CN105603738A - High-frequency hot-pressing PVC coated cloth process - Google Patents
High-frequency hot-pressing PVC coated cloth process Download PDFInfo
- Publication number
- CN105603738A CN105603738A CN201510787614.3A CN201510787614A CN105603738A CN 105603738 A CN105603738 A CN 105603738A CN 201510787614 A CN201510787614 A CN 201510787614A CN 105603738 A CN105603738 A CN 105603738A
- Authority
- CN
- China
- Prior art keywords
- coated
- pasting
- painting
- face
- plasticizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-frequency hot-pressing PVC coated cloth process which is characterized by comprising the following steps: step 1, selecting bottoming base cloth; step 2, carrying out vertical-coating paste coating on front and back surfaces; and step 3, carrying out top-coating paste coating, wherein in the step of carrying out vertical-coating paste coating on the front and back surfaces, a vertical-coating paste is used and comprises resin, a plasticizer, a stabilizer, calcium carbonate, a binding agent and a mildew preventive, and the ratio of the resin to the plasticizer to the stabilizer to the calcium carbonate to the binding agent to the mildew preventive is (100-120) to (75-100) to (2.5-5) to (50-60) to (6-8) to (2-4); in the step of carrying out top-coating paste coating, a top-coating paste is used and comprises resin, a plasticizer, a stabilizer, calcium carbonate and a mildew preventive, and the ratio of the resin to the plasticizer to the stabilizer to the calcium carbonate to the mildew preventive is (100-120) to (60-80) to (2.5-5) to (10-15) to (2-4). The high-frequency hot-pressing PVC coated cloth process is sample, and the PVC coated cloth is suitable for high-frequency hot-pressing, is conveniently processed into various sizes, and is suitable for various occasions when used as PVC coated cloth; a color can be customized according to needs of customers; the surface can be made matte or bright according to needs of the customers; and the gram weight also can be suitably changed according to needs of the customers.
Description
Technical field
The present invention relates to PVC coated fabric technical field, relate in particular to a kind of High frequency heating PVC coating.
Background technology
Along with the progress of social development, society, increasing new material is used in our life, wherein PVC coated fabric is taking glass-fiber-fabric, glass cotton, chemical fabric as base cloth, apply and form with special process, Main Feature: have waterproof, fire-retardant, mildew-resistant, cold-proof,, the feature such as anticorrosion, ageing-resistant, antiultraviolet.
But traditional PVC coated fabric is because it can not be high temperature resistant, thus be not suitable for doing high temperature hot pressing, thus inconvenient various sizes size customized has brought huge trouble to production, making, transport etc.
Summary of the invention
The object of the invention is the shortcoming existing in prior art in order to solve, and a kind of High frequency heating PVC coated fabric technique proposing.
To achieve these goals, the present invention has adopted following technical scheme:
A kind of High frequency heating PVC coated fabric technique, is characterized in that: comprise the following steps: the first step, selection bottoming base cloth; Second step, the pasting of vertical painting positive and negative; The 3rd step, face are coated with pasting.
Preferably, described base cloth specification is 1000DX1000D/23X23 woven fabric.
Preferably, the pasting of vertical painting positive and negative comprises the vertical slurry that is coated with, its neutral pasting material comprises resin, plasticizer, stabilizing agent, calcium carbonate, adhesive and mould inhibitor, and resin: plasticizer: stabilizing agent: calcium carbonate: adhesive: mould inhibitor=100-120:75-100:2.5-5:50-60:6-8:2-4.
Preferably, the technological parameter of the neutral painting of second step positive and negative pasting is: controlling vertical painting oven temperature is 170 DEG C-180 DEG C, and vertical painting starching is wanted evenly, guarantee to cover cloth cover, thickness is 0.38 ㎜, and sleeping sleeping while being coated with starching to be coated with baking oven control be 170 DEG C-180 DEG C, and thickness is 0.45 ㎜.
