CN105622050A - Environmentally-friendly anti-static floor and production method therefor - Google Patents
Environmentally-friendly anti-static floor and production method therefor Download PDFInfo
- Publication number
- CN105622050A CN105622050A CN201510972907.9A CN201510972907A CN105622050A CN 105622050 A CN105622050 A CN 105622050A CN 201510972907 A CN201510972907 A CN 201510972907A CN 105622050 A CN105622050 A CN 105622050A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight ratio
- floor
- environment
- friendly type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environmentally-friendly anti-static floor. The floor comprises the following raw materials in parts by weight: 35-40 parts of iron-smelting blast furnace molten slag, 10-15 parts of ultrafine talcum powder, 35-45 parts of coal ash, 30-40 parts of plant particles, 1-2 parts of mineral fibers, 5-8 parts of sepiolite, 4-6 parts of bentonite, 8-12 parts of quick lime, 0.6-0.8 parts of magnesium silicate, 0.6-0.8 parts of a silane-based water repellent SEAL80, 6-8 parts of a wetting agent, 2-3 parts of a thermal stabilizer and 2-3 parts of an anti-static agent. According to the floor, high-temperature iron-smelting furnace slag discharged by a blast furnace in an iron-smelting plant is taken as a raw material, so that wastes are turned into wealth; components such as the plant particles, the mineral fibers and the like are added, so that a heat insulation material has very good aging resistance and light degradation resistance, and the mechanical property is superior to that of a general material; the mineral fibers improve the strength and toughness of the heat insulation material; the anti-static agent enables the material to have an anti-static effect; and the floor is low in heat conduction coefficient and good in energy-saving effect, and is an environmentally-friendly decoration material.
Description
Technical field
The invention belongs to decorative materials technology, be specifically related to a kind of environment-friendly type antistatic floor and preparation method thereof.
Background technology
The antistatic technique of computer floor, is belonging to a part for computer room safety and protection category. The electrostatic produced for various reasons, is that generation is most frequent, is most difficult to one of harm of elimination. Electrostatic not only can make computer occur random fault, misoperation or operation mistake when running, but also may result in some components and parts, puncturing and damaging such as CMOS, MOS circuit, twin-stage circuit etc. In addition the external equipment of computer is also had obvious impact by electrostatic, with the display device of cathode ray tube, when being subject to static interference, image can be caused disorderly, please obscure. Electrostatic also can cause the work such as Modem, network interface card, Fax not normal, the fault such as the printing of printer is abnormal. The problem that electrostatic causes not only hardware personnel be difficult to find, and sometimes may also be peopleware thinks it is software fault by mistake, thus causing work chaotic. Additionally, (so-called sparking) reaches to a certain degree when energy when computer or other equipment are discharged by electrostatic by human body, the sensation of electric shock also can be given.
Energy-saving material refers to that energy-conserving and environment-protective industry refers to as saving energy resources, develop a circular economy, protecting environment to provide the industry of technical foundation and equipment Safeguard, mainly include Energy Saving Industry, resoures recycling based industry and environmental protection equipment industry, relate to energy-conserving and environment-protective technology and equipment, energy-conserving product and service etc.; Its six big field includes: power-saving technology and equipment, energy-efficient product, energy conservation service industry, advanced green technology and equipment, environment-friendly products and environmental protection service.
Industrial residue utilization rate constantly rose in recent years. The dry slag of solid-state is mainly used in building highway, railway, foundation engineering, the raw material of melting mineral wool or make aggregate, and Water Quenching Slag is used as cement mixture (filler) in a large number, also has a small amount of slag to change into swollen pearl and is used as ornament materials lightweight aggregate.
But dry, grinding that Water Quenching Slag is in utilizing process process and not only to exhaust substantial amounts of energy, and smelt a large amount of waste heats entrained by high-temperature liquid state slag and also can be wasted. Therefore, studying the high-temperature liquid state slag discharged by steelmaking furnace and be made directly process without shrend, the new energy-saving process making ornament materials is significant.
At present, clay class that furnishing fields uses and the wall decorative material being gellant with cement, although it has the advantages such as intensity height, good endurance, but its unit weight is big, and antistatic, sound insulation, heat-proof quality are poor so that it is range of application is restricted. Also exist simultaneously high cost source and fuel, complex process, very easily to environment.
Summary of the invention
The invention aims to make full use of industrial residue and coal ash is base stock, make the ornament materials with advantages such as higher-strength, static electricity resistance, insulation and sound insulations.
The technical scheme that the present invention takes is:
A kind of environment-friendly type antistatic floor, it is characterised in that feed components is composed as follows according to weight portion:
Blast furnace slag 35-40 part, superfine talcum powder 10-15 part, flyash 35-45 part, plant granule 30-40 part, mineral fibres 1-2 part, meerschaum 5-8 part, bentonite 4-6 part, quick lime 8-12 part, magnesium silicate 0.6-0.8 part, silylation hydrophober SEAL800.6-0.8 part, wetting agent 6-8 part, heat stabilizer 2-3 part, antistatic agent 2-3 part.
