CN105503136A - Negative ion plate used for house decoration - Google Patents
Negative ion plate used for house decoration Download PDFInfo
- Publication number
- CN105503136A CN105503136A CN201511032508.0A CN201511032508A CN105503136A CN 105503136 A CN105503136 A CN 105503136A CN 201511032508 A CN201511032508 A CN 201511032508A CN 105503136 A CN105503136 A CN 105503136A
- Authority
- CN
- China
- Prior art keywords
- parts
- negative ion
- ion plate
- adlerika
- flyash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a negative ion plate used for house decoration. The negative ion plate comprises a faceplate and a middle plate, wherein the faceplate is prepared from the following components in parts by mass: 8-15 parts of magnesium oxide, 8-15 parts of magnesium sulfate solution, 0.5-1 part of flyash, 2-6 parts of anorthoclase, 8-12 parts of schorlite, 0.1-0.3 part of monazite, 1-3 parts of zeolite, 0.1-0.5 part of calcium stearate and 0.3-1 part of zinc oxide; the middle plate is prepared from the following components in parts by mass: 15-35 parts of magnesium oxide, 15-35 parts of magnesium sulfate solution, 1-3 parts of flyash, 6-12 parts of saw dust and 0.5-1 part of composite modifier. The negative ion plate has the excellent effects that the negative ion plate is simple in preparation process and low in raw material price, is obtained through solid waste utilization, has durability, high efficiency and environment friendliness and is an environment-friendly interior decorative plate used for buildings.
Description
Technical field
The present invention relates to a kind of decorative sheet, be specifically related to a kind of house decoraton negative ion plate.
Background technology
Living environment constantly receives the concern of people to healthy impact, people pursue indoor decorating luxurious, attractive in appearance while, also paying close attention to indoor pollution affects HUMAN HEALTH, the feature of environmental protection of construction timber, and on the impact that HUMAN HEALTH produces.Therefore, various wholesome novel building functional material arises at the historic moment.
Anion material has one of the multifunctional novel such as environmental protection, health material representative as one, is widely used in the fields such as textiles, pottery, material of construction.Since Aschkinass and Caspan affirmative negative aeroion in 1902 has biological meaning, since Soviet Union scholar in 1903 has delivered and has utilized negative aeroion to eliminate the paper of germ, in recent years, scientific research personnel has carried out lot of experiments, has affirmed the value of negative aeroion further.
Negative oxygen ion concentration in room, city is 100 every cubic centimetre, concentration in building office is even low to 40 ~ 50 every cubic centimetre, and the standard that the World Health Organization delimit, the negative oxygen ion content of fresh air is be not less than 1000 ~ 1500 in every cc of air, so often easily bring out the discomforts such as headache and insomnia such environmental work.The white-collar job of a lot of cities feels to feel dizzy after one day, just and air inadequate " nutrition " have certain relation.And forest and waterfall area, " air VITAMIN " content in high mountain seashore and park are very abundant, 10000 ~ 20000 every cubic centimetre, 5000 ~ 10000 and 400 ~ 1000 can be reached respectively.Negative oxygen ion can promote human metabolism, flu-prevention, enhancing body resistance against diseases.
Negative ion sheet material adds anionic additive, a kind of feature of environmental protection inner wall decoration plate that can continue to produce negatively charged ion made.Negative ion has several functions, very useful to HUMAN HEALTH.
CN104400878A Chinese patent discloses a kind of health care sheet material and the Composite health care pad that can produce negative ion and far infrared rays, it stresses the preparation technology setting forth health care sheet material, wherein do not disclose starting material, the concentration of obtained health care sheet material anion releasing reaches 6000/cm
3.
The invention provides a kind of negative ion plate, solid waste utilizes, and can cut arbitrarily, and manufacture craft is simple, the prices of raw and semifnished materials are cheap, be applicable to scale operation, can the anion releasing of efficient stable, can purify air, eliminate foreign flavor indoors and various obnoxious flavour.
Summary of the invention
The invention provides a kind of negative ion plate being applicable to house decoraton, can the anion releasing of efficient stable, can purify air, eliminate foreign flavor indoors and various obnoxious flavour, be a kind of new and effective stable negative ion plate.