Preferably, face is coated with pasting and comprises that face is coated with slurry, and wherein face painting slurry comprises resin, plasticizer, stabilizing agent, calcium carbonate and mould inhibitor, wherein resin: plasticizer: stabilizing agent: calcium carbonate: mould inhibitor=100-120:60-80:2.5-5:10-15:2-4.
Preferably, in the 3rd step, the technological parameter of face painting pasting is: face is coated with 25m oven temperature and is set to 170 DEG C-185 DEG C, and gross thickness is 0.55 ㎜.
Preferably, the vertical viscosity that is coated with positive and negative pasting or face painting pasting is 5500cp-6500cp.
The coating process of tent cloth provided by the invention, this High frequency heating PVC coated fabric technique is simple, be applicable to High frequency heating, be convenient to be processed as all size, as PVC coated fabric, be applicable to various occasions, color can need customized according to client, sub-light or light can need to be made according to client in surface, and grammes per square metre also can need appropriate change according to client.
Detailed description of the invention
In order to make object of the present invention, technical scheme and advantage clearer, below in conjunction with specific embodiment, the present invention is further elaborated. Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not intended to limit the present invention.
Embodiment 1
A kind of High frequency heating PVC coated fabric technique, is characterized in that: comprise the following steps: the first step, selection bottoming base cloth; Second step, the pasting of vertical painting positive and negative; The 3rd step, face are coated with pasting.
Preferably, described base cloth specification is 1000DX1000D/23X23 woven fabric.
Preferably, the pasting of vertical painting positive and negative comprises the vertical slurry that is coated with, its neutral pasting material comprises resin, plasticizer, stabilizing agent, calcium carbonate, adhesive and mould inhibitor, and resin: plasticizer: stabilizing agent: calcium carbonate: adhesive: mould inhibitor=100:75:2.5:50:6:2.
Preferably, the neutral technological parameter that is coated with positive and negative pasting of second step is: control that vertical to be coated with oven temperature be 170 DEG C, be vertically coated with starching and want evenly, guarantee to cover cloth cover, thickness is 0.38 ㎜, and sleeping sleeping while being coated with starching to be coated with baking oven control be 170 DEG C, and thickness is 0.45 ㎜.
Preferably, face is coated with pasting and comprises that face is coated with slurry, and wherein face painting slurry comprises resin, plasticizer, stabilizing agent, calcium carbonate and mould inhibitor, wherein resin: plasticizer: stabilizing agent: calcium carbonate: mould inhibitor=100:60:2.5:10:2.
Preferably, in the 3rd step, the technological parameter of face painting pasting is: face is coated with 25m oven temperature and is set to 170 DEG C, and gross thickness is 0.55 ㎜.
Preferably, the vertical viscosity that is coated with positive and negative pasting or face painting pasting is 5500cp.
Embodiment 2
A kind of High frequency heating PVC coated fabric technique, is characterized in that: comprise the following steps: the first step, selection bottoming base cloth; Second step, the pasting of vertical painting positive and negative; The 3rd step, face are coated with pasting.
Preferably, described base cloth specification is 1000DX1000D/23X23 woven fabric.
Preferably, the pasting of vertical painting positive and negative comprises the vertical slurry that is coated with, its neutral pasting material comprises resin, plasticizer, stabilizing agent, calcium carbonate, adhesive and mould inhibitor, and resin: plasticizer: stabilizing agent: calcium carbonate: adhesive: mould inhibitor=120:100:5:60:8:4.
Preferably, the neutral technological parameter that is coated with positive and negative pasting of second step is: control that vertical to be coated with oven temperature be 180 DEG C, be vertically coated with starching and want evenly, guarantee to cover cloth cover, thickness is 0.38 ㎜, and sleeping sleeping while being coated with starching to be coated with baking oven control be 180 DEG C, and thickness is 0.45 ㎜.
Preferably, face is coated with pasting and comprises that face is coated with slurry, and wherein face painting slurry comprises resin, plasticizer, stabilizing agent, calcium carbonate and mould inhibitor, wherein resin: plasticizer: stabilizing agent: calcium carbonate: mould inhibitor=120:80:5:15:4.
