CN105602404B - Concrete surface carbonization-resistant nano coating and preparation process thereof - Google Patents
Concrete surface carbonization-resistant nano coating and preparation process thereof Download PDFInfo
- Publication number
- CN105602404B CN105602404B CN201610069430.8A CN201610069430A CN105602404B CN 105602404 B CN105602404 B CN 105602404B CN 201610069430 A CN201610069430 A CN 201610069430A CN 105602404 B CN105602404 B CN 105602404B
- Authority
- CN
- China
- Prior art keywords
- component
- concrete surface
- carbonization
- parts
- nano paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Project | Parameter | Standard |
28d carbonation depths, mm | <1 | GB/T 50082-2009 |
Hubbing adhesive force is tested, MPa | 1 grade | GB/T 5210-2006 |
Pencil hardness | 6H is not scratched | GB/T 6739-2006 |
Water resistance (leaching 31 days) | It is unchanged | GB/T 1733-1993 |
Alkali resistance (saturation Ca (OH) 10 days) | It is unchanged | GB/T 9274-1988 |
Acid resistance ((0.1mol/L) HCI4 days) | It is unchanged | GB/T 9274-1988 |
Project | Parameter | Standard |
28d carbonation depths, mm | <1 | GB/T 50082-2009 |
Hubbing adhesive force is tested, MPa | 1 grade | GB/T 5210-2006 |
Pencil hardness | 6H is not scratched | GB/T 6739-2006 |
Water resistance (leaching 32 days) | It is unchanged | GB/T 1733-1993 |
Alkali resistance (saturation Ca (OH) 11 days) | It is unchanged | GB/T 9274-1988 |
Acid resistance ((0.1mol/L) HCI5 days) | It is unchanged | GB/T 9274-1988 |
Project | Parameter | Standard |
28d carbonation depths, mm | <1 | GB/T 50082-2009 |
Hubbing adhesive force is tested, MPa | 1 grade | GB/T 5210-2006 |
Pencil hardness | 6H is not scratched | GB/T 6739-2006 |
Water resistance (leaching 34 days) | It is unchanged | GB/T 1733-1993 |
Alkali resistance (saturation Ca (OH) 13 days) | It is unchanged | GB/T 9274-1988 |
Acid resistance ((0.1mol/L) HCI6 days) | It is unchanged | GB/T 9274-1988 |
Project | Parameter | Standard |
28d carbonation depths, mm | <1 | GB/T 50082-2009 |
Hubbing adhesive force is tested, MPa | 1 grade | GB/T 5210-2006 |
Pencil hardness | 6H is not scratched | GB/T 6739-2006 |
Water resistance (leaching 31 days) | It is unchanged | GB/T 1733-1993 |
Alkali resistance (saturation Ca (OH) 10 days) | It is unchanged | GB/T 9274-1988 |
Acid resistance ((0.1mol/L) HCI1 days) | It is unchanged | GB/T 9274-1988 |
Claims (4)