Described antistatic agent is that fluorite, prodan and EVA re-dispersible glue powder are according to the weight ratio 3:5:1 mixture formed;
Described plant granule be wheat straw and corn stalk according to particle diameter after weight ratio 2:3 co-grinding at the granule of 10-20mm.
Further, described mineral fibres is that methylcellulose, vinal and glass fibre are according to the weight ratio 1:2:1 mixture formed.
Further, described wetting agent is succinic acid dibutyl ester sodium sulfonate is 1:15 with its weight ratio of sodium alkyl sulfonate.
Further, described heat stabilizer is that calcium carbonate and soda are according to the weight ratio 3:1 mixture formed. Beneficial effects of the present invention:
The high bloomery furnace slag that the present invention discharges with Iron Works, for raw material, is turned waste into wealth, and adds the composition such as plant granule and mineral fibres so that the insulation material of the present invention has good aging resistance, anti-light degradability, and mechanical property is superior to common material. Mineral fibres adds intensity and the toughness of insulation material, and antistatic agent makes material material have effect of antistatic, and its heat conductivity is low, good energy-conserving effect, is a kind of environment-friendly type decorating material.
Detailed description of the invention
Embodiment 1
A kind of environment-friendly type antistatic floor, it is characterised in that feed components is composed as follows according to weight portion:
Blast furnace slag 35 parts, superfine talcum powder 10 parts, 35 parts of flyash, plant granule 30 parts, mineral fibres 1 part, meerschaum 5 parts, bentonite 4 parts, quick lime 8 parts, magnesium silicate 0.6 part, silylation hydrophober SEAL800.6 part, wetting agent 6 parts, heat stabilizer 2 parts, antistatic agent 2 parts.
Described antistatic agent is that fluorite, prodan and EVA re-dispersible glue powder are according to the weight ratio 3:5:1 mixture formed;
Described plant granule be wheat straw and corn stalk according to particle diameter after weight ratio 2:3 co-grinding at the granule of 10-20mm.
Further, described mineral fibres is that methylcellulose, vinal and glass fibre are according to the weight ratio 1:2:1 mixture formed.
Further, described wetting agent is succinic acid dibutyl ester sodium sulfonate is 1:15 with its weight ratio of sodium alkyl sulfonate.
Further, described heat stabilizer is that calcium carbonate and soda are according to the weight ratio 3:1 mixture formed.
Embodiment 2
A kind of environment-friendly type antistatic floor, it is characterised in that feed components is composed as follows according to weight portion:
Blast furnace slag 40 parts, superfine talcum powder 15 parts, 45 parts of flyash, plant granule 40 parts, mineral fibres 2 parts, meerschaum 8 parts, bentonite 6 parts, quick lime 12 parts, magnesium silicate 0.8 part, silylation hydrophober SEAL800.8 part, wetting agent 8 parts, heat stabilizer 3 parts, antistatic agent 3 parts.
Described antistatic agent is that fluorite, prodan and EVA re-dispersible glue powder are according to the weight ratio 3:5:1 mixture formed;
Described plant granule be wheat straw and corn stalk according to particle diameter after weight ratio 2:3 co-grinding at the granule of 10-20mm.
Further, described mineral fibres is that methylcellulose, vinal and glass fibre are according to the weight ratio 1:2:1 mixture formed.
Further, described wetting agent is succinic acid dibutyl ester sodium sulfonate is 1:15 with its weight ratio of sodium alkyl sulfonate.
Further, described heat stabilizer is that calcium carbonate and soda are according to the weight ratio 3:1 mixture formed.
Claims (4)
1. an environment-friendly type antistatic floor, it is characterised in that feed components is composed as follows according to weight portion:
Blast furnace slag 35-40 part, superfine talcum powder 10-15 part, flyash 35-45 part, plant granule 30-40 part, mineral fibres 1-2 part, meerschaum 5-8 part, bentonite 4-6 part, quick lime 8-12 part, magnesium silicate 0.6-0.8 part, silylation hydrophober SEAL800.6-0.8 part, wetting agent 6-8 part, heat stabilizer 2-3 part, antistatic agent 2-3 part;
Described antistatic agent is that fluorite, prodan and EVA re-dispersible glue powder are according to the weight ratio 3:5:1 mixture formed;
Described plant granule be wheat straw and corn stalk according to particle diameter after weight ratio 2:3 co-grinding at the granule of 10-20mm.
2. a kind of environment-friendly type antistatic floor according to claim 1, it is characterised in that described mineral fibres is that methylcellulose, vinal and glass fibre are according to the weight ratio 1:2:1 mixture formed.
3. a kind of environment-friendly type antistatic floor according to claim 1, it is characterised in that described wetting agent is succinic acid dibutyl ester sodium sulfonate is 1:15 with its weight ratio of sodium alkyl sulfonate.
4. a kind of environment-friendly type antistatic floor according to claim 1, it is characterised in that described heat stabilizer is that calcium carbonate and soda are according to the weight ratio 3:1 mixture formed.