The present invention seeks to realize by the following technical solutions:
A kind of house decoraton negative ion plate, described negative ion plate comprises panel and middle plate, and according to mass fraction meter, described panel is obtained by following component: magnesium oxide 8-15 part, Adlerika 8-15 part, flyash 0.5-1 part, anorthoclase 2-6 part, schorl 8-12 part, monazite 0.1-0.3 part, zeolite 1-3 part, calcium stearate 0.1-0.5 part, zinc oxide 0.3-1 part;
Described middle plate is obtained by following component: magnesium oxide 15-35 part, Adlerika 15-35 part, flyash 1-3 part, wood chip 6-12 part, composite modifier 0.5-1 part.
A kind of first preferred version of house decoraton negative ion plate, described according to mass fraction meter, described panel is obtained by following component: magnesium oxide 8-10 part, Adlerika 10-15 part, flyash 0.8-1 part, anorthoclase 3-5 part, schorl 9-11 part, monazite 0.2-0.3 part, zeolite 2-3 part, calcium stearate 0.2-0.5 part, zinc oxide 0.5-1 part.
A kind of second preferred version of house decoraton negative ion plate, described according to mass fraction meter, panel is obtained by following component: 10 parts, magnesium oxide, Adlerika 12 parts, 1 part, flyash, anorthoclase 4 parts, schorl 10 parts, monazite 0.2 part, 2 parts, zeolite, calcium stearate 0.4 part, 0.5 part, zinc oxide.
3rd preferred version of house decoraton negative ion plate, middle plate is obtained by following component: magnesium oxide 15-30 part, Adlerika 15-30 part, flyash 2-3 part, wood chip 6-10 part, composite modifier 0.5-0.8 part.
4th preferred version of house decoraton negative ion plate, middle plate is obtained by following component: 20 parts, magnesium oxide, Adlerika 25 parts, 2 parts, flyash, wood chip 8 parts, composite modifier 0.8 part.
5th preferred version of house decoraton negative ion plate, the concentration 25 ~ 50% of Adlerika.
6th preferred version of house decoraton negative ion plate, the concentration 40% of Adlerika.
7th preferred version of house decoraton negative ion plate, the raw material of panel and middle plate also comprises coal gangue.
8th preferred version of house decoraton negative ion plate, negative ion plate is by the flat method of roller or laminating preparation.
Compared with immediate prior art, technical scheme provided by the invention has following excellent effect:
(1) negative ion plate provided by the invention is utilized by solid waste and obtains, and can cut arbitrarily, and manufacture craft is simple, the prices of raw and semifnished materials are cheap, is applicable to scale operation;
(2) negative ion plate provided by the invention can anion releasing 2200 ~ 4000/scm of efficient stable
2, can purify air, eliminate foreign flavor indoors and various obnoxious flavour;
(3) negative ion plate provided by the invention has persistence, high efficiency, the feature of environmental protection.
Embodiment
Below in conjunction with embodiment, be clearly and completely described technical scheme of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Case study on implementation 1:
Raw panels: 8 parts, magnesium oxide, Adlerika 8 parts, 1 part, flyash, anorthoclase 2 parts, schorl 8 parts, monazite 0.1 part, 1 part, zeolite, calcium stearate 0.1 part, 0.3 part, zinc oxide;
Middle board raw material: 15 parts, magnesium oxide, Adlerika 15 parts, 1 part, flyash, wood chip 9 parts, composite modifier 0.5 part.
Case study on implementation 2:
Raw panels: 10 parts, magnesium oxide, Adlerika 10 parts, 0.5 part, flyash, anorthoclase 4 parts, schorl 10 parts, monazite 0.2 part, 2 parts, zeolite, calcium stearate 0.3 part, 0.5 part, zinc oxide;
Middle board raw material: 30 parts, magnesium oxide, Adlerika 30 parts, 1.5 parts, flyash, wood chip 10 parts, composite modifier 0.5 part.
Case study on implementation 3:
Raw panels: 10 parts, magnesium oxide, Adlerika 8 parts, 0.8 part, flyash, anorthoclase 6 parts, schorl 12 parts, monazite 0.3 part, 3 parts, zeolite, calcium stearate 0.5 part, 1 part, zinc oxide;
Middle board raw material: 30 parts, magnesium oxide, Adlerika 30 parts, 1 part, flyash, wood chip 6 parts, composite modifier 0.2 part.
Case study on implementation 4:
Raw panels: 10 parts, magnesium oxide, Adlerika 12 parts, 1 part, flyash, anorthoclase 2 parts, schorl 12 parts, monazite 0.3 part, 2 parts, zeolite, calcium stearate 0.4 part, 0.5 part, zinc oxide;
Middle board raw material: 20 parts, magnesium oxide, Adlerika 25 parts, 2 parts, flyash, wood chip 8 parts, composite modifier 0.8 part.
