CN105601236A - Anion plate for house decoration - Google Patents
Anion plate for house decoration Download PDFInfo
- Publication number
- CN105601236A CN105601236A CN201511031802.XA CN201511031802A CN105601236A CN 105601236 A CN105601236 A CN 105601236A CN 201511031802 A CN201511031802 A CN 201511031802A CN 105601236 A CN105601236 A CN 105601236A
- Authority
- CN
- China
- Prior art keywords
- parts
- anion
- anion plate
- flyash
- magnesia
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anion plate for house decoration. The anion plate comprises a surface plate body and a middle plate body, wherein the surface plate body is made of, by mass, 8-15 parts of magnesium oxide, 8-15 parts of a magnesium sulfate solution, 0.5-1 part of coal ash, 3-7 parts of albite, 0.1-0.3 part of monazite, 1-3 parts of zeolite, 0.1-0.5 part of calcium stearate and 0.3-1 part of zinc oxide; the middle plate body is made of, by mass, 15-35 parts of magnesium oxide, 15-35 parts of a magnesium sulfate solution, 1-3 parts of coal ash, 6-12 parts of wood chips and 0.5-1 part of a compound modifying agent. The anion plate is simple in manufacturing process, solid waste is utilized, raw materials are low in price, and the anion plate has durability, high efficiency and environmental protection performance and is an environment-friendly interior decoration plate for a building.
Description
Technical field
The present invention relates to a kind of decorative panel, be specifically related to a kind of house decoraton anion plate.
Background technology
Living environment constantly receives people's concern on healthy impact, it is luxurious, attractive in appearance that people pursue indoor decoratingMeanwhile, also paying close attention to indoor pollution affects health, the feature of environmental protection of construction timber, and the impact that health is produced.Therefore, various wholesome novel building functional materials arise at the historic moment.
Anion material has one of the multifunctional novel such as environmental protection, health material representative as one, is widely used in and spinsThe fields such as fabric, pottery, construction material. Since Aschkinass in 1902 and Caspan certainly negative aeroion there is biologyMeaning, since Soviet Union scholar in 1903 has delivered and utilized negative aeroion to eliminate the paper of germ, in recent years, scientific research personnel has carried outLot of experiments, has further affirmed the value of negative aeroion.
Negative oxygen ion concentration in room, city is 100 every cubic centimetre, and the concentration in building office is even low to every cubeCentimetres 40～50, and the standard that the World Health Organization delimit, the negative oxygen ion content of fresh air is in every cc of airBe not less than 1000～1500, so often easily bring out the discomforts such as headache and insomnia such environmental work. A lot of cities white collar workDo after one day to feel to feel dizzy, just and air inadequate " nutrition " have certain relation. And forest and waterfall area, high mountain seashoreVery abundant with " atmosphere vitamin " content in park, can reach respectively 10000～20000 every cubic centimetre, 5000～10000Individual and 400～1000. Negative oxygen ion can promote human body metabolism, flu-prevention, enhancing body resistance against diseases.
Anion sheet material is to add anionic additive, and a kind of energy of making continues to produce the feature of environmental protection inner wall decoration plate of anion.Anion has several functions, very useful to health.
CN104400878A Chinese patent discloses a kind of health care sheet material and compound health that can produce anion and far infraredPlate, the preparation technology that it stresses to set forth health care sheet material, does not wherein disclose raw material, the health care sheet material anion releasing makingConcentration reaches 6000/cm3。
The invention provides a kind of anion plate, solid waste utilization, can cut arbitrarily, and manufacture craft is simple, the prices of raw and semifnished materialsCheap, be applicable to large-scale production, anion releasing that can efficient stable, can purify air, eliminate foreign flavor indoors and variousPernicious gas.
Summary of the invention
The invention provides a kind of anion plate that house decoraton is used that is applicable to, anion releasing that can efficient stable, can purifyAir, elimination foreign flavor indoors and various pernicious gas are a kind of new and effective stable negative ion plates.
The present invention seeks to realize by the following technical solutions:
A kind of house decoraton anion plate, described anion plate comprises panel and middle plate, according to mass fraction meter, described panelMade by following component: magnesia 8-15 part, Adlerika 8-15 part, flyash 0.5-1 part, albite 3-7 part, solelyOccupy stone 0.1-0.3 part, zeolite 1-3 part, calcium stearate 0.1-0.5 part, zinc oxide 0.3-1 part;
Described middle plate is made by following component: magnesia 15-35 part, Adlerika 15-35 part, flyash 1-3 part, wood chip6-12 part, composite modifier 0.5-1 part.
First preferred version of anion plate for house decoraton, described according to mass fraction meter, described panel is by following componentMake: magnesia 8-10 part, Adlerika 10-15 part, flyash 0.8-1 part, albite 3-6 part, monazite 0.2-0.3Part, zeolite 2-3 part, calcium stearate 0.2-0.5 part, zinc oxide 0.5-1 part.
Second preferred version of anion plate for house decoraton, described according to mass fraction meter, panel is made by following component:10 parts, magnesia, 12 parts of Adlerikas, 1 part, flyash, 5 parts of albites, 0.2 part of monazite, 2 parts, zeolite is hard0.4 part of resin acid calcium, 0.5 part, zinc oxide.
The 3rd preferred version of anion plate for house decoraton, middle plate is made by following component: magnesia 15-30 part, sulphurAcid magnesium solution 15-30 part, flyash 2-3 part, wood chip 6-10 part, composite modifier 0.5-0.8 part.
The 4th preferred version of anion plate for house decoraton, middle plate is made by following component: 20 parts, magnesia, magnesium sulfate25 parts of solution, 2 parts, flyash, 8 parts of wood chips, 0.8 part of composite modifier.
The 5th preferred version of anion plate for house decoraton, the concentration 25～50% of Adlerika.
The 6th preferred version of anion plate for house decoraton, the concentration 40% of Adlerika.
The 7th preferred version of anion plate for house decoraton, the raw material of panel and middle plate also comprises gangue.
The 8th preferred version of anion plate for house decoraton, anion plate is by the flat method of roller or laminating preparation.
Compared with immediate prior art, technical scheme provided by the invention has following excellent effect:
(1) anion plate provided by the invention obtains by solid waste utilization, can cut arbitrarily, and simple, the former material of manufacture craftExpect cheap, be applicable to large-scale production;
(2) 2000～3800/scm of anion releasing that anion plate provided by the invention can efficient stable2, can purifyAir, elimination foreign flavor indoors and various pernicious gas;
(3) anion plate provided by the invention has persistence, high efficiency, the feature of environmental protection.
Detailed description of the invention
Below in conjunction with embodiment, technical scheme of the present invention is clearly and completely described, obviously, described enforcementExample is only the present invention's part embodiment, instead of whole embodiment. Based on the embodiment in the present invention, the common skill in this areaArt personnel, not making the every other embodiment obtaining under creative work prerequisite, belong to the scope of protection of the invention.
Case study on implementation 1:
Raw panels: 8 parts, magnesia, 8 parts of Adlerikas, 1 part, flyash, 3 parts of albites, 0.1 part of monazite,1 part, zeolite, 0.1 part of calcium stearate, 0.3 part, zinc oxide;
Middle board raw material: 15 parts, magnesia, 15 parts of Adlerikas, 1 part, flyash, 9 parts of wood chips, composite modifier 0.5Part.
Case study on implementation 2:
Raw panels: 10 parts, magnesia, 10 parts of Adlerikas, 0.5 part, flyash, 5 parts of albites, 0.2 part of monazite,2 parts, zeolite, 0.3 part of calcium stearate, 0.5 part, zinc oxide;
Middle board raw material: 30 parts, magnesia, 30 parts of Adlerikas, 1.5 parts, flyash, 10 parts of wood chips, composite modifier 0.5Part.
Case study on implementation 3:
Raw panels: 10 parts, magnesia, 8 parts of Adlerikas, 0.8 part, flyash, 7 parts of albites, 0.3 part of monazite,3 parts, zeolite, 0.5 part of calcium stearate, 1 part, zinc oxide;
Middle board raw material: 30 parts, magnesia, 30 parts of Adlerikas, 1 part, flyash, 6 parts of wood chips, composite modifier 0.2Part.
Case study on implementation 4:
Raw panels: 10 parts, magnesia, 12 parts of Adlerikas, 1 part, flyash, 3 parts of albites, 0.3 part of monazite,2 parts, zeolite, 0.4 part of calcium stearate, 0.5 part, zinc oxide;
Middle board raw material: 20 parts, magnesia, 25 parts of Adlerikas, 2 parts, flyash, 8 parts of wood chips, composite modifier 0.8Part.