Preferably, in the 3rd step, the technological parameter of face painting pasting is: face is coated with 25m oven temperature and is set to 185 DEG C, and gross thickness is 0.55 ㎜.
Preferably, the vertical viscosity that is coated with positive and negative pasting or face painting pasting is 6500cp.
Embodiment tri-
A kind of High frequency heating PVC coated fabric technique, is characterized in that: comprise the following steps: the first step, selection bottoming base cloth; Second step, the pasting of vertical painting positive and negative; The 3rd step, face are coated with pasting.
Preferably, described base cloth specification is 1000DX1000D/23X23 woven fabric.
Preferably, the pasting of vertical painting positive and negative comprises the vertical slurry that is coated with, its neutral pasting material comprises resin, plasticizer, stabilizing agent, calcium carbonate, adhesive and mould inhibitor, and resin: plasticizer: stabilizing agent: calcium carbonate: adhesive: mould inhibitor=110:87.75:3.75:55:7:3.
Preferably, the neutral technological parameter that is coated with positive and negative pasting of second step is: control that vertical to be coated with oven temperature be 175 DEG C, be vertically coated with starching and want evenly, guarantee to cover cloth cover, thickness is 0.38 ㎜, and sleeping sleeping while being coated with starching to be coated with baking oven control be 175 DEG C, and thickness is 0.45 ㎜.
Preferably, face is coated with pasting and comprises that face is coated with slurry, and wherein face painting slurry comprises resin, plasticizer, stabilizing agent, calcium carbonate and mould inhibitor, wherein resin: plasticizer: stabilizing agent: calcium carbonate: mould inhibitor=110:70:3.75:12.5:3.
Preferably, in the 3rd step, the technological parameter of face painting pasting is: face is coated with 25m oven temperature and is set to 177.5 DEG C, and gross thickness is 0.55 ㎜.
Preferably, the viscosity of the pasting of described vertical painting positive and negative or face painting pasting is 6000cp.
Claims (7)
1. a High frequency heating PVC coated fabric technique, is characterized in that: comprise the following steps: the first step, selection bottoming base cloth; Second step, the pasting of vertical painting positive and negative; The 3rd step, face are coated with pasting.
2. the coating process of a kind of tent cloth according to claim 1, is characterized in that: described base cloth specification is 1000DX1000D/23X23 woven fabric.
3. a kind of High frequency heating PVC coated fabric technique according to claim 1, it is characterized in that: the pasting of vertical painting positive and negative comprises the vertical slurry that is coated with, its neutral pasting material comprises resin, plasticizer, stabilizing agent, calcium carbonate, adhesive and mould inhibitor, and resin: plasticizer: stabilizing agent: calcium carbonate: adhesive: mould inhibitor=100-120:75-100:2.5-5:50-60:6-8:2-4.
4. a kind of High frequency heating PVC coated fabric technique according to claim 3, it is characterized in that: the neutral technological parameter that is coated with positive and negative pasting of second step is: controlling vertical painting oven temperature is 170 DEG C-180 DEG C, vertical painting starching is wanted evenly, guarantee to cover cloth cover, thickness is 0.38 ㎜, and when sleeping painting starching, the control of sleeping painting baking oven is 170 DEG C-180 DEG C, and thickness is 0.45 ㎜.
5. a kind of High frequency heating PVC coated fabric technique according to claim 1, it is characterized in that: face is coated with pasting and comprises that face is coated with slurry, wherein face painting slurry comprises resin, plasticizer, stabilizing agent, calcium carbonate and mould inhibitor, wherein resin: plasticizer: stabilizing agent: calcium carbonate: mould inhibitor=100-120:60-80:2.5-5:10-15:2-4.
6. a kind of High frequency heating PVC coated fabric technique according to claim 5, is characterized in that: in the 3rd step, the technological parameter of face painting pasting is: face is coated with 25m oven temperature and is set to 170 DEG C-185 DEG C, and gross thickness is 0.55 ㎜.
7. a kind of High frequency heating PVC coated fabric technique according to claim 1, is characterized in that: the vertical viscosity that is coated with positive and negative pasting or face painting pasting is 5500cp-6500cp.