Case study on implementation 5:
Raw panels: 15 parts, magnesium oxide, Adlerika 15 parts, 0.8 part, flyash, anorthoclase 6 parts, schorl 8 parts, monazite 0.3 part, 2 parts, zeolite, calcium stearate 0.5 part, 1 part, zinc oxide;
Middle board raw material: 35 parts, magnesium oxide, Adlerika 35 parts, 3 parts, flyash, wood chip 10 parts, composite modifier 1 part.
Blank example:
Raw panels: 15 parts, magnesium oxide, Adlerika 15 parts, 0.8 part, flyash, monazite 0.3 part, 2 parts, zeolite, calcium stearate 0.5 part, 1 part, zinc oxide;
Middle board raw material: 35 parts, magnesium oxide, Adlerika 35 parts, 3 parts, flyash, wood chip 10 parts, composite modifier 1 part.
Also other building wastes such as coal gangue can be added in above-described embodiment; The concentration of Adlerika is 40%.
By each for the fabric in the various embodiments described above raw material mixing and stirring, uniform spreading is contained in die surface, by each for middle material raw material mixing and stirring, middle material is mated formation and to put down at fabric top roll, maintenance negative ion plate, " the JCT2040-2010 anion function indoor decoration material " standard of employing, carry out negative aeroion and induce measurement examination, test result is as shown in table 1:
The amount of table 1 negative ion plate anion releasing
Above embodiment is only in order to illustrate that technical scheme of the present invention is not intended to limit; those of ordinary skill in the field are to be understood that; can modify to the specific embodiment of the present invention with reference to above-described embodiment or equivalent to replace, these do not depart from any amendment of spirit and scope of the invention or equivalently to replace within the claims that all awaits the reply in application.
Claims (9)
1. a house decoraton negative ion plate, described negative ion plate comprises panel and middle plate, it is characterized in that, according to mass fraction meter, described panel is obtained by following component: magnesium oxide 8-15 part, Adlerika 8-15 part, flyash 0.5-1 part, anorthoclase 2-6 part, schorl 8-12 part, monazite 0.1-0.3 part, zeolite 1-3 part, calcium stearate 0.1-0.5 part, zinc oxide 0.3-1 part;
Described middle plate is obtained by following component: magnesium oxide 15-35 part, Adlerika 15-35 part, flyash 1-3 part, wood chip 6-12 part, composite modifier 0.5-1 part.
2. a kind of house decoraton negative ion plate according to claim 1, it is characterized in that, described according to mass fraction meter, described panel is obtained by following component: magnesium oxide 8-10 part, Adlerika 10-15 part, flyash 0.8-1 part, anorthoclase 3-5 part, schorl 9-11 part, monazite 0.2-0.3 part, zeolite 2-3 part, calcium stearate 0.2-0.5 part, zinc oxide 0.5-1 part.
3. a kind of house decoraton negative ion plate according to claim 2, it is characterized in that, described according to mass fraction meter, described panel is obtained by following component: 10 parts, magnesium oxide, Adlerika 12 parts, 1 part, flyash, anorthoclase 4 parts, schorl 10 parts, monazite 0.2 part, 2 parts, zeolite, calcium stearate 0.4 part, 0.5 part, zinc oxide.
4. a kind of house decoraton negative ion plate according to claim 1, it is characterized in that, described middle plate is obtained by following component: magnesium oxide 15-30 part, Adlerika 15-30 part, flyash 2-3 part, wood chip 6-10 part, composite modifier 0.5-0.8 part.
5. a kind of house decoraton negative ion plate according to claim 4, it is characterized in that, described middle plate is obtained by following component: 20 parts, magnesium oxide, Adlerika 25 parts, 2 parts, flyash, wood chip 8 parts, composite modifier 0.8 part.
6. a kind of house decoraton negative ion plate according to claim 1, is characterized in that, the concentration 25 ~ 50% of described Adlerika.
7. a kind of house decoraton negative ion plate according to claim 6, is characterized in that, the concentration of described Adlerika is 40%.
8. a kind of house decoraton negative ion plate according to claim 1, it is characterized in that, the raw material of described panel and middle plate also comprises coal gangue.
9. a kind of house decoraton negative ion plate according to claim 1, is characterized in that, the flat method of described negative ion plate roller or laminating preparation.