CN105623012A - Formula of anticorrosive rubber - Google Patents
Formula of anticorrosive rubber Download PDFInfo
- Publication number
- CN105623012A CN105623012A CN201610163951.XA CN201610163951A CN105623012A CN 105623012 A CN105623012 A CN 105623012A CN 201610163951 A CN201610163951 A CN 201610163951A CN 105623012 A CN105623012 A CN 105623012A
- Authority
- CN
- China
- Prior art keywords
- rubber
- parts
- formula
- follows
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A formula of anticorrosive rubber comprises the following components: nitrile rubber, zinc oxide, stearic acid, an antiager ODA (4,4'-dioctyl-diphenylamin), carbon black 880, light calcium carbonate, dioctyl phthalate, an accelerator C2, an accelerator TMTD (tetramethyl thiuram disulfide) and sulfur. The formula of the anticorrosive rubber has the benefits as follows: the formula of the sealing rubber is obtained through multiple tests; the prepared rubber has the hardness of 43 degrees and the tensile strength of 11.6MPa, is corrosion resistant and durable, and can be widely used in a variety of extreme environments; a preparation method of the rubber is simple and low in cost and can be widely applied.
Description
Technical field
The present invention relates to chemical technology field, especially relate to a kind of antiseptic rubber formula.
Background technology
Early stage rubber is the latex taking from the plant such as rubber tree, russian dandelion, the material with elasticity, insulativity, waterproof and air made after processing. Elastomeric macromolecular compound. It is divided into natural rubber and synthetic rubber two kinds. Natural rubber extracts colloid post-treatment from the plant such as rubber tree, russian dandelion to make; Synthetic rubber is then obtained through polyreaction by various monomer. Rubber item is widely used in industry or life each side. Rubber industry is one of important foundation industry of national economy. It is not only the light industry rubber product such as daily, medical that people provide daily life indispensable, and provides various rubber production unit or rubber components to the heavy industry such as digging, traffic, building, machinery, electronics and new industry. Visible, the product category of rubber industry is various, and backward industry is very wide, but current rubber facilitates effect general corrosion-resistant, does not reach the requirement of people.
Summary of the invention
For overcoming above-mentioned technical problem, the technical solution used in the present invention is as follows:
A kind of antiseptic rubber formula, described system component is as follows: paracril, zinc oxide, stearic acid, anti-aging agent ODA, carbon black 880, light calcium, o-phthalic acid dibutyl ester, accelerant C 2, Vulcanization accelerator TMTD, sulphur.
Described preferred part number is as follows: paracril 100 parts, 5 parts, zinc oxide, stearic acid 1.5 parts, anti-aging agent ODA1.5 part, carbon black 88070 parts, light calcium 10 parts, o-phthalic acid dibutyl ester 30 parts, accelerant C 21.5 parts, Vulcanization accelerator TMTD 1.5 parts, 0.3 part, sulphur.
The invention has the beneficial effects as follows: the formula of sealing rubber obtains through test of many times, obtained rubber hardness is 43 degree, tensile strength is 11.6MPa, have corrosion-resistant, durable, can widely use at various extreme environment, and method for preparing rubber is simple, cost is low, it is possible to widespread use.
Embodiment
A kind of antiseptic rubber formula, described system component is as follows: paracril 100 parts, 5 parts, zinc oxide, stearic acid 1.5 parts, anti-aging agent ODA1.5 part, carbon black 88070 parts, light calcium 10 parts, o-phthalic acid dibutyl ester 30 parts, accelerant C 21.5 parts, Vulcanization accelerator TMTD 1.5 parts, 0.3 part, sulphur.
By above-mentioned formula sulfuration, cure conditions: 155 DEG C, 15 minutes.
The above; being only the specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, any those of ordinary skill in the art are in the technical scope disclosed by the present invention; the change that can expect easily or replacement, all should be encompassed within protection scope of the present invention. Therefore, protection scope of the present invention should be as the criterion with the protection domain that claim book limits.
Claims (2)
1. an antiseptic rubber formula, it is characterised in that described system component is as follows: paracril, zinc oxide, stearic acid, anti-aging agent ODA, carbon black 880, light calcium, o-phthalic acid dibutyl ester, accelerant C 2, Vulcanization accelerator TMTD, sulphur.
2. a kind of antiseptic rubber formula according to claim 1, it is characterised in that described preferred part number is as follows: paracril 100 parts, 5 parts, zinc oxide, stearic acid 1.5 parts, anti-aging agent ODA1.5 part, carbon black 88070 parts, light calcium 10 parts, o-phthalic acid dibutyl ester 30 parts, accelerant C 21.5 parts, Vulcanization accelerator TMTD 1.5 parts, 0.3 part, sulphur.