Case study on implementation 5:
Raw panels: 15 parts, magnesia, 15 parts of Adlerikas, 0.8 part, flyash, 6 parts of albites, 0.3 part of monazite,2 parts, zeolite, 0.5 part of calcium stearate, 1 part, zinc oxide;
Middle board raw material: 35 parts, magnesia, 35 parts of Adlerikas, 3 parts, flyash, 10 parts of wood chips, 1 part of composite modifier.
Blank example:
Raw panels: 15 parts, magnesia, 15 parts of Adlerikas, 0.8 part, flyash, 0.3 part of monazite, 2 parts, zeolite,0.5 part of calcium stearate, 1 part, zinc oxide;
Middle board raw material: 35 parts, magnesia, 35 parts of Adlerikas, 3 parts, flyash, 10 parts of wood chips, 1 part of composite modifier.
In above-described embodiment, also can add other building wastes such as gangue; The concentration of Adlerika is 40%.
By each the fabric in the various embodiments described above raw material mixing and stirring, uniform spreading is contained in die surface, and each middle material raw material is mixedClose and stir, middle material is mated formation flat at fabric top roll, maintenance gets final product to obtain anion plate, adopts " JCT2040-2010 anionFunctional architecture house decorative material " standard, to carry out negative aeroion and induce measurement examination, test result is as shown in table 1:
The amount of table 1 anion plate anion releasing
Above embodiment is only in order to illustrate that technical scheme of the present invention is not intended to limit, and those of ordinary skill in the field shouldUnderstand, can modify or be equal to replacement the specific embodiment of the present invention with reference to above-described embodiment, these depart from thisAny amendment of invention spirit and scope or be equal to and replace the claim protection domain that all awaits the reply in application within.
Claims (9)
1. a house decoraton anion plate, described anion plate comprises panel and middle plate, it is characterized in that, according to mass partsNumber meter, described panel is made by following component: magnesia 8-15 part, Adlerika 8-15 part, flyash 0.5-1 part, sodiumFeldspar 3-7 part, monazite 0.1-0.3 part, zeolite 1-3 part, calcium stearate 0.1-0.5 part, zinc oxide 0.3-1 part;
Described middle plate is made by following component: magnesia 15-35 part, Adlerika 15-35 part, flyash 1-3 part, wood chip6-12 part, composite modifier 0.5-1 part.
2. a kind of house decoraton anion plate according to claim 1, is characterized in that, described according to mass fraction meter,Described panel is made by following component: magnesia 8-10 part, Adlerika 10-15 part, flyash 0.8-1 part, albite3-6 part, monazite 0.2-0.3 part, zeolite 2-3 part, calcium stearate 0.2-0.5 part, zinc oxide 0.5-1 part.
3. a kind of house decoraton anion plate according to claim 2, is characterized in that, described according to mass fraction meter,Described panel is made by following component: 10 parts, magnesia, and 12 parts of Adlerikas, 1 part, flyash, 5 parts of albites, solelyOccupy 0.2 part, stone, 2 parts, zeolite, 0.4 part of calcium stearate, 0.5 part, zinc oxide.
4. a kind of house decoraton anion plate according to claim 1, is characterized in that, described middle plate is by following componentMake: magnesia 15-30 part, Adlerika 15-30 part, flyash 2-3 part, wood chip 6-10 part, composite modifier 0.5-0.8Part.
5. a kind of house decoraton anion plate according to claim 4, is characterized in that, described middle plate is by following componentMake: 20 parts, magnesia, 25 parts of Adlerikas, 2 parts, flyash, 8 parts of wood chips, 0.8 part of composite modifier.
6. a kind of house decoraton anion plate according to claim 1, is characterized in that, described Adlerika denseDegree 25～50%.
7. a kind of house decoraton anion plate according to claim 6, is characterized in that, described Adlerika denseDegree is 40%.
8. a kind of house decoraton anion plate according to claim 1, is characterized in that, described panel and middle plate formerMaterial also comprises gangue.
9. a kind of house decoraton anion plate according to claim 1, is characterized in that, described anion plate is flat with rollerMethod or laminating preparation.