CN105568459A - Static-free polyvinyl alcohol fiber - Google Patents
Static-free polyvinyl alcohol fiber Download PDFInfo
- Publication number
- CN105568459A CN105568459A CN201510994793.8A CN201510994793A CN105568459A CN 105568459 A CN105568459 A CN 105568459A CN 201510994793 A CN201510994793 A CN 201510994793A CN 105568459 A CN105568459 A CN 105568459A
- Authority
- CN
- China
- Prior art keywords
- vinal
- electrostatic
- accounts
- mass percent
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a static-free polyvinyl alcohol fiber. The static-free polyvinyl alcohol fiber comprises a polyvinyl alcohol fiber, a plant fiber, an animal fiber and a conductive carbon fiber, wherein the polyvinyl alcohol fiber accounts for 32-50% by mass of the static-free polyvinyl alcohol fiber; the plant fiber accounts for 13-18% by mass of the static-free polyvinyl alcohol fiber; the animal fiber accounts for 10-15% by mass of the static-free polyvinyl alcohol fiber; and the conductive carbon fiber accounts for 27-35% by mass of the static-free polyvinyl alcohol fiber. Therefore, the polyvinyl alcohol fiber has the advantage of no static electricity.
Description
Technical field
The present invention relates to chemical fibre field, particularly relate to a kind of without electrostatic vinal.
Background technology
Take polyvinyl alcohol as the synthetic fiber that raw material spinning obtains.By this fiber through vinylon that formaldehyde treated obtains, China claims polyvinyl, claims vinylon in the world.Be raw material through the fiber that spinning is obtained than lower molecular weight polyethylene alcohol be water miscible, be called water-soluble polyvinyl alcohol fibers.General vinal does not possess necessary hot water resistance, and actual application value is little.Vinylon has softness, the characteristic such as warming, and especially hydroscopicity (can reach 5%) is higher in all kinds of synthetic fiber, therefore has the title of synthesis cotton; But its poor heat resistance, softening point only has 120 DEG C.
Summary of the invention
The technical problem that the present invention mainly solves is to provide a kind of without electrostatic vinal, and vinal can be made to have advantage without electrostatic.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: provide a kind of without electrostatic vinal, comprise: vinal, string, animal fiber and conductive carbon fibre, wherein, described vinal accounts for the 32%-50% of described a kind of mass percent without electrostatic vinal, described string accounts for the 13%-18% of described a kind of mass percent without electrostatic vinal, the described animal fiber being accounts for the 10%-15% of described a kind of mass percent without electrostatic vinal, described conductive carbon fibre accounts for the 27%-35% of described a kind of mass percent without electrostatic vinal.
In a preferred embodiment of the present invention, described string is bast fiber, mainly extracts from flax.
In a preferred embodiment of the present invention, described animal fiber is to consume ox hair for raw material.
In a preferred embodiment of the present invention, described vinal accounts for 45% of described a kind of mass percent without electrostatic vinal.
In a preferred embodiment of the present invention, described string accounts for 15% of described a kind of mass percent without electrostatic vinal.
In a preferred embodiment of the present invention, described in be animal fiber account for 13% of described a kind of mass percent without electrostatic vinal.
In a preferred embodiment of the present invention, described conductive carbon fibre accounts for 27% of described a kind of mass percent without electrostatic vinal.
The invention has the beneficial effects as follows: the present invention solves the electrostatic that vinal and other fiber blends produce, and has also distinctive gloss, fineness and flexibility, improve warmth retention property and feel.
Detailed description of the invention
Below preferred embodiment of the present invention is described in detail, can be easier to make advantages and features of the invention be readily appreciated by one skilled in the art, thus more explicit defining is made to protection scope of the present invention.
