-acrylamido propane sulfonic acid terpolymer, has the premium properties that in alkaline aqueous solution, disperses iron, zinc oxyhydroxide and calcium carbonate, calcium phosphate, because it has sulfonic acid group, so under high temperature, high-alkali, high calcium condition, still have good scale inhibition dissemination.Than some sulfonic acid copolymers in the market such as propene sulfonic acid resistance calcium phosphate scale rate height, and it can be composite to about 10% with zinc chloride, and zinc chloride does not produce precipitation in high alkali aqueous solution, with other anti-incrustation corrosion inhibitors are composite good synergistic arranged.Benzotriazole is a kind of effectively copper and copper alloy inhibiter, simultaneously multiple metals such as iron, carbon steel is also had corrosion inhibition.Zinc chloride is a kind of cathodic corrosion inhibitor, and is very easily water-soluble, solubilized oxidation on metal surface thing.Poly-epoxy succinic acid, poly-epoxy succinic acid (PESA) are a kind of no nitrogen, non-phosphorus organic compound, have the scale inhibitor double effects concurrently, and biodegradability is good and be applicable to high-alkali, high metal content water system, is a kind of green Water Treatment Chemicals.
The invention has the beneficial effects as follows 2-phosphonate group-1,2 among the present invention, the 4-tricarboxylic acid, hydroxy ethylene diphosphonic acid, acrylic terpolymer, benzotriazole, poly-epoxy succinic acid has good anticorrosion-antiscaling property, and the scale inhibitor effect after composite by the weight part of the present invention prescription obviously strengthens.The present invention is suitable for high hard, high-alkali, and carbonate deposit is had extremely strong complexing.Corrosion and scale inhibition performance is good, and phosphorus content is low, and each component is nontoxic, can not pollute compliance with environmental protection requirements to environment.The present invention is not only applicable to the more natural gas conditioning treatment plant of high rigidity, high basicity, high-temperature and calcium ions, magnesium ion and sulfate ion, chemical plant recirculating cooling water system, is applicable to the industry recirculating cooling water system such as chemical fertilizer, electric power, weaving of high rigidity, high basicity, high-temperature yet.Wide accommodation does not need to add acid and regulates pH value.
In order to further specify the present invention, below in conjunction with embodiment composite scale-inhibiting corrosion inhibitor provided by the invention is described in detail, but they can not be interpreted as restriction to protection domain of the present invention.
The embodiment of existing anti-incrustation corrosion inhibitor: