CN105621919A - 一种水泥用促凝剂的制备方法 - Google Patents
一种水泥用促凝剂的制备方法 Download PDFInfo
- Publication number
- CN105621919A CN105621919A CN201410579327.9A CN201410579327A CN105621919A CN 105621919 A CN105621919 A CN 105621919A CN 201410579327 A CN201410579327 A CN 201410579327A CN 105621919 A CN105621919 A CN 105621919A
- Authority
- CN
- China
- Prior art keywords
- parts
- setting accelerator
- cement setting
- calx
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种水泥用促凝剂的制备方法,按重量份数计:包括硫酸钠1-3份、硫酸铝1-2份、苏打1-3份、石灰石5-10份、硫酸钙2-5份。按以上配比取得上述原料,将以上组合物一次性全部混合,搅拌,研磨至粒度≤1mm的粉末状,封包即可。
Description
技术领域
本发明属于水泥外加剂技术领域,涉及一种水泥用促凝剂的制备方法。
背景技术
水泥是现代工业发展重要基础材料,围绕著水泥相关的技术研究也越来越多,其中水泥添加剂领域就包含各种各样,促凝剂就是其中一种。当下,市场上常见的促凝剂使用的大多数为氯化钙。而使用这种物质加速凝固的水泥坚固性不够高,且作业中会产生严重的环境污染问题。所以,需要研发一种替代方案。
发明内容
针对以上技术中存在的缺陷,本发明提供一种水泥用促凝剂的制备方法。
为解决上述技术问题,本发明所述水泥用促凝剂的制备方法,其特征在于包括以下步骤:
第一步,取硫酸钠1份、硫酸铝1份、苏打2份、石灰石6份、硫酸钙3份。
第二步,将以上组合物一次性全部混合。
第三步,搅拌,研磨至粒度≤1mm的粉末状。
第四步,封包即可。
具体实施方式
实施例1
一种水泥用促凝剂,其特征在于包括以下组成,按重量份数计:硫酸钠1份、硫酸铝1份、苏打2份、石灰石6份、硫酸钙3份。
本发明所述的水泥用促凝剂的制备方法如下:
将以上组合物一次性全部混合,搅拌,研磨至粒度≤1mm的粉末状,封包即可。
实施例2
一种水泥用促凝剂,其特征在于包括以下组成,按重量份数计:硫酸钠1份、硫酸铝1份、碳酸氢钠1.3份、熟石灰6份、硫酸钙3份,水0.5份。
本发明所述的水泥用促凝剂的制备方法如下:
首先将熟石灰与水混合,搅拌。置于通风处,待风干后,余剩余组合物全部混合,搅拌,研磨至粒度≤1mm的粉末状,封包即可。
Claims (5)
1.一种水泥用促凝剂的制备方法,其特征在于包括以下步骤:
第一步,取硫酸钠1份、硫酸铝1份、苏打2份、石灰石6份、硫酸钙3份。
第二步,将以上组合物一次性全部混合。
第三步,搅拌,研磨至粒度≤1mm的粉末状。
第四步,封包即可。
2.根据权利要求1所述的水泥用促凝剂的制备方法,其特征在于:所述苏打可用重量比约为1.2-1.5倍的碳酸氢钠替代。
3.根据权利要求1所述的水泥用促凝剂的制备方法,其特征在于:所述石灰石可用熟石灰代替。
4.根据权利要求3所述,当使用熟石灰替代石灰石时,需添加熟石灰使用量约5%-10%的水。
5.根据权利要求4所述,当使用熟石灰替代石灰石时,第一步需要单独混合熟石灰和水进行,然后风干。