Embodiment 1
A kind of without electrostatic vinal, comprise: vinal, string, animal fiber and conductive carbon fibre, wherein, described vinal accounts for the 32%-50% of described a kind of mass percent without electrostatic vinal, described string accounts for the 13%-18% of described a kind of mass percent without electrostatic vinal, the described animal fiber being accounts for the 10%-15% of described a kind of mass percent without electrostatic vinal, described conductive carbon fibre accounts for the 27%-35% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described string is bast fiber, mainly extracts from flax.
Further illustrate, described animal fiber is to consume ox hair for raw material.
Further illustrate, described vinal accounts for 45% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described string accounts for 15% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described in be animal fiber account for 13% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described conductive carbon fibre accounts for 27% of described a kind of mass percent without electrostatic vinal.
Embodiment 2
A kind of without electrostatic vinal, comprise: vinal, string, animal fiber and conductive carbon fibre, wherein, described vinal accounts for the 32%-50% of described a kind of mass percent without electrostatic vinal, described string accounts for the 13%-18% of described a kind of mass percent without electrostatic vinal, the described animal fiber being accounts for the 10%-15% of described a kind of mass percent without electrostatic vinal, described conductive carbon fibre accounts for the 27%-35% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described string is bast fiber, mainly extracts from flax.
Further illustrate, described animal fiber is to consume ox hair for raw material.
Further illustrate, described vinal accounts for 38% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described string accounts for 14% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described in be animal fiber account for 14% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described conductive carbon fibre accounts for 34% of described a kind of mass percent without electrostatic vinal.
Embodiment 3
A kind of without electrostatic vinal, comprise: vinal, string, animal fiber and conductive carbon fibre, wherein, described vinal accounts for the 32%-50% of described a kind of mass percent without electrostatic vinal, described string accounts for the 13%-18% of described a kind of mass percent without electrostatic vinal, the described animal fiber being accounts for the 10%-15% of described a kind of mass percent without electrostatic vinal, described conductive carbon fibre accounts for the 27%-35% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described string is bast fiber, mainly extracts from flax.
Further illustrate, described animal fiber is to consume ox hair for raw material.
Further illustrate, described vinal accounts for 40% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described string accounts for 13% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described in be animal fiber account for 14% of described a kind of mass percent without electrostatic vinal.
Further illustrate, described conductive carbon fibre accounts for 33% of described a kind of mass percent without electrostatic vinal.
The foregoing is only embodiments of the invention; not thereby the scope of the claims of the present invention is limited; every utilize description of the present invention to do equivalent structure or equivalent flow process conversion; or be directly or indirectly used in other relevant technical fields, be all in like manner included in scope of patent protection of the present invention.
Claims (7)
1. one kind without electrostatic vinal, it is characterized in that, comprise: vinal, string, animal fiber and conductive carbon fibre, wherein, described vinal accounts for the 32%-50% of described a kind of mass percent without electrostatic vinal, described string accounts for the 13%-18% of described a kind of mass percent without electrostatic vinal, the described animal fiber being accounts for the 10%-15% of described a kind of mass percent without electrostatic vinal, described conductive carbon fibre accounts for the 27%-35% of described a kind of mass percent without electrostatic vinal.
2. according to claim 1 a kind of without electrostatic vinal, it is characterized in that: described string is bast fiber, mainly extracts from flax.
3. according to claim 1 a kind of without electrostatic vinal, it is characterized in that: described animal fiber is to consume ox hair for raw material.
4. according to claim 1 a kind of without electrostatic vinal, it is characterized in that: described vinal accounts for 45% of described a kind of mass percent without electrostatic vinal.
5. according to claim 1 a kind of without electrostatic vinal, it is characterized in that: described string accounts for 15% of described a kind of mass percent without electrostatic vinal.
6. according to claim 1 a kind of without electrostatic vinal, it is characterized in that: described in be animal fiber account for 13% of described a kind of mass percent without electrostatic vinal.
7. according to claim 1 a kind of without electrostatic vinal, it is characterized in that: described conductive carbon fibre accounts for 27% of described a kind of mass percent without electrostatic vinal.