CN105642822B - 一种新型离心铸造用涂料及其制备方法 - Google Patents
一种新型离心铸造用涂料及其制备方法 Download PDFInfo
- Publication number
- CN105642822B CN105642822B CN201610185164.5A CN201610185164A CN105642822B CN 105642822 B CN105642822 B CN 105642822B CN 201610185164 A CN201610185164 A CN 201610185164A CN 105642822 B CN105642822 B CN 105642822B
- Authority
- CN
- China
- Prior art keywords
- coating
- novel centrifugal
- foundry facing
- preparation
- phenolic resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种新型离心铸造用涂料,其由以下重量百分比的原料组成:粘结剂2-8%、耐火骨料18-28%、松节油0.02-0.03%、酚醛树脂0.03-0.05%,余量为水。本发明涂料配比简单、易操作,该涂料具有较高的抗冲刷能力和耐火强度,较低的发气量和较好的脱模效果(铸件表面光洁)等。
Description
技术领域
本发明属于涂料制备技术领域,具体涉及一种新型离心铸造金属型模具使用的涂料及其制备方法。
背景技术
使用金属型离心铸造工艺生产气缸套时,要求涂料起到保护模具、改善铸件毛坯外表面质量、控制高温溶液向模具的导热速率。这就要求离心铸造涂料具有较高的抗冲刷能力、高耐火强度、低的发气量和较好的脱模效果,即要求铸件脱离铸型后,金属模具上没有残余的涂料。
发明内容
本发明目的在于克服现有技术缺陷,提供一种配比简单、易操作的新型离心铸造用涂料,该涂料具有较高的抗冲刷能力和耐火强度,较低的发气量和较好的脱模效果(铸件表面光洁)等。
本发明另一目的在于还提供了上述新型离心铸造用涂料的制备方法。
为实现上述目的,本发明采用如下技术方案:
一种新型离心铸造用涂料,其由以下重量百分比的原料组成:
粘结剂2-8%、耐火骨料18-28%、松节油0.02-0.03%、酚醛树脂0.03-0.05%,余量为水。
具体的,所述粘结剂优选为钠基膨润土。
具体的,所述耐火骨料选用SiO2含量80%以上的硅藻土。
本发明涂料配方中,使用的松节油和酚醛树脂两者都是作为涂料的改性粘结剂,酚醛树脂具有耐高温性,即使在非常高的温度下,也能保持其结构的整体性和尺寸的稳定性,且能和其它有机或无机填料都能相溶。两种添加剂的加入,提高了涂料在金属模具中的粘结强度,使得在浇注过程中涂料不容易被冲刷掉。
上述新型离心铸造用涂料的制备方法,具体为:按比例取各原料,将粘结剂和水混合均匀,然后加入耐火骨料,混匀后再加入松节油和酚醛树脂,混合均匀后即可使用。在室温条件下(25±2℃),采用φ4流量杯检测粘度,涂料粘度在35-45s;采用比重杯称量检测比重,涂料比重在1.1-1.2 g/cm3。
和现有技术相比,本发明的有益效果:
通过生产实践证明:使用本发明涂料后,铸件表面光洁、平整。铸件的设计加工余量也大大减少;金属模具内孔也没有残留的涂料粘附。此外,由于本发明涂料要求使用的模具温度低,且铸件在出模型时能将涂料整体全部带出,和现有涂料工艺相比,使用本发明涂料大大提高了金属模具的寿命。
具体实施方式
以下结合实施例对本发明的技术方案作进一步地详细介绍,但本发明的保护范围并不局限于此。
下述实施例中,所用耐火骨料选用SiO2含量80%以上的硅藻土。硅藻土和酚醛树脂购买普通市售产品即可。
实施例1
一种新型离心铸造用涂料,其由以下重量百分比的原料组成:
钠基膨润土5%、硅藻土25%、松节油0.02%、酚醛树脂0.04%,余量为水。
上述新型离心铸造用涂料的制备方法,具体为:按比例取各原料,将膨润土和水混合均匀(搅拌约5h),然后加入硅藻土,继续搅拌1h后再加入松节油和酚醛树脂,混合均匀(搅拌约1h)后即可使用。
所得涂料的粘度约32s,比重约1.18g/cm3。
实施例2
一种新型离心铸造用涂料,其由以下重量百分比的原料组成:
钠基膨润土3%、硅藻土18%、松节油0.03%、酚醛树脂0.05%,余量为水。
上述新型离心铸造用涂料的制备方法参照实施例1。
所得涂料的粘度约35s ,比重约1.18 g/cm3。
实施例3
一种新型离心铸造用涂料,其由以下重量百分比的原料组成:
钠基膨润土8%、硅藻土22%、松节油0.03%、酚醛树脂0.03%,余量为水。
上述新型离心铸造用涂料的制备方法参照实施例1。
所得涂料的粘度约45s,比重控制在1.1-1.2 g/cm3。
本发明涂料的创新点在于原料的选择和加入比例,尤其是松节油、酚醛树脂的添加量,若超出范围,则在生产上达不到好的使用效果。使用本发明涂料时,将涂料装入压力容器内,并用软管接入能调节的自动喷涂设备上,在生产前调整喷涂速度和喷涂量。喷涂前金属模具的温度要预热到200-300℃,待转速达到600-700r/min并稳定后开始喷涂,喷涂4-6个来回,保持涂料厚度在0.8-1.4mm即可。
应用效果
使用现有涂料,金属模具的预热温度要达到400℃以上,才能保证铸件的金相A型石墨达到70%以上,且金属浇注模具寿命只能达到300-500件。而使用本发明的涂料后,金属模具只需要预热到200℃左右,铸件的金相A型石墨就能达到90%以上,且金属浇注模具寿命能达到800-1000件。此外,由于现有涂料中添加有表面活性剂,使得铸件表面粗糙,所以铸件的单边加工余量达到3-5mm;而使用本发明涂料后,铸件的单边加工余量可以减少到1.5-2.5mm。
Claims (2)
1.一种新型离心铸造用涂料,其特征在于,由以下重量百分比的原料组成:
粘结剂2-8%、耐火骨料18-28%、松节油0.02-0.03%、酚醛树脂0.03-0.05%,余量为水;所述粘结剂为钠基膨润土;
所述耐火骨料选用SiO2含量80%以上的硅藻土。
2.权利要求1所述新型离心铸造用涂料的制备方法,其特征在于,按比例取各原料,将粘结剂和水混合均匀,然后加入耐火骨料,混匀后再加入松节油和酚醛树脂,混合均匀后即可使用。